CN105774104A - Fabrication process for mould-proof colorful jacquard denim fabric - Google Patents
Fabrication process for mould-proof colorful jacquard denim fabric Download PDFInfo
- Publication number
- CN105774104A CN105774104A CN201610135790.3A CN201610135790A CN105774104A CN 105774104 A CN105774104 A CN 105774104A CN 201610135790 A CN201610135790 A CN 201610135790A CN 105774104 A CN105774104 A CN 105774104A
- Authority
- CN
- China
- Prior art keywords
- denim
- fiber
- fabric
- jacquard
- softening agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a fabrication process for a mould-proof colorful jacquard denim fabric comprising a jacquard layer and a backing material layer, wherein the jacquard layer and the backing material layer are connected together through a fabric hot-press compounding process; the jacquard layer is a denim jacquard fabric; the backing material layer is formed by blending bamboo charcoal fiber, nipagin esters and a denim fabric; the denim fabric is formed by blending cotton fiber, tencel fiber and wool fiber; the denim jacquard fabric is made from hemp fiber and flax fiber through weaving by ring spinning. The denim fabric is compact in texture, thick, bright in color, clear in weave grain and attractive in appearance; the fabric can be endowed with good mould-proof effect; the fabrication process solves the problems that the traditional denim fabric has single color and dull style on fabric cover and lacks visual impact, and keeps pace with the time.
Description
Technical field
The present invention relates to garment material field, particularly the processing technology of a kind of mildew-resistant colour jacquard jean.
Background technology
In the eighties in 20th century, U.S.'s denim yield is the 50% of whole world yield, but among nearest 10 years, China, India, Pakistan, Malaysia, Tu Er itself and Mexico establish substantial amounts of denim factory, the denim center of production in the U.S. or even the world has been transferred to the country of the low labor cost in Asia, denim is also called and splits silks, it is that a kind of relatively thick thick color is knitted through face jean, warp thread color is deep, it is generally indigo, weft yarn is of light color, is generally the raw white yarn after light gray or kiering, also known as indigo denim.Starting from US West, the personnel that herd gain the name in order to make clothing.
Bamboo carbon fiber is that to take Phyllostachys pubescens Mazei ex H.de Lebaie be raw material, have employed the calcining new technology of pure oxygen high temperature and nitrogen obstruct time delay and new technique, the micropore that bamboo charcoal innately has more is refined and honeycomb, then again with have honeycomb microporous structure trend polyester modification cut into slices melt spinning and make.The fibre structure design of this uniqueness, can make bringing into play of the function 100% that bamboo charcoal has.It is described as " the new bodyguard of 21st century environmental protection " in the world.
Although denim is solid endurable, but cloth pattern is simple, if wearing jean for a long time, it is easy to be corroded, if cleaned not in time, denim can be made mouldy, it is easy to rot, affect the later stage clean once again after serviceability.
Summary of the invention
Goal of the invention: the invention aims to solve the deficiencies in the prior art, it is provided that a kind of jacquard weave mildew-resistant jean, it is possible to make fabric have good anti-mold effect, solve tradition denim color single, cloth style is dull, the problem lacking visual impact, has adapted to the trend in epoch.
Technical scheme: in order to realize object above, specifically comprising the following steps that of the processing technology of a kind of mildew-resistant colour jacquard jean of the present invention
A () is weaved cotton cloth
By jacquard layer (1) by the weaving braiding of RING SPINNING of hemp and flax fiber with by bamboo carbon fiber, the initial bed (2) of Nipagin ester and jean blending is connected together formation denim by fabric hot pressing combination process;
(b) pre-treatment, enter cloth
After denim having been processed with alkali, refining agent, hydrogen peroxide, cloth inlet mechanism with the speed of 5m/s~8m/s, denim is transported out, through being possible to prevent the fabric guide roll that crimping occurs in denim transmission;
(c) drinking water infiltration
Arriving infiltration tank through the denim of fabric guide roll output, make denim launch in water and fully permeate drinking water, reaching the water content of denim is till 60%~80%, and control water temperature is 50 DEG C~90 DEG C simultaneously;
(d) whole latitude, overfeeding
Through weft straightener, the denim after infiltration is corrected the crooked of broadwise silk tuft, and the speed controlling of stenter is at 3m/s~4m/s;
E () toasts
By stenter, by correcting the denim after broadwise silk tuft, to send in the baking oven that temperature is 150 DEG C~200 DEG C baking 10min~20min to moisture content be 5%~10%;;
F () is dyeed
The complete denim of baking is put in the dyeing installation of deployed dyestuff and dye;
(g) upper softening agent
By denim from taking out in dyeing installation and it being cleaned again, inserting the ratio being placed with in the cylinder of softening agent 15min~30min, softening agent and water after having cleaned is 1:50~1:100;
H () is shaped
To soak the denim after softening agent operation completes and send into shaping baking oven sizing, setting temperature is 150 DEG C~200 DEG C, until moisture content is take out after 3%~5%, cooling, cropping can pack warehouse-in.
