CN105713419A - Method for preparing high-purity natural dye with semen euryales shells and dyeing method implemented by aid of high-purity natural dye - Google Patents
Method for preparing high-purity natural dye with semen euryales shells and dyeing method implemented by aid of high-purity natural dye Download PDFInfo
- Publication number
- CN105713419A CN105713419A CN201610038407.2A CN201610038407A CN105713419A CN 105713419 A CN105713419 A CN 105713419A CN 201610038407 A CN201610038407 A CN 201610038407A CN 105713419 A CN105713419 A CN 105713419A
- Authority
- CN
- China
- Prior art keywords
- natural dye
- semen euryales
- shell
- purity
- textile
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides a method for preparing high-purity natural dye with semen euryales shells and a dyeing method implemented by the aid of the high-purity natural dye. The particular method includes washing and drying the semen euryales shells, grinding the semen euryales shells in a claw type grinder to obtain powder, filtering the powder and drying and storing the powder in a drying oven to obtain coarse powder of the semen euryales shells; arranging the coarse powder of the semen euryales shells in a supercritical carbon dioxide extraction kettle, venting the supercritical carbon dioxide extraction kettle, starting a main pump, regulating the pressure of the extraction kettle until the pressure reaches 20-40 MPa, extracting the coarse powder, collecting extract in a separation kettle to obtain supercritical carbon dioxide extract of the semen euryales shells, and respectively extracting the supercritical carbon dioxide extract by the aid of petroleum ether, ethyl acetate and water-saturated butanol to obtain extract liquid; concentrating the extract liquid to obtain the high-purity natural dye with the semen euryales shells. The particular dyeing method includes drying textiles in a drying oven; keeping the textiles in balance for 24 h; arranging the pretreated textiles in a steam chamber with the high-purity natural dye with the semen euryales shells and turning the pretreated textiles to dye the textiles; keeping the dyed textiles in balance in a dryer and cooling the dyed textiles; washing and drying the textiles to obtain textiles dyed by the natural dye with the semen euryales shells.
Description
Technical field:
The invention belongs to textile material technical field, be specifically related to a kind of high-purity natural dye of gordon euryale seed shell
Preparation method and colouring method.
Background technology:
Semen Euryales, also referred to as Gorgon fruit, thorn Rhizoma Nelumbinis, belong to nymphaeaceae plant, and annual aquatic and herbaceous is planted
Thing, has stimulating appetite, helps effect of air culture unit, be traditional Chinese crude drug and precious natural benefit
Product, dietotherapeutic.Being similar to Caput Gallus domesticus when Semen Euryales is in bud, root, stem, leaf, fruit all can be used as medicine, on the ground
Organ is in addition to blade back spinosity, and remainder is smooth stingless, has white fibrous root and unconspicuous stem.
The petiole of Semen Euryales, bennet can be as fresh vegetables during summer, and flower, leaf have ornamental value.Semen Euryales taste
Sweet, complex chemical composition, containing substantial amounts of protein, carbohydrate, riboflavin and other dimensions
Raw element composition, has the curative effect of supplementing the kidney to control the nocturnal, tonifying spleen and stopping diarrhea, eliminating dampness and arresting leucorrhea.
Owing to the thought of resource reclaim recycling is progressively rooted in the hearts of the people, to the seed coat of Semen Euryales, petiole, flower
The developmental research at the positions such as stalk, extracts its effective ingredient, other application of development Semen Euryales.Outside Semen Euryales
Shell and seed coat are the most all used as feedstuff, or discarded, not only waste the energy, and can pollute ring
Border, has had a small amount of research report by extracting natural dye in Semen Euryales shell and can be used for textile dye
Color.
The shell of Semen Euryales and seed coat can extract the natural dye of brown, and the seed coat of Semen Euryales contains
Single-character given name material, in shell, fatty acid and trace element also compare many, in the natural dye therefore extracted also
Possesses certain antibacterial oxidation resistance.Chinese patent CN 101775234B (publication date 2010.7.14)
The extracting method of disclosed natural dye of gordon euryale seed shell and the application in pure cotton dyeing, clean Semen Euryales shell
Clean pulverizing, through ultrasonic Treatment, ethanol extraction 2 times, decompression distillation and concentration filtrate obtains thick Semen Euryales
Hull natural dye, then after cation macroporous resin column separating-purifying, obtain brownish-yellow powder shape Semen Euryales shell
Natural dye extract, obtains knitting through the cotton textiles of natural dye of gordon euryale seed shell dyeing through direct staining technique
Thing.(natural dye of gordon euryale seed shell silk dyeing dynamics research, the pretty tinkling of pieces of jade etc. of recording, Changzhou is big for Chinese literature
Learn journal, in June, 2011, the 2nd phase of volume 23, the 24-28 page) disclosed in Semen Euryales shell natural
The dyestuff application to silk dyeing, by cleaned for Semen Euryales shell, dry, pulverizing, ethonal extraction,
Filter, be concentrated under reduced pressure to give powder natural dye, mulberry silk fiber is obtained after direct staining Gorgon euryale
The mulberry silk fiber of real hull natural dye dyeing.
