CN105753506A - 净化与吸附的复合硅藻泥粉末涂料及其制备和施工方法 - Google Patents
净化与吸附的复合硅藻泥粉末涂料及其制备和施工方法 Download PDFInfo
- Publication number
- CN105753506A CN105753506A CN201610085840.1A CN201610085840A CN105753506A CN 105753506 A CN105753506 A CN 105753506A CN 201610085840 A CN201610085840 A CN 201610085840A CN 105753506 A CN105753506 A CN 105753506A
- Authority
- CN
- China
- Prior art keywords
- weight portion
- powder
- diatom ooze
- mesh
- weight
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种净化与吸附的复合硅藻泥粉末涂料及其制备和施工方法,属于建筑材料领域。所述涂料由下述成分按重量比构成:6001000目硅藻土2060重量份、325500目海泡石粉1050重量份、6001000目白云石粉1045重量份、400600目沸石粉1040重量份、8001000目凹凸棒土粉220重量份、8001000目尖晶石粉1045重量份、纳米二氧化钛115重量份、负离子粉0.510重量份、甲基纤维素0.25重量份、可再分散性乳胶粉120重量份、13X粉末状分子筛0.510重量份。本发明解决了现有硅藻泥壁材质感粗糙难以大面积施工、施工速度慢等问题。
Description
技术领域
本发明涉及建筑材料领域,特别是指一种净化与吸附的复合硅藻泥粉末涂料及其制备和施工方法。
背景技术
硅藻泥的主要原材料是硅藻土。硅藻土质地轻柔,富含多种有益矿物质,它的粒子表面有无数微小的孔穴(孔直径约0.1-0.2微米),规则、整齐地排列成圆形和针形,孔隙率高达90%,比表面积高达65㎡/g。这种独特的分子筛结构决定了其具有极强的物理吸附性能和离子交换性能。所以使用硅藻泥作为建筑墙面材料,具有净化空气、调节湿度、释放负氧离子、防火阻燃、墙面自洁、杀菌除臭等功能,受到人们青睐。
目前国内硅藻泥市场已日渐成熟,在装饰装修领域得到了广泛应用。现有的硅藻泥涂料中通常使用各种各样的填料来实现多种功能,但是原料和配比选择不够合理,使得现有的硅藻泥涂料一般质感粗糙,而且大面积施工较困难,施工速度也难以提升,容易造成色差。
发明内容
本发明要解决的技术问题是提供一种质感细腻,易于大面积施工,施工速度快,避免色差的净化与吸附的复合硅藻泥粉末涂料及其制备和施工方法。
为解决上述技术问题,本发明提供技术方案如下:
一方面,提供一种净化与吸附的复合硅藻泥粉末涂料,由下述成分按重量比构成:
600-1000目硅藻土20-60重量份
325-500目海泡石粉10-50重量份
600-1000目白云石粉10-45重量份
400-600目沸石粉10-40重量份
800-1000目凹凸棒土粉2-20重量份
800-1000目尖晶石粉10-50重量份
纳米二氧化钛1-15重量份
负离子粉0.5-10重量份
甲基纤维素0.2-5重量份
可再分散性乳胶粉1-20重量份
13X粉末状分子筛0.5-10重量份。
进一步地,所述涂料由下述成分按重量比构成:
硅藻土25-55重量份
海泡石粉15-40重量份
白云石粉18-35重量份
沸石粉12-30重量份
凹凸棒土粉5-16重量份
尖晶石粉20-40重量份
纳米二氧化钛2-10重量份
负离子粉1-5重量份
甲基纤维素0.5-3重量份
可再分散性乳胶粉2-18重量份
13X粉末状分子筛1-8重量份。
优选地,所述涂料由下述成分按重量比构成
硅藻土30-50重量份
海泡石粉20-35重量份
白云石粉20-30重量份
