CN105856000B - A kind of polishing method of daily-use fine without glaze paint carcass - Google Patents
A kind of polishing method of daily-use fine without glaze paint carcass Download PDFInfo
- Publication number
- CN105856000B CN105856000B CN201610436576.1A CN201610436576A CN105856000B CN 105856000 B CN105856000 B CN 105856000B CN 201610436576 A CN201610436576 A CN 201610436576A CN 105856000 B CN105856000 B CN 105856000B
- Authority
- CN
- China
- Prior art keywords
- daily
- carcass
- use fine
- glaze paint
- polishing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention discloses a kind of polishing method of daily-use fine without glaze paint carcass, and the daily-use fine is polished without glaze paint carcass using Sponge sand paper, polishing fluid and electric angle grinder；The polishing method comprises the following steps：Polishing fluid is first prepared, then the daily-use fine is placed in polishing fluid without glaze paint carcass and roughly ground with Sponge sand paper, clear water is dried after cleaning, and is polished with electric angle grinder, obtains the daily-use fine polished without glaze paint carcass；Wherein, described polishing fluid is made up of each raw material of following parts by weight：25~60 parts of ceramic polished 1 part of powder, 0.1~0.25 part of thickening agent and water.The polishing method of the present invention realizes the mechanization polishing of daily-use fine plane, cambered surface and irregular male and fomale(M＆F) without glaze paint carcass, reduce production cost, production efficiency is improved, the daily-use fine for polishing to obtain is more than 97% without the disposable qualification rate of glaze paint carcass, while surface roughness is less than 5nm.
Description
Technical field
The present invention relates to ceramic product processing technique field, more particularly to a kind of polishing side of the daily-use fine without glaze paint carcass
Method.
Background technology
With the continuous improvement of living standard, consumption demand of the people to domestic ceramic product is made by original generality
It is converted into function with higher artistry, aesthetic property, sight, the use demand of security.Particularly to its outward appearance matter
Amount is that porcelain, tone, moulding, glaze paint propose higher requirement, such as require that whiteness is high, translucence is good, heat endurance, machine
Tool intensity is big etc..Ceramic is from passing single nontoxic, harmless white tire Pengyang china stone, to color diversification, nothing
Malicious, harmless Pengyang china stone transformation.The glazing mode of Pengyang china stone is also changed to local base substrate from whole base substrate glazing
Glazing has also obtained widely should in daily life to show tire matter U.S. without the white tire of glaze and without glaze colours tire daily-use fine
With.
In order to meet the white tire of no glaze and requirement without glaze colours tire daily-use fine in life, it is necessary to obtain high smooth
Plane, cambered surface and irregular male and fomale(M＆F) can only realize plane polishing without glaze carcass using common polishing method, and broken
Loss rate is big, and also to expend substantial amounts of equipment cost, also takes up substantial amounts of place, and efficiency is also very low.Therefore, from prior art
In can not obtain high smooth, the daily-use fine plane of low roughness, cambered surface and irregular male and fomale(M＆F) without glaze carcass.
The content of the invention
In view of this, it is an object of the invention to propose a kind of polishing method of daily-use fine without glaze paint carcass, this method
Mechanization polishing of the daily-use fine without glaze paint carcass is realized, production cost is reduced, improves production efficiency, polish what is obtained
Daily-use fine is low without the disposable qualification rate height of glaze paint carcass, surface roughness.
Based on above-mentioned purpose, polishing method of a kind of daily-use fine without glaze paint carcass provided by the invention, sand sponge is used
Paper, polishing fluid and electric angle grinder polish to the daily-use fine without glaze paint carcass；The polishing method comprises the following steps：First
Polishing fluid is prepared, then the daily-use fine is placed in polishing fluid without glaze paint carcass and roughly ground with Sponge sand paper, clear water is done after cleaning
It is dry, it is polished with electric angle grinder, obtains the daily-use fine polished without glaze paint carcass；
Wherein, described polishing fluid is made up of each raw material of following parts by weight：Ceramic polished 1 part of powder, thickening agent 0.1~
0.25 part and 25~60 parts of water.
