CN109305812A - Anion titanium crystalline substance sterilizes ecological brick - Google Patents
Anion titanium crystalline substance sterilizes ecological brick Download PDFInfo
- Publication number
- CN109305812A CN109305812A CN201710614725.3A CN201710614725A CN109305812A CN 109305812 A CN109305812 A CN 109305812A CN 201710614725 A CN201710614725 A CN 201710614725A CN 109305812 A CN109305812 A CN 109305812A
- Authority
- CN
- China
- Prior art keywords
- anion
- raw material
- crystalline substance
- ecological brick
- sterilization
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention provides the preparation method of anion titanium crystalline substance sterilization ecological brick, include following processing step: preparing ingredient, it is made of the raw material of following dosage ratio: rare earth 3%-10%, silver ion 0.1%-3%, titanium dioxide 20%-30%, parent glaze raw material 45%-60%, diatom ooze 0.5%-3%, zinc chloride 8%-15%, water 28%-35%.The product that the present invention produces not only stablize by surface effect and product quality situation, moreover it is possible to have the effects that purify air, sterilization, sterilize, eliminates the unusual smell, is anti-oxidant, anti-aging, bring the higher level health experience of client.
Description
Technical field
The invention belongs to build floor field, and in particular to be anion titanium crystalline substance sterilization ecological brick.
Background technique
Traditional floor brick is repressed, firing, polishing, classification by raw materials such as clay, feldspars after certain proportion matches
Enter warehouse after packaging to sell.The floor tile of the product produced through the technique in general sense can satisfy client's finishing
Demand above cannot discharge anion, be unable to satisfy purification air, sterilization, sterilize, eliminate the unusual smell, is anti-oxidant, anti-aging, mentioning
Rise the higher level health demands such as client health experience.
Summary of the invention
It is an object of the invention to overcome the deficiencies in the prior art, on the basis of original glaze raw material, are guaranteeing not shadow
Under the premise of sound glaze normal use combines the various physicochemical properties of glaze slip, three kinds of addition rare earth, silver ion, titanium dioxide etc. is new
Ingredient, making the product produced, not only surface effect and new product quality condition are stablized, moreover it is possible to have purification air, sterilization,
Sterilize, eliminate the unusual smell, is anti-oxidant, anti-aging the effects of, bring client it is higher level health experience.
The present invention is achieved by the following technical solutions, and anion titanium crystalline substance sterilizes the preparation method of ecological brick, includes
Following processing step:
1), prepare ingredient, be made of the raw material of following dosage ratio: rare earth 3%-10%, silver ion 0.1%-3%, titanium dioxide 20%-
30%, parent glaze raw material 45%-60%, diatom ooze 0.5%-3%, zinc chloride 8%-15%, water 28%-35%;
2) after, uniformly deploying ingredient in proportion, ball milling is packed into the mud with certain fineness, mill puts mud into after grinding
Pond carry out it is aging after, then pump after drying tower is dried to the powder with certain granules degree and grain mixture ratio, be transported to press vehicle
Between be pressed, molding adobe enters the glazing ink-jet of glaze line after dry kiln is dry, after enter back into kiln through 1250 degree
High temperature is fired into blank, and blank is packed and stored after being classified respectively using polish line polishing deburring.
The beneficial effects of the invention are that: guaranteeing that not influencing glaze normal use combines the various physicochemical properties of glaze slip
Under the premise of, three kinds of new components such as addition rare earth, silver ion, titanium dioxide make the product produced not only surface effect and new production
Quality situation is stablized, moreover it is possible to have the effects that purify air, sterilization, sterilize, eliminates the unusual smell, is anti-oxidant, anti-aging, bring client
Higher level health experience.
Specific embodiment
Below with reference to specific embodiment, description is of the invention in further detail.
Embodiment one, anion titanium crystalline substance sterilize the preparation method of ecological brick, include following processing step:
1), prepare ingredient, be made of the raw material of following dosage ratio: rare earth 3%-10%, silver ion 0.1%-3%, titanium dioxide 20%-
30%, parent glaze raw material 45%-60%, diatom ooze 0.5%-3%, zinc chloride 8%-15%, water 28%-35%;
2) after, uniformly deploying ingredient in proportion, ball milling is packed into the mud with certain fineness, mill puts mud into after grinding
Pond carry out it is aging after, then pump after drying tower is dried to the powder with certain granules degree and grain mixture ratio, be transported to press vehicle
Between be pressed, molding adobe enters the glazing ink-jet of glaze line after dry kiln is dry, after enter back into kiln through 1250 degree
High temperature is fired into blank, and blank is packed and stored after being classified respectively using polish line polishing deburring.
Rare earth, silver ion, titanium dioxide are added in original base composition of raw materials.The floor tile produced is because containing rare earth member
Element, can the vertical anion, that is, negative oxygen ion of permanent stabilization release ecology, the interior of paving anion titanium crystalline substance brick, negative ion concentration reaches
Several times to even more than natural forest are horizontal, your family is allowed to become a qualified forest oxygen bar, you can be allowed sufficient not
Forest Bath is enjoyed at family out.It is crucial that the generation anion that anion titanium crystalline substance brick is able to continuously not electricity consumption, while
Ozone is not generated, it is without any side effects to human body.Secondly as anion, which has, can neutralize in air haze particle institute band just
Charge makes it easier to the effect of floc sedimentation sedimentation, can play the effect of purification air;The oxidisability of anion, can play point
The effect for solving the volatile organic gas such as formaldehyde, keeps domestic environment safer;Anion also has the function of antibacterial, anti-mildew, very
Just play the effect of protection whole family's health;Anion is also slow in stabilizing blood pressure, adjusting sleep, promotion children's brain development, treatment
Venereal disease etc. has apparent effect.Third not only improves the strong of glaze paint because joined silver ion and titanium dioxide in formula
Degree and Baidu, keep glaze paint not only wear-resisting, are the color development apparent nature of pattern under glaze paint while whiteness is high;The silver ion of addition
Also have the function of Continuous sterilization, disinfection with titanium dioxide, increasingly meets the needs of modern client is for health.
Through detecting, after the polished refine of this product is stored for a long time, its anion radioactivity is detected, anion is put
Penetrating property is between 20000-30000;Anion titanium crystalline substance brick has no any crackle by 5 heat stability testings of 180 degree, brick face,
5 degree of surface hardness Mohs or more, wear resistance level Four, brick face feels excellent thoroughly.
The above examples are only used to illustrate the technical scheme of the present invention and are not limiting, such as technical solution of the present invention is carried out
Modification or equivalent replacement should all cover and want in right of the invention without departing from the objective and range of technical solution of the present invention
It asks in range.
Claims (1)
1. the preparation method of anion titanium crystalline substance sterilization ecological brick, which is characterized in that include following processing step:
1), prepare ingredient, be made of the raw material of following dosage ratio: rare earth 3%-10%, silver ion 0.1%-3%, titanium dioxide 20%-
30%, parent glaze raw material 45%-60%, diatom ooze 0.5%-3%, zinc chloride 8%-15%, water 28%-35%;
2) after, uniformly deploying ingredient in proportion, ball milling is packed into the mud with certain fineness, mill puts mud into after grinding
Pond carry out it is aging after, then pump after drying tower is dried to the powder with certain granules degree and grain mixture ratio, be transported to press vehicle
Between be pressed, molding adobe enters the glazing ink-jet of glaze line after dry kiln is dry, after enter back into kiln through 1250 degree
High temperature is fired into blank, and blank is packed and stored after being classified respectively using polish line polishing deburring.