CN101899744A - Polyester coral blanket - Google Patents
Polyester coral blanket Download PDFInfo
- Publication number
- CN101899744A CN101899744A CN200910143067XA CN200910143067A CN101899744A CN 101899744 A CN101899744 A CN 101899744A CN 200910143067X A CN200910143067X A CN 200910143067XA CN 200910143067 A CN200910143067 A CN 200910143067A CN 101899744 A CN101899744 A CN 101899744A
- Authority
- CN
- China
- Prior art keywords
- polyester
- blanket
- raw material
- coral
- terylene thread
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides a polyester coral blanket. In the blanket, 0.58 to 1.16dtex of polyester yarn is adopted as a fleece yarn raw material, and 70 to 140dtex of polyester FDY is adopted as base yarn, wherein the polyester yarn accounts for 60 to 80 mass percent of the blanket, and the polyester FDY accounts for 20 to 40 mass percent of the blanket. The blanket has relative wide raw material source, thus reducing production cost, and better fulfilling the requirement of the market to high-quality blanket.
Description
Technical field
The present invention relates to a kind of is the woollen blanket that raw material adopts the warp-knitting explained hereafter with the terylene thread, more particularly, is a kind of polyester coral blanket.
Background technology
Existing woollen blanket has all woolen blanket, woollen mixed blanket, acrylic blanket, cotton blanket and adopt polar fleece woollen blanket that polyester raw material produces etc. on weft-knitted large circle machine on the market.For many years, these woollen blankets are not having obvious improvement aspect feel, the style, are difficult to satisfy the needs to high-quality life that people improve day by day.For example, though all woolen blanket thermal property is better, not mildew-resistant, not mothproof, the overworked sense of bedding spinosity next to the shin, comfortable inadequately.Though woollen mixed blanket slightly improves than all woolen blanket aspect material, its defective is similar to all woolen blanket.Though beautiful in colour, the anti-mould and anti-moth of acrylic blanket, its feel and property next to the shin are still undesirable.Cotton blanket has good hygroscopicity, and quality is comparatively comfortable, but it still remains at aspects such as warmth retention property and level of comforts to be improved.The polar fleece woollen blanket is owing to adopt the spin PROCESS FOR TREATMENT, and its matte is coarse; Compare with cotton blanket, acrylic blanket, its properties of product and production technology all exist than obvious defects.
Chinese patent ZL 200510050367.5 has disclosed a kind of terylene superfine-denier coral fleece and production method thereof.It adopts 0.58dtex or following terylene thread or the polyamide composite filaments of this specification is suede yarn raw material, and the 111-167dtex polyester FDY is an end silk, and wherein, terylene thread or polyamide composite filaments account for 60-80 quality %, and polyester FDY accounts for 20-40 quality %.This woollen blanket has soft comfortable characteristics, and has property next to the shin preferably and heat-insulating property.
Summary of the invention
The objective of the invention is on the basis of existing technology, a series of improved polyester coral blankets be provided, thus greatly improved this type of woollen blanket the raw material applicability, reduce production costs, satisfy on the market demand better for high-quality woollen blanket.
Foregoing invention purpose of the present invention is achieved through the following technical solutions: adopting the 0.58dtex-1.16dtex terylene thread is suede yarn raw material, is end silk with the 70-140dtex polyester FDY; Wherein, described terylene thread accounts for 60-80 quality %, and polyester FDY accounts for 20-40 quality %.
According to polyester coral blanket provided by the present invention, preferably described woollen blanket is weaved by following raw material respectively and is formed:
(a) being suede yarn raw material with 0.77dtex (200D/288F DTY) terylene thread, is end silk with 137.5dtex (125D/48F) polyester FDY;
(b) being suede yarn raw material with 0.60dtex (156D/288F DTY) terylene thread, is end silk with 74.8dtex (68D/36F) polyester FDY;
(c) being suede yarn raw material with 0.60dtex (156D/288F DTY) terylene thread, is end silk with 82.5dtex (75D/36F) polyester FDY;
(d) being suede yarn raw material with 0.60dt ex (156D/288F DTY) terylene thread, is end silk with 137.5dtex (125D/48F) polyester FDY;
(e) being suede yarn raw material with 0.77dtex (100D/144F DTY) terylene thread, is end silk with 110dtex (100D/48F) polyester FDY;
(f) being suede yarn raw material with 1.16dtex (150D/144F DTY) terylene thread, is end silk with 82.5dtex (75D) polyester FDY;
(g) being suede yarn raw material with 0.77dtex (100D/144F DTY) terylene thread, is end silk with 110dtex (100D) polyester FDY;
(h) being suede yarn raw material with 0.58dtex (150D/288F DTY) terylene thread, is end silk with 74.8dtex (68D) polyester FDY.
Wherein, further preferably respectively by above-mentioned (a) and (b) and (c) described raw material weave the woollen blanket that forms.
