CN105834444A - 一种以胸腺嘧啶为模板合成荧光铜纳米簇的方法 - Google Patents

一种以胸腺嘧啶为模板合成荧光铜纳米簇的方法 Download PDF

Info

Publication number
CN105834444A
CN105834444A CN201610167448.1A CN201610167448A CN105834444A CN 105834444 A CN105834444 A CN 105834444A CN 201610167448 A CN201610167448 A CN 201610167448A CN 105834444 A CN105834444 A CN 105834444A
Authority
CN
China
Prior art keywords
copper
thymine
solution
hydroxylamine hydrochloride
template
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201610167448.1A
Other languages
English (en)
Inventor
韩冰雁
相荣超
侯绪芬
许杰
于明波
李莹
彭婷婷
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Dalian University of Technology
Original Assignee
Dalian University of Technology
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Dalian University of Technology filed Critical Dalian University of Technology
Priority to CN201610167448.1A priority Critical patent/CN105834444A/zh
Publication of CN105834444A publication Critical patent/CN105834444A/zh
Pending legal-status Critical Current

Abstract

本发明涉及一种以胸腺嘧啶为模板合成荧光铜纳米簇的方法，属于生物工程技术领域，所述方法包括如下步骤：①将胸腺嘧啶溶液与硫酸铜溶液混匀，所述胸腺嘧啶与硫酸铜的摩尔比为2～5：2；②将盐酸羟胺溶液加入到步骤①所得产品中混匀，所述胸腺嘧啶、硫酸铜与盐酸羟胺的摩尔比为2～5：2：2～40；③将步骤②所得产品调节pH至7～12，反应1～2h，本发明有益效果为：本发明通过引入胸腺嘧啶为模板，以盐酸羟胺为还原剂在水相中实现铜纳米簇的合成，与现有技术比，具有稳定性强和荧光强度高的优点。

