KR100626870B1 - Natural mineral composition for flooring and the preparating method thereof - Google Patents

Natural mineral composition for flooring and the preparating method thereof Download PDF

Info

Publication number
KR100626870B1
KR100626870B1 KR1020040082486A KR20040082486A KR100626870B1 KR 100626870 B1 KR100626870 B1 KR 100626870B1 KR 1020040082486 A KR1020040082486 A KR 1020040082486A KR 20040082486 A KR20040082486 A KR 20040082486A KR 100626870 B1 KR100626870 B1 KR 100626870B1
Authority
KR
South Korea
Prior art keywords
natural
weight
flooring
composition
powder
Prior art date
Application number
KR1020040082486A
Other languages
Korean (ko)
Other versions
KR20050099450A (en
Inventor
조삼동
성경출
Original Assignee
조삼동
성경출
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 조삼동, 성경출 filed Critical 조삼동
Priority to KR1020040082486A priority Critical patent/KR100626870B1/en
Publication of KR20050099450A publication Critical patent/KR20050099450A/en
Application granted granted Critical
Publication of KR100626870B1 publication Critical patent/KR100626870B1/en

Abstract

본 발명은 견운모 25 내지 30 중량%, 음이온 분말 5 내지 10 중량%, 가소제 65 내지 75 중량%, 충전제 40 내지 80 중량%, 안정제 2 내지 4 중량%, 저온코팅 광촉매 복합금속산화물 5 내지 15 중량%을 포함하는 바닥장식재용 천연 광석물 조성물을 제공한다. 또한 본 발명은 상기 조성물을 포함하는 천연 바닥장식재 및 이의 제조방법을 제공한다.The present invention 25 to 30% by weight of mica, 5 to 10% by weight of anionic powder, 65 to 75% by weight of plasticizer, 40 to 80% by weight of filler, 2 to 4% by weight of stabilizer, 5 to 15% by weight of low temperature coating photocatalyst composite metal oxide It provides a natural mineral composition for floor decoration. In another aspect, the present invention provides a natural floor decoration comprising the composition and a method for producing the same.

본 발명의 천연 광석물 조성물은 견운모, 음이온 분말을 사용하여 인체에 유익한 음이온 및 원적외선을 다량 방출하고, 천연 소재만을 사용하여 인체에 유해한 유해물질이 배출되지 않을 뿐만 아니라, 우수한 항균 활성, 탈취 기능 및 오염방지 효과를 가짐으로써, 사용자에게 보다 친환경적이며, 청정한 다기능성 바닥장식재를 제공한다.The natural mineral composition of the present invention releases a large amount of anion and far infrared rays, which are beneficial to the human body, using biotite and anion powder, and does not emit harmful substances harmful to the human body using only natural materials, as well as excellent antibacterial activity, deodorizing function and By having anti-pollution effect, it provides users with more eco-friendly and clean multi-functional flooring materials.

견운모, 음이온 분말, 음이온, 원적외선, 항균, 바닥장식재Cicada, Anion Powder, Anion, Far Infrared, Antibacterial, Flooring Materials

Description

바닥장식재용 천연 광석물 조성물 및 이를 이용한 천연 바닥장식재의 제조방법{NATURAL MINERAL COMPOSITION FOR FLOORING AND THE PREPARATING METHOD THEREOF}NATURAL COMPOSITION FOR FLOORING AND THE PREPARATING METHOD THEREOF

도 1 은 본 발명에 따른 천연 바닥장식재 제조방법을 도시한 블록도1 is a block diagram showing a natural floor decoration manufacturing method according to the invention

도 2 는 본 발명에 따른 천연 바닥장식재가 설치된 모습을 보이는 단면도Figure 2 is a cross-sectional view showing a state in which the natural flooring according to the invention installed

<도면의 주요부분에 대한 부호의 설명><Description of the symbols for the main parts of the drawings>

10 : 본 발명에 따른 천연 바닥장식재10: natural floor decoration according to the present invention

11 : 본 발명에 따른 코팅층11: coating layer according to the present invention

12 : 바닥장식재 하부층12: bottom layer of flooring material

20 : 단열재20: insulation

21 : 콘크리트 바닥21: concrete floor

본 발명은 바닥장식재용 천연 광석물 조성물 및 이를 이용한 천연 바닥장식재의 제조 방법에 관한 것으로, 보다 상세하게는 견운모와 음이온 분말 등의 천연 광석물을 사용하여 인체에 유익한 음이온 및 원적외선을 방사하고 방염 및 항균 활성을 갖는 다기능성 바닥장식재 및 이의 제조방법에 관한 것이다.The present invention relates to a natural ore composition for flooring materials and a method for producing a natural flooring material using the same, more specifically using natural minerals such as biotite and anion powder to radiate and prevent anion and far infrared rays beneficial to the human body The present invention relates to a multifunctional floor covering having an antimicrobial activity and a method of manufacturing the same.

현대의 전자문명 발달, 자동차 문화사회의 편리에 의해, 공기 오염 및 자연 환경의 파괴가 사회의 큰 문제점으로 대두됨에 따라, 기존의 대기오염 문제에 한정되지 않고 생명 존속을 좌우하는 사람의 신체 주위에 존재하는 공기의 질이 중요한 문제로 부각되었으며, 그 중 대기 공기가 양이온에 대전돼 있는 것으로 밝혀졌다. 또한, 화학물질과 신축 건물의 실내에도 많은 유독 물질의 잔류가 발견되고 있는데, 이것들은 양이온과의 관계성에 더욱 관심의 대상이 되고 있다. 이와 같은 양이온화는 인간의 건강에 큰 문제, 즉 두통, 어지러움, 구토, 멀미의 불쾌감을 증가시킬 뿐만 아니라 인체조직의 세포를 산화시켜 자율 신경을 자극시킴으로써 내분비계나 면역, 체액의 순환을 악화시켜 몸의 노화를 촉진한다고 알려져 있다.With the development of modern electronic civilization and the convenience of automobile culture society, air pollution and destruction of natural environment have become a big problem of society, so it is not limited to the existing air pollution problem. The quality of the air present is an important issue, of which atmospheric air is found to be charged with positive ions. In addition, many toxic substances remain in the interiors of chemicals and new buildings, which are of greater concern for their relationship to cations. Such cationization not only increases the discomfort of human health problems such as headache, dizziness, vomiting and motion sickness, but also oxidizes cells of human tissues to stimulate autonomic nerves, worsening the circulation of endocrine system, immunity and body fluids. It is known to promote aging.

