CN105908303A - Preparation method of summer skinny skirt fabric - Google Patents

Preparation method of summer skinny skirt fabric Download PDF

Info

Publication number
CN105908303A
CN105908303A CN201610372249.4A CN201610372249A CN105908303A CN 105908303 A CN105908303 A CN 105908303A CN 201610372249 A CN201610372249 A CN 201610372249A CN 105908303 A CN105908303 A CN 105908303A
Authority
CN
China
Prior art keywords
expanded vermiculite
vermiculite powder
summer
preparation
powder
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201610372249.4A
Other languages
Chinese (zh)
Other versions
CN105908303B (en
Inventor
包新姐
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
CHANGXING ZHIHENG CLOTHING MATERIAL Co Ltd
Original Assignee
CHANGXING ZHIHENG CLOTHING MATERIAL Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by CHANGXING ZHIHENG CLOTHING MATERIAL Co Ltd filed Critical CHANGXING ZHIHENG CLOTHING MATERIAL Co Ltd
Priority to CN201610372249.4A priority Critical patent/CN105908303B/en
Publication of CN105908303A publication Critical patent/CN105908303A/en
Application granted granted Critical
Publication of CN105908303B publication Critical patent/CN105908303B/en
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

The invention provides a preparation method of a summer skinny skirt fabric. Modified polyester fibers, natural fibers and chinlon fibers are blended, the quite good moisture absorption, sweat releasing, skin care, shielding and body shaping effects can be achieved, the fabric has the semi-transparent effect, the skin appears and disappears now and then, and the fabric meets the romantic aesthetic taste of modern females.