From prior art, the preparation method of current natural dye of gordon euryale seed shell is similar to, and is used for attempting
In the dyeing of natural fiber, and because the natural dye of gordon euryale seed shell prepared of the method still contains
Plurality of impurities, the dyeability fluctuation of the natural fiber after dyeing is relatively big, more unstable, thus for
The preparation method of natural dye of gordon euryale seed shell remains a need for studying further, stablizes excellent in the hope of obtaining dyeability
Good textile.
Summary of the invention:
The technical problem to be solved in the present invention is to provide the preparation side of a kind of high-purity natural dye of gordon euryale seed shell
Method and colouring method thereof, the present invention selects Semen Euryales shell coarse powder as raw material, extracts through supercritical carbon dioxide
Take to extract with chemical reagent and be concentrated to give highly purified natural dye of gordon euryale seed shell, the most highly purified Semen Euryales
Hull natural dye atomization forms steam, is placed in one by the textile of pretreatment and dyes, obtains Gorgon euryale
The textile of real hull natural dye dyeing.Natural dye of gordon euryale seed shell purity prepared by the present invention is high, and is
The utilization rate improving dyestuff selects steam to dye textile, obtains the weaving that dye-uptake is good
Product, and textile also has certain health-care effect.
For solving above-mentioned technical problem, the technical scheme is that
A kind of preparation method of high-purity natural dye of gordon euryale seed shell, it is characterised in that: include following step
Rapid:
(1) by Semen Euryales shell clean dry, it is placed in disk mill and is ground into powder, filter, put
Kept dry in baking oven, obtains Semen Euryales shell coarse powder;
(2) Semen Euryales shell coarse powder prepared by step (1) is placed in supercritical carbon dioxide extraction still,
Emptying, starts main pump, the pressure of regulation extraction kettle to 20-40MPa, extraction, collects in separating still
Extract, obtains Semen Euryales shell supercritical carbon dioxide extraction thing;
(3) the Semen Euryales shell supercritical carbon dioxide extraction thing prepared by step (2) respectively with petroleum ether,
Ethyl acetate, water-saturated n-butanol extract, and extracting solution is concentrated to give the high-purity natural dye of Semen Euryales shell
Material.
Preferred as technique scheme, the particle diameter of the Semen Euryales shell coarse powder in described step (1) is
0.5-1μm。
Preferred as technique scheme, the extraction temperature in described step (2) is 50-60 DEG C,
Extraction time is 2-3h.
Preferred as technique scheme, the high-purity natural dye of gordon euryale seed shell in described step (3)
Purity higher than 95%.
The present invention also provides for the colouring method of a kind of high-purity natural dye of gordon euryale seed shell, it is characterised in that:
Comprise the following steps:
(1) textile is placed in baking oven be dried, take out be placed in exsiccator inner equilibrium 24h, obtain pre-
The textile processed;
(2) textile of pretreatment step (1) prepared is placed in high-purity natural dye of gordon euryale seed shell
Vaporium in, rotate pretreatment textile make it dye, then the textile of dyeing is placed in dry
Balance cooling in dry device, washing is dried, and obtains the textile of natural dye of gordon euryale seed shell dyeing.
Preferred as technique scheme, in described step (1), textile is natural fiber, again
Raw egg white matter fiber and the fiber of regenerated celulose fibre or fabric.
Preferred as technique scheme, in described step (1), the textile of pretreatment aqueous
Rate is 6-10%.
Preferred as technique scheme, in described step (2), high-purity natural dye of gordon euryale seed shell
Vaporium in the concentration of high-purity natural dye of gordon euryale seed shell be 35-55%.
Preferred as technique scheme, in described step (2), the time of dyeing is
30-90min。
Preferred as technique scheme, in described step (2), natural dye of gordon euryale seed shell dyeing
The dye-uptake of textile is 85-92%.
