CN105859249A - Beautifying cleansing basin - Google Patents
Beautifying cleansing basin Download PDFInfo
- Publication number
- CN105859249A CN105859249A CN201610236835.6A CN201610236835A CN105859249A CN 105859249 A CN105859249 A CN 105859249A CN 201610236835 A CN201610236835 A CN 201610236835A CN 105859249 A CN105859249 A CN 105859249A
- Authority
- CN
- China
- Prior art keywords
- mud
- cleaning
- beauty
- washbasin
- stone
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to the technical field of ceramics manufacturing, in particular to a beautifying cleansing basin which can activate small molecular group water, improve water activity and generate ionic energy water. The beautifying cleansing basin is characterized by being prepared from 16-18% of hexacyclic stone, 4-6% of germanite, 8-10% of stone needle, 17-18.5% of medical stone, 5-7% of jade, 14-16% of rectorite, 10-12% of attapulgite, 4-6% of bentonite, 6-8% of diopside and 3-4% of tourmaline. The beautifying cleansing basin is mainly used for face cleansing.
Description
Technical field
Cleaning and beauty washbasin of the present invention, relates to ceramic fabrication technique field, particularly relates to one and can activate small-micelle water, strengthen the activity of water, produces the face cleaning basin of ion energy water, be mainly used in washing one's face.
Technical background
Face cleaning basin on the market has plastics, pottery, rustless steel etc. material.
Commonplace on market is pottery face cleaning basin, uses as the container being filled with water.
Do not circulate on market this kind of function face cleaning basin at present.
Summary of the invention
Cleaning and beauty washbasin purpose of the present invention is by special formula materials, it is provided that one can activate small-micelle water, strengthens the activity of water, produces the face cleaning basin of ion energy water.
The realization of cleaning and beauty washbasin of the present invention, by the repetition test to compositing formula, it is thus achieved that with skin care, can increase the moisture of skin, the cleaning and beauty washbasin of cleaning face skin.Specifically, cleaning and beauty washbasin of the present invention is characterized in that main by hexacyclic ring stone 16-18%, germanite 4-6%, stone needle 8-10%, Maifanitum 17-18.5%, jade 5-7%, rectorite 14-16%, attapulgite 10-12%, bentonite 4-6%, diopside 6-8%, tourmaline 3-4% etc. form.
In cleaning and beauty washbasin of the present invention:
Hexacyclic ring stone: being a kind of natural energy stone, iron oxide content is more than 3%.1173/s.cm of negative oxygen ion emissivity3, far infrared wavelength 8-15um, containing a large amount noble metal germanium, and the bio electricity of needed by human body etc..Mainly realize radiation negative oxygen ion and far infrared function in the present invention.Germanite: more than the 30 kind of trace element useful to human body such as selenium containing needed by human body, zinc, nickel, cobalt, manganese, magnesium, calcium, the startup ripple starting ripple and human body cell that these elements distribute is same fluctuation status, human body cell is empathized along with the fluctuation given out from germanite and is resonated, make human cell tissue more vigourous, and promote that blood follows bad, enhancing metabolism and enters to get rid of bodily waste.Germanium can make Drinking Water and Natural Water become activated water, helps human body to improve immunity.
Stone needle: main component is a kind of mineral being referred to as " micrite ", the most most is strontium, calcium oxide, next to that silicon oxide, sodium oxide etc., also have the multiple elements such as aluminum, ferrum, magnesium, phosphorus, trace element and rare earth element contain the elements useful to human body more than 36 kinds such as chromium, manganese, nickel, copper, yttrium, and content of radioactive substance is atomic.
Maifanitum: also known as long-lived stone, health-care stone, be a kind of natural medicine Ore, containing 18 kinds of trace element such as potassium, sodium, calcium, magnesium, phosphorus macroelement and zinc, ferrum, selenium, copper, strontium, iodine, fluorine, metasilicic acid necessary to human body.Maifanitum is contained within a large amount of zircon, can discharge the far infrared useful to human body, far-infrared radiation rate ＞ 0.88～0.92 under room temperature, bacteriostasis rate (escherichia coli, staphylococcus aureus) ＞ 90% under room temperature.Mainly realize radiation far infrared function in the present invention.
Jade: containing the multiple trace element useful to human body, such as calcium, selenium, stannum, zinc, copper, ferrum, manganese, magnesium, cobalt, chromium, nickel, lithium, potassium, sodium, titanium etc..Special photoelectric effect can also be produced, form special electromagnetic field, and the biological magnetic field resonance of human body self, thus promote the metabolism of human body, improve every physiological function of human body.Additionally jade itself contains multiple middle trace element, people can be allowed to suck by skin, thus every technical ability of balanced human, reach effect of disease curing health.