Description

Cultivate one's moral character a kind of summer the preparation method of skirt fabric
Technical field
The present invention relates to functional type garment material field, the preparation side of the skirt fabric that particularly relates to cultivate one's moral character a kind of summer Method.
Background technology
Polyster fibre is as most widely used chemical fibre, and it has good fibre-forming performance and mechanical performance, intensity High, fast light, heat-resisting and resistance to acids and bases is good, there is good processability and Yi Fangxing, can pure spin, blending and intertexture.Polyester fabric Washable and wearable, ironing and anti-crease, clothing, home textile, decoration and product with etc. field be widely used.But, polyster fibre is also deposited , fabric not absorbing sweat poor in hygroscopicity, dress have feeling of oppression and heat, anti-static ability difference and easily stain the shortcomings such as dust, the most significantly make The about application of polyster fibre and development.For improving the snugness of fit of polyster fibre, improve the application added value of polyster fibre, It is typically polyster fibre is carried out the improvement of chemically or physically aspect, and then the moisture absorbing and sweat releasing property that endowing terylene fiber is higher, carries High dacron wearing comfort.
Tencel fiber is the wood pulp based on coniferous tree, water and solvent NMMO (4-methyhnorpholine-N-oxide) mixing, adds Heat, to being completely dissolved, will not produce any derivant and chemical action, the direct fabrics through remove impurity, its molecule in course of dissolution Structure is simple carbohydrate.Tencel fiber can decompose in earth completely, environmentally safe；It addition, institute in Sheng Chaning Use amine oxide solvent the most harmless to human body, almost be entirely capable of reclaim, can Reusability, in production contained by material pulp Cellulosic molecule does not play chemical change, no coupling product, discharges outside factory without garbage, is environmental protection or green fiber.This fabric There is good hygroscopicity, comfortableness, drapability and stiffness and dyeability is good, can mix with cotton, hair, fiber crops, nitrile, wash etc. the most again Spin, can spin with RING SPINNING, air spinning, cored, be spun into various cotton and wool type yarn, covering yarn etc..Therefore this fiber can not only be transported In the fabric of underwear produces, the fabric for coat ready-made clothes uses the most extensive.
Summary of the invention
In view of this, it is an object of the invention to provide one there is good moisture permeability, pro-skin performance and cover effect Cultivate one's moral character the summer of fruit the preparation method of skirt fabric.
Cultivate one's moral character a kind of summer the preparation method of skirt fabric, carry out as steps described below:
A, expanded vermiculite are pulverized, and cross 250 mesh sieves, obtain expanded vermiculite powder；
B, expanded vermiculite powder is put in water, add vegetable dyeing agent, expanded vermiculite powder is carried out high-energy ball milling, by centrifugal point From accelerating precipitation, isolate extra-fine grinding precipitate, send extra-fine grinding link back to and again participate in high-energy ball milling；Remove sedimentary Slurry, obtains filter cake by filter pressing；
C, by filter cake under the conditions of 40-50 DEG C be dried 10-15h, the most again under the conditions of 100-120 DEG C be dried 2-5h, received Meter level expanded vermiculite powder；
D, by metering rotating disk nanoscale expanded vermiculite powder and micron order Margarita powder it is quantitatively adding the polyester slice of molten condition In, and within the 3-5s time, polyester slice high speed spinning on spinning-drawing machine is made as-spun fibre, concrete technology condition is: spin Silk temperature 280-300 DEG C, spinning speed is 1350-1450m/min；
E, as-spun fibre using parallel drafting machine shape, i.e. can get modified polyester fibre, drafting multiple is 3-4 times；
F, modified polyester fibre and tencel fiber and nylon fibre are carried out blending, be made into blending blank；
G, blending blank is carried out stamp, rear shaping and drying, obtain skirt fabric of cultivating one's moral character summer.
Preferably, the addition of described tencel fiber is the 8-15% of composite material quality, and the addition of nylon fibre is The 3-5% of composite material quality.
Preferably, the described vegetable dyeing agent in step B is (3-8) with the mass ratio of expanded vermiculite powder: 1.
Preferably, in described step B, being additionally added olive oil, the addition of described olive oil is expanded vermiculite opaque The 10-15% of amount.
Preferably, nanoscale expanded vermiculite powder, micron order Margarita powder and the weight percent of polyester slice in described step D Than being:
Nanoscale expanded vermiculite powder 0.5-0.8%
Micron order Margarita powder 3-5%
Polyester slice surplus.
Preferably, in described step C, the water content of nanoscale expanded vermiculite powder is less than 0.1%.
Cultivate one's moral character a kind of summer provided by the present invention the preparation method of skirt fabric, have the advantage that
1, do not use chemicals, be the tencel preparation method of a kind of environmental protection.
2, use micron order Margarita powder that polyster fibre is modified, obtain ganoid modified polyester fibre, have Pro-skin, the effect of health care.
3, by expanded vermiculite powder and vegetable dyeing agent co-ground, vegetable dyeing agent is entered the stratiform in expanded vermiculite powder Structure, Color is good, and screening effect is good.
4, add olive oil, improve stain dispersion effect in expanded vermiculite powder further, also there is special perfume (or spice) Taste.
5, blended yarn weaved fabric only adds a small amount of tencel fiber and nylon fibre, and the color of polyster fibre is relatively deep, blending Rear color varies less, it is not necessary to dyes further and arranges, environmental protection and energy saving；
6, the blended yarn weaved fabric being made into has that extraordinary moisture absorption is ventilative, pro-skin, cover and slimming effect, and fabric has semi-transparent obvious results Really, flickering, meet the esthetic sentiment that modern female is romantic.
Detailed description of the invention
Embodiment 1
Cultivate one's moral character a kind of summer the preparation method of skirt fabric, carry out as steps described below:
A, expanded vermiculite are pulverized, and cross 250 mesh sieves, obtain expanded vermiculite powder；