Compared with prior art, the method have the advantages that
(1) the critical carbon dioxide extraction skill that the high-purity natural dye of gordon euryale seed shell that prepared by the present invention is selected
Art is extracted concentration with chemical reagent and is combined, and obtains the natural dye of gordon euryale seed shell that purity is high, with traditional
Chemical reagent extracts and compares, and the foreign material in natural dye are few, and purity is high, and extraction efficiency is high, nothing
Pollute.
(2) colouring method of the high-purity natural dye of gordon euryale seed shell that prepared by the present invention selects steam-colour
Method, can avoid using natural dye reagent in a large number, improves the utilization rate of natural dye, and selects
The dye-uptake of the textile of the method dyeing is high, meets the requirement of dyeing.
(3) purity of the high-purity natural dye of gordon euryale seed shell that prepared by the present invention is high, stable performance, impurity
Few, the aberration gap of the textile therefore dyeed is little, stable performance between each batch, the utilization rate of dyestuff
Height, the textile of dyeing also has antioxidation, antibacterial, antineoplastic effect.
Detailed description of the invention:
The present invention is described in detail, in the schematic enforcement of this present invention below in conjunction with specific embodiment
Example and explanation are used for explaining the present invention, but not as a limitation of the invention.
Embodiment 1:
(1) by Semen Euryales shell clean dry, it is placed in disk mill and is ground into powder, filter, put
Kept dry in baking oven, obtaining particle diameter is 0.5 μm Semen Euryales shell coarse powder.
(2) Semen Euryales shell coarse powder prepared by step (1) is placed in supercritical carbon dioxide extraction still,
Emptying, starts main pump, and the pressure of regulation extraction kettle, to 20MPa, extracts 2h, collection point at 50 DEG C
Extract in still, obtains Semen Euryales shell supercritical carbon dioxide extraction thing.
(3) the Semen Euryales shell supercritical carbon dioxide extraction thing prepared by step (2) respectively with petroleum ether,
Ethyl acetate, water-saturated n-butanol extract, and extracting solution is concentrated to give the high-purity Gorgon euryale that purity is 95%
Real hull natural dye.
(4) natural fiber cotton fiber is placed in baking oven be dried, take out be placed in exsiccator inner equilibrium
24h, obtains the textile of the pretreatment that moisture content is 6%.
(5) textile of pretreatment step (4) prepared is placed in concentration is 35% high-purity Semen Euryales
In the vaporium of hull natural dye, rotate the textile dyeing 30min of pretreatment, then by dyeing
Textile is placed in exsiccator balance cooling, and washing is dried, and obtains spinning of natural dye of gordon euryale seed shell dyeing
Fabric.
Embodiment 2:
(1) by Semen Euryales shell clean dry, it is placed in disk mill and is ground into powder, filter, put
Kept dry in baking oven, obtaining particle diameter is 1 μm Semen Euryales shell coarse powder.
(2) Semen Euryales shell coarse powder prepared by step (1) is placed in supercritical carbon dioxide extraction still,
Emptying, starts main pump, and the pressure of regulation extraction kettle, to 40MPa, extracts 3h, collection point at 60 DEG C
Extract in still, obtains Semen Euryales shell supercritical carbon dioxide extraction thing.
(3) the Semen Euryales shell supercritical carbon dioxide extraction thing prepared by step (2) respectively with petroleum ether,
Ethyl acetate, water-saturated n-butanol extract, and extracting solution is concentrated to give the high-purity Gorgon euryale that purity is 97%
Real hull natural dye.
(4) fabric of soybean fiber is placed in baking oven be dried, take out be placed in exsiccator inner equilibrium
24h, obtains the textile of the pretreatment that moisture content is 8%.
(5) textile of pretreatment step (4) prepared is placed in concentration is 55% high-purity Semen Euryales
In the vaporium of hull natural dye, rotate the textile dyeing 90min of pretreatment, then by dyeing
Textile is placed in exsiccator balance cooling, and washing is dried, and obtains spinning of natural dye of gordon euryale seed shell dyeing
Fabric.
Embodiment 3:
(1) by Semen Euryales shell clean dry, it is placed in disk mill and is ground into powder, filter, put
Kept dry in baking oven, obtaining particle diameter is 0.7 μm Semen Euryales shell coarse powder.
(2) Semen Euryales shell coarse powder prepared by step (1) is placed in supercritical carbon dioxide extraction still,
Emptying, starts main pump, and the pressure of regulation extraction kettle, to 30MPa, extracts 2.5h at 55 DEG C, collects
Extract in separating still, obtains Semen Euryales shell supercritical carbon dioxide extraction thing.
