CN107814520A - 一种硅藻泥装饰材料及其制备方法 - Google Patents
一种硅藻泥装饰材料及其制备方法 Download PDFInfo
- Publication number
- CN107814520A CN107814520A CN201711116572.6A CN201711116572A CN107814520A CN 107814520 A CN107814520 A CN 107814520A CN 201711116572 A CN201711116572 A CN 201711116572A CN 107814520 A CN107814520 A CN 107814520A
- Authority
- CN
- China
- Prior art keywords
- parts
- ornament materials
- diatom ooze
- ooze ornament
- materials according
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种硅藻泥装饰材料及其制备方法，所述硅藻泥装饰材料由以下重量份的原料组成：硅藻土40‑60份、坡缕石1.0‑1.5份、硅酸镁3.0‑3.5份、纤维素1.5‑2份、重质碳酸钙50‑60份、粗砂20‑25份、灰钙粉4‑5份、纳米二氧化钛2.0‑2.5份、抗菌剂1‑3份、消泡剂0.2‑0.4份。本发明制得的硅藻泥装饰材料无需添加化学胶黏剂，无胶上墙，绿色环保，具有较好的吸湿性和保温增氧效果，并且还具有较好的吸附效果和墙面肌理感，绿色环保，综合效果好。
Description
技术领域
本发明涉及硅藻泥装饰材料技术领域，具体涉及一种硅藻泥装饰材料及其制备方法。
背景技术
目前，随着经济发展和人们生活水平的不断提高，墙面装饰涂料得到了广泛使用。由于室内装修的墙面装饰涂料使用了大量的化学物质，引发了“室内装修污染综合症”，严重影响了人们的身体健康。因此市场上出现了一种墙面装饰涂料，该涂料以无机多孔粉体为主要成份，其优点是不会损害人们的身体健康。
但是，上述这些无机多孔粉体涂料为了能够与墙面牢固结合，往往在配方中添加了化学胶黏剂。所添加的化学胶黏剂将这些涂料原有的微孔全部堵死，造成涂料结板固化而失去原有的过滤吸附功能，并且胶黏剂本身还会释放甲醛等有害物质，不属于真正的环保绿色的产品。
发明内容
本发明的目的在于提供一种硅藻泥装饰材料，一种以硅藻泥等无机多孔粉体为主要成分且无须添加化学胶黏剂的室内用建材。
为实现上述目的，本发明的技术方案为：
一种硅藻泥装饰材料，所述硅藻泥装饰材料由以下重量份的原料组成：硅藻土40-60份、坡缕石1.0-1.5份、硅酸镁3.0-3.5份、纤维素1.5-2份、重质碳酸钙50-60份、粗砂20-25份、灰钙粉4-5份、纳米二氧化钛2.0-2.5份、抗菌剂1-3份、消泡剂0.2-0.4份。
优选地，所述硅藻泥装饰材料由以下重量份的原料组成:硅藻土45份、坡缕石1.2份、硅酸镁3.2份、纤维素1.6份、重质碳酸钙55份、粗砂2份、灰钙粉4.5份、纳米二氧化钛2.2份、抗菌剂2份、消泡剂0.3份。
优选地，所述硅藻土的粒径不大于5000目。
优选地，所述坡缕石的粒径不大于400目。
优选地，所述纤维素的长度为1-4mm。
优选地，所述粗砂为7#粗砂。
更进一步地，所述抗菌剂为纳米氧化锌或氧化铜。
