CN105712663A - 袋装可储式smc常温改性沥青混合料 - Google Patents

袋装可储式smc常温改性沥青混合料 Download PDF

Info

Publication number
CN105712663A
CN105712663A CN201610047559.9A CN201610047559A CN105712663A CN 105712663 A CN105712663 A CN 105712663A CN 201610047559 A CN201610047559 A CN 201610047559A CN 105712663 A CN105712663 A CN 105712663A
Authority
CN
China
Prior art keywords
smc
asphalt
normal temperature
modified asphalt
formula
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201610047559.9A
Other languages
English (en)
Inventor
王洪先
郭朝阳
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Xinjiang Fuxiang Traffic Engineering Materials Co Ltd
Original Assignee
Xinjiang Fuxiang Traffic Engineering Materials Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Xinjiang Fuxiang Traffic Engineering Materials Co Ltd filed Critical Xinjiang Fuxiang Traffic Engineering Materials Co Ltd
Priority to CN201610047559.9A priority Critical patent/CN105712663A/zh
Publication of CN105712663A publication Critical patent/CN105712663A/zh
Pending legal-status Critical Current

Abstract

本发明提供的袋装可储式SMC常温改性沥青混合料，属于建筑材料领域，主要包括主要包括石油沥青、SMC常温沥青改性剂、集料和填料，其特征在于：所述SMC常温沥青改性剂占石油沥青质量的10?20%，改性温度为60?100℃,改性时间为2?3h，改性沥青占混合料的3.5?4.5%，余量为集料和填料的混合物，拌合温度为60?100℃，从而提供一种低温拌合、可长期存放、制备工艺简单、冬季可施工、施工简便的袋装可储式SMC常温改性沥青混合料。

