CN107032683A - A kind of energy-saving environment protection brick and preparation method - Google Patents
A kind of energy-saving environment protection brick and preparation method Download PDFInfo
- Publication number
- CN107032683A CN107032683A CN201710412941.XA CN201710412941A CN107032683A CN 107032683 A CN107032683 A CN 107032683A CN 201710412941 A CN201710412941 A CN 201710412941A CN 107032683 A CN107032683 A CN 107032683A
- Authority
- CN
- China
- Prior art keywords
- parts
- energy
- waste
- environment protection
- saving environment
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses a kind of energy-saving environment protection brick and preparation method, brick body includes following component：Cement, flyash, waste or used plastics, waste and old fibre, straw, river bed sludge, calcium carbonate, glass bead, silica flour, wood chip, high viscous Concave-convex clay rod.Preparation method includes：Cement, flyash, river bed sludge, calcium carbonate, silica flour are mixed evenly, waste or used plastics, waste and old fibre, straw, the wood chip added after crushing is well mixed, add water stirring mixing；Glass bead, silica flour and high viscous Concave-convex clay rod are added, is sufficiently mixed uniform；Then form the mixture into, be placed in steam curing system carrying out steam curing, you can.The characteristics of energy-saving environment protection brick of the present invention has low manufacture cost, light weight, using waste material come instead of soil sand, cobble etc., environmental disruption caused by exhaustive exploitation is avoided, while realizing the recycling of discarded object, brick body also has preferable waterproof, insulation effect.
Description
Technical field
The present invention relates to environment-friendly building materials technical field, and in particular to a kind of energy-saving environment protection brick and preparation method.
Background technology
Brick is one of essential material in building, and in the prior art, using it is quite varied be exactly use soil,
Sand, cobble and water etc. are the brick that main raw material(s) is manufactured, and increasing with the demand of brick, therefore, many brick fields are
Expand the scale of production, increase yield, destructive exploitation is taken to natural environment, result in the production base of many bricks
Soil sand, the transition exploitation of cobble drastically influence natural environment.
As long as at present production self-insulating concrete composite block admixture is done with 40% or so waste coal ash, with cement, lime, gypsum,
Adhesive does binder materials；Blinding, sand, haydite do aggregate, mix and stir liquid with underground water or running water, use organic or inorganic
Industrial chemicals make exciting agent and be made, finished product density is in more than 800kg/m3, and the program disposes a certain amount of trade waste（About
40%）, while expending substantial amounts of industrial product and part non-renewable resources, just there is higher cost.
Therefore, research and develop a kind of building brick with low cost, multifunctionality significant, also comply with present
The demand in market, with preferable application prospect.
The content of the invention
It is described it is an object of the invention to provide a kind of energy-saving environment protection brick and preparation method for defect of the prior art
The characteristics of brick body low manufacture cost, light weight, using waste material come instead of soil sand, cobble etc., it is to avoid ring caused by exhaustive exploitation
Border is destroyed, while the recycling of discarded object is realized, and brick body also has preferable waterproof, insulation effect, and in addition, described
Preparation method is simple and easy to apply, with preferable application value.
The present invention solves technical problem and adopted the following technical scheme that：
The present invention relates to a kind of energy-saving environment protection brick, include each component of following parts by weight：20 ~ 30 parts of cement, flyash 60 ~ 80
Part, 10 ~ 20 parts of waste or used plastics, 8 ~ 15 parts of waste and old fibre, 6 ~ 10 parts of straw, 15 ~ 22 parts of river bed sludge, calcium carbonate 10 ~ 18
Part, 8 ~ 16 parts of glass bead, 12 ~ 17 parts of silica flour, 5 ~ 11 parts of wood chip, 10 ~ 15 parts of high viscous Concave-convex clay rod.
Preferably, the energy-saving environment protection brick includes each component of following parts by weight：It is 26 parts of cement, 75 parts of flyash, waste and old
15 parts of plastics, 12 parts of waste and old fibre, 8 parts of straw, 20 parts of river bed sludge, 16 parts of calcium carbonate, 14 parts of glass bead, silica flour
15 parts, 8 parts of wood chip, 13 parts of high viscous Concave-convex clay rod.