其中，所述消泡剂可以选择乳化硅油、聚氧乙烯聚氧丙醇胺醚、聚氧丙烯甘油醚或聚二甲基硅氧烷中的一种或两种。
上述硅藻泥装饰材料的制备方法是将各原料按其重量比称重混合，将其加入搅拌机搅拌15～25分钟，混合均匀后，装入5公斤塑料袋中，包装出厂。
施工方法：将成品袋中所装的全部材料加入盛20公升的塑料桶中，加入1∶1比例的清水，用电动搅拌机将桶中材料搅拌成稠状。用泥板刀涂刮在腻子打磨平整的墙面、玻璃、木板上，待六成干时用专用工具做出各种肌理，也可做成平面印花。刮涂后的泥面4小时表面即干燥，24小时后可干透。
本发明主要材料性能如下：
1)硅藻是最早在地球上出现的一种单细胞藻类，生存在海水或者湖水中，形体极为微小，一般只有几微米到十几微米。硅藻能进行光合作用，自制有机物，常常以惊人的速度生长繁殖，它的遗骸沉积形成硅藻土。硅藻土主要成分是硅酸质，表面有无数细孔，可吸附、分解空气中的异味，具有调湿、除臭功能。采用硅藻土为原料所生产的建材，不仅具有不燃、除湿、除臭和通透性好的特点，而且还能够净化空气、隔音、防水和隔热，并且成本也不高。
2)坡缕石，又叫凹凸棒土，是指以凹凸棒石为主要组分的一种粘土矿物。凹凸棒石呈土状、致密块状产于沉积岩和风化壳中，颜色呈白色，灰白色，青灰色，灰绿色或弱丝绢光泽。土质细腻，有油脂滑感，质轻、性脆，断口呈贝壳状或参差状，吸水性强。具有很大的比表面积和吸附能力，很好的流变性和催化性能，同时，具有理想的胶体性能和耐热性能，是一种少见的矿物。湿时具粘性和可塑性，干燥后收缩小，不大显裂纹，水浸泡崩散。凹凸棒石作为涂料的填充剂、流平剂、增稠剂和稳定剂，其性能好，成本低，可代替传统的轻钙。凹凸棒石涂料的涂膜在电镜里观察，其晶体呈网状排列，均匀地分布在有机粘结剂中，所以涂膜耐洗擦。尤其是凹土在外力搅拌下分散性好，形成稳定的不被电解质破坏的悬浮液，使涂料不沉淀、不分层，与传统的106涂料相比较，具有多种优越性：涂刷性能好，不流挂，节约钛白粉的用量，还可作油漆的填料，墙板材料的填料，生产天花板墙壁板，其特点是：对水份接受、排放性能强，不膨胀不变形，粘结性能好，质轻韧性大，具有隔热保暖、吸声的作用，可防虫蛀，抗垂度强，能适应空气温度的变化，且不变形。
3)硅酸镁在本发明的装饰材料中主要起到保温的效果。
4)纤维素在本发明的装饰材料中主要起到装饰的效果。
5)重质碳酸钙是由天然碳酸盐矿物如方解石、大理石、石灰石磨碎而成。是常用的粉状无机填料，具有化学纯度高、惰性大、不易化学反应、热稳定性好、在400℃以下不会分解、白度高、吸油率低、折光率低、质软、干燥、不含结晶水、硬度低磨耗值小、无毒、无味、无臭、分散性好等优点。用在本发明的装饰材料中不仅可以降低生产成本，还可以增加产品的韧性和强度。
6)粗砂是指粒径大于0.5mm的颗粒含量超过权重的50％的砂石，在本发明的装饰材料中主要起到降低成本的作用。
7)灰钙粉是由以CaCO3为主要成分的天然优质石灰石，经高温煅烧后成为生石灰(CaO)后，再经精选，部分消化，然后再通过高速风选锤式粉碎机粉碎而成的，其表观洁白细腻，灰钙粉能够在较低的成本下赋予涂料优异性能，在本发明的装饰材料中主要起到降低成本的作用。
8)纳米二氧化钛是白色固体或粉末状的两性氧化物，是一种白色无机颜料，具有无毒、最佳的不透明性、最佳白度和光亮度，被认为是目前世界上性能最好的一种白色颜料。钛白的粘附力强，不易起化学变化，永远是雪白的，在本发明的装饰材料中能够起到增白装饰材料的作用。
本发明方法具有如下优点：
