CN105769907A - 强效杀菌络合物及其制备方法 - Google Patents
强效杀菌络合物及其制备方法 Download PDFInfo
- Publication number
- CN105769907A CN105769907A CN201610129355.XA CN201610129355A CN105769907A CN 105769907 A CN105769907 A CN 105769907A CN 201610129355 A CN201610129355 A CN 201610129355A CN 105769907 A CN105769907 A CN 105769907A
- Authority
- CN
- China
- Prior art keywords
- silver powder
- complex compound
- nano
- ozone
- strong bactericidal
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种强效杀菌络合物及其制备方法,该络合物包括纳米银粉和臭氧化油,纳米银粉和臭氧化油按照重量百分比的比例为99.8:0.2。制备方法为:按照重量百分比将纳米银粉和臭氧化油加入到搅拌机内进行搅拌;搅拌混合后静置5‑6小时,静置完成后形成药液;将该药液导入外接容器;封装该外接容器。本发明将上述两者结合,可以对金黄色葡萄球菌、链球菌、绿脓杆菌、大肠杆菌、真菌、霉菌、白色念珠菌等多种细菌具有很强烈的灭菌效果,对人体皮肤的刀伤、创伤有非常好的抑菌、杀菌、治愈作用。
Description
技术领域
本发明涉及络合物领域,尤其涉及一种强效杀菌络合物及其制备方法。
背景技术
创伤是指机械性致上因子所造成的损伤,创伤学是指外科的重要基础之一,皮肤致伤原因主要分为:刺伤、切割伤、挫伤、挤压伤、擦伤、撕裂伤、火器伤、冲击伤等;临床表现为红、肿、热、痛。皮肤组织修复通常有三个阶段:一,局部炎症反应阶段,持续3-5天,主要是血管和细胞反应阶段,免疫应答,血液凝固和纤维蛋白溶解;二,细胞增生分化和肉芽组织形成阶段,伤后6小时左右,伤口边缘可出现纤维细胞,约24-48小时血管内皮细胞增生,分泌组织基质共同构成肉芽组织;三,组织塑形阶段,新生组织不能达到原组织的结构和功能要求,需要进一步构造和重建。
目前市面上主要是采用抗生素消炎杀菌,抗生素以前被称为抗菌素,事实上它不仅能杀灭细菌而且对霉菌、支原体、衣原体、螺旋体、立克次氏体等其它致病微生物也有良好的抑制和杀灭作用,通常将抗菌素改称为抗生素。抗生素可以是某些微生物生长繁殖过程中产生的一种物质,用于治病的抗生素除由此直接提取外;还有完全用人工合成或部分人工合成的。通俗地讲,抗生素就是用于治疗各种非病毒感染的药物。但是在临床使用中已经显现了许多副作用。
另据1995~2007年疾病分类调查,中国感染性疾病占全部疾病总发病数的49%,其中细菌感染性占全部疾病的18%~21%,也就是说80%以上属于滥用抗生素,每年有8万人因此死亡。这些数字使中国成为世界上滥用抗生素问题最严重的国家。
发明内容
针对上述技术中存在的不足之处,本发明提供一种杀菌效果好、制备方法简单、成本低及可批量生产的强效杀菌络合物及其制备方法。
为实现上述目的,本发明提供一种强效杀菌络合物,一种强效杀菌络合物,包括纳米银粉和臭氧化油,纳米银粉和臭氧化油按照重量百分比的比例为99.8:0.2。
其中,所述臭氧化油为含臭氧是70-80%之间的臭氧化油;臭氧化油中臭氧的最佳含量为75%。
其中,所述纳米银粉的浓度为1.95-2.05PPM之间;纳米银粉的最佳浓度为25PPM。
其中,100g络合物由99.8g的臭氧化油和0.2g的纳米银粉。
为实现上述目的,本发明还提供了一种强效杀菌络合物的制备方法,包括以下步骤:
步骤1,按照重量百分比将纳米银粉和臭氧化油加入到搅拌机内进行搅拌7-8小时;
步骤2,搅拌混合后静置5-6小时,静置完成后形成药液;
步骤3,将该药液导入外接容器;
步骤4,封装该外接容器。
其中,所述步骤2中的静置温度为20-40度之间。