Preferably, the straw is any of maize straw, peanut straw, wheat stalk.
Preferably, the high viscous Concave-convex clay rod be that natural attapulgite clay is purified, the product after thermal activation.
The invention further relates to a kind of method for preparing energy-saving environment protection brick, comprise the following steps：
（1）Take waste or used plastics, waste and old fibre, straw, wood chip to crush respectively according to proportioning and cross 50 ~ 100 mesh sieves, mixing is equal
It is even, it is standby；
（2）Cement, flyash, river bed sludge, calcium carbonate, silica flour are mixed evenly according to proportioning, step is added（1）
Obtained mixed powder, after stirring, adds water into mixture, 10 ~ 30min of stirring mixing；
（3）According still further to proportioning to step（2）Glass bead, silica flour and high viscous Concave-convex clay rod are added in middle mixture, is filled
Divide well mixed, obtain mixture a1；
（4）Mixture a1 is placed in forming brick machine and is molded, then is placed in steam curing system in the brick after by shaping
Row steam curing, is warming up to 80 ~ 100 DEG C, 3 ~ 5h of constant temperature, Temperature fall produces the energy-conservation with 10 DEG C/min programming rate
Environmental protection brick.
Preferably, the step（2）The quality of middle addition water is 5 ~ 10 times of mixture gross mass.
Preferably, the step（3）The preparation method of middle high viscous Concave-convex clay rod comprises the following steps：
Take natural attapulgite clay to be crushed and cross 200 mesh sieves, add water, stirring forms mud in suspension, then at ultrasonic wave bar
10 ~ 20min of ultrasound under part, takes upper suspension 5 ~ 10min of centrifugal treating, vacuum in 2000 ~ 3000 turns/min centrifuge
Suction filtration obtains filter cake；
By filter cake in vacuum drying chamber dry, be subsequently placed in Muffle furnace, with 20 DEG C/min speed program be warming up to 800 DEG C ~
900 DEG C of 3 ~ 5h of roasting, is ground to particle diameter for 100 ~ 200 mesh after cooling, obtain high viscous Concave-convex clay rod.
Preferably, the step（4）Before the middle shaping by mixture a1, the rolling that pressurizes first is placed in pressurization edge runner
5~10min。
Compared with prior art, the present invention has following beneficial effect：
（1）Energy-saving environment protection brick of the present invention, soil sand, cobble etc. are replaced using a variety of waste and scraps and building chip,
Avoid because exhaustive exploitation causes environmental disruption caused by a large amount of sand using soil, while realizing the sharp again of discarded object
With the characteristics of brick body has low manufacture cost, light weight, also with preferable waterproof, insulation effect, with preferable application
Value.
（2）High viscous Concave-convex clay rod is added with energy-saving environment protection brick of the present invention, because Concave-convex clay rod is only
Special chain layer structure and larger specific surface area, makes it have preferable absorption property, effectively can adsorb in surrounding environment
Toxic and harmful gas, be that the depollution of environment contribute to a strength, and the high viscosity energy of the high viscous Concave-convex clay rod, significantly
The cohesive force between each component of brick body is improved, so as to improve brick strength, it is ensured that building safety.
（3）Glass bead is also added with energy-saving environment protection brick of the present invention, with excellent thermal insulation, fire prevention, sound-absorbing
Performance, is added the intensity that brick body is substantially increased in environmental protection brick, reduces the shrinkage factor of brick body, improves the comprehensive of brick body
Close performance, the comprehensive production cost of reduction, with preferable use value.
（4）The preparation technology of energy-saving environment protection brick of the present invention is simple, mild condition, and preparation process thing pollutant is produced,
Safety and environmental protection, is adapted to popularization and application.
Embodiment
With reference to specific embodiment, the present invention is expanded on further.These embodiments be merely to illustrate the present invention and without
In limitation the scope of the present invention.The experimental method of unreceipted actual conditions in the following example, generally according to normal condition, for example
Sambrook equimoleculars are cloned：Laboratory manual（New York:Cold Spring Harbor Laboratory Press,
1989）Described in condition, or according to the condition proposed by manufacturer.