Daily-use fine in the present invention refers to that daily-use fine product does not have the carcass of glazing part without glaze paint carcass.
Preferably, described polishing fluid is made up of each raw material of following parts by weight：Ceramic polished 1 part of powder, thickening agent 0.15
~0.25 part and 40~60 parts of water.
Preferably, the ceramic polished powder includes the Al that average diameter of particles is 1~3 μm2O3Particulate；The thickening agent is
Xanthans.
The polishing fluid of the present invention adds xanthans in preparation process, and the Main Ingredients and Appearance of xanthans is carbohydrate, right
Ceramic polished powder plays suspension effect, makes mobility or soft durometer complementation between the powder of ceramic polished powder, reaches more preferable throwing
Light effect.Xanthans also functions to lubrication simultaneously, will not hurt ceramic body.
Preferably, the Sponge sand paper fineness is the mesh of 300 mesh~600；The rotating speed of the electric angle grinder is 11000r/
Min, the wool that the bistrique that the electric angle grinder uses is diameter 100mm mirror-finish bistrique.
The present invention can grind off the coarse part of daily-use fine product surface, the generation of surface roughness features using Sponge sand paper
Reason is the fine porcelain product vestige that wash water leaves in green compact, and the green compact of all ceramic products have wash water process, can all stayed
The vestige of lower wash water, if glazing can covers vestige after wash water, if not glazing vestige will show, and the day of the present invention
No longer glazing, as finished product after being polished with fine porcelain without glaze paint carcass.So before polishing, it is necessary to need to select according to production
Sponge sand paper is roughly ground to daily-use fine without glaze paint carcass.
Preferably, the surface roughness of the daily-use fine polished without glaze paint carcass is less than 5nm.
Preferably, the daily-use fine includes white tire and color tire daily-use fine.
Preferably, the daily-use fine includes white tire and color tire daily-use fine plane, cambered surface and irregular without glaze paint carcass
Male and fomale(M＆F) is without glaze paint carcass.
Preferably, the time roughly ground with Sponge sand paper is no more than 1min；The time of the polishing is often to polish 1cm2
Daily-use fine without being 0.06~0.12s the time required to glaze paint carcass.
The daily-use fine that polishing method according to the present invention obtains is more than 97% without glaze paint carcass, disposable qualification rate, day
It is less than 5nm with surface roughness of the fine porcelain without glaze paint carcass.
The polishing method of daily-use fine plane, cambered surface and irregular male and fomale(M＆F) without glaze carcass of the present invention belongs to mechanical grinding
Polishing technology, chemical property of the daily-use fine without glaze paint carcass will not be changed, will not be to using the consumer without glaze daily-use fine
Have an impact.
Further, present invention also offers a kind of polishing fluid of daily-use fine without glaze paint carcass, described polishing fluid by
Each raw material of following parts by weight is made：25~60 parts of ceramic polished 1 part of powder, 0.1~0.25 part of thickening agent and water；The ceramics
Polishing powder includes the Al that average diameter of particles is 1~3 μm2O3Particulate；The thickening agent is xanthans.
Preferably, the ceramic polished powder is made up of each raw material of following parts by weight：Ceramic polished 1 part of powder, thickening agent
0.15~0.25 part and 40~60 parts of water.
The present invention also develops the polishing fluid matched with daily-use fine without glaze paint carcass product, polishes obtained daily-use fine
It is high without the disposable qualification rate of glaze paint carcass product and surface roughness of the daily-use fine without glaze paint carcass product is low.
Compared with prior art, method of the invention has the advantages that：
(1) polishing method of the invention realizes daily-use fine plane, cambered surface and irregular male and fomale(M＆F) without glaze paint carcass
Mechanization polishes, and disposable qualification rate is more than 97%, and surface roughness is less than 5nm, polishing efficiency greatly improved, significantly
Reduce polishing cost.
(2) present invention, which uses, contains Al2O3The polishing fluid of particulate, wherein Al2O3The average diameter of particulate is 1~3 μm, is thrown
Light liquid is readily available, and cost is low.