Description

袋装可储式SMC常温改性沥青混合料
技术领域：
本发明的袋装可储式SMC常温改性沥青混合料属于建筑材料领域，尤其涉及袋装可储式SMC常温改性沥青混合料。
背景技术：
随着交通运输科技的发展，“节能、低碳、环保”筑路材料不断涌现，特别是SMC溶剂型常温改性剂的出现，弥补了以往水介质冷补材料路用性能不良、不适宜全幅摊铺及使用的技术缺陷，该类材料以其显著的技术优势受到越来越多的关注与研究，与传统的热拌沥青混合料和温拌沥青混合料而言，其消耗的能源、释放的有害气体更少，且能在低温和负温条件下施工，解决了沥青路面只能在高温季节施工的技术难题，实现了沥青路面在特殊环境（主要是低温）特殊条件（路面周边无热拌站）下的修筑及养护；
尤其以SMC常温沥青改性剂，是从废旧塑料、废旧橡胶中生产出来的甲基苯乙烯类嵌段共聚物（Styreneic Methyl Copolymers, SMC），可熔融或分散在沥青中以改善或提高沥青的路用性能。主要提高沥青混合料在常温条件下（0～40℃）的施工和易性，同时提高沥青及沥青混合料的其他路用性能，如低温抗裂性能、抗水损害性能及抗疲劳开裂性能等；
但在路面养护过程中，一些偏远、冬季或较小工程量的施工或路面养护，动用大型工程车辆或准备专门的拌合场修复，耗费人力物力的同时，养护施工耗时较长。
发明内容：
本发明的目的在于提供一种低温拌合、可长期存放、制备工艺简单、冬季可施工、施工简便的袋装可储式SMC常温改性沥青混合料。
本发明的目的是这样实现的，袋装可储式SMC常温改性沥青混合料，主要包括石油沥青、SMC常温沥青改性剂、集料和填料，其特征在于：所述SMC常温沥青改性剂占石油沥青质量的10-20%，改性温度为60-100℃，改性时间为：2-3h；改性沥青占混合料的3.5-4.5%，余量为集料和填料的混合物，拌合温度为60-100℃；
优选SMC常温沥青改性剂占石油沥青质量的15-18%，改性温度为80℃；
所述混合料拌合后经真空包装储存；存储时间为1-3个月；
进一步的所述石油沥青为70#、90#或110#；
所述集料为级配碎石及机制砂；
集料中大于4.75mm的颗粒含量大于65%；
所述填料为矿粉；
其中SMC常温改性剂在5℃~60℃范围内均呈液态，加热蒸馏后亦无性状变化，其主要技术要求参照下表：
由于实行上述技术，利用SMC常温沥青改性剂中含有少量的树脂类固化剂，掺加到沥青混合料中后，会缓慢发生交联固化，只有在荷载作用、阳光照射和空气流动条件下，密度才会逐渐增大，空隙率逐渐减小，形成成型的沥青混合料，因此将拌合好的沥青混合料经真空包装储存，延长其保鲜时间，在较偏远、冬季或较小工程量的路面养护中进行利用，工艺简单，省时省力。
具体实施方式
以下对本发明的优选实施例进行说明，应当理解，此处所描述的优选实施例仅用于说明和解释本发明，并不用于限定本发明。
实施例1
袋装可储式SMC常温改性沥青混合料，主要包括110#石油沥青、SMC常温沥青改性剂、级配碎石、机制砂和矿粉，所述SMC常温沥青改性剂占石油沥青质量的18%，改性温度为60℃，改性时间为3h；改性沥青占混合料的4.5%，余量为级配碎石、机制砂和矿粉的混合物，在80℃下拌合，拌合后经真空包装储存；存储时间为1-3个月。
实施例2
袋装可储式SMC常温改性沥青混合料，主要包括石油沥青、SMC常温沥青改性剂、集料和填料，其特征在于：所述SMC常温沥青改性剂占石油沥青质量的15%，改性温度为60℃，改性时间为2h；改性沥青占混合料的4.5%，余量为集料和填料的混合物，拌合温度为80℃；所述混合料拌合后经真空包装储存；存储时间为1-3个月；所述石油沥青为90#；所述集料为级配碎石及机制砂；集料中大于4.75mm的颗粒含量大于65%；所述填料为矿粉；该产品由乌鲁木齐市政养护处在冬季进行路面修补试用，效果良好。
实施例3
其他与实施例1相同，所述石油沥青为70#，SMC常温沥青改性剂占石油沥青质量的20%，改性沥青占混合料的3.5%，拌合温度为100℃。
实施例4
其他与实施例2相同，所述SMC常温沥青改性剂占石油沥青质量的10%，改性温度为100℃，拌合温度为60摄氏度。
由于实行上述技术，利用SMC常温沥青改性剂中含有少量的树脂类固化剂，掺加到沥青混合料中后，会缓慢发生交联固化，只有在荷载作用、阳光照射和空气流动条件下，密度才会逐渐增大，空隙率逐渐减小，形成成型的沥青混合料，因此将拌合好的沥青混合料经真空包装储存，延长其保鲜时间，在较偏远、冬季或较小工程量的路面养护中进行利用，工艺简单，省时省力。
以上所述仅为本发明的优选实施例而已，并不用于限制本发明，尽管参照前述实施例对本发明进行了详细的说明，对于本领域的技术人员来说，其依然可以对前述各实施例所记载的技术方案进行修改，或者对其中部分技术特征进行等同替换。凡在本发明的精神和原则之内，所作的任何修改、等同替换、改进等，均应包含在本发明的保护范围之内。

Claims (8)

1.袋装可储式SMC常温改性沥青混合料，主要包括石油沥青、SMC常温沥青改性剂、集料和填料，其特征在于：所述SMC常温沥青改性剂占石油沥青质量的10-20%，改性温度为60-100℃，改性时间2-3h，改性沥青占混合料的3.5-4.5%，余量为集料和填料的混合物，拌合温度为60-100℃。
2.根据权利要求1所述的袋装可储式SMC常温改性沥青混合料，其特征在于：所述SMC常温沥青改性剂占石油沥青质量的15-18%，混合料拌合温度为80℃。
3.根据权利要求1或2所述的袋装可储式SMC常温改性沥青混合料，其特征在于：所述混合料拌合后经密封包装储存。
4.根据权利要求3所述的袋装可储式SMC常温改性沥青混合料，其特征在于：所述混合料存贮时间为1-3个月。
5.根据权利要求4的袋装可储式SMC常温改性沥青混合料，其特征在于：所述石油沥青为70#、90#或110#。
6.根据权利要求5述的袋装可储式SMC常温改性沥青混合料，其特征在于：所述集料为级配碎石及机制砂。
7.根据权利要求6的袋装可储式SMC常温改性沥青混合料，其特征在于：集料中大于4.75mm的颗粒含量大于65%。
8.根据权利要求7袋装可储式SMC常温改性沥青混合料，其特征在于：所述所述填料为矿粉。
CN201610047559.9A 2016-01-25 2016-01-25 袋装可储式smc常温改性沥青混合料 Pending CN105712663A (zh)