CN105860750A - 一种高附着力涂料漆 - Google Patents
一种高附着力涂料漆 Download PDFInfo
- Publication number
- CN105860750A CN105860750A CN201610284560.3A CN201610284560A CN105860750A CN 105860750 A CN105860750 A CN 105860750A CN 201610284560 A CN201610284560 A CN 201610284560A CN 105860750 A CN105860750 A CN 105860750A
- Authority
- CN
- China
- Prior art keywords
- paint
- parts
- high adhesion
- resin
- solvent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开一种高附着力涂料漆，包括如下质量份数的组分：环氧树脂30‑50份，聚氨酯树脂5‑15份，溶剂8‑12份，填料10‑20份，流平剂0.5‑2份。本发明提出的配方特定质量的各组分相互配合，制得的涂料具有很强的附着能力，且较高的抗腐蚀性、耐磨损性和固化效果，涂刷后不易开裂和有刷痕。
Description
技术领域
本发明涉及一种涂料，特别涉及一种高附着力涂料漆。
背景技术
目前涂料漆有多种，一般的涂料均是各种性能的折中，特别是一些烘烤成型后需进一步加工，涂料漆的附着力不能满足加工要求，经常导致涂层开裂，甚至脱皮现象。
发明内容
发明目的：针对上述涂料漆存在的问题，本发明提供一种高附着力涂料漆，提高了涂料的附着能力、柔韧性、抗冲击强度。
技术方案：一种高附着力涂料漆，包括如下质量份数的组分：环氧树脂30-50份，聚氨酯树脂5-15份，溶剂8-12份，填料10-20份，流平剂0.5-2份。
优选的，所述高附着力涂料漆包括如下质量份数的组分：环氧树脂45份，聚氨酯树脂12份，溶剂11份，填料16份，流平剂1份。
优选的，所述环氧树脂为双酚A环氧树脂，其工艺性能好，具有较好的耐化学品性、耐水性和硬度，对于各种基材都具有较好的粘接性。聚氨酯树脂具有高强度、耐磨、耐溶剂性，与双酚A环氧树脂配合，提高了涂料漆的附着力、耐磨性和耐高低温性。
优选的，所述高附着力涂料漆还包括3-8份的醇酸树脂，提高了涂料漆的干燥速率、附着力、保光性和耐候性。
优选地，所述溶剂为乙酸丁酯，可用作多种合成树脂的溶剂。
优选的，所述填料为碳酸钙和滑石粉混合物，其质量比为3:2，该混合物提高了涂料漆的柔韧性，减少了漆膜的开裂和粉化。
有益效果：本发明提出的配方特定质量的各组分相互配合，制得的涂料具有很强的附着能力，且较高的抗腐蚀性、耐磨损性和固化效果，涂刷后不易开裂和有刷痕。
具体实施方式
下面结合具体实施例，进一步阐明本发明，应理解这些实施例仅用于说明本发明而不用于限制本发明的范围，在阅读了本发明之后，本领域技术人员对本发明的各种等同变换均落于本申请所附权利要求所限定的范围。
实施例1：
一种高附着力涂料漆，包括如下质量份数的组分：环氧树脂30份，聚氨酯树脂5份，醇酸树脂3份，溶剂8份，填料10份，流平剂0.5份，所述环氧树脂为双酚A环氧树脂，所述溶剂为乙酸丁酯，所述填料为碳酸钙和滑石粉混合物，其质量比为3:2。
实施例2：
一种高附着力涂料漆，包括如下质量份数的组分：环氧树脂50份，聚氨酯树脂15份，醇酸树脂8份，溶剂12份，填料20份，流平剂2份，所述环氧树脂为双酚A环氧树脂，所述溶剂为乙酸丁酯，所述填料为碳酸钙和滑石粉混合物，其质量比为3:2。
实施例3：
一种高附着力涂料漆，包括如下质量份数的组分：环氧树脂45份，聚氨酯树脂12份，溶剂11份，填料16份，流平剂1份，所述环氧树脂为双酚A环氧树脂，所述溶剂为乙酸丁酯，所述填料为碳酸钙和滑石粉混合物，其质量比为3:2。
实施例4：
一种高附着力涂料漆，包括如下质量份数的组分：环氧树脂45份，聚氨酯树脂12份，醇酸树脂6份，溶剂11份，填料16份，流平剂1份，所述环氧树脂为双酚A环氧树脂，所述溶剂为乙酸丁酯，所述填料为碳酸钙和滑石粉混合物，其质量比为3:2。
Claims (6)
1.一种高附着力涂料漆，其特征在于，包括如下质量份数的组分：环氧树脂30-50份，聚氨酯树脂5-15份，溶剂8-12份，填料10-20份，流平剂0.5-2份。
2.根据权利要求1所述的高附着力涂料漆，其特征在于，包括如下质量份数的组分：环氧树脂45份，聚氨酯树脂12份，溶剂11份，填料16份，流平剂1份。
3.根据权利要求1所述的高附着力涂料漆，其特征在于，所述环氧树脂为双酚A环氧树脂。
4.根据权利要求1所述的高附着力涂料漆，其特征在于，所述高附着力涂料漆还包括3-8份的醇酸树脂。
5.根据权利要求1所述的高附着力涂料漆，其特征在于，所述溶剂为乙酸丁酯。
6.根据权利要求1所述的高附着力涂料漆，其特征在于，所述填料为碳酸钙和滑石粉混合物，其质量比为3:2。