Description

一种以胸腺嘧啶为模板合成荧光铜纳米簇的方法
技术领域
本发明涉及一种以胸腺嘧啶为模板合成荧光铜纳米簇的方法，属于生物工程技术领域。
背景技术
金属纳米簇由几个至十几个原子组成，由于其具有毒性低、尺寸小、光稳定性强以及水溶性好等优点，使得金属纳米簇在纳米科技许多领域中逐渐成为一种广泛应用的纳米材料。
金属纳米簇的合成主要采用模板合成法，常使用的模板有聚合物、DNA、多肽和蛋白质。DNA组成的基本单位是脱氧核苷酸，每个脱氧核苷酸由一个磷酸基团、一个五碳糖和一个碱基构成。首先研究以单独的碱基或脱氧核苷酸为保护剂合成铜纳米簇的过程。利用DNA单体上的N可以与金属特异的结合，合成金属纳米簇已被广泛应用。
目前，人们对纳米簇的研究逐渐由价格昂贵的金、银、铂转移到价格低廉的铜上，但是，合成的铜纳米簇具有很多缺点，例如：稳定性差和荧光强度低等。
发明内容
本发明通过以胸腺嘧啶为模板，解决了上述以单链或双链DNA为模板合成铜纳米簇稳定性差和荧光强度低的问题。
本发明提供了一种以胸腺嘧啶为模板合成荧光铜纳米簇的方法，所述方法包括如下步骤：
①将胸腺嘧啶溶液与硫酸铜溶液混匀，所述胸腺嘧啶与硫酸铜的摩尔比为2～5：2；
②将盐酸羟胺溶液加入到步骤①所得产品中混匀，所述胸腺嘧啶、硫酸铜与盐酸羟胺的摩尔比为2～5：2：2～40；
③将步骤②所得产品调节pH至7～12，反应1～2h。
本发明所述胸腺嘧啶溶液的浓度优选为8～20mM。
本发明所述硫酸铜溶液的浓度优选为8mM。
本发明所述盐酸羟胺溶液的浓度优选为8～160mM。
本发明所述步骤③中的pH优选为调节至11.5。
本发明所述步骤③中的反应时间优选为2h。
本发明有益效果为：
本发明通过引入胸腺嘧啶为模板，以盐酸羟胺为还原剂在水相中实现铜纳米簇的合成，与现有技术比，具有稳定性强和荧光强度高的优点。
附图说明
本发明附图4幅，
图1为实施例2合成的铜纳米簇荧光激发及发射谱图；
图2为不同浓度的胸腺嘧啶溶液对铜纳米簇荧光强度的影响；
图3为不同浓度的盐酸羟胺溶液对铜纳米簇荧光强度的影响；
图4为不同pH值对铜纳米簇荧光强度的影响。
具体实施方式
下述非限制性实施例可以使本领域的普通技术人员更全面地理解本发明，但不以任何方式限制本发明。
下述实施例中，如无特殊说明，所使用的实验方法均为常规方法，所用试剂等均可从化学或生物试剂公司购买。
以下结合技术方案详细叙述本发明的具体实施方式。
实施例1～4
一种以胸腺嘧啶为模板合成荧光铜纳米簇的方法，所述方法包括如下步骤：
①将9.4mL不同浓度的胸腺嘧啶溶液与100μL的800mM硫酸铜溶液混合，搅拌5min；
②将500μL的800mM盐酸羟胺溶液加入到步骤①所得产品中，搅拌1min；
③将步骤②所得产品用10M氢氧化钠溶液调节pH至11.5，静置反应2h，得到荧光铜纳米簇，所述实施例1～4胸腺嘧啶溶液的浓度见表1。
表1实施例1～4胸腺嘧啶溶液的浓度
实施例5～8
一种以胸腺嘧啶为模板合成荧光铜纳米簇的方法，所述方法包括如下步骤：
①将9.4mL的12mM胸腺嘧啶溶液与100μL的800mM硫酸铜溶液混合，搅拌5min；
②将500μL不同浓度的盐酸羟胺溶液加入到步骤①所得产品中，搅拌1min；
③将步骤②所得产品用10M氢氧化钠溶液调节pH至11.5，静置反应2h，得到荧光铜纳米簇，所述实施例5～8盐酸羟胺溶液的浓度见表2。
表2实施例5～8盐酸羟胺溶液的浓度
实施例9～15
一种以胸腺嘧啶为模板合成荧光铜纳米簇的方法，所述方法包括如下步骤：
①将9.4mL的12mM胸腺嘧啶溶液与100μL的800mM硫酸铜溶液混合，搅拌5min；
②将500μL的800mM盐酸羟胺溶液加入到步骤①所得产品中，搅拌1min
③将步骤②所得产品用10M氢氧化钠溶液调节不同的pH值，静置反应2h，得到荧光铜纳米簇，所述实施例9～15的pH值见表3。
表3实施例9～15的pH值

Claims (4)

1.一种以胸腺嘧啶为模板合成荧光铜纳米簇的方法，其特征在于：所述方法包括如下步骤：
①将胸腺嘧啶溶液与硫酸铜溶液混匀，所述胸腺嘧啶与硫酸铜的摩尔比为2～5：2；
②将盐酸羟胺溶液加入到步骤①所得产品中混匀，所述胸腺嘧啶、硫酸铜与盐酸羟胺的摩尔比为2～5：2：2～40；
③将步骤②所得产品调节pH至7～12，反应1～2h。
2.根据权利要求1所述的方法，其特征在于：所述胸腺嘧啶溶液的浓度为8～20mM。
3.根据权利要求1所述的方法，其特征在于：所述硫酸铜溶液的浓度为8mM。
4.根据权利要求1所述的方法，其特征在于：所述盐酸羟胺溶液的浓度为8～160mM。
CN201610167448.1A 2016-03-22 2016-03-22 一种以胸腺嘧啶为模板合成荧光铜纳米簇的方法 Pending CN105834444A (zh)