CN105838189A - 一种高附着力的涂料配方 - Google Patents

一种高附着力的涂料配方 Download PDF

Info

Publication number
CN105838189A
CN105838189A CN201610284082.6A CN201610284082A CN105838189A CN 105838189 A CN105838189 A CN 105838189A CN 201610284082 A CN201610284082 A CN 201610284082A CN 105838189 A CN105838189 A CN 105838189A
Authority
CN
China
Prior art keywords
parts
formulation
high adhesion
coating material
adhesion force
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201610284082.6A
Other languages
English (en)
Inventor
吴阳
王凤
吴清翠
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Nanjing Chenguang Art Engineering Co Ltd
Original Assignee
Nanjing Chenguang Art Engineering Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Nanjing Chenguang Art Engineering Co Ltd filed Critical Nanjing Chenguang Art Engineering Co Ltd
Priority to CN201610284082.6A priority Critical patent/CN105838189A/zh
Publication of CN105838189A publication Critical patent/CN105838189A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种高附着力的涂料配方，包括如下质量份数的组份：环氧树脂30‑40份，聚氨酯树脂8‑10份，溶剂6‑10份，填料15‑25份，助剂1‑3份。本发明提出的配方特定质量的各组分相互配合，制得的涂料具有很强的附着能力，且干燥时间短、抗腐蚀、耐磨损、固化效果和涂刷效果也好。

Description

一种高附着力的涂料配方
技术领域
本发明涉及一种涂料，特别涉及一种高附着力涂料。
背景技术
雕塑、建筑物、机械、飞机、轮船等涂布涂料的物体，都存在涂料脱落的问题，然而弥补脱落的地方并不是特别容易，因此，对涂料的附着能力提出了更高的要求。
发明内容
发明目的：针对现有涂料存在的问题，本发明提供一种高附着力涂料，有效防止雕塑等物体涂料的脱落现象。
技术方案：一种高附着力的涂料配方，包括如下质量份数的组份：环氧树脂30-40份，聚氨酯树脂8-10份，溶剂6-10份，填料15-25份，助剂1-3份。
优选的，所述高附着力涂料配方包括如下质量份数的组份：环氧树脂38份，聚氨酯树脂8.5份，溶剂8份，填料22份，助剂2份。
优选的，所述环氧树脂为双酚A环氧树脂，其具有很好的沾粘，粘接强度高，并且来源广泛、生产成本低，而聚氨酯树脂具有良好的装饰性和防护性，弥补了双酚A环氧树脂固话脆性大的缺点，提高了涂料的抗冲击强度，使得涂料具备较强的附着力。
优选的，所述溶剂为甲乙酮，蒸发较快，且适用于双酚A环氧树脂和聚氨酯树脂。
优选的，所述填料为滑石粉和石英粉的混合物，其质量比为3:7，该成分提高了涂料的柔韧性和机械强度，消除了固化时的内应力，增强了涂料的附着力。
优选的，所述助剂为分散剂和流平剂的混合物，其质量比为1:1，使涂料具备防起粒、防刷痕、防桔皮的效果。
有益效果：本发明提出的配方特定质量的各组分相互配合，制得的涂料具有很强的附着能力，且干燥时间短、抗腐蚀、耐磨损、固化效果和涂刷效果也好。
具体实施方式
下面结合具体实施例，进一步阐明本发明，应理解这些实施例仅用于说明本发明而不用于限制本发明的范围，在阅读了本发明之后，本领域技术人员对本发明的各种等同变换均落于本申请所附权利要求所限定的范围。
实施例1：
一种高附着力涂料配方，包括如下质量份数的组份：双酚A环氧树脂30份，聚氨酯树脂8份，甲乙酮6份，滑石粉4.5份，石英粉7.5份，分散剂0.5份，流平剂0.5份。
实施例2：
一种高附着力涂料配方，包括如下质量份数的组份：双酚A环氧树脂40份，聚氨酯树脂10份，甲乙酮10份，滑石粉10.5份，石英粉7.5份，分散剂1.5份，流平剂1.5份。
实施例3：
一种高附着力涂料配方，包括如下质量份数的组份：双酚A环氧树脂38份，聚氨酯树脂8.5份，甲乙酮8份，滑石粉6.6份，石英粉15.4份，分散剂1份，流平剂1份。

Claims (6)

1.一种高附着力的涂料配方，其特征在于，包括如下质量份数的组份：环氧树脂30-40份，聚氨酯树脂8-10份，溶剂6-10份，填料15-25份，助剂1-3份。
2.根据权利要求1所述的高附着力的涂料配方，其特征在于，所述高附着力涂料配方包括如下质量份数的组份：环氧树脂38份，聚氨酯树脂8.5份，溶剂8份，填料22份，助剂2份。
3.根据权利要求1所述的高附着力的涂料配方，其特征在于，所述环氧树脂为双酚A环氧树脂。
4.根据权利要求1所述的高附着力的涂料配方，其特征在于，所述溶剂为甲乙酮。
5.根据权利要求1所述的高附着力的涂料配方，其特征在于，所述填料为滑石粉和石英粉的混合物，其质量比为3:7。
6.根据权利要求1所述的高附着力的涂料配方，其特征在于，所述助剂为分散剂和流平剂的混合物，其质量比为1:1。
CN201610284082.6A 2016-04-29 2016-04-29 一种高附着力的涂料配方 Pending CN105838189A (zh)