沸石粉16-25重量份
凹凸棒土粉8-12重量份
尖晶石粉25-35重量份
纳米二氧化钛5-8重量份
负离子粉2-4重量份
甲基纤维素1-2.5重量份
可再分散性乳胶粉5-15重量份
13X粉末状分子筛2-6重量份。
进一步地,所述纳米二氧化钛的粒径为5nm~20nm,纳米二氧化钛优选为金红石型。
优选地,所述负离子粉中,负离子发生量:10000ions1500目。
优选地,甲基纤维素粘度优选为100000mPa.s~200000mPa.s。
优选地,可再分散性乳胶粉优选为乙烯-醋酸乙烯酯共聚物、醋酸乙烯酯-乙烯-叔碳酸乙烯酯共聚物或醋酸乙烯酯-乙烯-甲基丙烯酸甲酯共聚物中的任意一种或多种。
优选地,13X粉末状分子筛静态水吸附量≥23.5%,二氧化碳空气处理量NL/g≥18。
另一方面,本发明还提供了一种上述硅藻泥粉末涂料的制备方法,包括以下步骤:将原料与水混合充分搅拌至均匀。
再一方面,本发明还提供了一种上述硅藻泥粉末涂料的施工方法,包括以下步骤:进行喷涂或滚涂施工。
本发明涉及的净化与吸附的复合硅藻泥粉末涂料的主要材料性能如下:
硅藻土由硅藻的细胞壁沉积而成,质地软而轻,可轻易的磨成粉末,密度低、多孔隙、有粗糙感,有极强的吸水性,是热、声和电的不良导体,因此可作轻质、绝缘、隔音材料,又用作过滤物质、打磨物质、液体的吸附物。
海泡石是含水富镁硅酸盐粘土矿物,收缩率低,可塑性好,比表面大,吸附性强,溶于盐酸、质轻,同时还具有脱色、隔热、绝缘、抗腐蚀、抗辐射及热稳定等性能。
白云石主要用作炼钢时用的转化炉的耐火内层、造渣剂、水泥原料、玻璃熔剂、窑业、肥料、建筑与装饰用石材、油漆、杀虫剂与医药等各种用途,可用于建材、陶瓷、玻璃和耐火材料、化工以及农业、环保、节能等领域。
凹凸棒石在湿时具粘性和可塑性,干燥后收缩小,不大显裂纹,水浸泡崩散,所以常作为涂料的填充剂、流平剂、增稠剂和稳定剂,其性能好,成本低,可代替传统的轻钙。
尖晶石是镁铝氧化物组成的矿物,因为含有镁、铁、锌、锰等元素,不同的尖晶石可以有不同的颜色,具有良好的抗侵蚀,腐蚀、剥落能力强,抗渣性能好,抗磨蚀能力,热震稳定性好,耐高温等性能特点。
沸石是一种含水的碱金属或碱土金属的铝硅酸矿物,它具有吸附性、离子交换性、催化和耐酸耐热等性能,因此被广泛用作吸附剂、离子交换剂和催化剂,也可用于气体的干燥、净化和污水处理等方面。
负离子粉是人类利用自然界产生负离子的原理,人工合成或者配比的一种复合矿物,一般都是电气石粉+镧系元素或者稀土元素,负离子不仅能促成人体合成和储存维生素,强化和激活人体的生理活动,对人体及其他生物的生命活动有着十分重要的影响。
纳米二氧化钛化学性质稳定,在一般情况下与大部分物质不发生反应,是重要的白色颜料和瓷器釉料,与其他白色颜料比较有优越的白度、着色力、遮盖力、耐候性、耐热性、和化学稳定性,特别是没有毒性,广泛应用于涂料、塑料、造纸、印刷油墨、化纤、橡胶、化妆品等工业。
可再分散性乳胶粉为水溶性可再分散粉末,具有极突出的防水性能,粘结强度好,增加砂浆的弹性并有较长之开放时间,赋予砂浆优良的耐碱性,改善砂浆的粘附性/粘合性、抗折强度、可塑性、耐磨性能和施工性外,在柔性抗裂砂浆中更具有较强的柔韧性。
甲基纤维素广泛用于陶瓷制造、涂料业、油墨印刷、医药行业、纸制品业、果蔬保鲜和纺织业中,也可作为硅藻泥墙面腻子中的保水剂、缓凝剂,可延长可操作时间,使硅藻泥在涂抹后不会因干得太快而龟裂,增强硬化后强度,改善硅藻墙面腻子施工流动性能、增加触变与抗垂性、抗水性,施工性及隔热性等。
13X粉末状分子筛是通过改进对原粉、粘合剂配方、成型工艺和优选,二次晶化使高岭土粘结剂转化为分子筛,产品单位吸附容量及强度得到提高。其孔径为吸附小于的任何分子,可用于催化剂协载体、水和二氧化碳共吸附、水和硫化氢气体共吸附,具有吸附容量大、抗压强度大、使用寿命长、再生能耗小等优点。
综上所述,本发明的有益效果表现为:
