CN105799244A - Production process of mildew-proof jacquard denim with warm-keeping function - Google Patents

Production process of mildew-proof jacquard denim with warm-keeping function Download PDF

Info

Publication number
CN105799244A
CN105799244A CN201610136175.4A CN201610136175A CN105799244A CN 105799244 A CN105799244 A CN 105799244A CN 201610136175 A CN201610136175 A CN 201610136175A CN 105799244 A CN105799244 A CN 105799244A
Authority
CN
China
Prior art keywords
denim
jacquard
fabric
mildew
softening agent
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201610136175.4A
Other languages
Chinese (zh)
Inventor
蒋岑章
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
TAICANG QIDE GARMENT CO Ltd
Original Assignee
TAICANG QIDE GARMENT CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by TAICANG QIDE GARMENT CO Ltd filed Critical TAICANG QIDE GARMENT CO Ltd
Priority to CN201610136175.4A priority Critical patent/CN105799244A/en
Publication of CN105799244A publication Critical patent/CN105799244A/en
Pending legal-status Critical Current

Abstract

The invention discloses a production process of mildew-proof jacquard denim with a warm-keeping function. The mildew-proof jacquard denim comprises a jacquard layer, a base material layer and a lint layer, wherein the jacquard layer and the base material layer, and the base material layer and the lint layer are connected together through a fabric hot pressing compounding process, respectively; the jacquard layer is a denim jacquard fabric; the base material is formed by blending bamboo charcoal fiber, nipagin esters and a denim fabric; the denim fabric is formed by blending cotton fibers, natural silk fibers and wool fibers; and the denim jacquard fabric is formed by spinning and weaving hemp fibers and flax fibers through ring spinning. The denim fabric has a tight and thick texture, bright color and luster, clear weaving grains and beautiful appearance, and has a good mildew-proof effect, so that the problems of traditional denim that the color is single, a fabric surface style is dull and visual impact is lacked are solved, and the denim fabric is adaptive to the trend of times.

