CN105778235A - Fishing net manufactured from plastics modified by potassium feldspar powder and calcium carbonate powder mixture - Google Patents
Fishing net manufactured from plastics modified by potassium feldspar powder and calcium carbonate powder mixture Download PDFInfo
- Publication number
- CN105778235A CN105778235A CN201610287608.6A CN201610287608A CN105778235A CN 105778235 A CN105778235 A CN 105778235A CN 201610287608 A CN201610287608 A CN 201610287608A CN 105778235 A CN105778235 A CN 105778235A
- Authority
- CN
- China
- Prior art keywords
- calcium carbonate
- powder
- feldspar
- fishing net
- carbonate powder
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a fishing net manufactured from plastics modified by a potassium feldspar powder and calcium carbonate powder mixture. The fishing net is manufactured from glycidyl methacrylate, a polyamide 6 and polyvinylidene chloride mixture, low-density polyethylene, the potassium feldspar powder and calcium carbonate powder mixture, polyarylester, butadiene-acrylonitrile rubber, polyacrylonitrile fiber, zinc dihydrogen phosphate, rosin and assistant modifiers. The fishing net combines the advantages of the raw materials such as the polyamide 6 and polyvinylidene chloride mixture and the low-density polyethylene, the potassium feldspar powder and calcium carbonate powder mixture is used for modifying the plastics and the raw materials such as the zinc dihydrogen phosphate, the rosin and the assistant modifiers are used for assistant modification, so that the modified plastics are high in mechanical performance, further the manufactured fishing net is high in strength, and tensile strength and toughness of the fishing net are greatly improved and are 1.83 times and twice of those of a common fishing net respectively.
Description
Technical field
The present invention relates to fishing gear field, particularly relate to the fishing net that a kind of feldspar in powder is made with the mixed and modified plastics of calcium carbonate powder.
Background technology
Fishing net is the net of fishing, and it is numb as raw material that men of old uses coarse cloth to add, makes fishnet by tying the method for volume.Although this fishing net is perishable, toughness is poor, but its fishing efficiency is greatly improved.Along with the development of fishery, the object of fishing and hunting is more than fish, and the instrument fished for also grows with each passing hour.It is numb as raw material that men of old uses coarse cloth to add, by the method tying volume
Make fishnet.Although this fishing net is perishable, toughness is poor, but its fishing efficiency is greatly improved.Along with the development of fishery, the object of fishing and hunting is more than fish, and the instrument fished for also grows with each passing hour.Modern fishing net mainly adopts Low Density Polyethylene, the raw materials such as nylon are processed, there are longer life cycle and higher catching rate, but the mechanical property of Low Density Polyethylene itself is general, hot strength is relatively low, creep resistance is bad, results in the tradition intensity of fishing net, anti-wear performance, toughness are unsuitable at the bottom of Complex Sea and wind and waves environment fishing operation, reduce the service life of fishing gear, not only waste resource, also directly affect catch.
Summary of the invention
It is an object of the invention to provide the fishing net that a kind of feldspar in powder is made with the mixed and modified plastics of calcium carbonate powder, be achieved through the following technical solutions:
The fishing net that a kind of feldspar in powder and the mixed and modified plastics of calcium carbonate powder are made, is made up of following component by weight: glycidyl methacrylate 0.8, nylon 6 and Vingon mixture 38, Low Density Polyethylene 120, feldspar in powder and calcium carbonate powder mixture 0.4, polyarylate 4, nitrile rubber 0.2, polyacrylonitrile fibre 0.3, zinc dihydrogen phosphate 0.1, Colophonium 2, auxiliary modifier 0.3；Described auxiliary modifier is made up of following component by weight: Flos Caryophylli oil 5, titanium dioxide 1, dimethyl phthalate 1, di-sec-octyl phthalate 3, sodium lauryl sulphate 2,2-Propenoic acid, 2-methyl-, isooctyl ester 4, Tert-butyl Methacrylate 3；Preparation method is calcined 18 minutes at 300 DEG C by titanium dioxide, adopt heating in water bath to 80 DEG C Flos Caryophylli oil, dimethyl phthalate and di-sec-octyl phthalate, then the titanium dioxide after calcining, sodium lauryl sulphate, 2-Propenoic acid, 2-methyl-, isooctyl ester, Tert-butyl Methacrylate are added, first stir 20 minutes with 450r/min speed, stir 15 minutes with 1000r/min speed again,；Auxiliary modifier can improve the comprehensive mechanical property of fishing net, promotes generation adhesion between each composition, improves the interfacial gluing of each one-tenth.