한편, 공기가 맑고 청정한 교외의 숲이나 연못, 저수지, 호수, 폭포의 주위 등 물이 풍부한 지역에는 음이온이 많으며, 이로 인해 모든 사람들이 기분 좋고 상쾌한 기분을 느낄 수 있다. 상기한 음이온은 생태계의 동식물 생육에도 큰 영향을 준다고 알려져 있으므로, 오늘날 음이온에 따른 유용한 역할을 응용한 산업분야가 다방면으로 활용될 조짐이 고조되고 있고, 실제 기능성에 착안한 제품이 많이 개발되고 있다. On the other hand, there are many negative ions in the water-rich areas such as forests, ponds, reservoirs, lakes, and waterfalls, where the air is clean and clean, and everyone can feel pleasant and refreshed. Since the anion is known to have a great influence on the growth of animals and plants in the ecosystem, there is a growing indication that industrial fields applying a useful role according to the anion are being utilized in various fields, and many products have been developed focusing on actual functionality.

건강을 해하고 허파의 산소 흡수 능력을 저하시키는 양이온과는 달리, 음이온은 인체 내에서 과량의 세로토닌(serotonin)/히스타민을 분비하게 하여 혈액 중의 미네랄 성분 등의 이온화율을 상승시키고 알칼리화함으로써, 혈액을 정화시키고 세포막에서 전기적 물질 교류를 촉진시켜 신진대사를 왕성하게 하여 체내의 노폐물을 신속히 배출시키는 한편, 혈청속의 면역성분의 양을 증가시켜 저항력을 증대시키고 자율신경계통, 혈액 및 임파액을 활성화시키는 것으로 알려져 있다.Unlike cations, which damage health and reduce lungs' ability to absorb oxygen, negative ions secrete excess serotonin / histamine in the human body, increasing the ionization rate of minerals and the like in the blood and alkalizing the blood. It is known to purify and accelerate the exchange of electrical substances in the cell membranes to stimulate the metabolism and release the wastes in the body quickly, while increasing the amount of immune components in the serum to increase resistance and activate the autonomic nervous system, blood and lymphatic fluid. have.

상기에 나타난 바와 같이, 사람은 주거 환경에 의해 건강이 크게 좌우될 수 있으며, 특히 24 시간동안 건물 내부에서 생활하는 근래의 생활에서는 건물의 내벽면, 건물 마감재 및 바닥장식재와 바닥장식재가 매우 큰 비중을 차지하고 있다. As indicated above, the health of a person can be greatly influenced by the living environment, especially in the recent life of living inside the building for 24 hours, the inner wall of the building, building finishing and flooring and flooring materials are very large Occupies.

일반적으로 바닥장식재는 건물의 콘크리트 바닥(21) 또는 그 위에 단열재(20)등을 적층한 후 깔아주거나, 주거 환경을 개선하거나 소비자의 취향에 따라 건물이 주는 느낌이나 분위기를 전환하고자 할 때 이용되는 건물 마감재로서, 일반적으로 하부로부터 하지층, 발포층, 함침층, 인쇄층, 상지층 및 코팅층으로 순차적으로 적층된 구조를 갖는 바닥장식재에 각종 물질을 첨가하거나 상기 구성들을 변화시켜 다양한 소비자의 욕구를 충족시킬 수 있는 바닥재의 다양한 특성을 살려, 장식성을 부각시킨 바닥재 및 기능성을 부각시킨 바닥재 등을 얻어 그 용도에 맞게 사용해 오고 있다.In general, the flooring material is used when the concrete floor 21 of the building or the insulation material 20 laminated thereon and then laid, or to improve the living environment or to change the feeling or atmosphere of the building according to the consumer's taste. As a building finishing material, various materials are added to the flooring material having a structure laminated in general from the bottom to the base layer, the foaming layer, the impregnating layer, the printing layer, the upper layer and the coating layer, or the above configurations are changed to satisfy various consumer needs. Taking advantage of the various properties of the flooring that can be satisfied, and has been used for the purpose of obtaining a flooring that highlights the decorative and functional flooring.

종래의 바닥장식재들은 미적인 효과를 높이는 방법으로 염화비닐수지 등과 같은 합성수지를 표면에 코팅시키고, 이 수지의 표면에 인쇄를 하거나 내측에 인쇄층을 삽입하는 방법을 주로 사용하였다. 그러나, 이러한 합성수지들은 염화비닐중량체(poly vinyl chloride: PVC)를 비롯한 실리콘, 멜라민, 폴리아미드, 아크릴산, 에스테르와 같은 화합합성 수지들이 단가적 측면에서 많이 사용됨으로써 건물 안에 휘발성 유기용제(VOCs), 포름알데히드(HCHO) 등과 같은 인체에 유해한 성분이 방출 되는 문제점이 있었다.Conventional flooring materials mainly used a method of coating a synthetic resin such as vinyl chloride resin on the surface, printing on the surface of the resin or inserting a printing layer inside the method to enhance the aesthetic effect. However, these synthetic resins are polyvinyl chloride (PVC), including synthetic resins such as silicone, melamine, polyamide, acrylic acid, ester, etc., in terms of unit cost, so volatile organic solvents (VOCs), There was a problem in that harmful ingredients such as formaldehyde (HCHO) is released.

