CN105693206A - Environment-friendly decorative brick with mango aromatic smell - Google Patents
Environment-friendly decorative brick with mango aromatic smell Download PDFInfo
- Publication number
- CN105693206A CN105693206A CN201610160543.9A CN201610160543A CN105693206A CN 105693206 A CN105693206 A CN 105693206A CN 201610160543 A CN201610160543 A CN 201610160543A CN 105693206 A CN105693206 A CN 105693206A
- Authority
- CN
- China
- Prior art keywords
- parts
- brick
- soak
- fragment
- attapulgite clay
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses an environment-friendly decorative brick with mango aromatic smell, and relates to the field of building materials. The brick is prepared from the following raw materials in parts by weight: 30-45 parts of attapulgite clay, 20-25 parts of plant ash, 5-10 parts of rosin oil, 25-30 parts of coal gangue, 10-15 parts of river sand, 10-15 parts of lime powder and 60-80 parts of soak solution. Compared with the conventional brick, the brick has the advantages that the raw material components of the brick do not contain any chemical additive component, a manufacturing process is improved greatly, the brick has light mango aromatic smell and an effect of improving the environment, does not release harmful gas, and is more environmentally friendly; the problems of pollution on the environment and harm to body health due to the fact that the conventional decorative brick has strong sharp aroma and tends to release harmful gas after long-time use are solved.
Description
Technical field:
The present invention relates to building material field, be specifically related to a kind of environmental-protection decorative fragment of brick with Fructus Mangifera Indicae aromatic odor。
Background technology:
Along with social progress and development, fragment of brick no longer only limits to for house foundation, wall support etc., increasing fragment of brick is applied to beautify the environment and decorative environment, such as laying the grass-planting brick on lawn, decoration fragment of brick for shop interior decoration, and it is solely for the appreciation fragment of brick appreciated, no matter it is in technique or in moulding, there is very big breakthrough, to meet the demand of the mankind and market, traditional decoration fragment of brick is due to the difference of composition of raw materials and manufacturing process, only in comparatively attractive in moulding, but ignore brick body self to improve, cause that a variety of decorative brick block self is with bigger sharp aroma, long-time use, easily discharge harmful gas, not only contaminated environment, and health is brought damage。
Summary of the invention:
The present invention solves the problems referred to above, a kind of environmental-protection decorative fragment of brick with Fructus Mangifera Indicae aromatic odor is provided, this fragment of brick in composition of raw materials and manufacturing process with tradition fragment of brick compared be all significantly improved, without chemical addition agent composition, not only self is with light Fructus Mangifera Indicae fragrance, there is the effect improving environment, and harmful gas will not be discharged, environmental protection more。
The technical problem to be solved adopts following technical scheme to realize:
A kind of environmental-protection decorative fragment of brick with Fructus Mangifera Indicae aromatic odor, it is characterised in that described fragment of brick is made up of the formulation ratio of following weight portion:
Attapulgite clay 30-45 part, plant ash 20-25 part, retinal 5-10 part, gangue 25-30 part, river sand 10-15 part, pulverized limestone 10-15 part, soak 60-80 part。
Preferably, described fragment of brick is made up of the formulation ratio of following weight portion: attapulgite clay 30 parts, plant ash 20 parts, retinal 5 parts, gangue 25 parts, river sand 10 parts, pulverized limestone 10 parts, soak 60 parts。
Described attapulgite clay is made up of the formulation ratio of following weight portion: attapulgite 100 parts, rap oil seedcake 35 parts, distilled water 100 parts。
Described soak is made up of formulation ratio and the processing technology of following weight portion: mango powder 40 parts, vegetable oil 8 parts, white vinegar 5 parts, ethanol 5 parts, 80 parts of water。
Present invention additionally comprises the manufacture method of a kind of environmental-protection decorative fragment of brick with Fructus Mangifera Indicae aromatic odor, the raw material according to weight portion described above, it is characterised in that following steps:
