CN107188418A - A kind of anion wood grain tile - Google Patents
A kind of anion wood grain tile Download PDFInfo
- Publication number
- CN107188418A CN107188418A CN201710548127.0A CN201710548127A CN107188418A CN 107188418 A CN107188418 A CN 107188418A CN 201710548127 A CN201710548127 A CN 201710548127A CN 107188418 A CN107188418 A CN 107188418A
- Authority
- CN
- China
- Prior art keywords
- parts
- anion
- raw material
- wood grain
- grain tile
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to the present invention relates to a kind of brick, there is provided a kind of anion wood grain tile, the floor tile for solving prior art leads to not the problems such as release anion can not purify air because the selection on formula is unreasonable, includes each raw material of following parts by weight：30~60 parts of raw material of 3~10 parts of rare earth, 0.1~3 part of silver ion, 15~40 parts of titanium dioxide, parent glaze.
Description
Technical field
The present invention relates to a kind of brick, more particularly to a kind of anion wood grain tile.
Background technology
Traditional floor brick be by the raw materials such as clay it is repressed, burn till, polish, be classified packaging after enter warehouse sale.It is advised
Lattice are more, matter is hard, unit weight is small, pressure-resistant wear-resisting, can be moistureproof；Have through glazing treatment, with decoration function；Be used for public building and
The ground and floor of civil buildings.
Traditional floor brick be by raw material such as clay, feldspars after certain proportion is matched, load ball milling into
The mud of certain fineness, put into after milling mud pit carry out it is old after, then pump drying tower be dried to certain granules degree and
After the powder of grain mixture ratio, it is transported to press workshop and is pressed, the adobe of shaping enters glaze line after being dried through dry kiln
Glazing ink-jet, after enter back into kiln through 1200 degree or so high-temperature firings into blank, blank is polished deburring by polish line again, is passed through
Packaging and storage is distinguished after classification, into sale flow.The product come out through the technique productions is floor tile in general sense, can
To meet the demand of client's finishing above, it is impossible to discharge anion, it is impossible to meet purification air, sterilize, sterilize, eliminating the unusual smell, resisting
The higher level health demands such as oxidation, anti-aging, lifting client health experience.
The content of the invention
Therefore, for above content, the present invention provides a kind of anion wood grain tile, solve the floor tile of prior art due to
Selection on formula is unreasonable to lead to not the problems such as release anion can not purify air.
To reach above-mentioned purpose, the present invention is achieved by the following technical solutions：A kind of anion wood grain tile, including with
Each raw material of lower parts by weight：
3~10 parts of rare earth
0.1~3 part of silver ion
15~40 parts of titanium dioxide
30~60 parts of raw material of parent glaze.
Further, each raw material of following parts by weight is included：
5 parts of rare earth
2 parts of silver ion
33 parts of titanium dioxide
60 parts of raw material of parent glaze.
Further：The base oil is made up of with raw material following raw material：Clay, feldspar, imitation wood line coating, quartz.
Further：The clay, feldspar, imitation wood line coating, quartz press 2：2：1：0.5~1 weight is than collocation.
By using preceding solution, the beneficial effects of the invention are as follows：This patent formula is on original glaze raw material basis
On, ensure do not influence glaze normally using while taking into account the various physicochemical properties of glaze slip on the premise of, add rare earth, silver ion,
Three kinds of new components such as titanium dioxide, making the product produced, not only surface effect and product quality situation are stablized, moreover it is possible to net
Change air, sterilize, sterilize, eliminating the unusual smell, anti-oxidant, anti-ageing waiting for a long time effect, bring client it is higher level health experience
Rare earth, silver ion, titanium dioxide are added in original base composition of raw materials, the floor tile produced is because containing rare earth member
Element, can permanent stabilization release ecological anion (negative oxygen ion), the interior of paving anion titanium crystalline substance brick, negative ion concentration reaches
To the several times level of even more than natural forest, the family of user is allowed to turn into a qualified forest oxygen bar, can allow makes
User's is home-confined, enjoys Forest Bath.It is crucial that, the generation being able to continuously anion titanium crystalline substance brick " not electricity consumption " is born
Ion, while ozone is not also produced, it is without any side effects to human body.Secondly as anion, which has, can neutralize mist in air
Haze particle (PM2.5) institute is positively charged, makes it easier to the effect of floc sedimentation sedimentation, can play the effect of purification air；Anion
Oxidisability, the organic volatile gas such as decomposing formaldehyde can be played a part of, make domestic environment safer；Anion also has
The effect of antibacterial, anti-mildew, really plays the effect of protection whole family's health；Anion is also in stabilizing blood pressure, regulation sleep, promotion youngster
There is obvious effect in terms of virgin brain development, treatment chronic disease.3rd, because adding silver ion and titanium dioxide in formula, no
The intensity and whiteness of glaze are only improved, makes glaze not only wear-resisting, is that the color development of pattern under glaze is apparent while whiteness is high
It is natural；The silver ion and titanium dioxide of addition, which also have, persistently sterilization, sterilization, increasingly meets modern client for health
Demand.
