CN105837164A - Environment-friendly decorative brick block with juicy peach aromatic smell - Google Patents
Environment-friendly decorative brick block with juicy peach aromatic smell Download PDFInfo
- Publication number
- CN105837164A CN105837164A CN201610160451.0A CN201610160451A CN105837164A CN 105837164 A CN105837164 A CN 105837164A CN 201610160451 A CN201610160451 A CN 201610160451A CN 105837164 A CN105837164 A CN 105837164A
- Authority
- CN
- China
- Prior art keywords
- parts
- brick
- soak
- honey peach
- fragment
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses an environment-friendly decorative brick block with a juicy peach aromatic smell, and relates to the field of building materials; the brick block is prepared from the following components in parts by weight: 30-45 parts of attapulgite clay, 20-25 parts of plant ash, 5-10 parts of rosin oil, 25-30 parts of coal gangue, 10-15 parts of river sand, 10-15 parts of a lime powder, and 60-80 parts of a soaking liquid. Compared with traditional brick blocks, the brick block does not contain chemical additive components in raw material ingredients, has the manufacturing process greatly improved, has light juicy peach aroma, has the efficacy of improving the environment, moreover, does not release harmful gases, is greener and more environmentally friendly, and solves the problems that traditional decorative brick block bodies have larger pungent odor, easily release harmful gases with long-term use, and not only pollute the environment but also bring damage problem to human body health.
Description
Technical field:
The present invention relates to building material field, be specifically related to a kind of environmental protection with honey peach aromatic odor and fill
Decorations fragment of brick.
Background technology:
Along with social progress and development, fragment of brick is the most only limited to the use of house foundation, wall support etc.,
Increasing fragment of brick is applied to beautify the environment and decorative environment, such as laying the grass-planting brick on lawn,
For the decoration fragment of brick of shop interior decoration, and it is solely for the appreciation fragment of brick appreciated, no matter is in technique
Or in moulding, there is the biggest breakthrough, to meet the demand of the mankind and market, traditional decorative brick
Block is due to composition of raw materials and the difference of manufacturing process, only the most attractive in moulding, but ignores brick
Body self improves, and causes a variety of decorative brick block self with bigger sharp aroma, uses for a long time,
Easily discharge harmful gas, not only pollute environment, and health is brought damage.
Summary of the invention:
The present invention solves the problems referred to above, it is provided that a kind of environmental-protection decorative fragment of brick with honey peach aromatic odor,
This fragment of brick in terms of composition of raw materials and manufacturing process with tradition fragment of brick compared be all significantly improved, do not contain
Chemical addition agent composition, not only self is with light honey peach fragrance, has the effect improving environment,
And harmful gas, more environmental protection will not be discharged.
The technical problem to be solved uses following technical scheme to realize:
A kind of environmental-protection decorative fragment of brick with honey peach aromatic odor, it is characterised in that described fragment of brick by with
The formulation ratio of lower weight portion is made:
Attapulgite clay 30-45 part, plant ash 20-25 part, retinal 5-10 part, gangue 25-30 part,
River sand 10-15 part, pulverized limestone 10-15 part, soak 60-80 part.
Preferably, described fragment of brick is made up of the formulation ratio of following weight portion: attapulgite clay 30 parts, grass
Wood ash 20 parts, retinal 5 parts, gangue 25 parts, river sand 10 parts, pulverized limestone 10 parts, soak 60 parts.
Described attapulgite clay is made up of the formulation ratio of following weight portion: attapulgite 100 parts, Oleum Brassicae campestris
Cake 35 parts, distilled water 100 parts.
Described soak is made up of formulation ratio and the processing technology of following weight portion: 40 parts of honey peach fruit jam,
Vegetable oil 8 parts, white vinegar 5 parts, ethanol 5 parts, 80 parts of water.