B, expanded vermiculite powder is put in water, add vegetable dyeing agent and olive oil, expanded vermiculite powder is carried out high-energy ball milling, logical Cross centrifugation and accelerate precipitation, isolate extra-fine grinding precipitate, send extra-fine grinding link back to and again participate in high-energy ball milling；Remove Sedimentary slurry, obtains filter cake by filter pressing；
C, by filter cake under the conditions of 45 DEG C be dried 12h, the most again under the conditions of 110 DEG C be dried 3h, obtain nanoscale expanded vermiculite Powder；
D, by metering rotating disk nanoscale expanded vermiculite powder and micron order Margarita powder it is quantitatively adding the polyester slice of molten condition In, and within the 3-5s time, polyester slice high speed spinning on spinning-drawing machine is made as-spun fibre, concrete technology condition is: spin Silk temperature 280 DEG C, spinning speed is 1450m/min；
E, as-spun fibre using parallel drafting machine shape, i.e. can get modified polyester fibre, drafting multiple is 4 times；
F, modified polyester fibre and tencel fiber and nylon fibre are carried out blending, be made into blending blank；
G, blending blank is carried out stamp, rear shaping and drying, obtain skirt fabric of cultivating one's moral character summer.
The addition of described tencel fiber is 12%, and the addition of nylon fibre is the 4% of composite material quality.
The described vegetable dyeing agent in step B is 5:1 with the mass ratio of expanded vermiculite powder.
The addition of described olive oil is the 12% of expanded vermiculite powder quality.
In described step D, the percentage by weight of nanoscale expanded vermiculite powder, micron order Margarita powder and polyester slice is:
Nanoscale expanded vermiculite powder 0.6%
Micron order Margarita powder 4%
Polyester slice surplus.
In described step C, the water content of nanoscale expanded vermiculite powder is 0.03%.
Embodiment 2
Cultivate one's moral character a kind of summer the preparation method of skirt fabric, carry out as steps described below:
A, expanded vermiculite are pulverized, and cross 250 mesh sieves, obtain expanded vermiculite powder；
B, expanded vermiculite powder is put in water, add vegetable dyeing agent and olive oil, expanded vermiculite powder is carried out high-energy ball milling, logical Cross centrifugation and accelerate precipitation, isolate extra-fine grinding precipitate, send extra-fine grinding link back to and again participate in high-energy ball milling；Remove Sedimentary slurry, obtains filter cake by filter pressing；
C, by filter cake under the conditions of 40 DEG C be dried 10h, the most again under the conditions of 120 DEG C be dried 2h, obtain nanoscale expanded vermiculite Powder；
D, by metering rotating disk nanoscale expanded vermiculite powder and micron order Margarita powder it is quantitatively adding the polyester slice of molten condition In, and within the 3-5s time, polyester slice high speed spinning on spinning-drawing machine is made as-spun fibre, concrete technology condition is: spin Silk temperature 300 DEG C, spinning speed is 1350m/min；
E, as-spun fibre using parallel drafting machine shape, i.e. can get modified polyester fibre, drafting multiple is 3 times；
F, modified polyester fibre and tencel fiber and nylon fibre are carried out blending, be made into blending blank；
G, blending blank is carried out stamp, rear shaping and drying, obtain skirt fabric of cultivating one's moral character summer.
The addition of described tencel fiber is 15%, and the addition of nylon fibre is the 3% of composite material quality.
The described vegetable dyeing agent in step B is 3:1 with the mass ratio of expanded vermiculite powder.
The addition of described olive oil is the 10% of expanded vermiculite powder quality.
In described step D, the percentage by weight of nanoscale expanded vermiculite powder, micron order Margarita powder and polyester slice is:
Nanoscale expanded vermiculite powder 0.5%
Micron order Margarita powder 5%
Polyester slice surplus.
In described step C, the water content of nanoscale expanded vermiculite powder is 0.08%.
Embodiment 3
Cultivate one's moral character a kind of summer the preparation method of skirt fabric, carry out as steps described below:
A, expanded vermiculite are pulverized, and cross 250 mesh sieves, obtain expanded vermiculite powder；
B, expanded vermiculite powder is put in water, add vegetable dyeing agent and olive oil, expanded vermiculite powder is carried out high-energy ball milling, logical Cross centrifugation and accelerate precipitation, isolate extra-fine grinding precipitate, send extra-fine grinding link back to and again participate in high-energy ball milling；Remove Sedimentary slurry, obtains filter cake by filter pressing；
C, by filter cake under the conditions of 50 DEG C be dried 10h, the most again under the conditions of 100 DEG C be dried 5h, obtain nanoscale expanded vermiculite Powder；
D, by metering rotating disk nanoscale expanded vermiculite powder and micron order Margarita powder it is quantitatively adding the polyester slice of molten condition In, and within the 3-5s time, polyester slice high speed spinning on spinning-drawing machine is made as-spun fibre, concrete technology condition is: spin Silk temperature 290 DEG C, spinning speed is 1350m/min；
E, as-spun fibre using parallel drafting machine shape, i.e. can get modified polyester fibre, drafting multiple is 3 times；
F, modified polyester fibre and tencel fiber and nylon fibre are carried out blending, be made into blending blank；
G, blending blank is carried out stamp, rear shaping and drying, obtain skirt fabric of cultivating one's moral character summer.
The addition of described tencel fiber is 8%, and the addition of nylon fibre is the 5% of composite material quality.
The described vegetable dyeing agent in step B is 8:1 with the mass ratio of expanded vermiculite powder.
The addition of described olive oil is the 15% of expanded vermiculite powder quality.
In described step D, the percentage by weight of nanoscale expanded vermiculite powder, micron order Margarita powder and polyester slice is:
Nanoscale expanded vermiculite powder 0.5%
Micron order Margarita powder 3%
Polyester slice surplus.
In described step C, the water content of nanoscale expanded vermiculite powder is 0.01%.
The above, the only present invention preferably detailed description of the invention, but protection scope of the present invention is not limited thereto, Any those familiar with the art in the technical scope that the invention discloses, according to technical scheme and Inventive concept equivalent or change in addition, all should contain within protection scope of the present invention.

