CN105908303B - A kind of summer cultivates one's moral character the preparation method of skirt fabric - Google Patents
A kind of summer cultivates one's moral character the preparation method of skirt fabric Download PDFInfo
- Publication number
- CN105908303B CN105908303B CN201610372249.4A CN201610372249A CN105908303B CN 105908303 B CN105908303 B CN 105908303B CN 201610372249 A CN201610372249 A CN 201610372249A CN 105908303 B CN105908303 B CN 105908303B
- Authority
- CN
- China
- Prior art keywords
- expanded vermiculite
- vermiculite powder
- summer
- cultivates
- preparation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
Cultivated one's moral character the preparation method of skirt fabric the invention provides a kind of summer, by the way that modified polyester fibre and tencel fiber and nylon fibre are carried out into blending, extraordinary moisture absorbing and sweat releasing, pro-skin, masking and slimming effect can be reached, fabric has translucent effect, it is flickering, meet the romantic esthetic sentiment of modern female.
Description
Technical field
The present invention relates to functional form garment material field, cultivated one's moral character the preparation side of skirt fabric more particularly to a kind of summer
Method.
Background technology
For polyester fiber as most widely used chemical fibre, it has good fibre-forming performance and mechanical performance, intensity
High, fast light, heat-resisting and resistance to acids and bases is good, has good processability and Yi Fangxing, pure can spin, blending and intertexture.Polyester fabric
Washable and wearable, ironing and anti-crease, clothes, home textile, decoration and product with etc. field be widely used.However, polyester fiber is also deposited
Hygroscopicity is poor, absorbing sweat, dress do not have the shortcomings that feeling of oppression and heat, anti-static ability difference and easily stain dust fabric, therefore make significantly
The about application and development of polyester fiber.To improve the snugness of fit of polyester fiber, the application added value of polyester fiber is improved,
The improvement of chemically or physically aspect, and then the moisture absorbing and sweat releasing property that endowing terylene fiber is higher are typically carried out to polyester fiber, is carried
High dacron wearing comfort.
Tencel fiber is wood pulp, water and solvent NMMO (4- methyhnorpholine-N-oxides) mixing based on coniferous tree, is added
Heat will not produce any derivative and chemical action to being completely dissolved in course of dissolution, the direct fabrics through removal of impurities, its molecule
Structure is simple carbohydrate.Tencel fiber can decompose completely in soil, environmentally safe；In addition, institute in production
The amine oxide solvent used is completely harmless to human body, is almost entirely capable of reclaiming, can Reusability, in production contained by material pulp
Cellulosic molecule does not play chemical change, no coupling product, and no discarded object is discharged outside factory, is environmental protection or green fiber.The fabric
With good hygroscopicity, comfortableness, drapability and stiffness and dyeability it is good, in addition and can and cotton, hair, fiber crops, nitrile, wash etc. it is mixed
Spin, various cotton and wool type yarn, covering yarn etc. can be spun into RING SPINNING, air spinning, core spinning.Therefore the fiber can not only be transported
For in the fabric production of underwear, the fabric utilization for coat ready-made clothes to be also very extensive.
The content of the invention
In view of this, it is an object of the invention to provide one kind to have good moisture permeability, pro-skin performance and masking effect
The summer of fruit cultivates one's moral character the preparation method of skirt fabric.
