CN105694591A - Digital printing ink and preparation method thereof - Google Patents
Digital printing ink and preparation method thereof Download PDFInfo
- Publication number
- CN105694591A CN105694591A CN201610266147.4A CN201610266147A CN105694591A CN 105694591 A CN105694591 A CN 105694591A CN 201610266147 A CN201610266147 A CN 201610266147A CN 105694591 A CN105694591 A CN 105694591A
- Authority
- CN
- China
- Prior art keywords
- digital ink
- distilled water
- formula
- preparation
- added
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to the technical field of printing raw materials and particularly discloses digital printing ink and a preparation method thereof.The digital printing ink is prepared from, by mass, 9.0-25.0% of a wetting agent, 3.0-10.0% of a penetrating agent, 0.25-0.5% of a surface active agent, 10.0-60.0% of color paste, 0.2% of preservative and the balance distilled water.The preparation method includes the steps that the penetrating agent, the wetting agent and the surface active agent in the formula are sequentially added into a reaction kettle slowly, stirring is started and conducted at the rotation speed of 70 rpm, the distilled water accounting for 50% of the total content in the formula is slowly added, then the color paste is added slowly, and stirring is conducted at a low speed; the remaining distilled water in the formula is weighed, added into the reaction kettle slowly and stirred at a low speed for 30 minutes, and the preservative is added; a pH blending agent is utilized to adjust the pH value of a product to be 7.5-8.5, the product surface tension is controlled to be 35-42 mN/m, and viscosity at the temperature of 25 DEG C is 3-5 cps; after the steps are completed, the mixture stands still and is filtered and output.The digital printing ink and the preparation method thereof are low in preparation cost and better in printing effect, energy is saved, and the environment is protected.
Description
Technical field
The present invention relates to printed material technical field, be specifically related to a kind of digital ink and preparation method thereof。
Background technology
Digital ink-jet printed is that pattern is passed through scanner, layout is retouched original text system editing and processing by computer color separation in printing, controlled minute-pressure electric-type ink nozzle by computer again and special dye liquor (being referred to as digital ink-jet printed ink) is directly injected on textile, after color mixture, be reduced into original scan pattern。As the digital ink of one of digital ink-jet printed main consumptive material, it also it is the key factor determining ink-jet printed technology success or not。In prior art, digital ink raw materials particle diameter is big, and it is poor to permeate, and attachment degree is low;Spray printing fastness is low, not water-fastness, not sun-proof, easily causes color flower, mottle during spray printing;Raw material particle size is easy to greatly blocking digital spray head, and stamp is not smooth, it is necessary to often change digital spray head, unfavorable protection digital machine;And it is generally required to high-temperature steam presses after stamp, time consumption and energy consumption。
Summary of the invention
In view of this, it is necessary to for above-mentioned problem, it is provided that a kind of digital ink and preparation method thereof。
For achieving the above object, the present invention takes following technical scheme:
The digital ink of the present invention, its mass percent consists of:
Further, described wetting agent includes the alcohols such as glycerol, hexanediol, pentanediol;Described penetrating agent is Polyethylene Glycol;Described surfactant is fatty alcohol ethers or triglyceride。A kind of preparation method of digital ink, including:
Step 1, the penetrating agent by formula, wetting agent, surfactant are slowly added into reactor successively, open speed of agitator 70rpm, are slowly added in formula the 50% of distilled water total content, and adding distilled water duration is 10 minutes;Being slowly added into mill base again, the persistent period adding mill base is 15 minutes;Carry out low rate mixing;
Step 2, weigh remaining distilled water in formula and be slowly added in reactor low rate mixing 30 minutes, add preservative;
Step 3, with pH blender adjust product pH value be 7.5-8.5, control product surface tension force at 35-42mN/m, when 25 DEG C, viscosity is 3-5cps;
Step 4, complete after stand, filter discharging。
The invention have the benefit that
1, the present invention selection by raw material, prepares the digital ink of wide, the effective high osmosis of the suitability and high fastness, and the more traditional ink of the present invention reduces the cost of 2-5%。
2, the raw material feature of environmental protection of the present invention is higher, conductivity is less, penetration is better, and final products adhesive force is big, and the fastness of stamp, water-fastness, sun-proof dynamics, resistance to dry, fastness to wet rubbing etc. are all improved。
3, particle diameter less (0.2-0.8um), stamp is more smooth, will not block digital spray head, better protects digital machine。Stamp spray-painting is evenly painted, and decreases aberration, avoids mottle。Stamp is once completed by digital spray printing, it is not necessary to steam ironing;Technique is simple to operation;Product quality is substantially improved。
4, product of the present invention is without formaldehyde, without APEO, without organic solvent, without heavy metal ion;Without allergy, teratogenesis, mutagenesis, the ill effect such as carcinogenic, safe to the human body, meet European Union's OeKo-TEXStandard100, REACH standard-required。Process of producing product does not have the three wastes produce, the problem producing a large amount of contaminated wastewater environment when solving traditional dyeing;Working place saves more than 60% than traditional dyeing。
Detailed description of the invention
For making the object, technical solutions and advantages of the present invention clearly, below in conjunction with the embodiment of the present invention, make to describe clearly and completely further to technical scheme。It should be noted that described embodiment a part of embodiment that is only the present invention, rather than whole embodiment。Based on the embodiment in the present invention, the every other embodiment that those of ordinary skill in the art obtain under not making creative work premise, broadly fall into the scope of protection of the invention。