Claims (6)

1. cultivate one's moral character in summer the preparation method of skirt fabric, it is characterised in that carry out as steps described below:
A, expanded vermiculite are pulverized, and cross 250 mesh sieves, obtain expanded vermiculite powder；
B, expanded vermiculite powder is put in water, add vegetable dyeing agent, expanded vermiculite powder is carried out high-energy ball milling, by centrifugal point From accelerating precipitation, isolate extra-fine grinding precipitate, send extra-fine grinding link back to and again participate in high-energy ball milling；Remove sedimentary Slurry, obtains filter cake by filter pressing；
C, by filter cake under the conditions of 40-50 DEG C be dried 10-15h, the most again under the conditions of 100-120 DEG C be dried 2-5h, received Meter level expanded vermiculite powder；
D, by metering rotating disk nanoscale expanded vermiculite powder and micron order Margarita powder it is quantitatively adding the polyester slice of molten condition In, and within the 3-5s time, polyester slice high speed spinning on spinning-drawing machine is made as-spun fibre, concrete technology condition is: spin Silk temperature 280-300 DEG C, spinning speed is 1350-1450m/min；
E, as-spun fibre using parallel drafting machine shape, i.e. can get modified polyester fibre, drafting multiple is 3-4 times；
F, modified polyester fibre and tencel fiber and nylon fibre are carried out blending, be made into blending blank；
G, blending blank is carried out stamp, rear shaping and drying, obtain skirt fabric of cultivating one's moral character summer.
2. cultivate one's moral character summer as claimed in claim 1 the preparation method of skirt fabric, it is characterised in that in described step B Vegetable dyeing agent is (3-8) with the mass ratio of expanded vermiculite powder: 1.
3. cultivate one's moral character summer as claimed in claim 1 the preparation method of skirt fabric, it is characterised in that in described step B, also Adding olive oil, the addition of described olive oil is the 10-15% of expanded vermiculite powder quality.
4. cultivate one's moral character summer as claimed in claim 1 the preparation method of skirt fabric, it is characterised in that described step D is received The percentage by weight of meter level expanded vermiculite powder, micron order Margarita powder and polyester slice is:
Nanoscale expanded vermiculite powder 0.5-0.8%
Micron order Margarita powder 3-5%
Polyester slice surplus.
5. cultivate one's moral character summer as claimed in claim 1 the preparation method of skirt fabric, it is characterised in that in described step C, receive The water content of meter level expanded vermiculite powder is less than 0.1%.
6. cultivate one's moral character summer as claimed in claim 1 the preparation method of skirt fabric, it is characterised in that described tencel fiber Addition is the 8-15% of composite material quality, and the addition of nylon fibre is the 3-5% of composite material quality.
CN201610372249.4A 2016-05-31 2016-05-31 A kind of summer cultivates one's moral character the preparation method of skirt fabric Active CN105908303B (en)