本发明得到的硅藻泥粉末涂料,选用的硅藻土粒径为600-1000目,能够保留硅藻土自身的微孔结构,起到净化与吸附的作用。本发明采用了完善配比的天然无机矿物原料,绿色环保又降低了材料颗粒尺寸,既保证了涂料上墙后的质感均匀细腻,也能保证硅藻土颗粒的微孔发挥正常的净化与吸附功能。本发明在配方上作出了一系列的调整,不仅在功能上得到了提升,而且在施工性能方面也做出了重大改进,使硅藻泥加水搅拌后直接可喷涂或滚涂,解决了现有的硅藻泥壁材质感粗糙难以大面积施工且施工速度慢,容易造成色差等缺点,更好的促进了新型环保的硅藻泥产业发展。由于整体配方的选择以及各组分目数的选择,使用本发明得到的硅藻泥粉末涂料进行大面积施工时,易于涂刷,干燥迅速,大大提高施工速度,墙面颜色均匀统一。施工性能和粘接性能好,可在不同材质的表面形成涂层,本发明绝大多数使用了无机功能性材料,不含任何有害物质,而且还具有吸附:净化有害气体的功能,并具有调湿性,同时具备色装运输,施工简单的特点。
具体实施方式
本发明提供了一种净化与吸附的复合硅藻泥粉末涂料及其制备和施工方法,为使本发明的目的、技术方案及效果更加清楚、明确,以下对本发明进一步详细说明。应当理解,此处所描述的具体实施例仅仅用以解释本发明,并不用于限定本发明。实施例中未注明具体条件者,按照常规条件或制造商建议的条件进行。所用试剂或仪器未注明生产厂商者,均为可以通过市售购买获得的常规产品。
实施例1
按下述重量份配比称取原料:600目硅藻土25重量份、325目海泡石粉15重量份、600目白云石粉20重量份、400目沸石粉15重量份、800目凹凸棒土粉8重量份、800目尖晶石粉20重量份、纳米二氧化钛2重量份、负离子粉1重量份、甲基纤维素0.5重量份、可再分散性乳胶粉2重量份、13X粉末状分子筛2重量份。将原料与水混合并搅拌均匀,然后喷涂在房屋内墙上,彻底晾干。
实施例2
按下述重量份配比称取原料:600目硅藻土40重量份、325目海泡石粉30重量份、600目白云石粉30重量份、400目沸石粉20重量份、800目凹凸棒土粉12重量份、800目尖晶石粉30重量份、纳米二氧化钛6重量份、负离子粉3重量份、甲基纤维素2重量份、可再分散性乳胶粉8重量份、13X粉末状分子筛6重量份。将原料与水混合并搅拌均匀,然后喷涂在房屋内墙上,彻底晾干。
实施例3
按下述重量份配比称取原料:600目硅藻土50重量份、325目海泡石粉40重量份、600目白云石粉35重量份、400目沸石粉28重量份、800目凹凸棒土粉16重量份、800目尖晶石粉35重量份、纳米二氧化钛10重量份、负离子粉6重量份、甲基纤维素3重量份、可再分散性乳胶粉16重量份、13X粉末状分子筛8重量份。将原料与水混合并搅拌均匀,然后喷涂在房屋内墙上,彻底晾干。
实施例4
按下述重量份配比称取原料:1000目硅藻土25重量份、500目海泡石粉15重量份、1000目白云石粉20重量份、600目沸石粉15重量份、1000目凹凸棒土粉8重量份、1000目尖晶石粉20重量份、纳米二氧化钛2重量份、负离子粉1重量份、甲基纤维素0.5重量份、可再分散性乳胶粉2重量份、13X粉末状分子筛2重量份。将原料与水混合并搅拌均匀,然后喷涂在房屋内墙上,彻底晾干。
实施例5
按下述重量份配比称取原料:1000目硅藻土40重量份、500目海泡石粉30重量份、1000目白云石粉30重量份、600目沸石粉20重量份、1000目凹凸棒土粉12重量份、1000目尖晶石粉30重量份、纳米二氧化钛6重量份、负离子粉3重量份、甲基纤维素2重量份、可再分散性乳胶粉8重量份、13X粉末状分子筛6重量份。将原料与水混合并搅拌均匀,然后喷涂在房屋内墙上,彻底晾干。
实施例6
按下述重量份配比称取原料:1000目硅藻土50重量份、500目海泡石粉40重量份、1000目白云石粉35重量份、600目沸石粉28重量份、1000目凹凸棒土粉16重量份、1000目尖晶石粉35重量份、纳米二氧化钛10重量份、负离子粉6重量份、甲基纤维素3重量份、可再分散性乳胶粉16重量份、13X粉末状分子筛8重量份。将原料与水混合并搅拌均匀,然后喷涂在房屋内墙上,彻底晾干。