As present invention further optimization, fabric guide roll in step b is provided with thin groove, makes denim launch fully to permeate drinking water in water, it is ensured that the shrinkage of denim and stablizing of grammes per square metre, thus creating best cloth cover condition to denim sizing, the variety range of denim is greatly increased.
As present invention further optimization, the described dyestuff in step e is reactive dye, and dyestuff takes from any one or multiple mixing in orange X-GN, brilliant red X-3B, gorgeous blue X-BR, gorgeous blue B-RV, dark red E-2BD, bright red E-GGF, gorgeous blue KN-R, emerald green blue B-BGFN, red B-3BF, blue B-2GLN, light yellow B-4GLN, orange DC-3R, yellow DC-RL, orange DC-3G, blue FN-RN, red FL-2BL, dark blue DC-GB, army indigo plant GG, dark blue GW-HA, black GW-HA, green GW-HA, purple GW-HA, blue GW-HN, red GW-HA, emerald green blue GW-HA.
As present invention further optimization, softening agent in step h is ester based quaternary ammonium salt softening agent, fatty acid ester type softening agent, right wax pattern softening agent or polyethylene softening agent, textile is in the course of processing, after repeatedly processing, feel can become coarse, general synthetic fabrics is worse, especially Superfine Fibre Fabric.In order to make fabric have softness, smooth, comfortable feel, it is necessary to it is arranged, widely used is arrange with softening agent.
As present invention further optimization, described bamboo carbon fiber accounts for the 22%-30% of the mass percent of described jacquard weave mildew-resistant jean, and described Nipagin ester accounts for 60%~75% that 5%-8% son's cloth of the described mass percent planting jacquard weave mildew-resistant jean accounts for the mass percent of described jacquard weave mildew-resistant jean.
As present invention further optimization, the ratio of described cotton fiber, wool fiber and tencel fiber is 4:3:1,1, and it is relatively good that tencel fiber has soft warm property, does not crease easily, and cotton fiber comfort level is relatively good, and wool fiber has warming effect.
As present invention further optimization, the ratio of described hemp and described flax fiber is 1:1.5, hemp and flax fiber all have the effect of ventilative absorbing sweat, anti-wear performance is better, flax fiber is thick and short, soft identical with cotton, hemp cloth not only looks that gloss is soft, and the ultraviolet with advantage penetrates function.The filamentary fineness of Fructus Cannabis is about 2-3 times of Boehmeria, and close with cotton, fiber tip is blunt round, there is no the such pointed end of Boehmeria, Caulis et Folium Lini, therefore the textile formed with hemp processing, it is not necessary to special handling, just can be effectively prevented from coarse hard sense and the prodding and itching feeling of other gunny products
Beneficial effect: the invention provides the processing technology of a kind of mildew-resistant colour jacquard jean, this jean quality is tight, abundant, bright in colour, weavy grain is clear, good looking appearance, enabling to fabric and have good anti-mold effect, solve tradition denim color single, cloth style is dull, the problem lacking visual impact, has adapted to the trend in epoch.
Detailed description of the invention
Below in conjunction with embodiment, it is further elucidated with the present invention.