Further, the granularity of described feldspar in powder and calcium carbonate powder mixture is 5500-5800 order, described feldspar in powder and calcium carbonate powder mixture are uniformly mixed by 3:5 mass ratio, described feldspar in powder and the content of half in calcium carbonate powder mixture are through calcination processing, second half processes through solution modification agent, through the feldspar in powder of solution modification agent process with the processing method of calcium carbonate powder mixture it is: it is after soaking 3-4 hour in 7.85% cocamido propyl betaine solution that feldspar in powder and calcium carbonate powder mixture are put into mass concentration, filter, washing surface, dry；Being 225-230 DEG C through the feldspar in powder of calcination processing and the calcining heat of calcium carbonate powder mixture, calcination time is 20 minutes；Enabling to feldspar in powder and calcium carbonate powder compound particles miniaturization, specific surface area increases, and improves the affinity on its surface and Low Density Polyethylene, polrvinyl chloride and nylon 6.
Further, the granularity of described zinc dihydrogen phosphate is 5800-6000 order；The granularity of described titanium dioxide is 115-120nm.
Further, described Colophonium is through pretreatment: after Colophonium adopting soaked in absolute ethyl alcohol 10 hours, filters, and adopts 35 DEG C of temperature to toast 1 minute.
Further, described polyacrylonitrile fibre surface processes through inorganic agent, after polyacrylonitrile fibre mixes 20 minutes with inorganic agent with inorganic agent at 68 DEG C, filters, washing, dries,；Described inorganic agent is made up of following component in percentage terms: 50% sodium laureth sulfate, 10% silane resin acceptor kh-550,40% water；Add combine between treated polyacrylonitrile fibre not only polyacrylonitrile fibre and other composition tightr, and pliability and the tensile strength of fishing net can greatly be improved.
Further, described nylon 6 and nylon in Vingon mixture 6 are be uniformly mixed at 225 DEG C by 4:3 mass ratio with Vingon.
The preparation method of the fishing net that a kind of feldspar in powder and the mixed and modified plastics of calcium carbonate powder are made, puts into glycidyl methacrylate, nylon 6 and Vingon mixture, Low Density Polyethylene, feldspar in powder with calcium carbonate powder mixture by weight in the container of temperature 144-146 DEG C and mixes 40 minutes；When internal tank temperature is adjusted to 86-88 DEG C, be sequentially added into the polyarylate of corresponding weight portion in container, nitrile rubber, polyacrylonitrile fibre, zinc dihydrogen phosphate are stirred, the speed of stirring is 700r/min, after stirring 10 minutes, then add the Colophonium of corresponding weight portion and auxiliary modifier and stir 20 minutes with 1200r/min speed, finally add extruder to and carry out pelletize, then injection machine injection moulding is used, then use spray webbing machine spray webbing, finally weave, obtain made fishing net.
nullThe invention has the beneficial effects as follows: present invention incorporates nylon 6 and Vingon mixture、The advantage of the raw materials such as Low Density Polyethylene，Utilize feldspar in powder and calcium carbonate powder mixture that material has been carried out modification，And with zinc dihydrogen phosphate、Colophonium、Material has been carried out Aided Modification process by the raw materials such as auxiliary modifier，Material after improvement has good processing characteristics and mechanical performance，The fishing net intensity made is high，Good toughness，Strong shock resistance，Antioxidation，Aging resistance，Fishing lines single line knotting strength is high，Bending strength is improved largely，Especially，Tensile strength and toughness obtain the raising of high degree，Tensile strength is stronger than common fishing net 0.83 times，The common fishing net of fishing net Toughness Ratio of the present invention is strong 1 times，The fishing net normal service life that the present invention makes improves 22.8% than common fishing net，Fishing net of the present invention is applicable not only to fresh water fishing，Apply also at the bottom of Complex Sea and wind and waves environment fishing operation.
