CN105696372A - Dyeing and finishing technology of polyester fiber semi-memory fabric - Google Patents
Dyeing and finishing technology of polyester fiber semi-memory fabric Download PDFInfo
- Publication number
- CN105696372A CN105696372A CN201410684487.XA CN201410684487A CN105696372A CN 105696372 A CN105696372 A CN 105696372A CN 201410684487 A CN201410684487 A CN 201410684487A CN 105696372 A CN105696372 A CN 105696372A
- Authority
- CN
- China
- Prior art keywords
- fabric
- dyeing
- parts
- polyester fiber
- finishing technology
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a dyeing and finishing technology of a polyester fiber semi-memory fabric. The technology comprises the steps of desizing preshrinking, refining, dyeing, dehydration scotching, and fixing. The polyester fiber semi-memory fabric produced through the dyeing and finishing technology has the advantages of uniform dyeing, high accuracy, excellent color fastness, fluffiness, comfortable handle and strong drapability, and can be widely applied to fields of clothes, home textiles and carpets.
Description
Technical field
The present invention relates to textile dyeing, be specifically related to the dyeing and finishing technology of a kind of polyester fiber half memory face fabric。
Background technology
PTT belongs to polyester fiber, is the product of the same clan of conventional polyester (PET), and formal name used at school is PTT. and it is propylene glycol rather than ethylene glycol with the PET soft section of part being different in that in this fiber polymer。Due to the difference of soft section of composition in polymer。The performance making ptt fiber has very big difference with conventional PET。The C-C chain of soft section of part of PTT is longer, and this makes fiber have stronger shape memory function。Compared with PET, the Tg of ptt fiber is relatively low, easily paints, soft, and anti-wrinkle shrink-proof, drapability, pollution resistance are strong, are widely used to the fields such as clothing, home textile, carpet, one of new polyester material becoming great development prospect at present。PTT/PET half memory face fabric comfortable feel, has good crease recovery ability, and drapability is strong, and its style, feel and every color fastness are superior to chinlon and the fabric of terylene intertexture so that it is become the fabric that many high-grade clothings are first-selected。Owing to fabric existing two different kinds of fiber, so compared with the fabric of single component, needing more fully to consider at dyeing and finishing technology。
Summary of the invention
It is an object of the invention to overcome the defect existed in prior art, it is provided that the dyeing and finishing technology of a kind of polyester fiber half memory face fabric accurate, color fastness is strong that dyes。
For realizing above-mentioned technique effect, the technical scheme is that the dyeing and finishing technology of a kind of polyester fiber half memory face fabric, it is characterised in that comprise the following steps:
S1: desizing preshrunk, being placed in by fabric rolls in alkali liquor, then wash through hot water, warm water and cold water successively, described in roll alkali liquor consist of refining agent 4～8 parts, degreaser 2～4 parts, penetrating agent 1～2 part, chelated dispersants 1～2 part, 30% liquid caustic soda 40～70 parts, 900 parts of water；
S2: concise, is placed in the concise liquid of High Temperature High Pressure overflow dyeing machine by gained fabric in S1, refining liquid consist of soda 10～20 parts, degreaser 2～4 parts, softening agent 2～4 parts, refining temperature is 95 DEG C, and the time is 30min；
S3: dyeing, adopts multiplex disperse dyes that fabric is dyeed；
S4: dehydration open-width, removes the moisture on fabric with centrifugal dehydrator, by manual open-width, makes that fabric is smooth to be deposited；
S5: sizing, adds softening agent in fabric, is placed in by fabric on needle plate forming machine and shapes, and setting temperature is 120～130 DEG C。
Wherein, speed of shaping in described S5 is 25～35m/min。
Wherein, adding waterproofing agent in described S5 during sizing in fabric, described waterproofing agent is low temperature waterproofing agent。
Wherein, in described S3, dyeing temperature is 115～125 DEG C。
Advantages of the present invention and having the beneficial effects that:
High through polyester fiber half memory face fabric even dyeing and the accuracy of dyeing and finishing technology of the present invention production, color fastness is excellent, and the fluffy comfortable feel of fabric, pendency sense by force, can extensive use and clothing, home textile, carpet applications。
Detailed description of the invention
Below in conjunction with embodiment, the specific embodiment of the present invention is further described。Following example are only for clearly illustrating technical scheme, and can not limit the scope of the invention with this。
Embodiment 1
The dyeing and finishing technology of polyester fiber half memory face fabric of embodiment 1, comprises the following steps:
S1: desizing preshrunk, is placed in fabric and rolls in alkali liquor, then wash through hot water, warm water and cold water successively, described in roll alkali liquor consist of refining agent 4 parts, degreaser 2 parts, penetrating agent 1 part, chelated dispersants 1 part, 30% liquid caustic soda 40 parts, 900 parts of water；