(3) technological parameter is easily controlled in polishing method of the invention, and equipment is readily available, practical, and technique is simplified,
It is with short production cycle.
(4) present invention polishes daily-use fine without glaze paint carcass by mechanical grinding, and it is daily thin that the smooth no glaze in surface is made
Porcelain products, show tire matter U.S. of the white tire of daily-use fine and color tire, meet consumption demand.
Embodiment
For the object, technical solutions and advantages of the present invention are more clearly understood, below in conjunction with specific embodiment, to this hair
Bright further description.
Embodiment 1
The white tire plane of daily-use fine is polished without glaze paint carcass using Sponge sand paper, polishing fluid and electric angle grinder, including
Following steps：Polishing fluid is first prepared, the white tire plane of daily-use fine is placed in polishing fluid without glaze paint carcass, is 300 mesh with fineness
Sponge sand paper corase grind, corase grind the time be 1 minute, clear water clean after dry, the angular mill for being 11000r/min with 700W rotating speeds
Ray machine is polished, and the wool that the bistrique that electric angle grinder uses is diameter 100mm mirror-finishes bistrique, and the white tire of daily-use fine is put down
Area of the face without glaze paint carcass is less than or equal to 500CM2When, polishing time is less than 1 minute.Described polishing fluid includes 100g, 25g
With 6kg ceramic polished powder, thickening agent and water, the ceramic polished powder includes the Al that average diameter of particles is 1~3 μm2O3, institute
The thickening agent stated is xanthans, and Main Ingredients and Appearance is carbohydrate, and plane is made without the white tire of the smooth daily-use fine of glaze paint carcass
Product.
According to the white tire plane of daily-use fine that the present embodiment obtains without glaze paint carcass, disposable qualification rate is 98%, surface
Roughness is 3.2nm.
Embodiment 2
Daily-use fine color tire plane is polished without glaze paint carcass using Sponge sand paper, polishing fluid and electric angle grinder, including
Following steps：Polishing fluid is first prepared, daily-use fine color tire plane is placed in polishing fluid without glaze paint carcass, is 600 mesh with fineness
Sponge sand paper corase grind, corase grind the time be 0.2 minute, clear water clean after dry, be the angular of 11000r/min with 700W rotating speeds
Sanding machine is polished, and the wool that the bistrique that electric angle grinder uses is diameter 100mm mirror-finishes bistrique, daily-use fine color tire
Area of the plane without glaze paint carcass is in 500CM2And 1000CM2Between when, polishing time was more than 1 minute and less than 2 minute.It is described
Polishing fluid include 100g, 15g and 4kg ceramic polished powder, thickening agent and water, it is averagely straight that the ceramic polished powder includes particle
Footpath is 1~3 μm of Al2O3, described thickening agent is xanthans, and Main Ingredients and Appearance is carbohydrate, and plane is made without glaze paint carcass
Smooth daily-use fine color tire product.
According to the daily-use fine color tire plane that the present embodiment obtains without glaze paint carcass, disposable qualification rate is 98%, surface
Roughness is 3.4nm.
Embodiment 3
The white tire cambered surface of daily-use fine is polished without glaze paint carcass using Sponge sand paper, polishing fluid and electric angle grinder, including
Following steps：Polishing fluid is first prepared, the white tire cambered surface of daily-use fine is placed in polishing fluid without glaze paint carcass, is 450 mesh with fineness
Sponge sand paper corase grind, corase grind the time be 0.6 minute, clear water clean after dry, be the angular of 11000r/min with 700W rotating speeds
Sanding machine is polished, and the wool that the bistrique that electric angle grinder uses is diameter 100mm mirror-finishes bistrique, the white tire of daily-use fine
Area of the cambered surface without glaze paint carcass is in 500CM2And 1000CM2Between when, polishing time was more than 1 minute and less than 2 minute.It is described
Polishing fluid include 100g, 10g and 2.5kg ceramic polished powder, thickening agent and water, the ceramic polished powder is averaged including particle
A diameter of 1~3 μm of Al2O3, described thickening agent is xanthans, and Main Ingredients and Appearance is carbohydrate, and cambered surface is made without glaze paint tire
The white tire product of the smooth daily-use fine of body.