(3) the Semen Euryales shell supercritical carbon dioxide extraction thing prepared by step (2) respectively with petroleum ether,
Ethyl acetate, water-saturated n-butanol extract, and extracting solution is concentrated to give the high-purity Gorgon euryale that purity is 96%
Real hull natural dye.
(4) regenerated celulose fibre is placed in baking oven be dried, take out be placed in exsiccator inner equilibrium
24h, obtains the textile of the pretreatment that moisture content is 7%.
(5) textile of pretreatment step (4) prepared is placed in concentration is 45% high-purity Semen Euryales
In the vaporium of hull natural dye, rotate the textile dyeing 60min of pretreatment, then by dyeing
Textile is placed in exsiccator balance cooling, and washing is dried, and obtains spinning of natural dye of gordon euryale seed shell dyeing
Fabric.
Embodiment 4:
(1) by Semen Euryales shell clean dry, it is placed in disk mill and is ground into powder, filter, put
Kept dry in baking oven, obtaining particle diameter is 0.8 μm Semen Euryales shell coarse powder.
(2) Semen Euryales shell coarse powder prepared by step (1) is placed in supercritical carbon dioxide extraction still,
Emptying, starts main pump, and the pressure of regulation extraction kettle, to 40MPa, extracts 2h, collection point at 60 DEG C
Extract in still, obtains Semen Euryales shell supercritical carbon dioxide extraction thing.
(3) the Semen Euryales shell supercritical carbon dioxide extraction thing prepared by step (2) respectively with petroleum ether,
Ethyl acetate, water-saturated n-butanol extract, and extracting solution is concentrated to give the high-purity Gorgon euryale that purity is 97%
Real hull natural dye.
(4) natural fiber silk fabric is placed in baking oven be dried, take out be placed in exsiccator inner equilibrium
24h, obtains the textile of the pretreatment that moisture content is 10%.
(5) textile of pretreatment step (4) prepared is placed in concentration is 50% high-purity Semen Euryales
In the vaporium of hull natural dye, rotate the textile dyeing 80min of pretreatment, then by dyeing
Textile is placed in exsiccator balance cooling, and washing is dried, and obtains spinning of natural dye of gordon euryale seed shell dyeing
Fabric.
Embodiment 5:
(1) by Semen Euryales shell clean dry, it is placed in disk mill and is ground into powder, filter, put
Kept dry in baking oven, obtaining particle diameter is 0.9 μm Semen Euryales shell coarse powder.
(2) Semen Euryales shell coarse powder prepared by step (1) is placed in supercritical carbon dioxide extraction still,
Emptying, starts main pump, and the pressure of regulation extraction kettle, to 25MPa, extracts 3h, collection point at 50 DEG C
Extract in still, obtains Semen Euryales shell supercritical carbon dioxide extraction thing.
(3) the Semen Euryales shell supercritical carbon dioxide extraction thing prepared by step (2) respectively with petroleum ether,
Ethyl acetate, water-saturated n-butanol extract, and extracting solution is concentrated to give the high-purity Gorgon euryale that purity is 96%
Real hull natural dye.
(4) azlon fabric is placed in baking oven be dried, take out be placed in exsiccator inner equilibrium
24h, obtains the textile of the pretreatment that moisture content is 9%.
(5) textile of pretreatment step (4) prepared is placed in concentration is 55% high-purity Semen Euryales
In the vaporium of hull natural dye, rotate the textile dyeing 50min of pretreatment, then by dyeing
Textile is placed in exsiccator balance cooling, and washing is dried, and obtains spinning of natural dye of gordon euryale seed shell dyeing
Fabric.
Embodiment 6:
(1) by Semen Euryales shell clean dry, it is placed in disk mill and is ground into powder, filter, put
Kept dry in baking oven, obtaining particle diameter is 0.5 μm Semen Euryales shell coarse powder.
(2) Semen Euryales shell coarse powder prepared by step (1) is placed in supercritical carbon dioxide extraction still,
Emptying, starts main pump, and the pressure of regulation extraction kettle, to 40MPa, extracts 2.5h at 60 DEG C, collects
Extract in separating still, obtains Semen Euryales shell supercritical carbon dioxide extraction thing.
(3) the Semen Euryales shell supercritical carbon dioxide extraction thing prepared by step (2) respectively with petroleum ether,
Ethyl acetate, water-saturated n-butanol extract, and extracting solution is concentrated to give the high-purity Gorgon euryale that purity is 98%
Real hull natural dye.
(4) regenerated celulose fibre is placed in baking oven be dried, take out be placed in exsiccator inner equilibrium
24h, obtains the textile of the pretreatment that moisture content is 6-10%.
