CN105648781A - Adhesive interlining production method and adhesive interlining - Google Patents
Adhesive interlining production method and adhesive interlining Download PDFInfo
- Publication number
- CN105648781A CN105648781A CN201511008296.2A CN201511008296A CN105648781A CN 105648781 A CN105648781 A CN 105648781A CN 201511008296 A CN201511008296 A CN 201511008296A CN 105648781 A CN105648781 A CN 105648781A
- Authority
- CN
- China
- Prior art keywords
- base fabric
- preparation
- adhesive lining
- pur
- resin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses an adhesive interlining production method. The method comprises the following steps: 1, producing a base cloth; 2, dyeing the base cloth; 3, carrying out high temperature fixing rolling; and 4, coating a hot melt adhesive. The adhesive interlining production method has the advantages of simplicity, low production cost, great shortening of the product delivery time, and improvement of the comprehensive competitiveness of enterprises. The invention also discloses an adhesive interlining produced through the production method. The adhesive interlining has high stiffness, makes clothes be stiff and maintain shape, makes collars, sleeves and fronts using the adhesive interlining be more stiff, massy and plump than general lining clothes, and increases the wearing beauty of the clothes.
Description
Technical field
The present invention relates to textile technology field, be specially preparation method and the adhesive lining of a kind of adhesive lining.
Background technology
Thermal smelting adesive lining is to be covered with thermoplastic high molecular compound in base fabric, has bonding force strong, by the lining cloth that the effect of uniform temperature, time and pressure directly can bond with fabric. Thermal smelting adesive lining can be called for short adhesive lining, because its use is in extensive range, is sometimes also directly called lining cloth. Thermal smelting adesive lining is the one in garment accessories family, the product with strongest influence power, technological progress being as the differentiation of Garment Technology and occur, with other kinds clothing such as linen-cotton lining, hair interlining, hair-cloth, resin interlinings with contrasting relatively, there is prominent functional characteristics, and the development of self kind also gets more and more. But existing adhesive lining causes the on the high side of adhesive lining due to complex manufacturing.
Summary of the invention
The present invention proposes to solve above-mentioned technological deficiency, it is proposed that a kind of production cost is low, the preparation method of the simple a kind of adhesive lining of technological process and adhesive lining.
The technical scheme is that and be achieved in that: the preparation method of a kind of adhesive lining, comprise the following steps:
1) preparing base fabric, described base fabric polyester low stretch wire material is made;
2) base fabric is after Song Buji unclamps, and is input to high temperature overflow dye vat through defeated cloth device and carries out high temperature overflow dyeing, and base fabric dyeing condition is that dye liquor temperature is warming up to 120-130 DEG C of maintenance 1-3h according to 1-3 DEG C/min, after dyeing, base fabric is fully washed;
3) base fabric is immersed equipped with, in the resin stock tank of 4-25%, then the base fabric being soaked with resin being toasted at 160-220 DEG C 50-70s and carry out high-temperature shaping rolling;
4) in step 3) process after the one side of base fabric on coating machine, coat PUR, the coating weight of described PUR is 10-20g/m2, the base fabric of PUR will be scribbled in 150-200 DEG C of high-temperature baking 50-65s, cooled rolling.
Further, step 2) described dye liquor proportioning is disperse dyes 2-9%o.w.f, levelling agent 0.2-1.2g/L, degreaser 0.5-2g/L, defoamer 0.05-0.1g/L, dye bath ratio is 1:10-30.
Further, step 2) described dye liquor proportioning is disperse dyes 9%o.w.f, levelling agent 0.2g/L, degreaser 0.5g/L, defoamer 0.05g/L, dye bath ratio is 1:20.
Further, step 1) described base fabric grammes per square metre is 20-200g/m2��
Further, step 3) described resin is acrylic resin.
Further, step/4) described PUR is one or more of polyamide, polyester, polyethylene and polyesteramide.
The adhesive lining that the preparation method of a kind of adhesive lining produces.
The adhesive lining preparation technology of the present invention is simple, production cost is low, it is possible to shorten the product time of delivery, improves Enterprise Integrated competitiveness. The adhesive lining stiffness prepared by said method is greatly increased, it is possible to make clothing more well-pressed with guarantor's type, and more aobvious more wide, abundant, plentiful than general lining cloth after collar, coat-sleeve, the front part of a Chinese robe or jacket etc. use this lining cloth, what add clothing wears aesthetics.