Detailed description of the invention
The fishing net that a kind of feldspar in powder and the mixed and modified plastics of calcium carbonate powder are made, is made up of following component by weight: glycidyl methacrylate 0.8, nylon 6 and Vingon mixture 38, Low Density Polyethylene 120, feldspar in powder and calcium carbonate powder mixture 0.4, polyarylate 4, nitrile rubber 0.2, polyacrylonitrile fibre 0.3, zinc dihydrogen phosphate 0.1, Colophonium 2, auxiliary modifier 0.3；Described auxiliary modifier is made up of following component by weight: Flos Caryophylli oil 5, titanium dioxide 1, dimethyl phthalate 1, di-sec-octyl phthalate 3, sodium lauryl sulphate 2,2-Propenoic acid, 2-methyl-, isooctyl ester 4, Tert-butyl Methacrylate 3；Preparation method is calcined 18 minutes at 300 DEG C by titanium dioxide, adopt heating in water bath to 80 DEG C Flos Caryophylli oil, dimethyl phthalate and di-sec-octyl phthalate, then the titanium dioxide after calcining, sodium lauryl sulphate, 2-Propenoic acid, 2-methyl-, isooctyl ester, Tert-butyl Methacrylate are added, first stir 20 minutes with 450r/min speed, stir 15 minutes with 1000r/min speed again,；Auxiliary modifier can improve the comprehensive mechanical property of fishing net, promotes generation adhesion between each composition, improves the interfacial gluing of each one-tenth.
Further, the granularity of described feldspar in powder and calcium carbonate powder mixture is 5500-5800 order, described feldspar in powder and calcium carbonate powder mixture are uniformly mixed by 3:5 mass ratio, described feldspar in powder and the content of half in calcium carbonate powder mixture are through calcination processing, second half processes through solution modification agent, through the feldspar in powder of solution modification agent process with the processing method of calcium carbonate powder mixture it is: it is after soaking 3-4 hour in 7.85% cocamido propyl betaine solution that feldspar in powder and calcium carbonate powder mixture are put into mass concentration, filter, washing surface, dry；Being 225-230 DEG C through the feldspar in powder of calcination processing and the calcining heat of calcium carbonate powder mixture, calcination time is 20 minutes；Enabling to feldspar in powder and calcium carbonate powder compound particles miniaturization, specific surface area increases, and improves the affinity on its surface and Low Density Polyethylene, polrvinyl chloride and nylon 6.
Further, the granularity of described zinc dihydrogen phosphate is 5800-6000 order；The granularity of described titanium dioxide is 115-120nm.
Further, described Colophonium is through pretreatment: after Colophonium adopting soaked in absolute ethyl alcohol 10 hours, filters, and adopts 35 DEG C of temperature to toast 1 minute.
Further, described polyacrylonitrile fibre surface processes through inorganic agent, after polyacrylonitrile fibre mixes 20 minutes with inorganic agent with inorganic agent at 68 DEG C, filters, washing, dries,；Described inorganic agent is made up of following component in percentage terms: 50% sodium laureth sulfate, 10% silane resin acceptor kh-550,40% water；Add combine between treated polyacrylonitrile fibre not only polyacrylonitrile fibre and other composition tightr, and pliability and the tensile strength of fishing net can greatly be improved.
Further, described nylon 6 and nylon in Vingon mixture 6 are be uniformly mixed at 225 DEG C by 4:3 mass ratio with Vingon.
The preparation method of the fishing net that a kind of feldspar in powder and the mixed and modified plastics of calcium carbonate powder are made, puts into glycidyl methacrylate, nylon 6 and Vingon mixture, Low Density Polyethylene, feldspar in powder with calcium carbonate powder mixture by weight in the container of temperature 144-146 DEG C and mixes 40 minutes；When internal tank temperature is adjusted to 86-88 DEG C, be sequentially added into the polyarylate of corresponding weight portion in container, nitrile rubber, polyacrylonitrile fibre, zinc dihydrogen phosphate are stirred, the speed of stirring is 700r/min, after stirring 10 minutes, then add the Colophonium of corresponding weight portion and auxiliary modifier and stir 20 minutes with 1200r/min speed, finally add extruder to and carry out pelletize, then injection machine injection moulding is used, then use spray webbing machine spray webbing, finally weave, obtain made fishing net.