The present invention provides a kind of jacquard weave mildew-resistant jean, including: jacquard layer and initial bed, described jacquard layer and initial bed are connected together by fabric hot pressing combination process, described jacquard layer is cowboy's jacquard fabric, described initial bed is by bamboo carbon fiber, Nipagin ester and jean blending form, and described jean is added fleece fibre blended spinning by cotton fiber and tencel fiber and forms, and described cowboy's jacquard fabric is formed by the weaving braiding of RING SPINNING by hemp and flax fiber.
Embodiment 1
The present invention provides a kind of jacquard weave mildew-resistant jean, including: jacquard layer and initial bed, described jacquard layer and initial bed are connected together by fabric hot pressing combination process.
Jacquard layer is cowboy's jacquard fabric, hemp and flax fiber are formed by the weaving braiding of RING SPINNING with the ratio of 1:1.5;
Initial bed is to be formed by bamboo carbon fiber, Nipagin ester and jean blending, bamboo carbon fiber accounts for the 22% of fabric gross mass percentage ratio, Nipagin ester accounts for the 5% of fabric gross mass percentage ratio, denim accounts for the 73% of fabric gross mass percentage ratio, jean is added fleece fibre blended spinning by cotton fiber and tencel fiber and forms, and the ratio of cotton fiber, wool fiber and tencel fiber is 4:3:1.
Specifically comprising the following steps that of the processing technology of a kind of mildew-resistant colour jacquard jean
A () is weaved cotton cloth
By jacquard layer 1 by the weaving braiding of RING SPINNING of hemp and flax fiber with by bamboo carbon fiber, the initial bed 2 of Nipagin ester and jean blending is connected together formation denim by fabric hot pressing combination process;
(b) pre-treatment, enter cloth
After denim having been processed with alkali, refining agent, hydrogen peroxide, cloth inlet mechanism with the speed of 5m/s, denim is transported out, through being possible to prevent the fabric guide roll that crimping occurs in denim transmission;
(c) drinking water infiltration
Arriving infiltration tank through the denim of fabric guide roll output, make denim launch in water and fully permeate drinking water, reaching the water content of denim is till 60%, and control water temperature is 50 DEG C simultaneously;
(d) whole latitude, overfeeding
Through weft straightener, the denim after infiltration is corrected the crooked of broadwise silk tuft, and the speed controlling of stenter is at 3m/s;
E () toasts
By stenter, by correcting the denim after broadwise silk tuft, to send in the baking oven that temperature is 150 DEG C baking 10min to moisture content be 5%;;
F () is dyeed
The complete denim of baking is put in the dyeing installation of deployed dyestuff and dye;
(g) upper softening agent
By denim from taking out in dyeing installation and it being cleaned again, inserting the ratio being placed with in the cylinder of softening agent 15min, softening agent and water after having cleaned is 1:50;
H () is shaped
To soak the denim after softening agent operation completes and send into shaping baking oven sizing, setting temperature is 150 DEG C, until moisture content is take out after 3%, cooling, cropping can pack warehouse-in.
Embodiment 2
The present invention provides a kind of jacquard weave mildew-resistant jean, including: jacquard layer and initial bed, described jacquard layer and initial bed are connected together by fabric hot pressing combination process.
Jacquard layer is cowboy's jacquard fabric, hemp and flax fiber are formed by the weaving braiding of RING SPINNING with the ratio of 1:1.5;
Initial bed is to be formed by bamboo carbon fiber, Nipagin ester and jean blending, bamboo carbon fiber accounts for the 25% of fabric gross mass percentage ratio, Nipagin ester accounts for the 8% of fabric gross mass percentage ratio, denim accounts for the 67% of fabric gross mass percentage ratio, jean is added fleece fibre blended spinning by cotton fiber and tencel fiber and forms, and the ratio of cotton fiber, wool fiber and tencel fiber is 4:3:1.