1), make attapulgite clay: attapulgite and rap oil seedcake are put into grinder-mixer and carries out mix homogeneously after crushing, stirring, after crossing 200 eye mesh screens filtrations, add distilled water be again stirring for mixing after, insert autoclave to steam 8-10 hour, heating-up temperature is 180-230 DEG C, cooling is taken out, prepare attapulgite clay standby, the moisture content of attapulgite clay is 45-50%, after attapulgite mixes with rap oil seedcake stirring, filter out impurities, obtain attapulgite essence soil and pulverize rap oil seedcake granule, it is mixed to get attapulgite slurry through distilled water secondary stirring, by autoclave heating fumigating, attapulgite essence soil is fully merged with the Oleum Brassicae campestris in rap oil seedcake, the attapulgite clay prepared, granule is uniform, viscosity is big, adsorptivity is strong, add viscosity and the intensity of raw material, the fragment of brick of post-production also can be played the effect improving hardness and compactness, make the fragment of brick prepared durable；
2), make soak: by mango powder, vegetable oil, white vinegar, after ethanol and water stirring mixing, the steamer being placed in 120 DEG C heats steaming and decocting 1-2 hour, cooling, prepare soak standby, by mango powder and vegetable oil, white vinegar, ethanol adds water heating, vegetable oil increases the viscosity of mango powder, it is beneficial to the dissolving of mango powder after heating simultaneously, white vinegar and ethanol and mango powder produce reaction after heating, strengthen the abnormal smells from the patient of Fructus Mangifera Indicae self, by the post-heating that adds water, make mango powder fully and water dissolution, the distinctive fragrance of Fructus Mangifera Indicae is dissolved in water and is pinned by vegetable oil, avoid volatilization waste, when making the later stage manufacture fragment of brick, fully merge with fragment of brick, increase the aromatic odor of fragment of brick；
3) cross 200 eye mesh screens after, pulverizing coal gangue to filter out impurities, obtain gangue fines, by gangue fines and plant ash, river sand, pulverized limestone, attapulgite clay, it is uniformly mixed by sealing blender, prepare compound standby, by sealing stirring so that the above-mentioned full and uniform mixing of each raw material, ensure that during later stage brickmaking, the brick body texture of fragment of brick is fine and smooth, improves intensity；
4), above-mentioned compound is added soak and retinal, heated sealed stirs, heating-up temperature is 60-80 DEG C, mixing time is 6-8 hour, after stirring terminates, cooling stands to soak and is thoroughly mixed material absorption, prepare immersion compound standby, heated sealed stirs, soak and retinal are more easily merged with compound, with compound rapid fusion after soak heating, avoid fragrance volatilizing and escape, retinal increases the viscosity within compound, it is beneficial to the fragrance pinning soak, make the fragment of brick that the later stage makes, not only durable, texture is fine and smooth, and fragrance is more lasting；
5), above-mentioned immersion compound is poured into mould, after removing moisture, Quick-air-drying by steam pressurized, stripping and slicing, evacuation, namely the environmental-protection decorative fragment of brick with Fructus Mangifera Indicae aromatic odor is prepared, pass through above-mentioned steps, it is avoided by sintering processing, the Fructus Mangifera Indicae fragrance within brick body is caused to run off under high temperature sintering, pass through the mode of steam pressurized, stripping and slicing, evacuation removing moisture, Quick-air-drying simultaneously, it is beneficial to the Fructus Mangifera Indicae fragrance pinned within brick body, ensure the exquisiteness of brick body texture, and the compactness of brick body inner materials, to strengthen intensity and the durability degree of brick body。
A kind of environmental-protection decorative fragment of brick with Fructus Mangifera Indicae aromatic odor of offer is provided, compared with tradition fragment of brick, this fragment of brick is on material composition, without chemical addition agent composition, greatly improving in manufacturing process, not only self is with light Fructus Mangifera Indicae fragrance, has the effect improving environment, and harmful gas will not be discharged, environmental protection more。
Detailed description of the invention:
For the technological means making the present invention realize, creation characteristic, reach purpose and effect and be easy to understand, below in conjunction with embodiment, the present invention is expanded on further。
Embodiment one
A kind of environmental-protection decorative fragment of brick with Fructus Mangifera Indicae aromatic odor, is made up of the formulation ratio of following weight portion:
Attapulgite clay 30 parts, plant ash 20 parts, retinal 5 parts, gangue 25 parts, river sand 10 parts, pulverized limestone 10 parts, soak 60 parts。
Described attapulgite clay is made up of the formulation ratio of following weight portion: attapulgite 100 parts, rap oil seedcake 35 parts, distilled water 100 parts。