本发明通过采用合适的原料及其配比，制得的装饰材料美观、大方，结实耐用，并且无甲醛等有害物质，还能够保持天然材料的多孔结构，具有吸附、吸湿性能，可消除室内污染、调节室内湿度、消除异味、隔离噪音，涂饰表面肌理感强，防火阻燃，是一种更新换代的绿色环保建材。
本发明制得的硅藻泥装饰材料无需添加化学胶黏剂，无胶上墙，绿色环保，具有较好的吸湿性和保温增氧效果，并且还具有较好的吸附效果和墙面肌理感，绿色环保，综合效果好。
具体实施方式
下面将通过具体实施例对本发明进行详细的描述。提供这些实施例是为了能够更透彻地理解本发明，并且能够将本发明的范围完整的传达给本领域的技术人员。
如在通篇说明书及权利要求当中所提及的“包含”或“包括”为一开放式用语，故应解释成“包含但不限定于”。说明书后续描述为实施本发明的较佳实施方式，然所述描述乃以说明书的一般原则为目的，并非用以限定本发明的范围。本发明的保护范围当视所附权利要求所界定者为准。
以下实施例所选用的原料如无特殊说明均能从市场上购买，下面将用具体的例子对本发明做进一步详尽的描述。
实施例1
一种硅藻泥装饰材料，所述硅藻泥装饰材料由以下重量份的原料组成：硅藻土60份、坡缕石1.5份、硅酸镁3.0份、纤维素1.5份、重质碳酸钙50份、粗砂25份、灰钙粉4份、纳米二氧化钛2.5份、抗菌剂1份、消泡剂0.4份。
本实施例所选的硅藻土的粒径为6000目，所述坡缕石的粒径为500目，所述纤维素的长度为2mm，所述粗砂为7#粗砂，所述抗菌剂为氧化铜，所述消泡剂选择聚氧乙烯聚氧丙醇胺醚。
上述硅藻泥装饰材料的制备方法是将各原料按其重量比称重混合，将其加入搅拌机搅拌15分钟，混合均匀后，装入5公斤塑料袋中，包装出厂。
施工方法：将成品袋中所装的全部材料加入盛20公升的塑料桶中，加入1∶1比例的清水，用电动搅拌机将桶中材料搅拌成稠状。用泥板刀涂刮在腻子打磨平整的墙面、玻璃、木板上，待六成干时用专用工具做出各种肌理，也可做成平面印花。刮涂后的泥面4小时表面即干燥，24小时后可干透。
实施例2
一种硅藻泥装饰材料，所述硅藻泥装饰材料由以下重量份的原料组成：硅藻土40份、坡缕石1.0份、硅酸镁3.5份、纤维素1.5份、重质碳酸钙60份、粗砂20份、灰钙粉4份、纳米二氧化钛2.0份、抗菌剂1份、消泡剂0.2份。
本实施例所选的硅藻土的粒径为8000目，所述坡缕石的粒径为400目，所述纤维素的长度为1mm，所述粗砂为7#粗砂，所述抗菌剂为纳米氧化锌，所述消泡剂选择乳化硅油。
上述硅藻泥装饰材料的制备方法是将各原料按其重量比称重混合，将其加入搅拌机搅拌15分钟，混合均匀后，装入5公斤塑料袋中，包装出厂。
施工方法：将成品袋中所装的全部材料加入盛20公升的塑料桶中，加入1∶1比例的清水，用电动搅拌机将桶中材料搅拌成稠状。用泥板刀涂刮在腻子打磨平整的墙面、玻璃、木板上，待六成干时用专用工具做出各种肌理，也可做成平面印花。刮涂后的泥面4小时表面即干燥，24小时后可干透。
实施例3
一种硅藻泥装饰材料，所述硅藻泥装饰材料由以下重量份的原料组成：硅藻土45份、坡缕石1.2份、硅酸镁3.2份、纤维素1.6份、重质碳酸钙55份、粗砂2份、灰钙粉4.5份、纳米二氧化钛2.2份、抗菌剂2份、消泡剂0.3份。
本实施例所选用的硅藻土的粒径为10000目，坡缕石的粒径为600目，所述纤维素的长度为1mm，所述粗砂为7#粗砂，所述抗菌剂为纳米氧化锌。所述消泡剂为乳化硅油和聚氧丙烯甘油醚以1:1的体积比混合。