Description

A kind of processing technology of the mildew-resistant jacquard jean possessing heat-preserving function
Technical field
The present invention relates to garment material field, particularly the processing technology of a kind of mildew-resistant jacquard jean possessing heat-preserving function.
Background technology
In the eighties in 20th century, U.S.'s denim yield is the 50% of whole world yield, but among nearest 10 years, China, India, Pakistan, Malaysia, Tu Er itself and Mexico establish substantial amounts of denim factory, the denim center of production in the U.S. or even the world has been transferred to the country of the low labor cost in Asia, denim is also called and splits silks, it is that a kind of relatively thick thick color is knitted through face jean, warp thread color is deep, it is generally indigo, weft yarn is of light color, is generally the raw white yarn after light gray or kiering, also known as indigo denim.Starting from US West, the personnel that herd gain the name in order to make clothing.
Bamboo carbon fiber is that to take Phyllostachys pubescens Mazei ex H.de Lebaie be raw material, have employed the calcining new technology of pure oxygen high temperature and nitrogen obstruct time delay and new technique, the micropore that bamboo charcoal innately has more is refined and honeycomb, then again with have honeycomb microporous structure trend polyester modification cut into slices melt spinning and make.The fibre structure design of this uniqueness, can make bringing into play of the function 100% that bamboo charcoal has.It is described as " the new bodyguard of 21st century environmental protection " in the world.
Although denim is solid endurable, but cloth pattern is simple, if wearing jean for a long time, raising however as people's quality of the life, existing denim fabric is because of simply single thin money, it is impossible to accomplish warming function, is therefore subject to application restriction in making clothes field.
Summary of the invention
Goal of the invention: the invention aims to solve the deficiencies in the prior art, it is provided that a kind of mildew-resistant jacquard jeans fabric possessing heat-preserving function, have the fashionable element in traditional heat-preserving function and modern times concurrently.Solving tradition denim color single, cloth style is dull, and the problem lacking visual impact has adapted to the trend in epoch.
Technical scheme: in order to realize object above, specifically comprising the following steps that of the processing technology of of the present invention a kind of mildew-resistant colour jacquard jean possessing heat-preserving function
A () is weaved cotton cloth
By jacquard layer by the weaving braiding of RING SPINNING of hemp and flax fiber with by bamboo carbon fiber, the initial bed of Nipagin ester and jean blending is connected together formation denim by fabric hot pressing combination process；
(b) pre-treatment, enter cloth
After denim having been processed with alkali, refining agent, hydrogen peroxide, cloth inlet mechanism with the speed of 5m/s～8m/s, denim is transported out, through being possible to prevent the fabric guide roll that crimping occurs in denim transmission；
(c) drinking water infiltration
Arriving infiltration tank through the denim of fabric guide roll output, make denim launch in water and fully permeate drinking water, reaching the water content of denim is till 60%～80%, and control water temperature is 50 DEG C～90 DEG C simultaneously；
(d) whole latitude, overfeeding
Through weft straightener, the denim after infiltration is corrected the crooked of broadwise silk tuft, and the speed controlling of stenter is at 3m/s～4m/s；
E () toasts
By stenter, by correcting the denim after broadwise silk tuft, to send in the baking oven that temperature is 150 DEG C～200 DEG C baking 10min～20min to moisture content be 5%～10%；；
(f) upper softening agent
Putting into, by toasting complete denim, the water vat 15min～30min being equipped with softening agent, the ratio of softening agent and water is 1:50～1:100；
G () is shaped
To soak the denim after softening agent operation completes and send into shaping baking oven sizing, setting temperature is 150 DEG C～200 DEG C, until moisture content is take out after 3%～5%, cooling, cropping can pack warehouse-in.
(h) molding
The back side of initial bed and flannelette napped fabric layer are joined together to form the denim possessing heat insulation function by hot pressing combination process, and hot pressing combination process can pack warehouse-in after completing.
As present invention further optimization, fabric guide roll in step b is provided with thin groove, makes denim launch fully to permeate drinking water in water, it is ensured that the shrinkage of denim and stablizing of grammes per square metre, thus creating best cloth cover condition to denim sizing, the variety range of denim is greatly increased.
As present invention further optimization, softening agent in step f is ester based quaternary ammonium salt softening agent, fatty acid ester type softening agent, right wax pattern softening agent or polyethylene softening agent, textile is in the course of processing, after repeatedly processing, feel can become coarse, general synthetic fabrics is worse, especially Superfine Fibre Fabric.In order to make fabric have softness, smooth, comfortable feel, it is necessary to it is arranged, widely used is arrange with softening agent.
As present invention further optimization, described bamboo carbon fiber accounts for the 22%-30% of the mass percent of described jacquard weave mildew-resistant jean, and described Nipagin ester accounts for 60%～75% that 5%-8% son's cloth of the described mass percent planting jacquard weave mildew-resistant jean accounts for the mass percent of described jacquard weave mildew-resistant jean.
As present invention further optimization, the ratio of described cotton fiber, wool fiber and tencel fiber is 4:3:1,1, and it is relatively good that tencel fiber has soft warm property, does not crease easily, and cotton fiber comfort level is relatively good, and wool fiber has warming effect.