(5) textile of pretreatment step (4) prepared is placed in concentration is 40% high-purity Semen Euryales
In the vaporium of hull natural dye, rotate the textile dyeing 70min of pretreatment, then by dyeing
Textile is placed in exsiccator balance cooling, and washing is dried, and obtains spinning of natural dye of gordon euryale seed shell dyeing
Fabric.
After testing, the textile of the natural dye of gordon euryale seed shell dyeing that prepared by embodiment 1-6 and prior art
The real silk fabric of Semen Euryales shell dyeing compare, its dye-uptake, K/S value, aberration, color fastness
Result is as follows:
As seen from the above table, the dye-uptake of the textile of the natural dye of gordon euryale seed shell dyeing that prepared by the present invention
Height, compared with traditional Semen Euryales shell dyestuff, the color of the fabric of upper dye is deep, and aberration is little, and antifriction
Wipe and the performance of water-fastness color fastness has promoted.
The principle of above-described embodiment only illustrative present invention and effect thereof, not for limiting this
Bright.Any person skilled in the art all can be under the spirit and the scope of the present invention, to above-mentioned
Embodiment is modified or changes.Therefore, art has usually intellectual such as not
Depart from all equivalences completed under disclosed spirit and technological thought modify or change, still
Should be contained by the claim of the present invention.
Claims (10)
1. the preparation method of a high-purity natural dye of gordon euryale seed shell, it is characterised in that include following step
Rapid:
(1) by Semen Euryales shell clean dry, it is placed in disk mill and is ground into powder, filter, put
Kept dry in baking oven, obtains Semen Euryales shell coarse powder;
(2) Semen Euryales shell coarse powder prepared by step (1) is placed in supercritical carbon dioxide extraction still, row
Sky, starts main pump, the pressure of regulation extraction kettle to 20-40MPa, extraction, collects in separating still and extract
Thing, obtains Semen Euryales shell supercritical carbon dioxide extraction thing;
(3) the Semen Euryales shell supercritical carbon dioxide extraction thing prepared by step (2) respectively with petroleum ether,
Ethyl acetate, water-saturated n-butanol extract, and extracting solution is concentrated to give the high-purity natural dye of Semen Euryales shell
Material.
The preparation method of a kind of high-purity natural dye of gordon euryale seed shell the most according to claim 1, its
It is characterised by: the particle diameter of the Semen Euryales shell coarse powder in described step (1) is 0.5-1 μm.
The preparation method of a kind of high-purity natural dye of gordon euryale seed shell the most according to claim 1, its
Being characterised by: the extraction temperature in described step (2) is 50-60 DEG C, extraction time is 2-3h.
The preparation method of a kind of high-purity natural dye of gordon euryale seed shell the most according to claim 1, its
It is characterised by: the purity of the high-purity natural dye of gordon euryale seed shell in described step (3) is higher than 95%.
5. the colouring method of a high-purity natural dye of gordon euryale seed shell, it is characterised in that include following step
Rapid:
(1) textile is placed in baking oven be dried, take out be placed in exsiccator inner equilibrium 24h, obtain pre-
The textile processed;
(2) textile of pretreatment step (1) prepared is placed in high-purity natural dye of gordon euryale seed shell
In vaporium, the textile rotating pretreatment makes it dye, and is then placed in dry by the textile of dyeing
Balance cooling in device, washing is dried, and obtains the textile of natural dye of gordon euryale seed shell dyeing.
The colouring method of a kind of high-purity natural dye of gordon euryale seed shell the most according to claim 5, its
Being characterised by: in described step (1), textile is natural fiber, azlon and regeneration
The fiber of cellulose fibre or fabric.
The colouring method of a kind of high-purity natural dye of gordon euryale seed shell the most according to claim 5, its
Being characterised by: in described step (1), the moisture content of the textile of pretreatment is 6-10%.
The colouring method of a kind of high-purity natural dye of gordon euryale seed shell the most according to claim 5, its
It is characterised by: in described step (2), high-purity Gorgon euryale in the vaporium of high-purity natural dye of gordon euryale seed shell
The concentration of real hull natural dye is 35-55%.
The colouring method of a kind of high-purity natural dye of gordon euryale seed shell the most according to claim 5, its
Being characterised by: in described step (2), the time of dyeing is 30-90min.
The colouring method of a kind of high-purity natural dye of gordon euryale seed shell the most according to claim 5,
It is characterized in that: in described step (2), the dye-uptake of the textile of natural dye of gordon euryale seed shell dyeing is
85-92%.