CN105802216A - 一种导电抗老化塑胶 - Google Patents
一种导电抗老化塑胶 Download PDFInfo
- Publication number
- CN105802216A CN105802216A CN201610184507.6A CN201610184507A CN105802216A CN 105802216 A CN105802216 A CN 105802216A CN 201610184507 A CN201610184507 A CN 201610184507A CN 105802216 A CN105802216 A CN 105802216A
- Authority
- CN
- China
- Prior art keywords
- parts
- plastic cement
- iron powder
- aging resistance
- barium sulfate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种导电抗老化塑胶,由如下重量份的原料组成:导电聚苯胺5‑25份、硫酸钡2‑13份、铁粉1‑20份、氯化聚乙烯1‑18份、邻苯二甲酸酯1‑20份、异丁基三乙氧基硅7‑15份、磷酸锌0.4‑5份、玻璃纤维1‑20份。本发明制备的塑胶具有良好的导电性和抗老化性能,并且具有耐弱酸、导电聚苯胺不耐碱、高温的优点,机械强度高,满足市场的需要。
Description
技术领域
本发明涉及一种导电抗老化塑胶,属于化学塑胶材料领域。
背景技术
塑胶(英文名:plastic cement),主要由碳、氧、氢和氮及其他有机或无机元素所构成,成品为固体,在制造过程中是熔融状的液体,因此可以籍加热使其熔化、加压力使其流动、冷却使其固化,而形成各种形状,此庞大而变化多端的材料族群称为塑胶。
发明内容
本发明所要解决的技术问题是提供一种导电抗老化塑胶,本发明制备的塑胶具有良好的导电性和抗老化性能,并且具有耐弱酸、弱碱、高温的优点,机械强度高,满足市场的需要。
本发明解决上述技术问题的技术方案如下:一种导电抗老化塑胶,由如下重量份的原料组成:
导电聚苯胺5-25份、硫酸钡2-13份、铁粉1-20份、氯化聚乙烯1-18份、邻苯二甲酸酯1-20份、异丁基三乙氧基硅7-15份、磷酸锌0.4-5份、玻璃纤维1-20份。
在上述技术方案的基础上,本发明还可以做如下改进。
进一步,所述导电抗老化塑胶,由如下重量份的原料组成:
导电聚苯胺7份、硫酸钡8份、铁粉13份、氯化聚乙烯15份、邻苯二甲酸酯20份、异丁基三乙氧基硅15份、磷酸锌4.5份、玻璃纤维16份。
进一步,所述导电抗老化塑胶,由如下重量份的原料组成:
导电聚苯胺25份、硫酸钡8份、铁粉17份、氯化聚乙烯17份、邻苯二甲酸酯20份、异丁基三乙氧基硅15份、磷酸锌5份、玻璃纤维8份。
进一步,所述铁粉的粒径为100-200微米。
本发明的有益效果是:
本发明制备的塑胶具有良好的导电性和抗老化性能,并且具有耐弱酸、高温的优点,机械强度高,满足市场的需要。
具体实施方式
以下对本发明的原理和特征进行描述,所举实例只用于解释本发明,并非用于限定本发明的范围。
实施例1
所述导电抗老化塑胶,由如下重量份的原料组成:
导电聚苯胺7份、硫酸钡8份、铁粉13份、氯化聚乙烯15份、邻苯二甲酸酯20份、异丁基三乙氧基硅15份、磷酸锌4.5份、玻璃纤维16份。
制备方法:
将各组分混匀后,加入双螺杆挤出机内在150℃下熔融塑化造粒,粒料在50℃下鼓风工作5h后,与220℃下注塑成型。
经测试,本发明制备的导电抗老化塑胶的电阻值为3.6Ω·m,塑胶500h光老化冲击强度保持率100%,透光率93%,韧性256j/m。
实施例2
所述导电抗老化塑胶,由如下重量份的原料组成:
导电聚苯胺25份、硫酸钡8份、铁粉17份、氯化聚乙烯17份、邻苯二甲酸酯20份、异丁基三乙氧基硅15份、磷酸锌5份、玻璃纤维8份。
制备方法:
将各组分混匀后,加入双螺杆挤出机内在150℃下熔融塑化造粒,粒料在50℃下鼓风工作5h后,与220℃下注塑成型。
经测试,本发明制备的导电抗老化塑胶的电阻值为3.8Ω·m,塑胶500h光老化冲击强度保持率100%,韧性260j/m,耐温320度,较其他方法只能耐温250℃要高。
以上所述仅为本发明的较佳实施例,并不用以限制本发明,凡在本发明的精神和原则之内,所作的任何修改、等同替换、改进等,均应包含在本发明的保护范围之内。
Claims (4)
1.一种导电抗老化塑胶,其特征在于,由如下重量份的原料组成:
导电聚苯胺5-25份、硫酸钡2-13份、铁粉1-20份、氯化聚乙烯1-18份、邻苯二甲酸酯1-20份、异丁基三乙氧基硅7-15份、磷酸锌0.4-5份、玻璃纤维1-20份。
2.根据权利要求1所述的导电抗老化塑胶,其特征在于,由如下重量份的原料组成:
导电聚苯胺7份、硫酸钡8份、铁粉13份、氯化聚乙烯15份、邻苯二甲酸酯20份、异丁基三乙氧基硅15份、磷酸锌4.5份、玻璃纤维16份。
3.根据权利要求1所述的导电抗老化塑胶,其特征在于,由如下重量份的原料组成:
导电聚苯胺25份、硫酸钡8份、铁粉17份、氯化聚乙烯17份、邻苯二甲酸酯20份、异丁基三乙氧基硅15份、磷酸锌5份、玻璃纤维8份。
4.根据权利要求1-3任一所述的导电抗老化塑胶,其特征在于,所述铁粉的粒径为100-200微米。