Claims (7)
1. the fishing net that a feldspar in powder is made with the mixed and modified plastics of calcium carbonate powder, it is characterized in that, be made up of following component by weight: glycidyl methacrylate 0.8, nylon 6 and Vingon mixture 38, Low Density Polyethylene 120, feldspar in powder and calcium carbonate powder mixture 0.4, polyarylate 4, nitrile rubber 0.2, polyacrylonitrile fibre 0.3, zinc dihydrogen phosphate 0.1, Colophonium 2, auxiliary modifier 0.3；Described auxiliary modifier is made up of following component by weight: Flos Caryophylli oil 5, titanium dioxide 1, dimethyl phthalate 1, di-sec-octyl phthalate 3, sodium lauryl sulphate 2,2-Propenoic acid, 2-methyl-, isooctyl ester 4, Tert-butyl Methacrylate 3；Preparation method is calcined 18 minutes at 300 DEG C by titanium dioxide, adopt heating in water bath to 80 DEG C Flos Caryophylli oil, dimethyl phthalate and di-sec-octyl phthalate, then the titanium dioxide after calcining, sodium lauryl sulphate, 2-Propenoic acid, 2-methyl-, isooctyl ester, Tert-butyl Methacrylate are added, first stir 20 minutes with 450r/min speed, stir 15 minutes with 1000r/min speed again,.
2. the fishing net that a kind of feldspar in powder according to claim 1 and the mixed and modified plastics of calcium carbonate powder are made, it is characterized in that, the granularity of described feldspar in powder and calcium carbonate powder mixture is 5500-5800 order, described feldspar in powder and calcium carbonate powder mixture are uniformly mixed by 3:5 mass ratio, described feldspar in powder and the content of half in calcium carbonate powder mixture are through calcination processing, second half processes through solution modification agent, through the feldspar in powder of solution modification agent process with the processing method of calcium carbonate powder mixture it is: it is after soaking 3-4 hour in 7.85% cocamido propyl betaine solution that feldspar in powder and calcium carbonate powder mixture are put into mass concentration, filter, washing surface, dry；Being 225-230 DEG C through the feldspar in powder of calcination processing and the calcining heat of calcium carbonate powder mixture, calcination time is 20 minutes.
3. the fishing net that a kind of feldspar in powder according to claim 1 and the mixed and modified plastics of calcium carbonate powder are made, it is characterised in that the granularity of described zinc dihydrogen phosphate is 5800-6000 order；The granularity of described titanium dioxide is 115-120nm.
4. the fishing net that a kind of feldspar in powder according to claim 1 and the mixed and modified plastics of calcium carbonate powder are made, it is characterised in that described Colophonium is through pretreatment: after Colophonium adopting soaked in absolute ethyl alcohol 10 hours, filters, and adopts 35 DEG C of temperature to toast 1 minute.
5. the fishing net that a kind of feldspar in powder according to claim 1 and the mixed and modified plastics of calcium carbonate powder are made, it is characterized in that, described polyacrylonitrile fibre surface processes through inorganic agent, after polyacrylonitrile fibre mixes 20 minutes with inorganic agent with inorganic agent at 68 DEG C, filter, washing, dries,；Described inorganic agent is made up of following component in percentage terms: 50% sodium laureth sulfate, 10% silane resin acceptor kh-550,40% water.
6. the fishing net that a kind of feldspar in powder according to claim 1 and the mixed and modified plastics of calcium carbonate powder are made, it is characterized in that, described nylon 6 and nylon in Vingon mixture 6 are be uniformly mixed at 225 DEG C by 4:3 mass ratio with Vingon.
7. the preparation method of the fishing net that a kind of feldspar in powder according to any one of claim 1-6 and the mixed and modified plastics of calcium carbonate powder are made, it is characterized in that, by weight glycidyl methacrylate, nylon 6 and Vingon mixture, Low Density Polyethylene, feldspar in powder are put into calcium carbonate powder mixture in the container of temperature 144-146 DEG C and mix 40 minutes；When internal tank temperature is adjusted to 86-88 DEG C, be sequentially added into the polyarylate of corresponding weight portion in container, nitrile rubber, polyacrylonitrile fibre, zinc dihydrogen phosphate are stirred, the speed of stirring is 700r/min, after stirring 10 minutes, then add the Colophonium of corresponding weight portion and auxiliary modifier and stir 20 minutes with 1200r/min speed, finally add extruder to and carry out pelletize, then injection machine injection moulding is used, then use spray webbing machine spray webbing, finally weave, obtain made fishing net.