As present invention further optimization, the ratio of described hemp and described flax fiber is 1:1.5, hemp and flax fiber all have the effect of ventilative absorbing sweat, anti-wear performance is better, flax fiber is thick and short, soft identical with cotton, hemp cloth not only looks that gloss is soft, and the ultraviolet with advantage penetrates function.The filamentary fineness of Fructus Cannabis is about 2-3 times of Boehmeria, and close with cotton, fiber tip is blunt round, there is no the such pointed end of Boehmeria, Caulis et Folium Lini, therefore the textile formed with hemp processing, it is not necessary to special handling, just can be effectively prevented from coarse hard sense and the prodding and itching feeling of other gunny products.
As present invention further optimization, the material of described flannelette napped fabric layer is polar fleece, lamb floss or coral fleece, this material is fluffy intensive and not easily falls hair, balling-up, reverse side plucking is dredged rare well-balanced, and fine hair is short of, and tissue texture is clear, fluffy elastic special good, its composition is usually to be washed entirely, soft, cost is low, is the first-selected product of nearly resisting cold in two domestic winters.
Beneficial effect: the processing technology of a kind of mildew-resistant colour jacquard jean possessing heat-preserving function provided by the invention, this jean quality is tight, abundant, bright in colour, weavy grain is clear, good looking appearance, it is possible to make fabric have good anti-mold effect, solve tradition denim color single, cloth style is dull, the problem lacking visual impact, has adapted to the trend in epoch, jacquard layer embodies the element of fashion, and the flannelette napped fabric layer of internal layer and contact human skin play warming effect.
Accompanying drawing explanation
Fig. 1 is the structural representation of the present invention.
Detailed description of the invention
Below in conjunction with embodiment, it is further elucidated with the present invention.
The present invention provides a kind of mildew-resistant colour jacquard jean possessing heat-preserving function, including: jacquard layer 1, initial bed 2 and flannelette napped fabric layer 3, described jacquard layer 1 and initial bed 2, initial bed 2 and flannelette napped fabric layer 3 are connected together respectively through fabric hot pressing combination process, described jacquard layer 1 is cowboy's jacquard fabric, described initial bed 2 is by bamboo carbon fiber, Nipagin ester and jean blending form, described jean is added fleece fibre blended spinning by cotton fiber and tencel fiber and forms, described cowboy's jacquard fabric is formed by the weaving braiding of RING SPINNING by hemp and flax fiber.
Embodiment 1
The present invention provides a kind of mildew-resistant colour jacquard jean possessing heat-preserving function, including: jacquard layer 1 and initial bed 2, described jacquard layer 1 and initial bed 2 are connected together by fabric hot pressing combination process.
Jacquard layer 1 is cowboy's jacquard fabric, hemp and flax fiber are formed by the weaving braiding of RING SPINNING with the ratio of 1:1.5；
Initial bed 2 is to be formed by bamboo carbon fiber, Nipagin ester and jean blending, bamboo carbon fiber accounts for the 22% of fabric gross mass percentage ratio, Nipagin ester accounts for the 5% of fabric gross mass percentage ratio, denim accounts for the 73% of fabric gross mass percentage ratio, jean is added fleece fibre blended spinning by cotton fiber and tencel fiber and forms, and the ratio of cotton fiber, wool fiber and tencel fiber is 4:3:1.
Specifically comprising the following steps that of the processing technology of a kind of mildew-resistant colour jacquard jean
A () is weaved cotton cloth
By jacquard layer 1 by the weaving braiding of RING SPINNING of hemp and flax fiber with by bamboo carbon fiber, the initial bed 2 of Nipagin ester and jean blending is connected together formation denim by fabric hot pressing combination process；
(b) pre-treatment, enter cloth
After denim having been processed with alkali, refining agent, hydrogen peroxide, cloth inlet mechanism with the speed of 5m/s, denim is transported out, through being possible to prevent the fabric guide roll that crimping occurs in denim transmission；
(c) drinking water infiltration
Arriving infiltration tank through the denim of fabric guide roll output, make denim launch in water and fully permeate drinking water, reaching the water content of denim is till 60%, and control water temperature is 50 DEG C simultaneously；
(d) whole latitude, overfeeding
Through weft straightener, the denim after infiltration is corrected the crooked of broadwise silk tuft, and the speed controlling of stenter is at 3m/s；
E () toasts
By stenter, by correcting the denim after broadwise silk tuft, to send in the baking oven that temperature is 150 DEG C baking 10min to moisture content be 5%；；
(f) upper softening agent
Putting into, by toasting complete denim, the water vat 15min being equipped with softening agent, the ratio of softening agent and water is 1:50；
G () is shaped
To soak the denim after softening agent operation completes and send into shaping baking oven sizing, setting temperature is 150 DEG C, until moisture content is take out after 3%, and cooling, cropping；
(h) molding
The back side and the flannelette napped fabric layer 3 being made up of polar fleece of initial bed are joined together to form the denim possessing heat insulation function by hot pressing combination process, and hot pressing combination process can pack warehouse-in after completing.
Embodiment 2
The present invention provides a kind of mildew-resistant colour jacquard jean possessing heat-preserving function, including: jacquard layer 1 and initial bed 2, described jacquard layer 1 and initial bed 2 are connected together by fabric hot pressing combination process.