Embodiment 1
The digital ink of the present invention, its mass percent consists of:
Further, described wetting agent includes the alcohols such as glycerol, hexanediol, pentanediol;Described penetrating agent is Polyethylene Glycol;Described surfactant is fatty alcohol ethers or triglyceride。
Embodiment 2
The digital ink of the present invention, its mass percent consists of:
Further, described wetting agent includes the alcohols such as glycerol, hexanediol, pentanediol;Described penetrating agent is Polyethylene Glycol;Described surfactant is fatty alcohol ethers or triglyceride。
Embodiment 3
The digital ink of the present invention, its mass percent consists of:
Further, described wetting agent includes the alcohols such as glycerol, hexanediol, pentanediol;Described penetrating agent is Polyethylene Glycol;Described surfactant is fatty alcohol ethers or triglyceride。
Embodiment 4
The digital ink of the present invention, its mass percent consists of:
Further, described wetting agent includes the alcohols such as glycerol, hexanediol, pentanediol;Described penetrating agent is Polyethylene Glycol;Described surfactant is fatty alcohol ethers or triglyceride。
Embodiment 5
A kind of preparation method of digital ink, including:
Step 1, the penetrating agent by formula, wetting agent, surfactant are slowly added into reactor successively, open speed of agitator 70rpm, are slowly added in formula the 50% of distilled water total content, and adding distilled water duration is 10 minutes;Being slowly added into mill base again, the persistent period adding mill base is 15 minutes;Carry out low rate mixing;
Step 2, weigh remaining distilled water in formula and be slowly added in reactor low rate mixing 30 minutes, add preservative;
Step 3, with pH blender adjust product pH value be 7.5-8.5, control product surface tension force at 35-42mN/m, when 25 DEG C, viscosity is 3-5cps;
Step 4, complete after stand, filter discharging。
The digital ink of performance of the present invention and prior art compares, as shown in table 1:
The digital ink performance index test of table 1
The key technical indexes | Existing product | Product of the present invention |
PH value | 5.6-8.6 | 7.0-8.0 |
Particle diameter (um) | > 1.0 | 0.2-0.8 |
Electrical conductivity | > 750s/cm | < 40m/s |
Surface tension (mN/m) | > 40 | 30-40 |
Viscosity (CPS) | 1.5-2.0 | 5.0 |
Resistance to dry fastness | < 4 grades | > 4 grades |
Wet rubbing fastness | < 3 grades | > 3.5 grades |
Printing quality | Difficult quality controls, and feel is uneven | Uniformly, feel change is little in printing product colouring |
The detection method used includes:
PH value: measure by GB/T6368-93;
Outward appearance: range estimation;
Particle diameter: nanometer particle size analysis-e/or determining;
Conductivity: electric conductivity measuring instrument measures;
Surface tension: tensammetric determination;
Viscosity: adopt U.S.'s LVF viscometer determining。
As shown in Table 1, the ink for inkjet particle diameter that Current Domestic produces is big, reaches 1mm-1um, and it is poor to permeate, and attachment degree is low;Spray printing fastness is low, not water-fastness, not sun-proof, easily causes color flower, mottle during spray printing;Raw material particle size is easy to greatly blocking digital spray head, and stamp is not smooth, it is necessary to often change digital spray head, unfavorable protection digital machine。
This product adopts that environmental protection, particle diameter less (0.2-0.8um), conductivity be lower, the better raw material production of penetration, final products adhesive force increases, and the fastness of stamp, water-wash resistance, light resistance, dry tolerance and fastness to wet rubbing are all improved significantly;Particle diameter is less, and stamp is more smooth, will not block digital spray head, better protects digital machine;Stamp spray-painting is evenly painted, and decreases aberration, avoids mottle。Stamp is once completed by digital spray printing, it is not necessary to steam ironing;The simply advanced easily operation of technique;Product quality is substantially improved。Production process of the present invention produces entirely without the three wastes, produces a large amount of contaminated wastewater environmental problem when solving traditional dyeing;Environmental protection is had very big positive effect;Working place saves 60% than traditional dyeing。
Embodiment described above only have expressed the several embodiments of the present invention, and it describes comparatively concrete and detailed, but therefore can not be interpreted as the restriction to the scope of the claims of the present invention。It should be pointed out that, for the person of ordinary skill of the art, without departing from the inventive concept of the premise, it is also possible to making some deformation and improvement, these broadly fall into protection scope of the present invention。Therefore, the protection domain of patent of the present invention should be as the criterion with claims。
Claims (6)
1. a digital ink, it is characterised in that mass percent consists of:
2. digital ink according to claim 1, it is characterised in that mass percent consists of:
3. digital ink according to claim 1, it is characterised in that mass percent consists of:
4. digital ink according to claim 1, it is characterised in that mass percent consists of:
5. the digital ink according to claim 1-4 any one, it is characterised in that described wetting agent includes glycerol, hexanediol, pentanediol class;Described penetrating agent is Polyethylene Glycol;Described surfactant is fatty alcohol ethers or triglyceride。
6. the preparation method of the digital ink described in a claim 1, it is characterised in that including:
Step 1, the penetrating agent by formula, wetting agent, surfactant are slowly added into reactor successively, open speed of agitator 70rpm, are slowly added in formula the 50% of distilled water total content, and adding distilled water duration is 10 minutes;Being slowly added into mill base again, the persistent period adding mill base is 15 minutes;Carry out low rate mixing;
Step 2, weigh remaining distilled water in formula and be slowly added in reactor low rate mixing 30 minutes, add preservative;
Step 3, with pH blender adjust product pH value be 7.5-8.5, control product surface tension force at 35-42mN/m, when 25 DEG C, viscosity is 3-5cps;
Step 4, complete after stand, filter discharging。