상기의 문제점을 해결하기 위하여, 본 발명자는 인체에 유익한 물질을 방사할 수 있으며 동시에 유해물질을 흡착할 수 있는 바닥장식재용 천연 광석물 조성물을 제조하는 방법을 제공하는 것을 목적으로 한다.In order to solve the above problems, it is an object of the present invention to provide a method for producing a natural ore composition for flooring materials that can radiate substances beneficial to the human body and at the same time can adsorb harmful substances.

또한, 상기 조성물을 포함하는 천연 바닥장식재 및 이의 제조 방법을 제공하는 것을 또 다른 목적으로 한다.In addition, another object of the present invention is to provide a natural flooring material comprising the composition and a method for producing the same.

본 발명은 견운모 25 내지 30 중량%, 음이온 분말 5 내지 10 중량%, 가소제 65 내지 75 중량%, 충전제 40 내지 80 중량%, 안정제 2 내지 4 중량%, 저온코팅 광촉매 복합금속산화물 5 내지 15 중량%을 포함하는 바닥장식재용 천연 광석물 조성물 및 이를 포함하는 천연 바닥장식재 및 이의 제조방법을 제공함으로써 그 목적이 달성된다.The present invention 25 to 30% by weight of mica, 5 to 10% by weight of anionic powder, 65 to 75% by weight of plasticizer, 40 to 80% by weight of filler, 2 to 4% by weight of stabilizer, 5 to 15% by weight of low temperature coating photocatalyst composite metal oxide The object is achieved by providing a natural ore composition for flooring and natural flooring comprising the same and a method for producing the same.

또한, 본 발명은 a) 견운모 및 음이온 분말을 분쇄하는 공정(S10); b) 상기 공정 a)에서 분쇄된 분말에 가소제, 충전제, 안정제 및 염화비닐수지와 혼합하는 공정(S20); c) 상기 공정 b)의 혼합물에 천연 색소 및/또는 천연 접착제를 첨가 및 희석하는 공정(S30); d) 상기 공정 c)의 조성물을 6 내지 7 mm 두께를 갖는 바닥장식재에 도포하고, 압출금형 시루에서 200 내지 230 ℃에서 열처리 및 건조하는 공정(S40); e) 복합금속산화물을 저온촉매로 이용하여 배전코팅을 하는 광촉매 공정(S50); 및 f) 규조토로 흡습 및 방습하는 공정(S60);으로 제조되는 천연 바닥장식 재의 제조방법을 제공함으로써 그 목적이 달성된다.
In addition, the present invention is a) a step of grinding the mica and anionic powder (S10); b) mixing the powder ground in step a) with a plasticizer, a filler, a stabilizer and a vinyl chloride resin (S20); c) adding and diluting the natural pigment and / or natural adhesive to the mixture of step b) (S30); d) applying the composition of step c) to a flooring material having a thickness of 6 to 7 mm, heat treatment and drying at 200 to 230 ° C in an extrusion mold through (S40); e) a photocatalyst process of performing roasting coating using the composite metal oxide as a low temperature catalyst (S50); And f) a step of absorbing and moisture-proofing diatomaceous earth (S60).

이하, 본 발명을 도면을 참조하여 상세히 설명한다.Hereinafter, the present invention will be described in detail with reference to the drawings.

먼저, 도 1 은 본 발명에 따른 천연 바닥장식재 제조방법을 도시한 블록도이고, 도 2 는 본 발명에 따른 천연 바닥장식재가 설치된 모습을 보이는 단면도이다.First, Figure 1 is a block diagram showing a natural floor decoration method according to the invention, Figure 2 is a cross-sectional view showing a state in which the natural floor decoration according to the invention is installed.

종래의 바닥장식재를 사용시 휘발성 유기용제(VOCs) 또는 포름알데히드(HCHO) 등과 같은 인체에 유해한 성분이 다량 방출되는 문제점을 해결하기 위하여, 원적외선 및 음이온을 방사하는 견운모, 음이온 분말 등과 같은 천연 광석물을 포함하는 천연 소재 조성물을 이용하고자 한다.In order to solve the problem that harmful ingredients such as volatile organic solvents (VOCs) or formaldehyde (HCHO) are released when using conventional flooring materials, natural ore such as mica, anion powder, etc. that emit far infrared rays and anions To use a natural material composition comprising.

본 발명의 바닥장식재용 조성물에 사용되는 견운모(Ilite)는 일반적으로 용수 중의 양이온 부유 입자와 전기적인 중화응집으로 침전을 유발함으로써, 우수한 정수작용, 높은 보습 효과 및 활성도를 갖는다. 또한 인체의 혈액 순환을 촉진하고 세포활성을 활성화하는 원적외선을 90% 이상 방사하는 물질로서, 강력한 음이온을 발산하여 각종 유해 물질을 흡착할 수 있는 기능을 가지고 있으며, 습도 조절도 가능하다. 또한, 목재 펄프 지료와 강한 결속성을 가지므로, 상기와 같은 특성을 바닥장식재에 부가하고자 지료와 혼합하여 사용할 수도 있다. Ilite used in the flooring composition of the present invention generally causes precipitation by cationic floating particles and electrical neutralization in water, and thus has excellent water purification, high moisturizing effect and activity. In addition, it emits more than 90% of far-infrared rays, which promote blood circulation and activate cell activity of the human body, and has a function of adsorbing various harmful substances by emitting powerful anions and controlling humidity. In addition, since it has a strong binding with the wood pulp material, it can be used in combination with the paper to add the above characteristics to the flooring material.

본 발명의 조성물에서 사용되는 견운모의 양은 25 내지 30 중량%이고, 음이온 분말의 양은 5 내지 10 중량%가 바람직하다.(염화비닐수지 100 중량%를 기준)The amount of mica used in the composition of the present invention is 25 to 30% by weight, and the amount of anionic powder is preferably 5 to 10% by weight. (Based on 100% by weight of vinyl chloride resin)

또한, 가소제의 양은 65 내지 75 중량%, 충전제의 양은 40 내지 80 중량%, 안정제의 양은 2 내지 4 중량%, 저온코팅 광촉매 복합금속산화물의 양은 5 내지 15 중량%로 하는 것이 바람직하다. In addition, the amount of the plasticizer is 65 to 75% by weight, the amount of the filler is 40 to 80% by weight, the amount of the stabilizer is 2 to 4% by weight, the amount of the low-temperature coating photocatalyst composite metal oxide is preferably 5 to 15% by weight.