Rectorite: have high-temperature stability, refractoriness is up to 1650 DEG C, and can keep Stability Analysis of Structures under 500 DEG C of states.Also having polymolecularity and high-ductility, plasticity index may be up to 50, is easily bonded to shape, dries or sinters and does not crack.It is mainly used in the present invention during formed product increasing base substrate plasticity, reduces base substrate refractoriness.
Attapulgite: there is the dispersion of uniqueness, good colloidal nature and the higher adsorption bleaching ability such as saline and alkaline high temperature resistant, anti-, and there is certain plasticity and cohesive force.It is mainly used in the present invention realizing ionic adsorption translation function.
Bentonite: be the aqueous clay pit based on montmorillonite, there is special character.Such as bloating tendency, caking property, adsorptivity, catalytic, thixotropy, suspension and cation commutativity.
Diopside: being the conventional raw material of pottery, pyroxene is applied in Glaze for chinaware, the advantage combining Talcum and calcite, is possible not only to improve the glossiness of glaze, translucence and flatness.And the firing temperature of enamel can be reduced, expand firing range.
Tourmaline: be the silicate mineral of a kind of natural cyclic structure, containing elements such as aluminum, ferrum, magnesium, sodium, lithium, potassium, has antibiotic and sterilizing, radiates far infrared function.Mainly realize radiation far infrared function in the present invention.
nullThe production technology of cleaning and beauty washbasin of the present invention，Basic similar with ceramic product，Technique has no special requirements，Which is mainly characterized in that composition of raw materials，By hexacyclic ring stone 16-18%，Germanite 4-6%，Stone needle 8-10%，Maifanitum 17-18.5%，Xiuyan jade 5-7%，Version receive soil 14-16%，Attapulgite 10-12%，Bentonite 4-6%，Diopside 6-8%，Tourmaline 3-4% etc. form，Raw material mixture to scale is loaded in ball mill and carries out 30 hours fine gtindings，It is qualified mud to particle requirement than at below 0.2g，Mud is through 320 mesh boltings，Continue to employ the lower mud of sieve to carry out drainage and become mud cake，Again through stirring mud machine negative pressure of vacuum 10kp extrusion mud bar，Mud bar cutting，Roll forming，Molding blank is fired 8-9 hour through 1180 DEG C of oxidizing flames and is completed.
Cleaning and beauty washbasin of the present invention is high temperature resistant, wear-resistant, and corrosion resistance uses for a long time, without scratching.
Cleaning and beauty washbasin of the present invention adds clear water and at once plays a role, and uses simple.
Cleaning and beauty washbasin of the present invention persistently radiates far infrared and negative oxygen ion, can activate small-micelle water, strengthens the activity of water, produces ion energy water.
Cleaning and beauty washbasin of the present invention with skin care, can increase the moisture of skin, cleans face skin.
Cleaning and beauty washbasin of the present invention, has radiation negative oxygen ion and the function of far infrared, and negative oxygen ion exit dose is 800-1500/s.cm3, far infrared wavelength 5-14um, emissivity 0.90.
Specific embodiments
Embodiment 1: utilize cleaning and beauty washbasin of the present invention to wash one's face moist, non-greasy, regulation face water and oil balance, skin care, can thoroughly clean haze residual.
Claims (4)
- Cleaning and beauty washbasin the most of the present invention, it is characterised in that composition of raw materials is mainly by hexacyclic ring stone 16-18%, germanite 4-6%, stone needle 8-10%, Maifanitum 17-18.5%, jade 5-7%, rectorite 14-16%, attapulgite 10-12%, bentonite 4-6%, diopside 6-8%, tourmaline 3-4% etc. form.
- Cleaning and beauty washbasin the most according to claim 1,30 hours fine gtindings are carried out which is mainly characterized in that raw material mixture to scale loaded in ball mill, it is qualified mud to particle requirement than at below 0.2g, mud is through 320 mesh boltings, continue to employ the lower mud of sieve to carry out drainage and become mud cake, then through stirring mud machine negative pressure of vacuum 10kp extrusion mud bar, mud bar cutting, roll forming, molding blank is fired 8-9 hour through 1180 DEG C of oxidizing flames and is completed.
- 3. according to the cleaning and beauty washbasin described in claim 1,2, it is characterised in that the realization of its function will not be affected because of product design, size, the change of color.
- 4. according to the cleaning and beauty washbasin described in claim 1,2,3, it is characterised in that wash one's face.