Jacquard layer 1 is cowboy's jacquard fabric, hemp and flax fiber are formed by the weaving braiding of RING SPINNING with the ratio of 1:1.5；
Initial bed 2 is to be formed by bamboo carbon fiber, Nipagin ester and jean blending, bamboo carbon fiber accounts for the 25% of fabric gross mass percentage ratio, Nipagin ester accounts for the 8% of fabric gross mass percentage ratio, denim accounts for the 67% of fabric gross mass percentage ratio, jean is added fleece fibre blended spinning by cotton fiber and tencel fiber and forms, and the ratio of cotton fiber, wool fiber and tencel fiber is 4:3:1.
Specifically comprising the following steps that of the processing technology of a kind of mildew-resistant colour jacquard jean
A () is weaved cotton cloth
By jacquard layer 1 by the weaving braiding of RING SPINNING of hemp and flax fiber with by bamboo carbon fiber, the initial bed 2 of Nipagin ester and jean blending is connected together formation denim by fabric hot pressing combination process；
(b) pre-treatment, enter cloth
After denim having been processed with alkali, refining agent, hydrogen peroxide, cloth inlet mechanism with the speed of 6m/s, denim is transported out, through being possible to prevent the fabric guide roll that crimping occurs in denim transmission；
(c) drinking water infiltration
Arriving infiltration tank through the denim of fabric guide roll output, make denim launch in water and fully permeate drinking water, reaching the water content of denim is till 70%, and control water temperature is 60 DEG C simultaneously；
(d) whole latitude, overfeeding
Through weft straightener, the denim after infiltration is corrected the crooked of broadwise silk tuft, and the speed controlling of stenter is at 3.5m/s；
E () toasts
By stenter, by correcting the denim after broadwise silk tuft, to send in the baking oven that temperature is 180 DEG C baking 15min to moisture content be 8%；；
(f) upper softening agent
Putting into, by toasting complete denim, the water vat 20min being equipped with softening agent, the ratio of softening agent and water is 1:80；
G () is shaped
To soak the denim after softening agent operation completes and send into shaping baking oven sizing, setting temperature is 180 DEG C, until moisture content is take out after 4%, cooling, cropping can pack warehouse-in.
(h) molding
The back side and the flannelette napped fabric layer 3 being made up of lamb floss of initial bed 2 are joined together to form the denim possessing heat insulation function by hot pressing combination process, and hot pressing combination process can pack warehouse-in after completing.
Embodiment 3
The present invention provides a kind of mildew-resistant colour jacquard jean possessing heat-preserving function, including: jacquard layer 1 and initial bed 2, described jacquard layer 1 and initial bed 2 are connected together by fabric hot pressing combination process.
Jacquard layer 1 is cowboy's jacquard fabric, hemp and flax fiber are formed by the weaving braiding of RING SPINNING with the ratio of 1:1.5；
Initial bed 2 is to be formed by bamboo carbon fiber, Nipagin ester and jean blending, bamboo carbon fiber accounts for the 30% of fabric gross mass percentage ratio, Nipagin ester accounts for the 8% of fabric gross mass percentage ratio, denim accounts for the 62% of fabric gross mass percentage ratio, jean is added fleece fibre blended spinning by cotton fiber and tencel fiber and forms, and the ratio of cotton fiber, wool fiber and tencel fiber is 4:3:1.
Specifically comprising the following steps that of the processing technology of a kind of mildew-resistant colour jacquard jean
A () is weaved cotton cloth
By jacquard layer 1 by the weaving braiding of RING SPINNING of hemp and flax fiber with by bamboo carbon fiber, the initial bed 2 of Nipagin ester and jean blending is connected together formation denim by fabric hot pressing combination process；
(b) pre-treatment, enter cloth
After denim having been processed with alkali, refining agent, hydrogen peroxide, cloth inlet mechanism with the speed of 8m/s, denim is transported out, through being possible to prevent the fabric guide roll that crimping occurs in denim transmission；
(c) drinking water infiltration
Arriving infiltration tank through the denim of fabric guide roll output, make denim launch in water and fully permeate drinking water, reaching the water content of denim is till 80%, and control water temperature is 90 DEG C simultaneously；
(d) whole latitude, overfeeding
Through weft straightener, the denim after infiltration is corrected the crooked of broadwise silk tuft, and the speed controlling of stenter is at 4m/s；
E () toasts
By stenter, by correcting the denim after broadwise silk tuft, to send in the baking oven that temperature is 200 DEG C baking 20min to moisture content be 10%；；
(f)
Upper softening agent
By denim from taking out in dyeing installation and it being cleaned again, inserting the ratio being placed with in the cylinder of softening agent 30min, softening agent and water after having cleaned is 1:100；
G () is shaped
To soak the denim after softening agent operation completes and send into shaping baking oven sizing, setting temperature is 200 DEG C, until moisture content is take out after 5%, cooling, cropping can pack warehouse-in.
(h) molding
The back side and the flannelette napped fabric layer 3 being made up of coral fleece of initial bed 2 are joined together to form the denim possessing heat insulation function by hot pressing combination process, and hot pressing combination process can pack warehouse-in after completing.
Above-mentioned detailed description of the invention only for technology design and the feature of the present invention are described, its objective is to allow and is familiar with these those skilled in the art and will appreciate that present disclosure and implement according to this, can not limit the scope of the invention with this.All equivalents made according to spirit of the invention or modification, all should be encompassed within protection scope of the present invention.