Detailed description of the invention
Below in conjunction with the embodiment of the present invention, the technical scheme in the embodiment of the present invention is clearly and completely described, it is clear that described embodiment is only a part of embodiment of the present invention, rather than whole embodiments. Based on the embodiment in the present invention, the every other embodiment that those of ordinary skill in the art obtain under not making creative work premise, broadly fall into the scope of protection of the invention.
Embodiment 1
The production technology of a kind of resin-bonding lining, comprises the following steps:
Step 1: prepare base fabric, base fabric is that polyester low stretch wire material is made, base fabric be organized as 1/1 plain weave, base fabric grammes per square metre is 20g/m2;
Step 2: dyeing, base fabric is after Song Buji unclamps, it is input to high temperature overflow dye vat through defeated cloth device and carries out high temperature overflow dyeing, equipped with heat tinting liquid (namely joining dye liquor temperature >=40 DEG C of high temperature overflow dye vat) in high temperature overflow dye vat dye vat, dye liquor proportioning is disperse dyes 9%o.w.f, levelling agent 0.2g/L, degreaser 2g/L, defoamer 0.05g/L, dye bath ratio is 1:10, dye liquor temperature is warming up to 120 DEG C according to 2 DEG C/min, boil and wash base fabric 3h, base fabric after dyeing is fully washed, controlling temperature is 60-65 DEG C of washing 10min, after discharge opeing, water inlet adds detergent and is warming up to 95-98 DEG C of soap boiling 10min, controlling temperature again is 60-65 DEG C of washing 10min, complete dyeing,
Step 3: base fabric being immersed in the stock tank of resin of 4%, the resin that the present embodiment uses is acrylic resin, then the base fabric being soaked with resin is toasted at 220 DEG C 30s and carries out high-temperature shaping rolling, and this step can make base fabric have certain stiffness;
Step 4: the above-mentioned base fabric through heat treatment is carried out coating process, is specially in use lining cloth coating machine one side in base fabric and coats PUR, and the coating weight of PUR is 20g/m2, the PUR at this place is polyamide (PA), will scribble the base fabric of PUR at 150 DEG C of high-temperature baking 50s, cooled rolling, then test package finished product.
Embodiment 2
The production technology of a kind of resin-bonding lining, comprises the following steps:
Step 1: prepare base fabric, base fabric is that polyester low stretch wire material is made, base fabric be organized as 1/1 plain weave, base fabric grammes per square metre is 80g/m2;
Step 2: dyeing, base fabric is after Song Buji unclamps, it is input to high temperature overflow dye vat through defeated cloth device, equipped with heat tinting liquid (namely joining dye liquor temperature >=40 DEG C of high temperature overflow dye vat) in high temperature overflow dye vat dye vat, dye liquor proportioning is disperse dyes 2%o.w.f, levelling agent 1g/L, degreaser 1g/L, defoamer 0.1g/L, dye bath ratio is 1:15, dye liquor temperature is warming up to 120 DEG C according to 1 DEG C/min, boil and wash base fabric 3h, base fabric after dyeing is fully washed, controlling temperature is 60-65 DEG C of washing 10min, after discharge opeing, water inlet adds detergent and is warming up to 95-98 DEG C of soap boiling 10min, controlling temperature again is 60-65 DEG C of washing 10min, complete dyeing,
Step 3: immersing base fabric equipped with in the resin stock tank of 25%, resin is acrylic resin, then the base fabric being soaked with resin is toasted at 160 DEG C 70s and carries out high-temperature shaping rolling, and this step can make the base fabric of preparation have certain stiffness;
Step 4: the above-mentioned base fabric through heat treatment is carried out coating process, is specially in use lining cloth coating machine one side in base fabric and coats PUR, and the coating weight of PUR is 10g/m2, PUR can be polyester (PES), will scribble the base fabric of PUR at 150 DEG C of high-temperature baking 65s, cooled rolling, then test package finished product.