Present invention additionally comprises the manufacture method of a kind of environmental-protection decorative fragment of brick with honey peach aromatic odor, root
Raw material according to weight portion described above, it is characterised in that following steps:
1), attapulgite clay is made: attapulgite and rap oil seedcake are put into grinder-mixer and pulverizes
Mix homogeneously after stirring, cross 200 eye mesh screens filter after, add distilled water be again stirring for mixing after, insert high pressure
Steamer steams 8-10 hour, and heating-up temperature is 180-230 DEG C, and cooling is taken out, and prepares attapulgite clay standby,
The moisture content of attapulgite clay is 45-50%, after attapulgite mixes with rap oil seedcake stirring, filters impurity,
Obtain attapulgite essence soil and pulverize rap oil seedcake granule, being mixed to get attapulgite through distilled water secondary stirring
Slurry, by autoclave heating fumigating so that attapulgite essence soil is abundant with the Oleum Brassicae campestris in rap oil seedcake
Merging, the attapulgite clay prepared, granule is uniform, viscosity is big, adsorptivity is strong, adds the viscous of raw material
Degree and intensity, also can play raising hardness and the effect of compactness to the fragment of brick of post-production, makes to prepare
Fragment of brick is durable；
2), soak is made: after the stirring mixing of honey peach fruit jam, vegetable oil, white vinegar, ethanol and water,
The steamer being placed in 120 DEG C heats steaming and decocting 1-2 hour, cooling, prepares soak standby, by honey peach fruit jam
Adding water heating with vegetable oil, white vinegar, ethanol, vegetable oil increases the viscosity of honey peach fruit jam, heats simultaneously
The rear dissolving being beneficial to honey peach fruit jam, white vinegar and ethanol produce reaction after heating with honey peach fruit jam, strengthen
The abnormal smells from the patient of honey peach self, by the post-heating that adds water, makes honey peach fruit jam fully and water dissolution, honey peach
Distinctive fragrance be dissolved in water and pinned by vegetable oil, it is to avoid volatilization waste so that the later stage manufacture fragment of brick
Time, fully merge with fragment of brick, increase the aromatic odor of fragment of brick；
3), pulverize coal gangue after cross 200 eye mesh screens filter impurity, obtain gangue fines, by gangue
Fines and plant ash, river sand, pulverized limestone, attapulgite clay, be uniformly mixed by sealing blender,
Prepare compound standby, stirred by sealing so that the above-mentioned full and uniform mixing of each raw material, it is ensured that later stage
During brickmaking, the brick body texture of fragment of brick is fine and smooth, improves intensity；
4), above-mentioned compound being added soak and retinal, heated sealed stirs, and heating-up temperature is
60-80 DEG C, mixing time is 6-8 hour, and after stirring terminates, cooling standing is thoroughly mixed to soak
Material absorbs, and prepares immersion compound standby, and heated sealed stirs so that soak and retinal are easier
In merging with compound, with compound rapid fusion after soak heating, it is to avoid fragrance volatilizing and escape,
Retinal increases the viscosity within compound, is beneficial to pin the fragrance of soak so that the brick that the later stage makes
Block, the most durable, texture is fine and smooth, and also fragrance is more lasting；
5), pour above-mentioned immersion compound into mould, remove water by steam pressurization, stripping and slicing, evacuation
Point, after Quick-air-drying, i.e. prepare the environmental-protection decorative fragment of brick with honey peach aromatic odor, by above-mentioned step
Suddenly, it is to avoid by sintering processing, the honey peach fragrance within brick body is caused to run off under high temperature sintering, with
Time removed by the way of moisture, Quick-air-drying by steam pressurization, stripping and slicing, evacuation, be beneficial to pin brick body
Internal honey peach fragrance, it is ensured that the exquisiteness of brick body texture, and the compactness of brick body inner materials, with
Strengthen intensity and the durability degree of brick body.
A kind of environmental-protection decorative fragment of brick with honey peach aromatic odor of offer is provided,
Compared with tradition fragment of brick, this fragment of brick is on material composition, without chemical addition agent composition, in manufacturing process
On greatly improve, not only self is with light honey peach fragrance, has the effect improving environment, and
Harmful gas, more environmental protection will not be discharged.
Detailed description of the invention:
For the technological means making the present invention realize, creation characteristic, reach purpose and effect and be readily apparent from
Solve, below in conjunction with embodiment, the present invention is expanded on further.
Embodiment one
A kind of environmental-protection decorative fragment of brick with honey peach aromatic odor, by the formulation ratio system of following weight portion
Become:
Attapulgite clay 30 parts, plant ash 20 parts, retinal 5 parts, gangue 25 parts, river sand 10 parts, stone
Ashes 10 parts, soak 60 parts.
Described attapulgite clay is made up of the formulation ratio of following weight portion: attapulgite 100 parts, Oleum Brassicae campestris
Cake 35 parts, distilled water 100 parts.
Described soak is made up of formulation ratio and the processing technology of following weight portion: 40 parts of honey peach fruit jam,
Vegetable oil 8 parts, white vinegar 5 parts, ethanol 5 parts, 80 parts of water.