Claims (8)

1. the processing technology of the mildew-resistant jacquard jean possessing heat-preserving function, it is characterised in that: specifically comprising the following steps that of the method
A () is weaved cotton cloth
By jacquard layer (1) by the weaving braiding of RING SPINNING of hemp and flax fiber with by bamboo carbon fiber, the initial bed (2) of Nipagin ester and jean blending is connected together formation denim by fabric hot pressing combination process；
(b) pre-treatment, enter cloth
After denim having been processed with alkali, refining agent, hydrogen peroxide, cloth inlet mechanism with the speed of 5m/s ~ 8m/s, denim is transported out, through being possible to prevent the fabric guide roll that crimping occurs in denim transmission；
(c) drinking water infiltration
Arriving infiltration tank through the denim of fabric guide roll output, make denim launch in water and fully permeate drinking water, reaching the water content of denim is till 60%～80%, and control water temperature is 50 DEG C～90 DEG C simultaneously；
(d) whole latitude, overfeeding
Through weft straightener, the denim after infiltration is corrected the crooked of broadwise silk tuft, and the speed controlling of stenter is at 3m/s ~ 4m/s；
E () toasts
By stenter, by correcting the denim after broadwise silk tuft, to send in the baking oven that temperature is 150 DEG C ~ 200 DEG C baking 10min ~ 20min to moisture content be 5% ~ 10%；；
(f) upper softening agent
Putting into, by toasting complete denim, the water vat being equipped with softening agent, inserting the ratio being placed with in the cylinder of softening agent 15min ~ 30min, softening agent and water after having cleaned is 1:50 ~ 1:100；
G () is shaped
To soak the denim after softening agent operation completes and send into shaping baking oven sizing, setting temperature is 150 DEG C～200 DEG C, until moisture content is take out after 3% ~ 5%, and cooling, cropping；
(h) molding
The back side and the flannelette napped fabric layer (3) of initial bed (2) are joined together to form the denim possessing heat insulation function by hot pressing combination process, and hot pressing combination process can pack warehouse-in after completing.
2. the processing technology of a kind of mildew-resistant colour jacquard jean according to claim 1, it is characterised in that: the jean in step a is added fleece fibre blended spinning by cotton fiber and tencel fiber and forms.
3. the processing technology of a kind of mildew-resistant colour jacquard jean according to claim 2, it is characterised in that: the ratio of described cotton fiber, wool fiber and tencel fiber is 4:3:1.
4. the processing technology of a kind of mildew-resistant colour jacquard jean according to claim 1, it is characterized in that: the bamboo carbon fiber in step a accounts for the 22%-30% of the mass percent of denim, described Nipagin ester accounts for the 5%-8% of the mass percent of denim, and jean accounts for the 60% ~ 75% of the mass percent of denim.
5. the processing technology of a kind of mildew-resistant colour jacquard jean according to claim 1, it is characterised in that: the ratio of the hemp in step a and described flax fiber is 1:1.5.
6. the processing technology of a kind of mildew-resistant colour jacquard jean according to claim 1, it is characterised in that: the softening agent in step f is ester based quaternary ammonium salt softening agent, fatty acid ester type softening agent, right wax pattern softening agent or polyethylene softening agent.
7. the processing technology of a kind of colored soft denim according to claim 1, it is characterised in that: the fabric guide roll in step b is provided with groove.
8. a kind of mildew-resistant jacquard jeans fabric possessing heat-preserving function according to claim 1, it is characterised in that: the material of described flannelette napped fabric layer is polar fleece, lamb floss or coral fleece.
CN201610136175.4A 2016-03-10 2016-03-10 Production process of mildew-proof jacquard denim with warm-keeping function Pending CN105799244A (en)