其中实施例1~6中的纳米二氧化钛、负离子粉、甲基纤维素、可再分散性乳胶粉在选用本领域技术人员常用的规格时,在施工性能、净化效果方面也能够达到要求,整体效果略低于以下规格的原料:纳米二氧化钛为金红石型,粒径5nm~20nm;负离子粉中,负离子发生量:10000ions 1500目;甲基纤维素粘度为100000mPa.s~200000mPa.s;可再分散性乳胶粉为乙烯-醋酸乙烯酯共聚物、醋酸乙烯酯-乙烯-叔碳酸乙烯酯共聚物或醋酸乙烯酯-乙烯-甲基丙烯酸甲酯共聚物中的任意一种或多种;13X粉末状分子筛静态水吸附量≥23.5%,二氧化碳空气处理量NL/g≥18。
经检测实施例1-6硅藻泥涂料,施工性方面,以平常工人手刮10平方米为例,需30分钟。本发明硅藻泥涂料经直接配涂之后,3-5分钟即可完工。而且施工质量比手刮效果整体性好,手感更细腻,色泽均匀。功能性方面,甲醛的净化性能(%)≥83,标准要求(I类)≥75,超过国家指标要求。由测试结果可以看出,本发明硅藻泥涂料兼顾功能性和施工性,能够达到净化室内空气,吸附甲醛的效果,并且表面质感细腻,在大面积施工中涂料干燥迅速,不仅提高了施工速度,还能保证颜色均匀。
以上所述是本发明的优选实施方式,应当指出,对于本技术领域的普通技术人员来说,在不脱离本发明所述原理的前提下,还可以作出若干改进和润饰,这些改进和润饰也应视为本发明的保护范围。
Claims (10)
1.一种净化与吸附的复合硅藻泥粉末涂料,其特征在于,由下述成分按重量比构成:600-1000目硅藻土20-60重量份、325-500目海泡石粉10-50重量份、600-1000目白云石粉10-45重量份、400-600目沸石粉10-40重量份、800-1000目凹凸棒土粉2-20重量份、800-1000目尖晶石粉10-50重量份、纳米二氧化钛1-15重量份、负离子粉0.5-10重量份、甲基纤维素0.2-5重量份、可再分散性乳胶粉1-20重量份、13X粉末状分子筛0.5-10重量份。
2.根据权利要求1所述的净化与吸附的复合硅藻泥粉末涂料,其特征在于,硅藻土25-55重量份、海泡石粉15-40重量份、白云石粉18-35重量份、沸石粉12-30重量份、凹凸棒土粉5-16重量份、尖晶石粉20-40重量份、纳米二氧化钛2-10重量份、负离子粉1-5重量份、甲基纤维素0.5-3重量份、可再分散性乳胶粉2-18重量份、13X粉末状分子筛1-8重量份。
3.根据权利要求2所述的净化与吸附的复合硅藻泥粉末涂料,其特征在于,硅藻土30-50重量份、海泡石粉20-35重量份、白云石粉20-30重量份、沸石粉16-25重量份、凹凸棒土粉8-12重量份、尖晶石粉25-35重量份、纳米二氧化钛5-8重量份、负离子粉2-4重量份、甲基纤维素1-2.5重量份、可再分散性乳胶粉5-15重量份、13X粉末状分子筛2-6重量份。
4.根据权利要求1至3任一所述的净化与吸附的复合硅藻泥粉末涂料,其特征在于,所述纳米二氧化钛的粒径为5nm~20nm。
5.根据权利要求1至3任一所述的净化与吸附的复合硅藻泥粉末涂料,其特征在于,所述负离子粉中,负离子发生量:10000ions 1500目。
6.根据权利要求1至3任一所述的净化与吸附的复合硅藻泥粉末涂料,其特征在于,所述甲基纤维素粘度为100000mPa.s~200000mPa.s。
7.根据权利要求1至3任一所述的净化与吸附的复合硅藻泥粉末涂料,其特征在于,所述可再分散性乳胶粉为乙烯-醋酸乙烯酯共聚物、醋酸乙烯酯-乙烯-叔碳酸乙烯酯共聚物或醋酸乙烯酯-乙烯-甲基丙烯酸甲酯共聚物中的任意一种或多种。
8.根据权利要求1至3任一所述的净化与吸附的复合硅藻泥粉末涂料,其特征在于,13X粉末状分子筛静态水吸附量≥23.5%,二氧化碳空气处理量NL/g≥18。
9.权利要求1-8中任一所述的净化与吸附的复合硅藻泥粉末涂料的制备方法,其特征在于,将原料与水混合充分搅拌至均匀。
10.权利要求9所制得的净化与吸附的复合硅藻泥粉末涂料的施工方法,其特征在于,进行喷涂或滚涂施工。