After testing, after the polished refine of patented product is deposited for a long time, its anion radioactivity is detected, anion
Radioactivity is between 20000-30000；Anion wood grain tile is had no any and split by 5 heat stability testings of 180 degree, brick face
Feel excellent thoroughly in line, more than 5 degree of case hardness Mohs, abrasion resistance level Four, brick face.
Embodiment
Describe embodiments of the present invention in detail below with reference to specific embodiment, how skill is applied to the present invention whereby
Art means solve technical problem, and reach the implementation process of technique effect and can fully understand and implement according to this.
Unless otherwise specified, the conventional hand that the technological means employed in embodiment is well known to those skilled in the art
Section, the reagent and product used is also available commercial.The source of agents useful for same, trade name and it is necessary to list it
Constituent person, indicates on the first appearance.
Embodiment one
A kind of anion wood grain tile, includes each raw material of following parts by weight：
3 parts of rare earth
0.1 part of silver ion
15 parts of titanium dioxide
10 parts of clay
10 parts of feldspar
5 parts of imitation wood line coating
5 parts of quartz.
Embodiment two
A kind of anion wood grain tile, includes each raw material of following parts by weight：
5 parts of rare earth
2 parts of silver ion
33 parts of titanium dioxide
20 parts of the clay
20 parts of feldspar
10 parts of imitation wood line coating
10 parts of quartz.
Embodiment three
A kind of anion wood grain tile, includes each raw material of following parts by weight：
10 parts of rare earth
3 parts of silver ion
40 parts of titanium dioxide
Clay 20
Feldspar 20
Imitation wood line coating 10
Quartz 10.
Wherein, the preparation method of anion wood grain tile of the invention is such as tradition.Each material composition is following
The purpose of the present invention can be achieved in parameter area：3~10 parts of rare earth, 0.1~3 part of silver ion, 15~40 parts of titanium dioxide, basis
30~60 parts of raw material of glaze.
After testing, after the polished refine of patented product is deposited for a long time, its anion radioactivity is detected, anion
Radioactivity is between 20000-30000；Anion wood grain tile is had no any and split by 5 heat stability testings of 180 degree, brick face
Feel excellent thoroughly in line, more than 5 degree of case hardness Mohs, abrasion resistance level Four, brick face.
Described above, only using the embodiment of this origination techniques content, any those skilled in the art use this wound
Make done modifications and changes, all belong to the scope of the claims of this creation opinion, and be not limited to those disclosed embodiments.
Claims (4)
1. a kind of anion wood grain tile, it is characterised in that each raw material including following parts by weight：
3~10 parts of rare earth
0.1~3 part of silver ion
15~40 parts of titanium dioxide
30~60 parts of raw material of parent glaze.
2. anion wood grain tile according to claim 1, it is characterised in that each raw material including following parts by weight：
5 parts of rare earth
2 parts of silver ion
33 parts of titanium dioxide
60 parts of raw material of parent glaze.
3. anion wood grain tile according to claim 2, it is characterised in that：The base oil raw material is by following raw material
Composition：Clay, feldspar, imitation wood line coating, quartz.
4. anion wood grain tile according to claim 3, it is characterised in that：The clay, feldspar, imitation wood line coating, stone
English presses 2：2：1：0.5~1 weight is than collocation.