A kind of summer cultivates one's moral character the preparation method of skirt fabric, carries out as steps described below：
A, expanded vermiculite is crushed, and is crossed 250 mesh sieves, is obtained expanded vermiculite powder；
B, expanded vermiculite powder is put into water, add vegetable dyeing agent, to expanded vermiculite powder carry out high-energy ball milling, by from
Heart separation accelerates precipitation, isolates extra-fine grinding sediment, sends extra-fine grinding link back to and participate in high-energy ball milling again；Remove precipitation
The slurry of thing, filter cake is obtained by press filtration；
C, filter cake is dried into 10-15h under the conditions of 40-50 DEG C, then dries 2-5h under the conditions of 100-120 DEG C again, obtain
To nanoscale expanded vermiculite powder；
D, the polyester of molten condition is quantitatively adding by measuring rotating disk by nanoscale expanded vermiculite powder and micron order pearl powder
In section, and within the 3-5s times, by polyester slice, as-spun fibre, concrete technology condition is made in high speed spinning on spinning-drawing machine
For：280-300 DEG C of spinning temperature, spinning speed 1350-1450m/min；
E, as-spun fibre is shaped using parallel drafting machine, you can obtain modified polyester fibre, drafting multiple 3-4
Times；
F, modified polyester fibre and tencel fiber and nylon fibre are subjected to blending, are made into blending blank；
G, blending blank is subjected to stamp, rear shaping and drying, obtaining summer cultivates one's moral character skirt fabric.
Preferably, the addition of described tencel fiber is the 8-15% of composite material quality, and the addition of nylon fibre is
The 3-5% of composite material quality.
Preferably, the mass ratio of the vegetable dyeing agent in described step B and expanded vermiculite powder is（3-8）：1.
Preferably, in described step B, olive oil is additionally added, the addition of described olive oil is expanded vermiculite silty
The 10-15% of amount.
Preferably, in described step D nanoscale expanded vermiculite powder, micron order pearl powder and polyester slice weight percent
Than for：
Nanoscale expanded vermiculite powder 0.5-0.8%
Micron order pearl powder 3-5%
Polyester slice surplus.
Preferably, in described step C, the water content of nanoscale expanded vermiculite powder is less than 0.1%.
A kind of summer provided by the present invention cultivates one's moral character the preparation method of skirt fabric, has the following advantages that：
1st, it is a kind of environmentally friendly tencel preparation method without using chemicals.
2nd, polyester fiber is modified using micron order pearl powder, obtains the smooth modified polyester fibre in surface, have
Pro-skin, the effect of health care.
3rd, by expanded vermiculite powder and vegetable dyeing agent co-ground, the stratiform that vegetable dyeing agent is entered in expanded vermiculite powder
Structure, Color is good, and screening effect is good.
4th, olive oil is added, further improves dispersion effect of the coloring agent in expanded vermiculite powder, is also had special fragrant
Taste.
5th, a small amount of tencel fiber and nylon fibre are only added in blended yarn weaved fabric, and the color of polyester fiber is deeper, blending
Color change very little afterwards, further dye and arrange, environmental protection and energy saving without carrying out；
6th, there is the blended yarn weaved fabric being made into ventilative extraordinary moisture absorption, pro-skin, masking and slimming effect, fabric to have semi-transparent
Obvious results fruit, it is flickering, meet the romantic esthetic sentiment of modern female.
Embodiment
Embodiment 1
A kind of summer cultivates one's moral character the preparation method of skirt fabric, carries out as steps described below：
A, expanded vermiculite is crushed, and is crossed 250 mesh sieves, is obtained expanded vermiculite powder；
B, expanded vermiculite powder is put into water, adds vegetable dyeing agent and olive oil, high energy ball is carried out to expanded vermiculite powder
Mill, accelerate precipitation by centrifuging, isolate extra-fine grinding sediment, send extra-fine grinding link back to and participate in high energy ball again
Mill；The slurry of sediment is removed, filter cake is obtained by press filtration；
C, filter cake is dried into 12h under the conditions of 45 DEG C, then dries 3h under the conditions of 110 DEG C again, obtain nanoscale expansion
Vermiculite power；
D, the polyester of molten condition is quantitatively adding by measuring rotating disk by nanoscale expanded vermiculite powder and micron order pearl powder
In section, and within the 3-5s times, by polyester slice, as-spun fibre, concrete technology condition is made in high speed spinning on spinning-drawing machine
For：280 DEG C of spinning temperature, spinning speed 1450m/min；
E, as-spun fibre is shaped using parallel drafting machine, you can obtain modified polyester fibre, drafting multiple 4
Times；
F, modified polyester fibre and tencel fiber and nylon fibre are subjected to blending, are made into blending blank；
G, blending blank is subjected to stamp, rear shaping and drying, obtaining summer cultivates one's moral character skirt fabric.