견운모와 음이온 분말의 입도 크기는 1000 내지 1500 메쉬, 특히 1000 메쉬가 바람직하나, 이를 제한하는 것은 아니다. The particle size of the biotite and anionic powder is preferably 1000 to 1500 mesh, in particular 1000 mesh, but is not limited thereto.

본 발명에서 사용된 음이온 분말은 토르말린 또는 귀양석을 사용할 수 있다. 토르말린(Tormalin)은 일반적으로 붕소를 함유한 사이크로 규산염 결정구조로서, 태양 에너지로부터 전자파를 받을 경우, 인체에 유익한 0.06mA의 전류를 발생시키며, 인체와 동일한 4 내지 14 미크론의 원적외선을 방출하는 물질이다. 본 발명에서는 인체에 유익한 전류, 음이온 및 원적외선을 방출하는 기능을 부가하기 위하여 사용된다. The anionic powder used in the present invention may use tourmaline or jewels. Tourmalin is a boron-containing cyclosilicate crystal structure that generates 0.06 mA of current, which is beneficial to the human body when receiving electromagnetic waves from solar energy, and emits 4 to 14 microns of far-infrared radiation, which is the same as the human body. to be. In the present invention, it is used to add a function of emitting a current, anion and far infrared rays which is beneficial to the human body.

또한, 귀양석(Kiyoseki)은 다량의 음이온(24,140ea/cc)을 방출하고, 25℃의 상온에서 최고의 원적외선(96%)을 방출하는 신물질로서, 약 6,500만년 전의 지각변동에 따른 고온난수 작용에 의해 형성된 광산에 존재하며, 자연계의 에너지를 응축한 신비의 물질로서 전세계에서 유일하게 일본 군마현에서만 생산되는 장석 계열의 천연석이다. 귀양석은 높은 계면활성 효과(101% 증가)를 보이며, 뇌파 중 알파파 및 혈류량을 다량 증가시킬 뿐만 아니라, 혈류 속도를 7.2% 감소시키는 특징을 가지고 있으며, 본 발명에서는 인체에 유익한 전류, 음이온 및 원적외선을 방출하는 기능을 부가하기 위하여 사용된다. In addition, Kiyoseki is a new material that emits a large amount of anions (24,140ea / cc) and emits the best far-infrared (96%) at room temperature of 25 ° C. It is a mysterious substance condensed with the energy of the natural world and is the only feldspar family of natural stones produced only in Gunma Prefecture in the world. Guinea stone has a high surfactant effect (increased by 101%), not only increases alpha wave and blood flow rate in EEG, but also decreases blood flow rate by 7.2%. It is used to add the ability to emit light.

본 발명의 바닥장식재용 천연 광석물 조성물은 상기 천연 광석 이외에 천연 접착제 및/또는 천연 잉크(색소)를 포함할 수 있다.The natural ore composition for flooring of the present invention may include a natural adhesive and / or a natural ink (color) in addition to the natural ore.

상기에 있어서, 천연 접착제의 비제한적인 예로는 천연라텍스, 송진, 아교, 카제인, 알긴산나트륨, 벤토인 등을 들 수 있으며, 이를 혼합하여 사용할 수도 있다. In the above, non-limiting examples of natural adhesives include natural latex, rosin, glue, casein, sodium alginate, bentoin and the like, it may be used by mixing them.

상기에 있어서, 천연 잉크는 치자, 황백, 샤프란, 울금, 인디고, 솔잎 등과 같은 식물성 염료; 코치닐(cochenille), 커미즈(연지층)과 같은 동물성 염료, 벵가라, 연단, 주, 군청 등과 같은 광물성 염료를 사용하는 것이 바람직하며, 이중 수성(水性) 잉크가 더 바람직하다. 가장 바람직하게는 지당 902(티타늄 분말)이다. 이외에, 상업적으로 판매되는 천연 잉크도 사용 가능하다. 천연 잉크는 통상적으로 사용되는 양을 사용할 수 있으며, 상기의 천연 잉크들을 혼합하여 사용할 수 있다.In the above, the natural ink is a vegetable dye such as gardenia, yellowish white, saffron, turmeric, indigo, pine needles and the like; It is preferable to use animal dyes such as cochenille, chemise (solvent layer), mineral dyes such as bengala, podium, cast iron, ultramarine, and the like, and double aqueous ink is more preferable. Most preferably it is 902 (titanium powder) per fat. In addition, commercially available natural inks may also be used. The natural ink may be used in an amount commonly used, and may be used by mixing the above natural inks.

이와 같이, 본 발명의 바닥장식재용 천연 광석물 조성물은 천연 소재를 사용함으로써, 소재가 가지고 있는 특성을 최대한 활용할 수 있으며, 종래 화학재를 사용하여 발생하였던 유기물질의 배출을 감소 및 방지할 수 있다. 그러나 본 발명은 상술한 천연물질로 한정되는 것은 아니며, 당해 기술분야에서 통상의 지식을 가진 자가 용이하게 사용할 수 있는 천연 재료도 사용 가능하다.As such, the natural ore composition for the flooring material of the present invention can utilize the characteristics of the material to the maximum by using a natural material, it is possible to reduce and prevent the emission of organic substances generated by using a conventional chemical material. . However, the present invention is not limited to the above-described natural materials, and natural materials that can be easily used by those skilled in the art can also be used.