According to the white tire cambered surface of daily-use fine that the present embodiment obtains without glaze paint carcass, disposable qualification rate is 98%, surface
Roughness is 3.5nm.
Embodiment 4
Daily-use fine color tire cambered surface is polished without glaze paint carcass using Sponge sand paper, polishing fluid and electric angle grinder, including
Following steps：Polishing fluid is first prepared, daily-use fine color tire cambered surface is placed in polishing fluid without glaze paint carcass, is 300 mesh with fineness
Sponge sand paper corase grind, corase grind the time be 1 minute, clear water clean after dry, the angular mill for being 11000r/min with 700W rotating speeds
Ray machine is polished, and the wool that the bistrique that electric angle grinder uses is diameter 100mm mirror-finishes bistrique, daily-use fine color tire arc
Area of the face without glaze paint carcass is less than or equal to 500CM2When, polishing time is less than 1 minute.Described polishing fluid includes 100g, 18g
With 4.5kg ceramic polished powder, thickening agent and water, the ceramic polished powder includes the Al that average diameter of particles is 1~3 μm2O3,
Described thickening agent is xanthans, and Main Ingredients and Appearance is carbohydrate, and cambered surface is made without the smooth daily-use fine color of glaze paint carcass
Tire product.
According to the daily-use fine color tire cambered surface that the present embodiment obtains without glaze paint carcass, disposable qualification rate is 98%, surface
Roughness is 3.8nm.
Embodiment 5
The irregular male and fomale(M＆F) of the white tire of daily-use fine is thrown without glaze paint carcass using Sponge sand paper, polishing fluid and electric angle grinder
Light, comprise the following steps：Polishing fluid is first prepared, the irregular male and fomale(M＆F) of the white tire of daily-use fine is placed in polishing fluid without glaze paint carcass
In, roughly ground with fineness for the Sponge sand paper of 450 mesh, the corase grind time is 0.6 minute, and clear water is dried after cleaning, and is with 700W rotating speeds
11000r/min electric angle grinder is polished, and the wool that the bistrique that electric angle grinder uses is diameter 100mm mirror-finishes
Bistrique, area of the irregular male and fomale(M＆F) of the white tire of daily-use fine without glaze paint carcass is in 500CM2And 1000CM2Between when, polishing time
More than 1 minute and less than 2 minutes.Described polishing fluid includes 100g, 20g and 5.0kg ceramic polished powder, thickening agent and water,
The ceramic polished powder includes the Al that average diameter of particles is 1~3 μm2O3, described thickening agent is xanthans, and Main Ingredients and Appearance is
Carbohydrate, irregular male and fomale(M＆F) is made without the white tire product of the smooth daily-use fine of glaze paint carcass.
According to the present embodiment obtain the irregular male and fomale(M＆F) of the white tire of daily-use fine be without glaze paint carcass, disposable qualification rate
97%, surface roughness 4.0nm.
Embodiment 6
The irregular male and fomale(M＆F) of daily-use fine color tire is thrown without glaze paint carcass using Sponge sand paper, polishing fluid and electric angle grinder
Light, comprise the following steps：Polishing fluid is first prepared, the irregular male and fomale(M＆F) of daily-use fine color tire is placed in polishing fluid without glaze paint carcass
In, roughly ground with fineness for the Sponge sand paper of 600 mesh, the corase grind time is 0.2 minute, and clear water is dried after cleaning, and is with 700W rotating speeds
11000r/min electric angle grinder is polished, and the wool that the bistrique that electric angle grinder uses is diameter 100mm mirror-finishes
Bistrique, area of the irregular male and fomale(M＆F) of daily-use fine color tire without glaze paint carcass are less than or equal to 500CM2When, polishing time is less than 1 point
Clock.Described polishing fluid includes 100g, 25g and 6kg ceramic polished powder, thickening agent and water, and the ceramic polished powder includes
The Al that grain average diameter is 1~3 μm2O3, described thickening agent is xanthans, and Main Ingredients and Appearance is carbohydrate, is made irregular
Male and fomale(M＆F) is without the smooth daily-use fine color tire product of glaze paint carcass.