The addition of described tencel fiber is 12%, and the addition of nylon fibre is the 4% of composite material quality.
The mass ratio of vegetable dyeing agent and expanded vermiculite powder in described step B is 5：1.
The addition of described olive oil is the 12% of expanded vermiculite powder quality.
The percentage by weight of nanoscale expanded vermiculite powder, micron order pearl powder and polyester slice is in described step D：
Nanoscale expanded vermiculite powder 0.6%
Micron order pearl powder 4%
Polyester slice surplus.
In described step C, the water content of nanoscale expanded vermiculite powder is 0.03%.
Embodiment 2
A kind of summer cultivates one's moral character the preparation method of skirt fabric, carries out as steps described below：
A, expanded vermiculite is crushed, and is crossed 250 mesh sieves, is obtained expanded vermiculite powder；
B, expanded vermiculite powder is put into water, adds vegetable dyeing agent and olive oil, high energy ball is carried out to expanded vermiculite powder
Mill, accelerate precipitation by centrifuging, isolate extra-fine grinding sediment, send extra-fine grinding link back to and participate in high energy ball again
Mill；The slurry of sediment is removed, filter cake is obtained by press filtration；
C, filter cake is dried into 10h under the conditions of 40 DEG C, then dries 2h under the conditions of 120 DEG C again, obtain nanoscale expansion
Vermiculite power；
D, the polyester of molten condition is quantitatively adding by measuring rotating disk by nanoscale expanded vermiculite powder and micron order pearl powder
In section, and within the 3-5s times, by polyester slice, as-spun fibre, concrete technology condition is made in high speed spinning on spinning-drawing machine
For：300 DEG C of spinning temperature, spinning speed 1350m/min；
E, as-spun fibre is shaped using parallel drafting machine, you can obtain modified polyester fibre, drafting multiple 3
Times；
F, modified polyester fibre and tencel fiber and nylon fibre are subjected to blending, are made into blending blank；
G, blending blank is subjected to stamp, rear shaping and drying, obtaining summer cultivates one's moral character skirt fabric.
The addition of described tencel fiber is 15%, and the addition of nylon fibre is the 3% of composite material quality.
The mass ratio of vegetable dyeing agent and expanded vermiculite powder in described step B is 3：1.
The addition of described olive oil is the 10% of expanded vermiculite powder quality.
The percentage by weight of nanoscale expanded vermiculite powder, micron order pearl powder and polyester slice is in described step D：
Nanoscale expanded vermiculite powder 0.5%
Micron order pearl powder 5%
Polyester slice surplus.
In described step C, the water content of nanoscale expanded vermiculite powder is 0.08%.
Embodiment 3
A kind of summer cultivates one's moral character the preparation method of skirt fabric, carries out as steps described below：
A, expanded vermiculite is crushed, and is crossed 250 mesh sieves, is obtained expanded vermiculite powder；
B, expanded vermiculite powder is put into water, adds vegetable dyeing agent and olive oil, high energy ball is carried out to expanded vermiculite powder
Mill, accelerate precipitation by centrifuging, isolate extra-fine grinding sediment, send extra-fine grinding link back to and participate in high energy ball again
Mill；The slurry of sediment is removed, filter cake is obtained by press filtration；
C, filter cake is dried into 10h under the conditions of 50 DEG C, then dries 5h under the conditions of 100 DEG C again, obtain nanoscale expansion
Vermiculite power；
D, the polyester of molten condition is quantitatively adding by measuring rotating disk by nanoscale expanded vermiculite powder and micron order pearl powder
In section, and within the 3-5s times, by polyester slice, as-spun fibre, concrete technology condition is made in high speed spinning on spinning-drawing machine
For：290 DEG C of spinning temperature, spinning speed 1350m/min；
E, as-spun fibre is shaped using parallel drafting machine, you can obtain modified polyester fibre, drafting multiple 3
Times；
F, modified polyester fibre and tencel fiber and nylon fibre are subjected to blending, are made into blending blank；
G, blending blank is subjected to stamp, rear shaping and drying, obtaining summer cultivates one's moral character skirt fabric.