According to polyester coral blanket provided by the present invention, described terylene thread DTY preferably accounts for 65-75 quality %, and polyester FDY accounts for 25-35 quality %; Further preferred described terylene thread DTY accounts for 70 quality %, and polyester FDY accounts for 30 quality %.
The weaving method of polyester coral blanket of the present invention may further comprise the steps:
(1) raw material is prepared, and is suede yarn raw material with the 0.58dtex-1.16dtex terylene thread, is end silk with 70-140dt ex polyester FDY; Described terylene thread accounts for 60-80 quality %, and polyester FDY accounts for 20-40 quality %;
(2) weave grey cloth gram 200-1200g/m on the double-needle bed raschel warp knitting machine
2
(3) cut open the width of cloth;
(4) HEAT SETTING, temperature are 175-185 degree centigrade, fiber heated time 45-55 second;
(5) fabric is dyeed or stamp;
(6) fabric behind dyeing or the stamp is carried out necessary post processing;
(7) with napper the continuous plucking of envers 3-5 time;
(8) use combing machine for fur in the envers carding;
(9) envers cropping;
(10) use frizzing machine in the envers balling-up;
(11), make, become blanket through HEAT SETTING.
According to polyester coral blanket provided by the present invention, described terylene thread DTY is preferably twisted into the DTY silk raw material of same specification or different size (for example 2-4 root all can) by twisting mill the superfine denier fiber of the high F number of sub-thread before weaving, and then be used to weave, make fiber have good effect resistant to lodging, thereby improve the grammes per square metre and the suede height of fabric.
Compared with prior art, polyester coral blanket provided by the present invention has following characteristics: (a) raw material sources are extensive relatively, thereby improved this type of woollen blanket the raw material applicability, reduce production costs, satisfy on the market demand better for high-quality woollen blanket; (b) polyester coral blanket provided by the present invention is beautiful in colour, has good heat-insulating property, and quality softness, exquisiteness, is suitable for use next to the shin; (c) polyester coral blanket anti-mould and anti-moth provided by the present invention, but cyclic washing do not contain any harmful material.
The specific embodiment
Further describe polyester coral blanket provided by the present invention below in conjunction with the specific embodiment, but therefore the present invention is not subjected to any restriction.
Embodiment 1
This embodiment explanation: the weaving of ultra-fine plush stamp blanket.
Terylene coral suede individual layer stamp plucking blanket, finished product amplitude 152cm, grammes per square metre 280g/m
2, concrete production stage is as follows:
(1) raw material is prepared: with 0.77dtex (200D/288F DTY) dacron elasticity silk is suede yarn raw material, is end silk with 137.5dtex (125D/48F) polyester FDY; Described dacron elasticity silk accounts for 65 quality %, and polyester FDY accounts for 35 quality %;
(2) weave grey cloth gram 560g/m on the double-needle bed raschel warp knitting machine
2, fabric width 152cm;
(3) cut open the width of cloth;
(4) HEAT SETTING, temperature are 210 degrees centigrade, fiber heated time 45 seconds;
(5) fabric is carried out stamp: the printing paste prescription contains disperse red, disperse yellow, disperse blue, and all the other compositions are gelatinized corn starch; The consumption of above-mentioned material is according to color and different;
(6) will under 140-150 degree centigrade, evaporate behind the fabric drying behind the stamp, again with the washing of caustic soda and sodium hydrosulfite,, 70 degrees centigrade of washing temperature, time 15-20 minute, wherein the consumption of caustic soda and sodium hydrosulfite was decided according to color, and dark more their consumption of color is big more; Add softener then in the setting machine groove, the processing of finalizing the design prepares to carry out plucking after the oven dry down at 160 degrees centigrade, and wherein the consumption of softener is the 4-5% of fabric gross weight;
(7) with 36 porcupine roller nappers, with No. 42/80 stripping fillet, drum rotation speed 80rpm, cloth speed 15-20m/min is the continuous plucking of envers 4 times;
(8) with 24 porcupine roller combing machine for furs, drum rotation speed 80rpm, cloth speed 15-20m/min is in the envers carding;
(9) envers cropping, cloth speed 15-20m/min grabs roller speed 700-800rpm, scissors speed 1300-1400rpm;
(10) use frizzing machine envers balling-up 40 minutes, temperature is 120-130 degree centigrade;
(11) heat setting temperature is 180 degrees centigrade, fiber heated time 30-40 second, fabric width 152cm;
(12) become blanket, the examination and test of products and packing.
Embodiment 2
This embodiment explanation: the weaving of the plain color coral blanket that provides of the present invention, the one side of woollen blanket is ultra-fine plush, another side is not done napping and is handled.