S2: concise, is placed in the concise liquid of High Temperature High Pressure overflow dyeing machine by gained fabric in S1, refining liquid consist of soda 10 parts, degreaser 2 parts, softening agent 2 parts, refining temperature is 95 DEG C, and the time is 30min；
S3: dyeing, adopts multiplex disperse dyes that fabric is dyeed；
S4: dehydration open-width, removes the moisture on fabric with centrifugal dehydrator, by manual open-width, makes that fabric is smooth to be deposited；
S5: sizing, adds softening agent in fabric, is placed in by fabric on needle plate forming machine and shapes, and setting temperature is 120 DEG C。
Wherein, speed of shaping in S5 is 25m/min。
Wherein, adding waterproofing agent in S5 during sizing in fabric, described waterproofing agent is low temperature waterproofing agent。
Wherein, in S3, dyeing temperature is 115 DEG C。
Embodiment 2
The dyeing and finishing technology of polyester fiber half memory face fabric of embodiment 2, comprises the following steps:
S1: desizing preshrunk, is placed in fabric and rolls in alkali liquor, then wash through hot water, warm water and cold water successively, described in roll alkali liquor consist of refining agent 8 parts, degreaser 4 parts, penetrating agent 2 parts, chelated dispersants 2 parts, 30% liquid caustic soda 70 parts, 900 parts of water；
S2: concise, is placed in the concise liquid of High Temperature High Pressure overflow dyeing machine by gained fabric in S1, refining liquid consist of soda 20 parts, degreaser 4 parts, softening agent 4 parts, refining temperature is 95 DEG C, and the time is 30min；
S3: dyeing, adopts multiplex disperse dyes that fabric is dyeed；
S4: dehydration open-width, removes the moisture on fabric with centrifugal dehydrator, by manual open-width, makes that fabric is smooth to be deposited；
S5: sizing, adds softening agent in fabric, is placed in by fabric on needle plate forming machine and shapes, and setting temperature is 120～130 DEG C。
Wherein, speed of shaping in S5 is 35m/min。
Wherein, adding waterproofing agent in S5 during sizing in fabric, described waterproofing agent is low temperature waterproofing agent。
Wherein, in S3, dyeing temperature is 125 DEG C。
Embodiment 3
The dyeing and finishing technology of polyester fiber half memory face fabric of embodiment 3, comprises the following steps:
S1: desizing preshrunk, is placed in fabric and rolls in alkali liquor, then wash through hot water, warm water and cold water successively, described in roll alkali liquor consist of refining agent 6 parts, degreaser 3 parts, penetrating agent 1.5 parts, chelated dispersants 1.5 parts, 30% liquid caustic soda 55 parts, 900 parts of water；
S2: concise, is placed in the concise liquid of High Temperature High Pressure overflow dyeing machine by gained fabric in S1, refining liquid consist of soda 15 parts, degreaser 3 parts, softening agent 3 parts, refining temperature is 95 DEG C, and the time is 30min；
S3: dyeing, adopts multiplex disperse dyes that fabric is dyeed；
S4: dehydration open-width, removes the moisture on fabric with centrifugal dehydrator, by manual open-width, makes that fabric is smooth to be deposited；
S5: sizing, adds softening agent in fabric, is placed in by fabric on needle plate forming machine and shapes, and setting temperature is 125 DEG C。
Wherein, speed of shaping in S5 is 30m/min。
Wherein, adding waterproofing agent in S5 during sizing in fabric, described waterproofing agent is low temperature waterproofing agent。
Wherein, in S3, dyeing temperature is 120 DEG C。
The above is only the preferred embodiment of the present invention; it should be pointed out that, for those skilled in the art, under the premise without departing from the technology of the present invention principle; can also making some improvements and modifications, these improvements and modifications also should be regarded as protection scope of the present invention。
Claims (4)
1. the dyeing and finishing technology of polyester fiber half memory face fabric, it is characterised in that comprise the following steps:
S1: desizing preshrunk, being placed in by fabric rolls in alkali liquor, then wash through hot water, warm water and cold water successively, described in roll alkali liquor consist of refining agent 4～8 parts, degreaser 2～4 parts, penetrating agent 1～2 part, chelated dispersants 1～2 part, 30% liquid caustic soda 40～70 parts, 900 parts of water；
S2: concise, is placed in the concise liquid of High Temperature High Pressure overflow dyeing machine by gained fabric in S1, refining liquid consist of soda 10～20 parts, degreaser 2～4 parts, softening agent 2～4 parts, refining temperature is 95 DEG C, and the time is 30min；
S3: dyeing, adopts multiplex disperse dyes that fabric is dyeed；
S4: dehydration open-width, removes the moisture on fabric with centrifugal dehydrator, by manual open-width, makes that fabric is smooth to be deposited；
S5: sizing, adds softening agent in fabric, is placed in by fabric on needle plate forming machine and shapes, and setting temperature is 120～130 DEG C。
2. the dyeing and finishing technology of polyester fiber half memory face fabric according to claim 1, it is characterised in that speed of shaping in described S5 is 25～35m/min。
3. the dyeing and finishing technology of polyester fiber half memory face fabric according to claim 2, it is characterised in that adding waterproofing agent in described S5 during sizing in fabric, described waterproofing agent is low temperature waterproofing agent。
4. the dyeing and finishing technology of polyester fiber half memory face fabric according to claim 3, it is characterised in that in described S3, dyeing temperature is 115～125 DEG C。