본 발명은 상기한 바닥장식재용 천연 광석물 조성물을 포함하는 천연 바닥장식재(10)를 제공한다. 이의 제조방법으로는 통상적인 바닥재 제조방법을 사용할 수 있으며, 일례로, a) 견운모 및 음이온 분말을 분쇄하는 공정(S10); b) 상기 공정 a)에서 분쇄된 분말에 가소제, 충전제, 안정제 및 염화비닐수지와 혼합하는 공정(S20); c) 상기 공정 b)의 혼합물에 천연 색소 및/또는 천연 접착제를 첨가 및 희석하는 공정(S30); d) 상기 공정 c)의 조성물(11)을 6 내지 7 mm 두께를 갖는 바닥 장식재(12)에 도포하고, 압출금형 시루에서 200 내지 230 ℃에서 열처리 및 건조하는 공정(S40); e) 복합금속산화물을 저온촉매로 이용하여 배전코팅을 하는 광촉매 공정(S50); 및 f) 규조토로 흡습 및 방습하는 공정(S60);으로 제조될 수 있다.The present invention provides a natural flooring material 10 comprising the natural mineral composition for flooring. As a manufacturing method thereof, a conventional flooring manufacturing method may be used. For example, a) a step of pulverizing mica and anionic powder (S10); b) mixing the powder ground in step a) with a plasticizer, a filler, a stabilizer and a vinyl chloride resin (S20); c) adding and diluting the natural pigment and / or natural adhesive to the mixture of step b) (S30); d) applying the composition 11 of the step c) to the floor decoration material 12 having a thickness of 6 to 7 mm, and heat-treating and drying at 200 to 230 ° C. in an extrusion mold see-through (S40); e) a photocatalyst process of performing roasting coating using the composite metal oxide as a low temperature catalyst (S50); And f) a step of absorbing and dampening the diatomaceous earth (S60).

제공된 견운모, 음이온 분말은 상기에 기재된 바와 같이 각각 25 내지 30 중량%, 5 내지 10 중량%로 혼합하고, 가소제 65 내지 75 중량%, 충전제 40 내지 80 중량%, 안정제 2 내지 4 중량%, 저온코팅 광촉매 복합금속산화물 5 내지 15 중량%을 혼합한 후, 적절한 용매로 희석하여 사용하는 것이 바람직하다. 용매는 물이 적절하며, 특히 40℃의 정제수가 바람직하다. The provided mica, anionic powder is mixed at 25 to 30% by weight, 5 to 10% by weight, respectively, as described above, 65 to 75% by weight plasticizer, 40 to 80% by weight filler, 2 to 4% by weight stabilizer, low temperature coating After mixing 5 to 15% by weight of the photocatalyst composite metal oxide, it is preferable to dilute with an appropriate solvent. The solvent is suitably water, and especially purified water of 40 degreeC is preferable.

상기의 혼합물(11)은 실온, 바람직하게는 21℃에서 24 시간 경과 후, 물, 천연 잉크 및 천연 접착제를 첨가 및 혼합하여 수화(水化)시킨다. 이때 천연 접착제는 24 시간 전에 희석하여 혼합된 것이 바람직하며, 추가적으로 접착성의 향상과 바닥장식재(10)의 부스럼을 방지하기 위해 에탄올 또는 식물성 기름을 0.2 내지 0.3%를 첨가하여 사용할 수 있다. The mixture 11 is hydrated by adding and mixing water, a natural ink and a natural adhesive after 24 hours at room temperature, preferably at 21 ° C. At this time, the natural adhesive is preferably diluted before mixing for 24 hours, and may be used by adding 0.2 to 0.3% of ethanol or vegetable oil in order to further improve adhesion and to prevent crumb of the flooring material 10.

상기와 같이 제조된 본 발명의 바닥장식재용 천연 광석물 조성물(11)은 하부로부터 하지층, 발포층, 함침층, 인쇄층, 상지층이 순차적으로 적층된 구조를 갖는 바닥장식재(12)에 0.2 내지 0.5㎜, 바람직하게는 0.2 내지 0.3㎜의 두께가 되도록 도포 후, 건조하여 6 내지 7 mm의 천연 바닥장식재(10)를 제조할 수 있으며, 특히 로타리 스크린에 배전 및 입전한 후, 압출금형 시루에서 200 내지 230℃의 온도에서 건조 및 열처리하는 것이 바람직하다. 바닥장식재의 도포 두께가 0.2㎜ 이하일 경우, 천연재의 질감을 얻을 수 없으며, 0.5㎜ 이상의 두께일 경우, 음이온과 원적 외선의 방출량은 증가하나, 시료의 단가가 높아지며 건조시간이 길어지고 바닥장식재가 두꺼워져서 작업성이 떨어지는 문제점이 있다. The natural ore composition 11 for the flooring material of the present invention prepared as described above is 0.2 in the flooring material 12 having a structure in which a base layer, a foaming layer, an impregnation layer, a printing layer, and an upper layer are sequentially stacked from the bottom. To 0.5 mm, preferably 0.2 to 0.3 mm thick, and then dried to produce a 6 to 7 mm natural floor covering material 10, in particular, after roasting and entering the rotary screen, extrusion mold Preference is given to drying and heat treatment at a temperature of from 200 to 230 ° C. If the coating thickness of the flooring material is 0.2mm or less, the texture of the natural material cannot be obtained. If the thickness of the flooring material is 0.5mm or more, the amount of release of negative ions and far infrared rays increases, but the unit cost of the sample increases, the drying time is long, and the flooring material is thick. There is a problem of losing workability.

또한, 건조 및 열처리 공정이후, 복합금속산화물을 저온촉매로 이용하여 배전코팅을 하는 광촉매 공정을 통하여 각종 병원균 등을 살균할 수 있고 세균의 증식을 억제하는 기능을 얻게 된다. 상기 복합금속산화물은 Tio2, ZnO, CDS, ZrO2, SnO2, V2O2 및 WO3 등인 것이 사용된다.In addition, after the drying and heat treatment process, it is possible to sterilize various pathogens, etc. through the photocatalytic process of roasting coating using the composite metal oxide as a low-temperature catalyst, thereby obtaining a function of inhibiting the growth of bacteria. The composite metal oxide may be Tio 2 , ZnO, CDS, ZrO 2 , SnO 2 , V 2 O 2 , WO 3, or the like .