The finished product fabric width 165cm of this woollen blanket, double-deck grammes per square metre 400g/m
2, concrete production stage is as follows:
(1) raw material is prepared: with 0.77dtex (200D/288F DTY) terylene thread is suede yarn raw material, is end silk with 137.5dtex (125D/48F) polyester FDY; Described DTY terylene thread accounts for 65 quality %, and polyester FDY accounts for 35 quality %;
(2) weave grey cloth gram 400g/m on the double-needle bed raschel warp knitting machine
2, fabric width 165cm;
(3) cut open the width of cloth;
(4) HEAT SETTING, temperature are 210 degrees centigrade, fiber heated time 50 seconds;
(5) fabric is dyeed: be benchmark with the fabric weight, dye formulation changes to some extent according to different colours.Used coloring agent contains disperse red, disperse yellow, disperse blue, glacial acetic acid and levelling agent; At first fabric is put into color pond, be lower than 65 degrees centigrade of described color additives of adding down then, the pond temperature of color pond evenly rose to 130 degrees centigrade through 50 minutes then, be incubated 30 minutes, inject cold water in the steam off valve then, dyeing machine interlayer, go out cloth about temperature drop to 80 degree centigrade;
(6) dyeing post processing, caustic soda and sodium hydrosulfite, 70 degrees centigrade of washing temperature, time 15-20 minute, wherein the consumption of caustic soda and sodium hydrosulfite was decided according to color, and dark more their consumption of color is big more; The softener that in the setting machine groove, adds the 4-5% of fabric gross weight then, the processing of finalizing the design, 180 degrees centigrade of following HEAT SETTING, fiber heated time 30-40 second, fabric width 165cm;
(7) become blanket, the examination and test of products and packing.
If the back side of this woollen blanket need be done napping and be handled, the concrete operations step is identical with step (7)-(12) among the embodiment 1.
Claims (12)
1. polyester coral blanket is characterized in that it is suede yarn raw material that this woollen blanket adopts 0.58dt ex-1.16dtex terylene thread, is end silk with the 70-140dtex polyester FDY, and described terylene thread accounts for 60-80 quality %, and polyester FDY accounts for 20-40 quality %.
2. polyester coral blanket according to claim 1 is characterized in that this woollen blanket is a suede yarn raw material with the 0.77dtex terylene thread, is end silk with the 137.5dtex polyester FDY.
3. polyester coral blanket according to claim 1 is characterized in that this woollen blanket is a suede yarn raw material with the 0.60dtex terylene thread, is end silk with the 74.8dtex polyester FDY.
4. polyester coral blanket according to claim 1 is characterized in that this woollen blanket is a suede yarn raw material with the 0.60dtex terylene thread, is end silk with the 82.5dtex polyester FDY.
5. polyester coral blanket according to claim 1 is characterized in that this woollen blanket is a suede yarn raw material with the 0.60dtex terylene thread, is end silk with the 137.5dtex polyester FDY.
6. polyester coral blanket according to claim 1 is characterized in that this woollen blanket is a suede yarn raw material with 0.77dt ex terylene thread, is end silk with 110dt ex polyester FDY.
7. polyester coral blanket according to claim 1 is characterized in that this woollen blanket is a suede yarn raw material with the 1.16dtex terylene thread, is end silk with the 82.5dtex polyester FDY.
8. polyester coral blanket according to claim 1 is characterized in that this woollen blanket is a suede yarn raw material with 0.77dt ex terylene thread, is end silk with 110dt ex polyester FDY.
9. polyester coral blanket according to claim 1 is characterized in that this woollen blanket is a suede yarn raw material with the 0.58dtex terylene thread, is end silk with the 74.8dtex polyester FDY.
10. according to any described polyester coral blanket among the claim 2-9, it is characterized in that described terylene thread accounts for 65-75 quality %, polyester FDY accounts for 25-35 quality %.
11. polyester coral blanket according to claim 10 is characterized in that described terylene thread accounts for 70 quality %, polyester FDY accounts for 30 quality %.
12., it is characterized in that the weaving method of described polyester coral blanket may further comprise the steps according to claim 1 or 11 described polyester coral blankets:
(1) raw material is prepared, and is suede yarn raw material with the 0.58dtex-1.16dtex terylene thread, is end silk with the 70-140dtex polyester FDY; Described terylene thread accounts for 60-80 quality %, and polyester FDY accounts for 20-40 quality %;
(2) weave grey cloth gram 200-1200g/m on the double-needle bed raschel warp knitting machine
2
(3) cut open the width of cloth;
(4) HEAT SETTING, temperature are 175-185 degree centigrade, fiber heated time 45-55 second;
(5) fabric is dyeed or stamp;
(6) fabric behind dyeing or the stamp is carried out necessary post processing;
(7) with napper the continuous plucking of envers 3-5 time;
(8) use combing machine for fur in the envers carding;
(9) envers cropping;
(10) use frizzing machine in the envers balling-up;
(11), make, become blanket through HEAT SETTING.