CN105728615A - 一种3Cr2W8V热锻模具的锻造工艺 - Google Patents
一种3Cr2W8V热锻模具的锻造工艺 Download PDFInfo
- Publication number
- CN105728615A CN105728615A CN201410744849.XA CN201410744849A CN105728615A CN 105728615 A CN105728615 A CN 105728615A CN 201410744849 A CN201410744849 A CN 201410744849A CN 105728615 A CN105728615 A CN 105728615A
- Authority
- CN
- China
- Prior art keywords
- forging
- inspection
- conducted
- cleaning
- heat treatment
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种3Cr2W8V热锻模具的锻造工艺，包括如下步骤：1）、锻坯下料→锻孔→矫正→中间检验，检验锻件的尺寸和表面缺陷→锻件热处理，用以消除锻造应力，改善金属切削性能→清理，主要是去除表面氧化皮→矫正→检查，锻件要经过外观和硬度检查；2）、锻造加工过程包括：将材料切割成所需尺寸、加热、锻造、热处理、清理和检验；锻造温度：始锻温度1100～1180℃；终锻温度800～880℃之后空冷。本发明各参数搭配合理协调，能够有效地提高产品质量和生产效率。
Description
技术领域
本发明涉及一种3Cr2W8V热锻模具的锻造工艺。
背景技术
现有的3Cr2W8V热锻模具的锻造工艺存在工序安排不合理、工序繁多，工艺参数选择不合理，各工艺参数搭配不合理，且对操作者经验要求较高，使得生产成本偏高、产品质量偏低、成品率不高。
发明内容
有鉴于现有技术的上述缺陷，本发明所要解决的技术问题是提供一种工序合理、制造成本低的3Cr2W8V热锻模具的锻造工艺。
为实现上述目的，本发明提供了
一种3Cr2W8V热锻模具的锻造工艺，包括如下步骤：
1）、锻坯下料→锻孔→矫正→中间检验，检验锻件的尺寸和表面缺陷→锻件热处理，用以消除锻造应力，改善金属切削性能→清理，主要是去除表面氧化皮→矫正→检查，锻件要经过外观和硬度检查；
2）、锻造加工过程包括：将材料切割成所需尺寸、加热、锻造、热处理、清理和检验；
锻造温度：始锻温度1100～1180℃；
终锻温度800～880℃之后空冷。
本发明的有益效果是：本发明工序合理，制造成本低，各参数搭配合理协调，能够有效地提高产品质量和生产效率。
具体实施方式
下面结合实施例对本发明作进一步说明：
一种3Cr2W8V热锻模具的锻造工艺，包括如下步骤：
1）、锻坯下料→锻孔→矫正→中间检验，检验锻件的尺寸和表面缺陷→锻件热处理，用以消除锻造应力，改善金属切削性能→清理，主要是去除表面氧化皮→矫正→检查，锻件要经过外观和硬度检查；
2）、锻造加工过程包括：将材料切割成所需尺寸、加热、锻造、热处理、清理和检验；
锻造温度：始锻温度1100～1180℃；
终锻温度800～880℃之后空冷。
Claims (1)
1.一种3Cr2W8V热锻模具的锻造工艺，其特征是：包括如下步骤：
1）、锻坯下料→锻孔→矫正→中间检验，检验锻件的尺寸和表面缺陷→锻件热处理，用以消除锻造应力，改善金属切削性能→清理，主要是去除表面氧化皮→矫正→检查，锻件要经过外观和硬度检查；
2）、锻造加工过程包括：将材料切割成所需尺寸、加热、锻造、热处理、清理和检验；
锻造温度：始锻温度1100～1180℃；
终锻温度800～880℃之后空冷。