본 발명에서 제조된 바닥장식재(10)는 상기와 같은 통상적인 바닥장식재 제조방법 이외에, 규조토의 다공질을 통한 흡습 및 방습 단계를 반복 수행함으로써 다기능성 바닥장식재가 제조될 수 있다. 상기 단계는 2 내지 5회를 반복 수행하는 것이 바람직하며, 이 단계를 거친 후에는 결로가 발생되지 않을 뿐만 아니라 곰팡이 발생을 억제하여 우수한 항균 활성을 가질 수 있다.The flooring material 10 prepared in the present invention may be manufactured in a multifunctional flooring material by repeating the moisture absorption and moisture-proof step through the porous of diatomaceous earth in addition to the conventional method of manufacturing the flooring material as described above. The step is preferably repeated 2 to 5 times, after this step not only does not cause condensation but also inhibits the occurrence of mold can have excellent antimicrobial activity.

본 발명에 따른 천연 바닥장식재는 사용된 천연 광석물의 고유 성질인 원적외선 및 음이온 방출 뿐만 아니라 이들에 의한 우수한 불연 및 방염 효과, 탁월한 항균 및 탈취 기능 등을 나타낼 수 있다. Natural flooring according to the present invention may exhibit far infrared and anion emission, which are inherent properties of the natural ore used, as well as excellent non-flammable and flame-retardant effect, excellent antibacterial and deodorizing function.

이하, 본 발명에 따른 바닥장식재용 천연 광석물 조성물, 이를 포함하는 바닥장식재 및 이의 제조방법을 바람직한 실시예를 통하여 상세히 설명한다. Hereinafter, a natural ore composition for a floor decorative material according to the present invention, a floor decorative material comprising the same and a manufacturing method thereof will be described in detail through preferred embodiments.

다만 이들 실시예는 오로지 본 발명을 구체적으로 설명하기 위한 것으로 본 발명의 범위가 이들 실시예에 한정되지 않는다.However, these examples are only for illustrating the present invention specifically, the scope of the present invention is not limited to these examples.

실시예 1. 바닥장식재용 천연 광석물 조성물 제조 Example 1. Preparation of natural ore composition for flooring

염화비닐수지 100 중량% 당, 평균 입도가 각각 1000 메쉬인 견운모 27 중량%, 토르말린 및/또는 귀양석 7 중량%와 혼합한 후, 여기에 천연 라텍스 0.3 중량%, 천연 잉크인 지당(돌가루 색소) 902 및 에탄올을 0.2 중량% 첨가하였다. 전체 조성물의 색깔이 균등해질 때까지 혼합한 후, 균일하게 점성있는 3㎏의 바닥장식재용 천연 광석물 조성물을 얻었다. Per 100% by weight of vinyl chloride resin, mixed with 27% by weight of villus, each with an average particle size of 1000 mesh, tourmaline and / or jewels of 7% by weight, followed by 0.3% by weight of natural latex and fat sugar as a natural ink (stone color) ) 902 and ethanol 0.2% by weight. After mixing until the color of the entire composition was uniform, a uniformly viscous 3 kg natural ore composition for flooring was obtained.

실시예 2. 천연 바닥장식재의 제조방법 Example 2 Manufacturing Method of Natural Floor Decoration

상기 실시예 1에서 제조된 바닥장식재용 천연 광석물 조성물(11)을 바닥장식재(12)의 표면에 0.2㎜ 두께로 도포하였으며, 이때 상기 조성물(11)은 100 내지 300g/㎡ 정도의 고형분 기준으로 하여 상기 바닥장식재(12)에 도포되는 것이 바람직하다. 이를 215℃의 챔버에서 건조 및 열처리시켰다. 이후, Tio2 복합금속산화물을 저온촉매로 이용하여 배전코팅을 하는 광촉매 공정을 시켰다. 광촉매 공정을 거친 바닥장식재(10)를 권취하여 포장하였다.The natural ore composition 11 for floor decoration material prepared in Example 1 was applied to the surface of the floor decoration material 12 with a thickness of 0.2 mm, wherein the composition 11 is based on a solid content of about 100 to 300 g / ㎡ It is preferable to be applied to the floor decoration 12. It was dried and heat treated in a chamber at 215 ° C. Subsequently, a photocatalyst process was performed using the Tio 2 composite metal oxide as a low temperature catalyst to perform roast coating. The flooring material 10 subjected to the photocatalytic process was wound up and packaged.

실험예 1. 천연 바닥장식재의 음이온 방출 효과 측정Experimental Example 1. Measurement of Anion Release Effect of Natural Floor Decorations

본 발명의 실시예 1 및 2에서 제조된 천연 바닥장식재의 음이온 방출 효과를 측정하기 위하여, 하기와 같은 실험을 수행하였다.In order to measure the negative ion release effect of the natural flooring materials prepared in Examples 1 and 2 of the present invention, the following experiment was performed.

본 실험은 한국 건자재 시험연구원 원적외선 응용평가센터에서 시행하였고, 음이온 방출은 KICM-FIR-1042의 시험 방법으로 전하 입자 측정장치를 이용하여 측정하였다. 이때 측정은 온도 21℃, 습도 40% 및 대기중 음이온수 68/cc 조건하에서 수행하였으며, 측정대상물에서 방출되는 음이온을 단위체적당 이온수로 표시하였고, 그 결과는 하기 표 1에 나타내었다.This experiment was conducted at the Far Infrared Ray Evaluation Center, Korea Institute of Construction Materials, and the anion emission was measured using a charged particle measuring device as a test method of KICM-FIR-1042. At this time, the measurement was carried out under the conditions of temperature 21 ℃, humidity 40% and 68 / cc anion water in the air, the anion released from the measurement object was expressed in the number of ions per unit volume, the results are shown in Table 1 below.