Specifically comprising the following steps that of the processing technology of a kind of mildew-resistant colour jacquard jean
A () is weaved cotton cloth
By jacquard layer 1 by the weaving braiding of RING SPINNING of hemp and flax fiber with by bamboo carbon fiber, the initial bed 2 of Nipagin ester and jean blending is connected together formation denim by fabric hot pressing combination process;
(b) pre-treatment, enter cloth
After denim having been processed with alkali, refining agent, hydrogen peroxide, cloth inlet mechanism with the speed of 6m/s, denim is transported out, through being possible to prevent the fabric guide roll that crimping occurs in denim transmission;
(c) drinking water infiltration
Arriving infiltration tank through the denim of fabric guide roll output, make denim launch in water and fully permeate drinking water, reaching the water content of denim is till 70%, and control water temperature is 60 DEG C simultaneously;
(d) whole latitude, overfeeding
Through weft straightener, the denim after infiltration is corrected the crooked of broadwise silk tuft, and the speed controlling of stenter is at 3.5m/s;
E () toasts
By stenter, by correcting the denim after broadwise silk tuft, to send in the baking oven that temperature is 180 DEG C baking 15min to moisture content be 8%;;
F () is dyeed
The complete denim of baking is put in the dyeing installation of deployed dyestuff and dye;
(g) upper softening agent
By denim from taking out in dyeing installation and it being cleaned again, inserting the ratio being placed with in the cylinder of softening agent 20min, softening agent and water after having cleaned is 1:80;
H () is shaped
To soak the denim after softening agent operation completes and send into shaping baking oven sizing, setting temperature is 180 DEG C, until moisture content is take out after 4%, cooling, cropping can pack warehouse-in.
Embodiment 3
The present invention provides a kind of jacquard weave mildew-resistant jean, including: jacquard layer and initial bed, described jacquard layer and initial bed are connected together by fabric hot pressing combination process.
Jacquard layer is cowboy's jacquard fabric, hemp and flax fiber are formed by the weaving braiding of RING SPINNING with the ratio of 1:1.5;
Initial bed is to be formed by bamboo carbon fiber, Nipagin ester and jean blending, bamboo carbon fiber accounts for the 30% of fabric gross mass percentage ratio, Nipagin ester accounts for the 8% of fabric gross mass percentage ratio, denim accounts for the 62% of fabric gross mass percentage ratio, jean is added fleece fibre blended spinning by cotton fiber and tencel fiber and forms, and the ratio of cotton fiber, wool fiber and tencel fiber is 4:3:1.
Specifically comprising the following steps that of the processing technology of a kind of mildew-resistant colour jacquard jean
A () is weaved cotton cloth
By jacquard layer 1 by the weaving braiding of RING SPINNING of hemp and flax fiber with by bamboo carbon fiber, the initial bed 2 of Nipagin ester and jean blending is connected together formation denim by fabric hot pressing combination process;
(b) pre-treatment, enter cloth
After denim having been processed with alkali, refining agent, hydrogen peroxide, cloth inlet mechanism with the speed of 8m/s, denim is transported out, through being possible to prevent the fabric guide roll that crimping occurs in denim transmission;
(c) drinking water infiltration
Arriving infiltration tank through the denim of fabric guide roll output, make denim launch in water and fully permeate drinking water, reaching the water content of denim is till 80%, and control water temperature is 90 DEG C simultaneously;
(d) whole latitude, overfeeding
Through weft straightener, the denim after infiltration is corrected the crooked of broadwise silk tuft, and the speed controlling of stenter is at 4m/s;
E () toasts
By stenter, by correcting the denim after broadwise silk tuft, to send in the baking oven that temperature is 200 DEG C baking 20min to moisture content be 10%;;
F () is dyeed
The complete denim of baking is put in the dyeing installation of deployed dyestuff and dye;
(g) upper softening agent
By denim from taking out in dyeing installation and it being cleaned again, inserting the ratio being placed with in the cylinder of softening agent 30min, softening agent and water after having cleaned is 1:100;
H () is shaped
To soak the denim after softening agent operation completes and send into shaping baking oven sizing, setting temperature is 200 DEG C, until moisture content is take out after 5%, cooling, cropping can pack warehouse-in.
Above-mentioned detailed description of the invention only for technology design and the feature of the present invention are described, its objective is to allow and is familiar with these those skilled in the art and will appreciate that present disclosure and implement according to this, can not limit the scope of the invention with this.All equivalents made according to spirit of the invention or modification, all should be encompassed within protection scope of the present invention.