According to the present embodiment obtain the irregular male and fomale(M＆F) of daily-use fine color tire be without glaze paint carcass, disposable qualification rate
97%, surface roughness 4.5nm.
Those of ordinary skills in the art should understand that：The discussion of any of the above embodiment is exemplary only, not
It is intended to imply that the scope of the present disclosure (including claim) is limited to these examples；Under the thinking of the present invention, above example
Or can also be combined between the technical characteristic in different embodiments, and the different aspect of the present invention as described above be present
Many other changes, in order to it is concise they do not provided in details.Therefore, within the spirit and principles of the invention,
Any omission for being made, modification, equivalent substitution, improvement etc., should be included in the scope of the protection.
Claims (9)
1. polishing method of a kind of daily-use fine without glaze paint carcass, it is characterised in that use Sponge sand paper, polishing fluid and angular mill
Ray machine polishes to the daily-use fine without glaze paint carcass；The polishing method comprises the following steps：First prepare polishing fluid, then by institute
State daily-use fine and be placed in without glaze paint carcass in polishing fluid and roughly ground with Sponge sand paper, clear water is dried after cleaning, and is entered with electric angle grinder
Row polishing, the daily-use fine polished is obtained without glaze paint carcass；
Wherein, described polishing fluid is made up of each raw material of following parts by weight：Ceramic polished 1 part of powder, 0.1~0.25 part of thickening agent
And 25~60 parts of water；The ceramic polished powder includes the Al that average diameter of particles is 1~3 μm2O3Particulate；The thickening agent is
Xanthans.
2. polishing method of the daily-use fine according to claim 1 without glaze paint carcass, it is characterised in that described polishing fluid
It is made up of each raw material of following parts by weight：40~60 parts of ceramic polished 1 part of powder, 0.15~0.25 part of thickening agent and water.
3. polishing method of the daily-use fine according to claim 1 without glaze paint carcass, it is characterised in that the Sponge sand paper
Fineness is the mesh of 300 mesh~600；The rotating speed of the electric angle grinder is 11000r/min, the bistrique that the electric angle grinder uses
Bistrique is mirror-finished for diameter 100mm wool.
4. polishing method of the daily-use fine according to claim 1 without glaze paint carcass, it is characterised in that described to have polished
Surface roughness of the daily-use fine without glaze paint carcass is less than 5nm.
5. polishing method of the daily-use fine according to claim 1 without glaze paint carcass, it is characterised in that the daily-use fine
Including white tire and color tire daily-use fine.
6. polishing method of the daily-use fine according to claim 1 without glaze paint carcass, it is characterised in that the daily-use fine
Include white tire and color tire daily-use fine plane, cambered surface and irregular male and fomale(M＆F) without glaze paint carcass without glaze paint carcass.
7. polishing method of the daily-use fine according to claim 1 without glaze paint carcass, it is characterised in that described to use sand sponge
The time of paper corase grind is no more than 1min；The time of the polishing is often to polish 1cm2Daily-use fine without the time required to glaze paint carcass
For 0.06~0.12s.
8. polishing fluid of a kind of daily-use fine without glaze paint carcass, it is characterised in that described polishing fluid is each by following parts by weight
Raw material is made：25~60 parts of ceramic polished 1 part of powder, 0.1~0.25 part of thickening agent and water；The ceramic polished powder includes particle
Average diameter is 1~3 μm of Al2O3Particulate；The thickening agent is xanthans.
9. polishing fluid of the daily-use fine according to claim 8 without glaze paint carcass, it is characterised in that the ceramic polished powder
It is made up of each raw material of following parts by weight：40~60 parts of ceramic polished 1 part of powder, 0.15~0.25 part of thickening agent and water.