실험 결과, 본 천연 광석물 조성물에 의해 제조된 천연 바닥장식재는 1800의 음이온을 방출하는 것을 확인할 수 있었다As a result of the experiment, it was confirmed that the natural flooring material produced by the present natural mineral composition emits 1800 negative ions.

시험 항목Test Items 단위unit 천연 바닥장식재Natural Flooring Materials 대조시편 (일반온돌마루)Contrast Specimen (General Ondol Floor) 시험방법Test Methods 음이온Negative ion ION/ccION / cc 1800/cc1800 / cc 68/cc68 / cc KICM-FIR-1042KICM-FIR-1042

실험예 2. 천연 바닥장식재의 원적외선 방출 효과 측정Experimental Example 2 Measurement of Far-Infrared Emission Effect of Natural Floor Decorations

본 발명에 실시예 1 및 2에 의해 제조된 천연 바닥장식재의 원적외선 방출 효과를 측정하기 위해, 하기와 같은 실험을 수행하였다.In order to measure the far-infrared emission effect of the natural flooring material prepared by Examples 1 and 2 in the present invention, the following experiment was performed.

본 실험은 한국 건자재시험연구원에서 시행하였고, 원적외선 방출은 KSM의 시험 방법을 이용하였다. 이때 측정은 온도 21℃, 습도 40% 및 대기중 음이온수 68/cc 조건하에서 수행하였으며, 그 결과는 하기 표 2에 나타내었다.This experiment was conducted by the Korea Institute of Construction Materials, and the far infrared emission was used by KSM test method. At this time, the measurement was carried out under the conditions of temperature 21 ℃, humidity 40% and anion water 68 / cc in the air, the results are shown in Table 2 below.

실험 결과, 본 천연소재 조성물에 의해 제조된 천연 바닥장식재는 0.880의 원적외선 방사율을 갖는 것을 확인할 수 있었다.As a result of the experiment, it was confirmed that the natural flooring material prepared by the present natural material composition has a far-infrared emissivity of 0.880.

시험 항목Test Items 단위unit 방사율 (5∼20 mm)Emissivity (5-20 mm) 방사에너지 (W/㎡)Radiation energy (W / ㎡) 시험 방법Test Methods 원적외선Far Infrared ION/ccION / cc 0.8800.880 3.59X102 3.59X10 2 KSMKSM 한국건자재시험연구원Korea Building Materials Testing Institute

실험예 3. 천연 바닥장식재의 포름알데히드 방산량 측정Experimental Example 3 Measurement of Formaldehyde Dissipation of Natural Floor Decorations

본 발명에 실시예 1 및 2에 의해 제조된 천연 바닥장식재의 포름알데히드 방산량을 측정하기 위해, 하기와 같은 실험을 수행하였다.In order to measure the amount of formaldehyde dissipation of the natural flooring material prepared in Examples 1 and 2 in the present invention, the following experiment was performed.

본 실험은 한국 화학시험연구원에서 시행하였고, 포름알데히드 방출은 KSM 7305의 시험 방법을 이용하였다. 이때 측정은 온도 21℃, 습도 40% 및 대기중 음이온수 68/cc 조건하에서 수행하였으며, 그 결과는 하기 표 3에 나타내었다.This experiment was conducted by the Korea Testing and Research Institute, and the formaldehyde emission was tested by KSM 7305. At this time, the measurement was carried out under the conditions of temperature 21 ℃, humidity 40% and anionic water 68 / cc conditions, the results are shown in Table 3 below.

실험 결과, 본 천연소재 조성물에 의해 제조된 천연 바닥장식재는 포름알데히드를 방산하지 않음을 확인할 수 있었다.Experimental results, it was confirmed that the natural flooring material prepared by the natural material composition does not dissipate formaldehyde.

시험 항목Test Items 단위unit 시료구분Sample classification 결과result 시험방법Test Methods 포름알데히드 방산량Formaldehyde Dissipation ㎎/ℓMg / l 검출 안됨Not detected 한국 화학시험 연구원장Korea Chemical Testing Institute

실험예 4. 천연 바닥장식재의 휘발성 유기화합물 방산량 측정Experimental Example 4 Measurement of the Dispersion of Volatile Organic Compounds in Natural Flooring Materials

본 발명에 실시예 1 및 2에 의해 제조된 천연 바닥장식재의 휘발성 유기화합물 방산량을 측정하기 위해, 하기와 같은 실험을 수행하였다.In order to measure the amount of volatile organic compound dissipation of the natural flooring material prepared by Examples 1 and 2 in the present invention, the following experiment was performed.

본 실험은 한국 화학시험연구원에서 시행하였고, 휘발성 유기화합물 방출은 KSM의 시험 방법을 이용하였다. 이때 측정은 온도 21℃, 습도 40% 및 대기중 음이온수 68/cc 조건하에서 수행하였으며, 그 결과는 하기 표 4에 나타내었다.This experiment was conducted by the Korea Testing and Research Institute, and the release of volatile organic compounds using KSM test method. At this time, the measurement was carried out under the conditions of temperature 21 ℃, humidity 40% and anion water 68 / cc conditions in the air, the results are shown in Table 4 below.

실험 결과, 본 천연소재 조성물에 의해 제조된 천연 바닥장식재는 휘발성 유 기화합물을 방산하지 않음을 확인할 수 있었다.Experimental results, it was confirmed that the natural flooring material prepared by the natural material composition does not dissipate volatile organic compounds.

시험 항목Test Items 단위unit 시료구분Sample classification 결과result 시험 방법Test Methods 휘발성 유기화합물 방산량Volatile Organic Compounds Wt %Wt% 검출 안됨Not detected 한국 화학시험 연구원Korea Chemical Testing Institute

상기와 같이, 본 발명의 바닥장식재용 천연 광석물 조성물은 음이온 분말 및 견운모를 이용하여 인체에 유익한 음이온을 발생하고 원적외선을 다량 방출할 뿐만 아니라 천연소재만을 사용하여 인체에 유해한 휘발성 유기용제, 포름알데히드, 중금속 등의 유해물질이 배출되지 않음을 확인할 수 있었다.As described above, the natural ore composition for floor decoration of the present invention generates an anion beneficial for the human body using anion powder and mica, and emits a large amount of far infrared rays, as well as volatile organic solvents and formaldehyde harmful to the human body using only natural materials. , It was confirmed that no harmful substances such as heavy metals are emitted.