Described soak is made up of formulation ratio and the processing technology of following weight portion: mango powder 40 parts, vegetable oil 8 parts, white vinegar 5 parts, ethanol 5 parts, 80 parts of water。
A kind of manufacture method of the environmental-protection decorative fragment of brick with Fructus Mangifera Indicae aromatic odor, the raw material according to weight portion described above, it is characterised in that following steps:
1), attapulgite clay is made: attapulgite and rap oil seedcake are put into grinder-mixer and carries out mix homogeneously after crushing, stirring, after crossing 200 eye mesh screens filtrations, add distilled water be again stirring for mixing after, insert autoclave to steam 8-10 hour, heating-up temperature is 180-230 DEG C, cooling is taken out, and prepares attapulgite clay standby；
2), making soak: after the stirring mixing of mango powder, vegetable oil, white vinegar, ethanol and water, the steamer being placed in 120 DEG C heats steaming and decocting 1-2 hour, cooling, prepares soak standby；
3), pulverize coal gangue after cross 200 eye mesh screens and filter out impurities, obtain gangue fines, by gangue fines and plant ash, river sand, pulverized limestone, attapulgite clay, be uniformly mixed by sealing blender, prepare compound standby；
4), by above-mentioned compound adding soak and retinal, heated sealed stirs, and heating-up temperature is 60-80 DEG C, and mixing time is 6-8 hour, and after stirring terminates, cooling standing is thoroughly mixed material and absorbs to soak, prepares immersion compound standby；
5), pour above-mentioned immersion compound into mould, after removing moisture, Quick-air-drying by steam pressurized, stripping and slicing, evacuation, namely prepare the environmental-protection decorative fragment of brick with Fructus Mangifera Indicae aromatic odor。
Embodiment two
A kind of environmental-protection decorative fragment of brick with Fructus Mangifera Indicae aromatic odor, is made up of the formulation ratio of following weight portion:
Attapulgite clay 40 parts, plant ash 23 parts, retinal 8 parts, gangue 258 parts, river sand 12 parts, pulverized limestone 12 parts, soak 70 parts。
Described attapulgite clay is made up of the formulation ratio of following weight portion: attapulgite 100 parts, rap oil seedcake 35 parts, distilled water 100 parts。
Described soak is made up of formulation ratio and the processing technology of following weight portion: mango powder 40 parts, vegetable oil 8 parts, white vinegar 5 parts, ethanol 5 parts, 80 parts of water。
A kind of manufacture method of the environmental-protection decorative fragment of brick with Fructus Mangifera Indicae aromatic odor, the raw material according to weight portion described above, it is characterised in that following steps:
1), attapulgite clay is made: attapulgite and rap oil seedcake are put into grinder-mixer and carries out mix homogeneously after crushing, stirring, after crossing 200 eye mesh screens filtrations, add distilled water be again stirring for mixing after, insert autoclave to steam 8-10 hour, heating-up temperature is 180-230 DEG C, cooling is taken out, and prepares attapulgite clay standby；
2), making soak: after the stirring mixing of mango powder, vegetable oil, white vinegar, ethanol and water, the steamer being placed in 120 DEG C heats steaming and decocting 1-2 hour, cooling, prepares soak standby；
3), pulverize coal gangue after cross 200 eye mesh screens and filter out impurities, obtain gangue fines, by gangue fines and plant ash, river sand, pulverized limestone, attapulgite clay, be uniformly mixed by sealing blender, prepare compound standby；
4), by above-mentioned compound adding soak and retinal, heated sealed stirs, and heating-up temperature is 60-80 DEG C, and mixing time is 6-8 hour, and after stirring terminates, cooling standing is thoroughly mixed material and absorbs to soak, prepares immersion compound standby；
5), pour above-mentioned immersion compound into mould, after removing moisture, Quick-air-drying by steam pressurized, stripping and slicing, evacuation, namely prepare the environmental-protection decorative fragment of brick with Fructus Mangifera Indicae aromatic odor。
Embodiment three
A kind of environmental-protection decorative fragment of brick with Fructus Mangifera Indicae aromatic odor, is made up of the formulation ratio of following weight portion:
Attapulgite clay 45 parts, plant ash 25 parts, retinal 10 parts, gangue 30 parts, river sand 15 parts, pulverized limestone 15 parts, soak 80 parts。
Described attapulgite clay is made up of the formulation ratio of following weight portion: attapulgite 100 parts, rap oil seedcake 35 parts, distilled water 100 parts。
Described soak is made up of formulation ratio and the processing technology of following weight portion: mango powder 40 parts, vegetable oil 8 parts, white vinegar 5 parts, ethanol 5 parts, 80 parts of water。