The addition of described tencel fiber is 8%, and the addition of nylon fibre is the 5% of composite material quality.
The mass ratio of vegetable dyeing agent and expanded vermiculite powder in described step B is 8：1.
The addition of described olive oil is the 15% of expanded vermiculite powder quality.
The percentage by weight of nanoscale expanded vermiculite powder, micron order pearl powder and polyester slice is in described step D：
Nanoscale expanded vermiculite powder 0.5%
Micron order pearl powder 3%
Polyester slice surplus.
In described step C, the water content of nanoscale expanded vermiculite powder is 0.01%.
The foregoing is only a preferred embodiment of the present invention, but protection scope of the present invention be not limited thereto,
Any one skilled in the art the invention discloses technical scope in, technique according to the invention scheme and its
Inventive concept is subject to equivalent substitution or change, should all be included within the scope of the present invention.
Claims (6)
- The preparation method of skirt fabric 1. a kind of summer cultivates one's moral character, it is characterised in that carry out as steps described below：A, expanded vermiculite is crushed, and is crossed 250 mesh sieves, is obtained expanded vermiculite powder；B, expanded vermiculite powder is put into water, adds vegetable dyeing agent, high-energy ball milling is carried out to expanded vermiculite powder, passes through centrifugation point From precipitation is accelerated, extra-fine grinding sediment is isolated, extra-fine grinding link is sent back to and participates in high-energy ball milling again；Remove sediment Slurry, filter cake is obtained by press filtration；C, filter cake is dried into 10-15h under the conditions of 40-50 DEG C, then dries 2-5h under the conditions of 100-120 DEG C again, received Meter level expanded vermiculite powder；D, the polyester slice of molten condition is quantitatively adding by measuring rotating disk by nanoscale expanded vermiculite powder and micron order pearl powder In, and within the 3-5s times, by polyester slice, as-spun fibre is made in high speed spinning on spinning-drawing machine, and concrete technology condition is：Spin 280-300 DEG C of temperature of silk, spinning speed 1350-1450m/min；E, as-spun fibre is shaped using parallel drafting machine, you can obtain modified polyester fibre, drafting multiple is 3-4 times；F, modified polyester fibre and tencel fiber and nylon fibre are subjected to blending, are made into blending blank；G, blending blank is subjected to stamp, rear shaping and drying, obtaining summer cultivates one's moral character skirt fabric.
- The preparation method of skirt fabric 2. summer as claimed in claim 1 cultivates one's moral character, it is characterised in that in described step B The mass ratio of vegetable dyeing agent and expanded vermiculite powder is（3-8）：1.
- The preparation method of skirt fabric 3. summer as claimed in claim 1 cultivates one's moral character, it is characterised in that in described step B, also Olive oil is added, the addition of described olive oil is the 10-15% of expanded vermiculite powder quality.
- The preparation method of skirt fabric 4. summer as claimed in claim 1 cultivates one's moral character, it is characterised in that received in described step D The percentage by weight of meter level expanded vermiculite powder, micron order pearl powder and polyester slice is：Nanoscale expanded vermiculite powder 0.5-0.8%Micron order pearl powder 3-5%Polyester slice surplus.
- The preparation method of skirt fabric 5. summer as claimed in claim 1 cultivates one's moral character, it is characterised in that in described step C, receive The water content of meter level expanded vermiculite powder is less than 0.1%.
- The preparation method of skirt fabric 6. summer as claimed in claim 1 cultivates one's moral character, it is characterised in that described tencel fiber Addition is the 8-15% of composite material quality, and the addition of nylon fibre is the 3-5% of composite material quality.