The manufacture method of a kind of environmental-protection decorative fragment of brick with honey peach aromatic odor, according to described above
The raw material of weight portion, it is characterised in that following steps:
1), attapulgite clay is made: attapulgite and rap oil seedcake are put into grinder-mixer and pulverizes
Mix homogeneously after stirring, cross 200 eye mesh screens filter after, add distilled water be again stirring for mixing after, insert high pressure
Steamer steams 8-10 hour, and heating-up temperature is 180-230 DEG C, and cooling is taken out, and prepares attapulgite clay standby；
2), soak is made: after the stirring mixing of honey peach fruit jam, vegetable oil, white vinegar, ethanol and water,
The steamer being placed in 120 DEG C heats steaming and decocting 1-2 hour, cooling, prepares soak standby；
3), pulverize coal gangue after cross 200 eye mesh screens filter impurity, obtain gangue fines, by gangue
Fines and plant ash, river sand, pulverized limestone, attapulgite clay, be uniformly mixed by sealing blender,
Prepare compound standby；
4), above-mentioned compound being added soak and retinal, heated sealed stirs, and heating-up temperature is
60-80 DEG C, mixing time is 6-8 hour, and after stirring terminates, cooling standing is thoroughly mixed to soak
Material absorbs, and prepares immersion compound standby；
5), pour above-mentioned immersion compound into mould, remove water by steam pressurization, stripping and slicing, evacuation
Point, after Quick-air-drying, i.e. prepare the environmental-protection decorative fragment of brick with honey peach aromatic odor.
Embodiment two
A kind of environmental-protection decorative fragment of brick with honey peach aromatic odor, by the formulation ratio system of following weight portion
Become:
Attapulgite clay 40 parts, plant ash 23 parts, retinal 8 parts, gangue 258 parts, river sand 12 parts,
Pulverized limestone 12 parts, soak 70 parts.
Described attapulgite clay is made up of the formulation ratio of following weight portion: attapulgite 100 parts, Oleum Brassicae campestris
Cake 35 parts, distilled water 100 parts.
Described soak is made up of formulation ratio and the processing technology of following weight portion: 40 parts of honey peach fruit jam,
Vegetable oil 8 parts, white vinegar 5 parts, ethanol 5 parts, 80 parts of water.
The manufacture method of a kind of environmental-protection decorative fragment of brick with honey peach aromatic odor, according to described above
The raw material of weight portion, it is characterised in that following steps:
1), attapulgite clay is made: attapulgite and rap oil seedcake are put into grinder-mixer and pulverizes
Mix homogeneously after stirring, cross 200 eye mesh screens filter after, add distilled water be again stirring for mixing after, insert high pressure
Steamer steams 8-10 hour, and heating-up temperature is 180-230 DEG C, and cooling is taken out, and prepares attapulgite clay standby；
2), soak is made: after the stirring mixing of honey peach fruit jam, vegetable oil, white vinegar, ethanol and water,
The steamer being placed in 120 DEG C heats steaming and decocting 1-2 hour, cooling, prepares soak standby；
3), pulverize coal gangue after cross 200 eye mesh screens filter impurity, obtain gangue fines, by gangue
Fines and plant ash, river sand, pulverized limestone, attapulgite clay, be uniformly mixed by sealing blender,
Prepare compound standby；
4), above-mentioned compound being added soak and retinal, heated sealed stirs, and heating-up temperature is
60-80 DEG C, mixing time is 6-8 hour, and after stirring terminates, cooling standing is thoroughly mixed to soak
Material absorbs, and prepares immersion compound standby；
5), pour above-mentioned immersion compound into mould, remove water by steam pressurization, stripping and slicing, evacuation
Point, after Quick-air-drying, i.e. prepare the environmental-protection decorative fragment of brick with honey peach aromatic odor.
Embodiment three
A kind of environmental-protection decorative fragment of brick with honey peach aromatic odor, by the formulation ratio system of following weight portion
Become:
Attapulgite clay 45 parts, plant ash 25 parts, retinal 10 parts, gangue 30 parts, river sand 15 parts,
Pulverized limestone 15 parts, soak 80 parts.
Described attapulgite clay is made up of the formulation ratio of following weight portion: attapulgite 100 parts, Oleum Brassicae campestris
Cake 35 parts, distilled water 100 parts.
Described soak is made up of formulation ratio and the processing technology of following weight portion: 40 parts of honey peach fruit jam,
Vegetable oil 8 parts, white vinegar 5 parts, ethanol 5 parts, 80 parts of water.