本发明的有益效果是:与现有技术相比,本发明提供的强效杀菌络合物及其制备方法,主要由纳米银粉和臭氧化油按一定的配比通过搅拌静置后形成该络合物,纳米银粉对大肠杆菌、金黄色葡萄球菌等数十种致病微生物具有强烈的抑制和杀灭作用;臭氧化油主要用于抑制局部溃疡、细菌、真菌和寄生虫感染;将上述两者结合,可以对金黄色葡萄球菌、链球菌、绿脓杆菌、大肠杆菌、真菌、霉菌、白色念珠菌等多种细菌具有很强烈的灭菌效果,对人体皮肤的刀伤、创伤有非常好的抑菌、杀菌、治愈作用。
附图说明
图1为本发明的强效杀菌络合物的制备方法的流程图。
具体实施方式
为了更清楚地表述本发明,下面结合附图对本发明作进一步地描述。
请参阅图1,本发明的强效杀菌络合物,本发明提供一种强效杀菌络合物,一种强效杀菌络合物,包括纳米银粉和臭氧化油,纳米银粉和臭氧化油按照重量百分比的比例为99.8:0.2。该络合物的制备方法如下:
步骤S1,按照重量百分比将纳米银粉和臭氧化油加入到搅拌机内进行搅拌;
步骤S2,搅拌混合后静置5-6小时,静置完成后形成药液;该步骤中步骤2中的静置温度为20-40度之间。当然,最佳的温度范围值是在25-30度之间。
步骤S3,将该药液导入外接容器;
步骤S4,封装该外接容器。
相较于现有技术的情况,本发明提供的强效杀菌络合物及其制备方法,主要由纳米银粉和臭氧化油按一定的配比通过搅拌静置后形成该络合物,纳米银粉对大肠杆菌、金黄色葡萄球菌等数十种致病微生物具有强烈的抑制和杀灭作用;臭氧化油主要用于抑制局部溃疡、细菌、真菌和寄生虫感染;将上述两者结合,可以对金黄色葡萄球菌、链球菌、绿脓杆菌、大肠杆菌、真菌、霉菌、白色念珠菌等多种细菌具有很强烈的灭菌效果,对人体皮肤的刀伤、创伤有非常好的抑菌、杀菌、治愈作用。
在本实施例中,臭氧化油为含臭氧是70-80%之间的臭氧化油;臭氧化油中臭氧的最佳含量为75%。臭氧化油即臭氧油、超氧油,是医用臭氧治疗用途的延伸。它作为一种天然的制备物,在很多国家被广泛应用于治疗局部溃疡、细菌、真菌和寄生虫感染。Sedhi等(2001)检测了来自古巴的三氧化太阳花油(Oleozon),结果发现,这种三氧化油对所有检测的微生物都有杀灭活性的作用。臭氧化油的治疗作用是:抗炎、抗变态反应、杀灭细菌、微生物、及真菌、免疫诱导、促进肉芽颗粒形成等。治疗范围是:各种皮肤粘膜疾病、疱疹;急性湿疹;脓皮病;神经性皮炎;银屑病;疖;真菌感染;阴道炎;外阴干燥症;附件炎、其他妇科炎症、前列腺病(使用特殊方法);外伤(包括不愈伤口);褥疮;营养不良性溃疡;肛裂;口腔炎;齿龈炎;结膜炎;耳鼻喉及其他炎症。
在本实施例中,纳米银粉的浓度为1.95-2.05PPM之间;纳米银粉的最佳浓度为2PPM。本案中将都具有杀菌作用的纳米银粉与臭氧化油配合,形成了强有力的杀菌络合物。
本案中最佳的实施例是:100g络合物由99.8g的臭氧化油和0.2g的纳米银粉。将0.2g的纳米银粉和99.8g的臭氧化油加入到搅拌机内进行搅拌;搅拌混合后在温度为30度的条件下静置5小时,静置完成后形成药液;将该药液导入外接容器;封装该外接容器,就形成了标准包装。
以上公开的仅为本发明的几个具体实施例,但是本发明并非局限于此,任何本领域的技术人员能思之的变化都应落入本发明的保护范围。
Claims (6)
1.一种强效杀菌络合物,其特征在于,包括纳米银粉和臭氧化油,纳米银粉和臭氧化油按照重量百分比的例为99.8:0.2。
2.根据权利要求1所述的强效杀菌络合物,其特征在于,所述臭氧化油为含臭氧是70-80%之间的臭氧化油;臭氧化油中臭氧的最佳含量为75%。
3.根据权利要求1所述的强效杀菌络合物,其特征在于,所述纳米银粉的浓度为1.95-2.05PPM之间;纳米银粉的最佳浓度为2PPM。
4.根据权利要求1所述的强效杀菌络合物,其特征在于,100g络合物由99.8g的臭氧化油和0.2g的纳米银粉。
5.一种强效杀菌络合物的制备方法,其特征在于,包括以下步骤:步骤1,按照重量百分比将纳米银粉和臭氧化油加入到搅拌机内进行搅拌7-8小时;步骤2,搅拌混合后静置5-6小时,静置完成后形成药液;步骤3,将该药液导入外接容器;步骤4,封装该外接容器。
6.根据权利要求1所述的强效杀菌络合物的制备方法,其特征在于,所述步骤2中的静置温度为20-40度之间。