본 발명의 천연 광석물 조성물은 견운모, 음이온 분말을 사용하여 인체에 유익한 음이온 및 원적외선을 다량 방출하고, 천연 소재만을 사용하여 인체에 유해한 유해물질이 배출되지 않고, 방염 및 탈취 기능이 탁월할 뿐만 아니라 바닥장식재 공정 완료후 규조토를 이용한 방습 작용으로 인해 우수한 항균 활성을 가짐으로써, 위생적이고 안전하며 친환경적인 다기능성 바닥장식재를 제공할 수 있다.The natural ore composition of the present invention emits a large amount of anions and far infrared rays beneficial to the human body by using biotite and anion powder, and does not emit harmful substances harmful to the human body using only natural materials, and is excellent in flame retardant and deodorizing function. After the completion of the flooring process has excellent antibacterial activity due to the moisture-proof action using the diatomaceous earth, it can provide a hygienic, safe and eco-friendly multi-functional flooring.

Claims (8)

하지층, 발포층, 함침층, 인쇄층, 상지층 및 코팅층이 순차적으로 적층된 구조를 갖는 일반적인 바닥장식재에 있어서, In the general floor decorative material having a structure in which a base layer, a foam layer, an impregnation layer, a printing layer, an upper layer and a coating layer are sequentially stacked, 상기 코팅층은 염화비닐수지 100 중량% 당, 견운모 25 내지 30 중량%, 음이온 분말 5 내지 10 중량%, 가소제 65 내지 75 중량%, 충전제 40 내지 80 중량%, 안정제 2 내지 4 중량%, 저온코팅 광촉매 복합금속산화물 5 내지 15 중량%을 포함하는 것을 특징으로 하는 바닥장식재용 천연 광석물 조성물.The coating layer per 100% by weight of the vinyl chloride resin, 25 to 30% by weight of mica, 5 to 10% by weight anionic powder, 65 to 75% by weight plasticizer, 40 to 80% by weight filler, 2 to 4% by weight stabilizer, low temperature coating photocatalyst Natural mineral composition for flooring, characterized in that containing 5 to 15% by weight of the composite metal oxide. 제 1 항에 있어서, 상기 견운모 및 음이온 분말의 입도는 1000 메쉬(Mesh) 내지 1500 메쉬인 것을 특징으로 하는 바닥재용 천연 광석물 조성물.The natural mineral composition for flooring according to claim 1, wherein the particle size of the biotite and anionic powder is 1000 mesh to 1500 mesh. 제 1 항에 있어서, 상기 조성물은 추가적으로 천연 잉크 또는 천연 접착제를 포함하는 것을 특징으로 하는 바닥재용 천연 광석물 조성물.2. The natural ore composition for flooring according to claim 1, wherein the composition additionally comprises a natural ink or a natural adhesive. 제 1 항에 있어서, 상기 가소제는 DOP이고, 충전제는 CaCo이며, 복합금속산화물은 Tio2, ZnO, CDS, ZrO2, SnO2, V2O2 또는 WO3 인 것을 특징으로 하는 바닥장식재용 천연 광석물 조성물.The method of claim 1, wherein the plasticizer is DOP, the filler is CaCo, the composite metal oxide is Tio 2 , ZnO, CDS, ZrO 2 , SnO 2 , V 2 O 2 or WO 3 characterized in that the natural Mineral composition. 제 1 항 내지 제 4 항 중 어느 한 항의 조성물을 이용하여 제조된 것을 특징으로 하는 천연 바닥장식재.A natural flooring material prepared using the composition of any one of claims 1 to 4. a) 견운모 및 음이온 분말을 분쇄하는 공정(S10);a) grinding the sorghum and anionic powder (S10); b) 상기 공정 a)에서 분쇄된 분말에 가소제, 충전제, 안정제 및 염화비닐수지와 혼합하는 공정(S20);b) mixing the powder ground in step a) with a plasticizer, a filler, a stabilizer and a vinyl chloride resin (S20); c) 상기 공정 b)의 혼합물에 천연 색소 및/또는 천연 접착제를 첨가 및 희석하는 공정(S30);c) adding and diluting the natural pigment and / or natural adhesive to the mixture of step b) (S30); d) 상기 공정 c)의 조성물을 6 내지 7 mm 두께를 갖는 바닥장식재에 도포하고, 압출금형 시루에서 200 내지 230 ℃에서 열처리 및 건조하는 공정(S40);d) applying the composition of step c) to a flooring material having a thickness of 6 to 7 mm, heat treatment and drying at 200 to 230 ° C in an extrusion mold through (S40); e) 복합금속산화물을 저온촉매로 이용하여 배전코팅을 하는 광촉매 공정(S50); 및e) a photocatalyst process of performing roasting coating using the composite metal oxide as a low temperature catalyst (S50); And f) 규조토로 흡습 및 방습하는 공정(S60);으로 제조되는 것을 특징으로 하는 천연 바닥장식재의 제조방법.f) a step of absorbing and moisture-proof with diatomaceous earth (S60); manufacturing method of natural flooring material characterized in that it is produced by. 상기 제 6 항의 제조방법에 의해 제조된 천연 바닥장식재.Natural flooring manufactured by the manufacturing method of claim 6. 제 1 항에 있어서, 상기 음이온 분말은 토르말린 및/또는 귀양석인 것을 특징으로하는 바닥재용 천연 광석물 조성물.The natural ore composition for flooring according to claim 1, wherein the anionic powder is tourmaline and / or gemstone.
KR1020040082486A 2004-10-15 2004-10-15 Natural mineral composition for flooring and the preparating method thereof KR100626870B1 (en)