Claims (8)
1. the processing technology of a mildew-resistant colour jacquard jean, it is characterised in that: specifically comprising the following steps that of the method
A () is weaved cotton cloth
By jacquard layer (1) by the weaving braiding of RING SPINNING of hemp and flax fiber with by bamboo carbon fiber, the initial bed (2) of Nipagin ester and jean blending is connected together formation denim by fabric hot pressing combination process;
(b) pre-treatment, enter cloth
After denim having been processed with alkali, refining agent, hydrogen peroxide, cloth inlet mechanism with the speed of 5m/s ~ 8m/s, denim is transported out, through being possible to prevent the fabric guide roll that crimping occurs in denim transmission;
(c) drinking water infiltration
Arriving infiltration tank through the denim of fabric guide roll output, make denim launch in water and fully permeate drinking water, reaching the water content of denim is till 60%~80%, and control water temperature is 50 DEG C~90 DEG C simultaneously;
(d) whole latitude, overfeeding
Through weft straightener, the denim after infiltration is corrected the crooked of broadwise silk tuft, and the speed controlling of stenter is at 3m/s ~ 4m/s;
E () toasts
By stenter, by correcting the denim after broadwise silk tuft, to send in the baking oven that temperature is 150 DEG C ~ 200 DEG C baking 10min ~ 20min to moisture content be 5% ~ 10%;;
F () is dyeed
The complete denim of baking is put in the dyeing installation of deployed dyestuff and dye;
(g) upper softening agent
By denim from taking out in dyeing installation and it being cleaned again, inserting the ratio being placed with in the cylinder of softening agent 15min ~ 30min, softening agent and water after having cleaned is 1:50 ~ 1:100;
H () is shaped
To soak the denim after softening agent operation completes and send into shaping baking oven sizing, setting temperature is 150 DEG C~200 DEG C, until moisture content is take out after 3% ~ 5%, cooling, cropping can pack warehouse-in.
2. the processing technology of a kind of mildew-resistant colour jacquard jean according to claim 1, it is characterised in that: the jean in step a is added fleece fibre blended spinning by cotton fiber and tencel fiber and forms.
3. the processing technology of a kind of mildew-resistant colour jacquard jean according to claim 1, it is characterized in that: the bamboo carbon fiber in step a accounts for the 22%-30% of the mass percent of denim, described Nipagin ester accounts for the 5%-8% of the mass percent of denim, and jean accounts for the 60% ~ 75% of the mass percent of denim.
4. the processing technology of a kind of mildew-resistant colour jacquard jean according to claim 1, it is characterised in that: the ratio of described cotton fiber, wool fiber and tencel fiber is 4:3:1.
5. the processing technology of a kind of mildew-resistant colour jacquard jean according to claim 1, it is characterised in that: the ratio of described hemp and described flax fiber is 1:1.5.
6. the processing technology of a kind of mildew-resistant colour jacquard jean according to claim 1, it is characterized in that: the described dyestuff in step f is reactive dye, orange X-GN taken from by dyestuff, brilliant red X-3B, gorgeous blue X-BR, gorgeous blue B-RV, dark red E-2BD, bright red E-GGF, gorgeous blue KN-R, emerald green blue B-BGFN, red B-3BF, blue B-2GLN, light yellow B-4GLN, orange DC-3R, yellow DC-RL, orange DC-3G, blue FN-RN, red FL-2BL, dark blue DC-GB, army indigo plant GG, dark blue GW-HA, black GW-HA, green GW-HA, purple GW-HA, blue GW-HN, red GW-HA, any one or multiple mixing in emerald green blue GW-HA.
7. the processing technology of a kind of mildew-resistant colour jacquard jean according to claim 1, it is characterised in that: the softening agent in step h is ester based quaternary ammonium salt softening agent, fatty acid ester type softening agent, right wax pattern softening agent or polyethylene softening agent.
8. the processing technology of a kind of colored soft denim according to claim 1, it is characterised in that: the fabric guide roll in step b is provided with groove.