Embodiment 1：
A kind of energy-saving environment protection brick and preparation method of the preferred embodiment of the present invention；
The energy-saving environment protection brick, is prepared from by each raw material of following parts by weight：
26 parts of cement, 75 parts of flyash, 15 parts of waste or used plastics, 12 parts of waste and old fibre, 8 parts of straw, 20 parts of river bed sludge, carbon
Sour 16 parts of calcium, 14 parts of glass bead, 15 parts of silica flour, 8 parts of wood chip, 13 parts of high viscous Concave-convex clay rod.
The straw is wheat stalk, while reduction production cost, improves the intensity and heat-insulating property of brick body.
The high viscous Concave-convex clay rod is that natural attapulgite clay is purified, the product after thermal activation.Due to recessed
Convex rod stone clay unique chain layer structure and larger specific surface area, make it have preferable absorption property, can effectively inhale
Toxic and harmful gas in attached surrounding environment, is that the depollution of environment contribute to a strength, and the high viscous Concave-convex clay rod
High viscosity energy, substantially increases the cohesive force between each component of brick body, so as to improve brick strength, it is ensured that building safety
Property
The method of the present invention for preparing energy-saving environment protection brick, comprises the following steps：
（1）Take waste or used plastics, waste and old fibre, straw, wood chip to crush respectively according to proportioning and cross 50 ~ 100 mesh sieves, mixing is equal
It is even, it is standby；
（2）Cement, flyash, river bed sludge, calcium carbonate, silica flour are mixed evenly according to proportioning, step is added（1）
Obtained mixed powder, after stirring, the water of 8 times of amounts of mixture gross mass, stirring mixing are added into mixture
20min；
（3）According still further to proportioning to step（2）Glass bead, silica flour and high viscous Concave-convex clay rod are added in middle mixture, is filled
Divide well mixed, obtain mixture a1；
（4）Mixture a1 is placed in forming brick machine and is molded, then is placed in steam curing system in the brick after by shaping
Row steam curing, is warming up to 90 DEG C, constant temperature 4h, Temperature fall produces the energy-saving environment protection brick with 10 DEG C/min programming rate.
Step（3）The preparation method of middle high viscous Concave-convex clay rod comprises the following steps：
Take natural attapulgite clay to be crushed and cross 200 mesh sieves, add water, stirring forms mud in suspension, then at ultrasonic wave bar
Ultrasound 15min under part, takes upper suspension centrifugal treating 10min in 2500 turns/min centrifuge, is filtered
Cake；
Filter cake is dried in vacuum drying chamber, is subsequently placed in Muffle furnace, 800 DEG C is warming up to 20 DEG C/min speed program
4h is calcined, particle diameter is ground to after cooling for 100 ~ 200 mesh, high viscous Concave-convex clay rod is obtained.
Step（4）Before the middle shaping by mixture a1, pressurization rolling 10min in pressurization edge runner is first placed on.
Embodiment 2：
A kind of energy-saving environment protection brick and preparation method of the preferred embodiment of the present invention；
The energy-saving environment protection brick, is prepared from by each raw material of following parts by weight：
20 parts of cement, 60 parts of flyash, 10 parts of waste or used plastics, 8 parts of waste and old fibre, 6 parts of straw, 15 parts of river bed sludge, carbon
Sour 10 parts of calcium, 8 parts of glass bead, 12 parts of silica flour, 5 parts of wood chip, 10 parts of high viscous Concave-convex clay rod.
The straw is maize straw.
The high viscous Concave-convex clay rod is that natural attapulgite clay is purified, the product after thermal activation.
The method of the present invention for preparing energy-saving environment protection brick, comprises the following steps：
（1）Take waste or used plastics, waste and old fibre, straw, wood chip to crush respectively according to proportioning and cross 50 ~ 100 mesh sieves, mixing is equal
It is even, it is standby；
（2）Cement, flyash, river bed sludge, calcium carbonate, silica flour are mixed evenly according to proportioning, step is added（1）
Obtained mixed powder, after stirring, the water of 5 times of amounts of mixture gross mass, stirring mixing are added into mixture
10min；
（3）According still further to proportioning to step（2）Glass bead, silica flour and high viscous Concave-convex clay rod are added in middle mixture, is filled
Divide well mixed, obtain mixture a1；
（4）Mixture a1 is placed in forming brick machine and is molded, then is placed in steam curing system in the brick after by shaping
Row steam curing, is warming up to 80 DEG C, constant temperature 5h, Temperature fall produces the energy-saving environment protection brick with 10 DEG C/min programming rate.