The manufacture method of a kind of environmental-protection decorative fragment of brick with honey peach aromatic odor, according to described above
The raw material of weight portion, it is characterised in that following steps:
1), attapulgite clay is made: attapulgite and rap oil seedcake are put into grinder-mixer and pulverizes
Mix homogeneously after stirring, cross 200 eye mesh screens filter after, add distilled water be again stirring for mixing after, insert high pressure
Steamer steams 8-10 hour, and heating-up temperature is 180-230 DEG C, and cooling is taken out, and prepares attapulgite clay standby；
2), soak is made: after the stirring mixing of honey peach fruit jam, vegetable oil, white vinegar, ethanol and water,
The steamer being placed in 120 DEG C heats steaming and decocting 1-2 hour, cooling, prepares soak standby；
3), pulverize coal gangue after cross 200 eye mesh screens filter impurity, obtain gangue fines, by gangue
Fines and plant ash, river sand, pulverized limestone, attapulgite clay, be uniformly mixed by sealing blender,
Prepare compound standby；
4), above-mentioned compound being added soak and retinal, heated sealed stirs, and heating-up temperature is
60-80 DEG C, mixing time is 6-8 hour, and after stirring terminates, cooling standing is thoroughly mixed to soak
Material absorbs, and prepares immersion compound standby；
5), pour above-mentioned immersion compound into mould, remove water by steam pressurization, stripping and slicing, evacuation
Point, after Quick-air-drying, i.e. prepare the environmental-protection decorative fragment of brick with honey peach aromatic odor.
Claims (5)
1. the environmental-protection decorative fragment of brick with honey peach aromatic odor, it is characterised in that described fragment of brick by
The formulation ratio of following weight portion is made:
Attapulgite clay 30-45 part, plant ash 20-25 part, retinal 5-10 part, gangue 25-30 part,
River sand 10-15 part, pulverized limestone 10-15 part, soak 60-80 part.
A kind of environmental-protection decorative fragment of brick with honey peach aromatic odor the most according to claim 1, it is special
Levy and be, it is preferred that described fragment of brick is made up of the formulation ratio of following weight portion: attapulgite clay 30 parts,
Plant ash 20 parts, retinal 5 parts, gangue 25 parts, river sand 10 parts, pulverized limestone 10 parts, soak 60 parts.
A kind of environmental-protection decorative fragment of brick with honey peach aromatic odor the most according to claim 1, it is special
Levying and be, described attapulgite clay is made up of the formulation ratio of following weight portion: attapulgite 100 parts, dish
35 parts of seed oil cake, distilled water 100 parts.
A kind of environmental-protection decorative fragment of brick with honey peach aromatic odor the most according to claim 1, it is special
Levying and be, described soak is made up of formulation ratio and the processing technology of following weight portion: honey peach fruit jam
40 parts, vegetable oil 8 parts, white vinegar 5 parts, ethanol 5 parts, 80 parts of water.
5. with the manufacture method of environmental-protection decorative fragment of brick for honey peach aromatic odor, according to described above
The raw material of weight portion, it is characterised in that following steps:
1), attapulgite clay is made: attapulgite and rap oil seedcake are put into grinder-mixer and pulverizes
Mix homogeneously after stirring, cross 200 eye mesh screens filter after, add distilled water be again stirring for mixing after, insert high pressure
Steamer steams 8-10 hour, and heating-up temperature is 180-230 DEG C, and cooling is taken out, and prepares attapulgite clay standby,
The moisture content of attapulgite clay is 45-50%；
2), soak is made: after the stirring mixing of honey peach fruit jam, vegetable oil, white vinegar, ethanol and water,
The steamer being placed in 120 DEG C heats steaming and decocting 1-2 hour, cooling, prepares soak standby；
3), pulverize coal gangue after cross 200 eye mesh screens filter impurity, obtain gangue fines, by gangue
Fines and plant ash, river sand, pulverized limestone, attapulgite clay, be uniformly mixed by sealing blender,
Prepare compound standby；
4), above-mentioned compound being added soak and retinal, heated sealed stirs, and heating-up temperature is
60-80 DEG C, mixing time is 6-8 hour, and after stirring terminates, cooling standing is thoroughly mixed to soak
Material absorbs, and prepares immersion compound standby；
5), pour above-mentioned immersion compound into mould, remove water by steam pressurization, stripping and slicing, evacuation
Point, after Quick-air-drying, i.e. prepare the environmental-protection decorative fragment of brick with honey peach aromatic odor.