A kind of manufacture method of the environmental-protection decorative fragment of brick with Fructus Mangifera Indicae aromatic odor, the raw material according to weight portion described above, it is characterised in that following steps:
1), attapulgite clay is made: attapulgite and rap oil seedcake are put into grinder-mixer and carries out mix homogeneously after crushing, stirring, after crossing 200 eye mesh screens filtrations, add distilled water be again stirring for mixing after, insert autoclave to steam 8-10 hour, heating-up temperature is 180-230 DEG C, cooling is taken out, and prepares attapulgite clay standby；
2), making soak: after the stirring mixing of mango powder, vegetable oil, white vinegar, ethanol and water, the steamer being placed in 120 DEG C heats steaming and decocting 1-2 hour, cooling, prepares soak standby；
3), pulverize coal gangue after cross 200 eye mesh screens and filter out impurities, obtain gangue fines, by gangue fines and plant ash, river sand, pulverized limestone, attapulgite clay, be uniformly mixed by sealing blender, prepare compound standby；
4), by above-mentioned compound adding soak and retinal, heated sealed stirs, and heating-up temperature is 60-80 DEG C, and mixing time is 6-8 hour, and after stirring terminates, cooling standing is thoroughly mixed material and absorbs to soak, prepares immersion compound standby；
5), pour above-mentioned immersion compound into mould, after removing moisture, Quick-air-drying by steam pressurized, stripping and slicing, evacuation, namely prepare the environmental-protection decorative fragment of brick with Fructus Mangifera Indicae aromatic odor。
Claims (5)
1. the environmental-protection decorative fragment of brick with Fructus Mangifera Indicae aromatic odor, it is characterised in that described fragment of brick is made up of the formulation ratio of following weight portion:
Attapulgite clay 30-45 part, plant ash 20-25 part, retinal 5-10 part, gangue 25-30 part, river sand 10-15 part, pulverized limestone 10-15 part, soak 60-80 part。
2. a kind of environmental-protection decorative fragment of brick with Fructus Mangifera Indicae aromatic odor according to claim 1, it is characterized in that, preferably, described fragment of brick is made up of the formulation ratio of following weight portion: attapulgite clay 30 parts, plant ash 20 parts, retinal 5 parts, gangue 25 parts, river sand 10 parts, pulverized limestone 10 parts, soak 60 parts。
3. a kind of environmental-protection decorative fragment of brick with Fructus Mangifera Indicae aromatic odor according to claim 1, it is characterised in that described attapulgite clay is made up of the formulation ratio of following weight portion: attapulgite 100 parts, rap oil seedcake 35 parts, distilled water 100 parts。
4. a kind of environmental-protection decorative fragment of brick with Fructus Mangifera Indicae aromatic odor according to claim 1, it is characterized in that, described soak is made up of formulation ratio and the processing technology of following weight portion: mango powder 40 parts, vegetable oil 8 parts, white vinegar 5 parts, ethanol 5 parts, 80 parts of water。
5. with a manufacture method for the environmental-protection decorative fragment of brick of Fructus Mangifera Indicae aromatic odor, the raw material according to weight portion described above, it is characterised in that following steps:
1), attapulgite clay is made: attapulgite and rap oil seedcake are put into grinder-mixer and carries out mix homogeneously after crushing, stirring, after crossing 200 eye mesh screens filtrations, add distilled water be again stirring for mixing after, insert autoclave to steam 8-10 hour, heating-up temperature is 180-230 DEG C, cooling is taken out, and prepares attapulgite clay standby, and the moisture content of attapulgite clay is 45-50%；
2), making soak: after the stirring mixing of mango powder, vegetable oil, white vinegar, ethanol and water, the steamer being placed in 120 DEG C heats steaming and decocting 1-2 hour, cooling, prepares soak standby；
3), pulverize coal gangue after cross 200 eye mesh screens and filter out impurities, obtain gangue fines, by gangue fines and plant ash, river sand, pulverized limestone, attapulgite clay, be uniformly mixed by sealing blender, prepare compound standby；
4), by above-mentioned compound adding soak and retinal, heated sealed stirs, and heating-up temperature is 60-80 DEG C, and mixing time is 6-8 hour, and after stirring terminates, cooling standing is thoroughly mixed material and absorbs to soak, prepares immersion compound standby；
5), pour above-mentioned immersion compound into mould, after removing moisture, Quick-air-drying by steam pressurized, stripping and slicing, evacuation, namely prepare the environmental-protection decorative fragment of brick with Fructus Mangifera Indicae aromatic odor。