Step（3）The preparation method of middle high viscous Concave-convex clay rod comprises the following steps：
Take natural attapulgite clay to be crushed and cross 200 mesh sieves, add water, stirring forms mud in suspension, then at ultrasonic wave bar
Ultrasound 10min under part, takes upper suspension centrifugal treating 10min in 2000 turns/min centrifuge, is filtered
Cake；
Filter cake is dried in vacuum drying chamber, is subsequently placed in Muffle furnace, 800 DEG C is warming up to 20 DEG C/min speed program
5h is calcined, particle diameter is ground to after cooling for 100 ~ 200 mesh, high viscous Concave-convex clay rod is obtained.
Step（4）Before the middle shaping by mixture a1, pressurization rolling 5min in pressurization edge runner is first placed on.
Embodiment 3：
A kind of energy-saving environment protection brick and preparation method of the preferred embodiment of the present invention；
The energy-saving environment protection brick, is prepared from by each raw material of following parts by weight：
30 parts of cement, 80 parts of flyash, 20 parts of waste or used plastics, 15 parts of waste and old fibre, 10 parts of straw, 22 parts of river bed sludge,
18 parts of calcium carbonate, 16 parts of glass bead, 17 parts of silica flour, 11 parts of wood chip, 15 parts of high viscous Concave-convex clay rod.
The straw is peanut straw.
The high viscous Concave-convex clay rod is that natural attapulgite clay is purified, the product after thermal activation.
The method of the present invention for preparing energy-saving environment protection brick, comprises the following steps：
（1）Take waste or used plastics, waste and old fibre, straw, wood chip to crush respectively according to proportioning and cross 50 ~ 100 mesh sieves, mixing is equal
It is even, it is standby；
（2）Cement, flyash, river bed sludge, calcium carbonate, silica flour are mixed evenly according to proportioning, step is added（1）
Obtained mixed powder, after stirring, the water of 10 times of amounts of mixture gross mass, stirring mixing are added into mixture
30min；
（3）According still further to proportioning to step（2）Glass bead, silica flour and high viscous Concave-convex clay rod are added in middle mixture, is filled
Divide well mixed, obtain mixture a1；
（4）Mixture a1 is placed in forming brick machine and is molded, then is placed in steam curing system in the brick after by shaping
Row steam curing, is warming up to 100 DEG C, constant temperature 3h, Temperature fall produces the energy-conserving and environment-protective with 10 DEG C/min programming rate
Brick.
Step（3）The preparation method of middle high viscous Concave-convex clay rod comprises the following steps：
Take natural attapulgite clay to be crushed and cross 200 mesh sieves, add water, stirring forms mud in suspension, then at ultrasonic wave bar
Ultrasound 20min under part, takes upper suspension centrifugal treating 5min in 3000 turns/min centrifuge, is filtered
Cake；
Filter cake is dried in vacuum drying chamber, is subsequently placed in Muffle furnace, 900 DEG C is warming up to 20 DEG C/min speed program
3h is calcined, particle diameter is ground to after cooling for 100 ~ 200 mesh, high viscous Concave-convex clay rod is obtained.
Step（4）Before the middle shaping by mixture a1, pressurization rolling 10min in pressurization edge runner is first placed on.
In summary, energy-saving environment protection brick of the present invention, soil is replaced using a variety of waste and scraps and building chip
Sand, cobble etc., it is to avoid due to it is a large amount of using soil it is husky caused by exhaustive exploitation cause environmental disruption, while realize discarded
The recycling of thing, the characteristics of brick body has low manufacture cost, light weight, also with preferable waterproof, insulation effect, with compared with
Good application value.