上述硅藻泥装饰材料的制备方法是将各原料按其重量比称重混合，将其加入搅拌机搅拌20分钟，混合均匀后，装入5公斤塑料袋中，包装出厂。
施工方法：将成品袋中所装的全部材料加入盛20公升的塑料桶中，加入1∶1比例的清水，用电动搅拌机将桶中材料搅拌成稠状。用泥板刀涂刮在腻子打磨平整的墙面、玻璃、木板上，待六成干时用专用工具做出各种肌理，也可做成平面印花。刮涂后的泥面4小时表面即干燥，24小时后可干透。
实施例4
一种硅藻泥装饰材料，所述硅藻泥装饰材料由以下重量份的原料组成：硅藻土50份、坡缕石1.2份、硅酸镁3.2份、纤维素1.8份、重质碳酸钙58份、粗砂21份、灰钙粉4.2份、纳米二氧化钛2.3份、抗菌剂1.5份、消泡剂0.4份。
本实施例所选的硅藻土的粒径为8000目，坡缕石的粒径为450目，所述纤维素的长度为4mm，所述粗砂为7#粗砂，所述抗菌剂为氧化铜，所述消泡剂为聚氧乙烯聚氧丙醇胺醚和聚二甲基硅氧烷以1:2的体积比混合。
上述硅藻泥装饰材料的制备方法是将各原料按其重量比称重混合，将其加入搅拌机搅拌25分钟，混合均匀后，装入5公斤塑料袋中，包装出厂。
施工方法：将成品袋中所装的全部材料加入盛20公升的塑料桶中，加入1∶1比例的清水，用电动搅拌机将桶中材料搅拌成稠状。用泥板刀涂刮在腻子打磨平整的墙面、玻璃、木板上，待六成干时用专用工具做出各种肌理，也可做成平面印花。刮涂后的泥面4小时表面即干燥，24小时后可干透。
本发明制得的硅藻泥装饰材料无需添加化学胶黏剂，无胶上墙，绿色环保，具有较好的吸湿性和保温增氧效果，并且还具有较好的吸附效果和墙面肌理感，绿色环保，综合效果好。
虽然，上文中已经用一般性说明及具体实施例对本发明作了详尽的描述，但在本发明基础上，可以对之作一些修改或改进，这对本领域技术人员而言是显而易见的。因此，在不偏离本发明精神的基础上所做的这些修改或改进，均属于本发明要求保护的范围。
Claims (9)
1.一种硅藻泥装饰材料，其特征在于，所述硅藻泥装饰材料由以下重量份的原料组成：硅藻土40-60份、坡缕石1.0-1.5份、硅酸镁3.0-3.5份、纤维素1.5-2份、重质碳酸钙50-60份、粗砂20-25份、灰钙粉4-5份、纳米二氧化钛2.0-2.5份、抗菌剂1-3份和消泡剂0.2-0.4份。
2.根据权利要求1所述的硅藻泥装饰材料，其特征在于，所述硅藻泥装饰材料由以下重量份的原料组成:硅藻土45份、坡缕石1.2份、硅酸镁3.2份、纤维素1.6份、重质碳酸钙55份、粗砂2份、灰钙粉4.5份、纳米二氧化钛2.2份、抗菌剂2份和消泡剂0.3份。
3.根据权利要求1或2所述的硅藻泥装饰材料，其特征在于，所述硅藻土的粒径不大于5000目。
4.根据权利要求1或2所述的硅藻泥装饰材料，其特征在于，所述坡缕石的粒径不大于400目。
5.根据权利要求1或2所述的硅藻泥装饰材料，其特征在于，所述纤维素的长度为1-4mm。
6.根据权利要求1或2所述的硅藻泥装饰材料，其特征在于，所述粗砂为7#粗砂。
7.根据权利要求1或2所述的硅藻泥装饰材料，其特征在于，所述抗菌剂为纳米氧化锌或氧化铜。
8.根据权利要求1或2所述的硅藻泥装饰材料，其特征在于，所述消泡剂为乳化硅油、聚氧乙烯聚氧丙醇胺醚、聚氧丙烯甘油醚或聚二甲基硅氧烷中的一种或两种。
9.一种权利要求1-8任一项所述硅藻泥装饰材料的制备方法，其特征在于，所述制备方法是将各原料按其重量比称重混合，将其加入搅拌机搅拌15～25分钟，混合均匀后，装入5公斤塑料袋中，包装出厂。