The preparation technology of energy-saving environment protection brick of the present invention is simple, mild condition, and preparation process thing pollutant is produced, safety
Environmental protection, is adapted to industrialization promotion production.
The specific embodiment of the present invention is described above.It is to be appreciated that the invention is not limited in above-mentioned
Particular implementation, those skilled in the art can make various deformations or amendments within the scope of the claims, this not shadow
Ring the substantive content of the present invention.
Claims (8)
1. a kind of energy-saving environment protection brick, it is characterised in that include each component of following parts by weight：20 ~ 30 parts of cement, flyash 60 ~
80 parts, 10 ~ 20 parts of waste or used plastics, 8 ~ 15 parts of waste and old fibre, 6 ~ 10 parts of straw, 15 ~ 22 parts of river bed sludge, calcium carbonate 10 ~
18 parts, 8 ~ 16 parts of glass bead, 12 ~ 17 parts of silica flour, 5 ~ 11 parts of wood chip, 10 ~ 15 parts of high viscous Concave-convex clay rod.
2. energy-saving environment protection brick according to claim 1, it is characterised in that the energy-saving environment protection brick includes following parts by weight
Each component：26 parts of cement, 75 parts of flyash, 15 parts of waste or used plastics, 12 parts of waste and old fibre, 8 parts of straw, river bed sludge 20
Part, 16 parts of calcium carbonate, 14 parts of glass bead, 15 parts of silica flour, 8 parts of wood chip, 13 parts of high viscous Concave-convex clay rod.
3. energy-saving environment protection brick according to claim 1, it is characterised in that the straw is maize straw, peanut stems
Any of stalk, wheat stalk.
4. energy-saving environment protection brick according to claim 1, it is characterised in that the high viscous Concave-convex clay rod is natural concavo-convex
Rod stone clay is purified, the product after thermal activation.
5. the method that one kind prepares the energy-saving environment protection brick as described in any one of claim 1 ~ 4, it is characterised in that including following step
Suddenly：
（1）Take waste or used plastics, waste and old fibre, straw, wood chip to crush respectively according to proportioning and cross 50 ~ 100 mesh sieves, mixing is equal
It is even, it is standby；
（2）Cement, flyash, river bed sludge, calcium carbonate, silica flour are mixed evenly according to proportioning, step is added（1）
Obtained mixed powder, after stirring, adds water into mixture, 10 ~ 30min of stirring mixing；
（3）According still further to proportioning to step（2）Glass bead, silica flour and high viscous Concave-convex clay rod are added in middle mixture, is filled
Divide well mixed, obtain mixture a1；
（4）Mixture a1 is placed in forming brick machine and is molded, then is placed in steam curing system in the brick after by shaping
Row steam curing, is warming up to 80 ~ 100 DEG C, 3 ~ 5h of constant temperature, Temperature fall produces the energy-conservation with 10 DEG C/min programming rate
Environmental protection brick.
6. the preparation method of energy-saving environment protection brick according to claim 5, it is characterised in that the step（2）Middle addition water
Quality be 5 ~ 10 times of mixture gross mass.
7. the preparation method of energy-saving environment protection brick according to claim 5, it is characterised in that the step（3）It is middle high viscous recessed
The preparation method of convex rod stone clay comprises the following steps：
Take natural attapulgite clay to be crushed and cross 200 mesh sieves, add water, stirring forms mud in suspension, then at ultrasonic wave bar
10 ~ 20min of ultrasound under part, takes upper suspension 5 ~ 10min of centrifugal treating, vacuum in 2000 ~ 3000 turns/min centrifuge
Suction filtration obtains filter cake；
By filter cake in vacuum drying chamber dry, be subsequently placed in Muffle furnace, with 20 DEG C/min speed program be warming up to 800 DEG C ~
900 DEG C of 3 ~ 5h of roasting, is ground to particle diameter for 100 ~ 200 mesh after cooling, obtain high viscous Concave-convex clay rod.
8. the preparation method of energy-saving environment protection brick according to claim 5, it is characterised in that the step（4）It is middle to mix
Before thing a1 shapings, 5 ~ 10min of pressurization rolling in pressurization edge runner is first placed on.