Embodiment 3
The production technology of a kind of resin-bonding lining, comprises the following steps:
Step 1: prepare base fabric, base fabric is that polyester low stretch wire material is made, base fabric be organized as 2/2 twill, base fabric grammes per square metre is 200g/m2;
Step 2: dyeing, base fabric is after Song Buji unclamps, it is input to high temperature overflow dye vat through defeated cloth device and carries out high temperature overflow dyeing, equipped with heat tinting liquid (namely joining dye liquor temperature >=40 DEG C of high temperature overflow dye vat) in high temperature overflow dye vat dye vat, dye liquor proportioning is disperse dyes 5%o.w.f, levelling agent 1.2g/L, degreaser 2g/L, defoamer 0.08g/L, dye bath ratio is 1:20, dye liquor temperature is warming up to 130 DEG C according to 3 DEG C/min, boil and wash base fabric 1.5h, base fabric after dyeing is fully washed, controlling temperature is 60-65 DEG C of washing 20min, after discharge opeing, water inlet adds detergent and is warming up to 95-98 DEG C of soap boiling 10min, controlling temperature again is 60-65 DEG C of washing 20min, complete dyeing,
Step 3: immersing base fabric equipped with in the resin stock tank of 15%, resin is acrylic resin, then the base fabric being soaked with resin is toasted at 200 DEG C 50s and carries out high-temperature shaping rolling, and this step can make the base fabric of preparation have certain stiffness;
Step 4: the above-mentioned base fabric through heat treatment is carried out coating process, is specially in use lining cloth coating machine one side in base fabric and coats PUR, and the coating weight of PUR is 20g/m2, PUR can be polyethylene (LOPE and HDPE), and at 200 DEG C of high-temperature baking 50s, cooled rolling, then test package, the base fabric scribbling PUR is become finished product.
Embodiment 4
The production technology of a kind of resin-bonding lining, comprises the following steps:
Step 1: prepare base fabric, base fabric is that polyester low stretch wire material is made, base fabric be organized as 2/2 twill, base fabric grammes per square metre is 150g/m2;
Step 2: dyeing, base fabric is input to high temperature overflow dye vat through defeated cloth device after Song Buji unclamps and carries out high temperature overflow dyeing, equipped with heat tinting liquid (namely joining dye liquor temperature >=40 DEG C of high temperature overflow dye vat) in high temperature overflow dye vat dye vat, dye liquor proportioning is disperse dyes 6%o.w.f, levelling agent 1.0g/L, degreaser 1.5g/L, defoamer 0.1g/L, dye bath ratio is 1:18, dye liquor temperature is warming up to 130 DEG C according to 3 DEG C/min, boil and wash base fabric 1h, base fabric after dyeing is fully washed, controlling temperature is 60-65 DEG C of washing 10min, after discharge opeing, water inlet adds detergent and is warming up to 95-98 DEG C of soap boiling 10min, controlling temperature again is 60-65 DEG C of washing 10min, complete dyeing,
Step 3: immersing base fabric equipped with in the resin stock tank of 4%, resin is acrylic resin, then the base fabric being soaked with resin is toasted at 220 DEG C 60s and carries out high-temperature shaping rolling, and this step can make the base fabric of preparation have certain stiffness;
Step 4: the above-mentioned base fabric through heat treatment is carried out coating process, is specially in use lining cloth coating machine one side in base fabric and coats PUR, and the coating weight of PUR is 15g/m2, PUR can be polyesteramide (PEA), will scribble the base fabric of PUR at 150 DEG C of high-temperature baking 60s, cooled rolling, then test package finished product.
Embodiment 5
The production technology of a kind of resin-bonding lining, comprises the following steps:
Step 1: prepare base fabric, the base fabric of invention is that polyester low stretch wire material is made, base fabric be organized as 1/1 plain weave, base fabric grammes per square metre every square metre is 200g/m2;
Step 2: dyeing, base fabric is input to high temperature overflow dye vat through defeated cloth device after Song Buji unclamps and carries out high temperature overflow dyeing, equipped with heat tinting liquid (namely joining dye liquor temperature >=40 DEG C of high temperature overflow dye vat) in high temperature overflow dye vat dye vat, dye liquor proportioning is disperse dyes 9%o.w.f, levelling agent 1.2g/L, degreaser 2g/L, defoamer 0.1g/L, dye bath ratio is 1:30, dye liquor temperature is warming up to 130 DEG C according to 3 DEG C/min, boil and wash base fabric 1.5h, base fabric after dyeing is fully washed, controlling temperature is 60-65 DEG C of washing 10min, after discharge opeing, water inlet adds detergent and is warming up to 95-98 DEG C of soap boiling 10min, controlling temperature again is 60-65 DEG C of washing 10min, complete dyeing,
Step 3: immersing base fabric equipped with in the resin stock tank of 25%, resin is acrylate, then the base fabric being soaked with resin is toasted at 220 DEG C 40s and carries out high-temperature shaping rolling, and this step can make the base fabric of preparation have certain stiffness;
Step 4: the above-mentioned base fabric through heat treatment is carried out coating process, is specially in use lining cloth coating machine one side in base fabric and coats PUR, and the coating weight of PUR is 20g/m2, PUR can be polyamide (PA), will scribble the base fabric of PUR at 200 DEG C of high-temperature baking 50s, cooled rolling, then test package finished product.
Adhesive lining prepared by the present invention is mainly used in the positions such as the collar of easy suit dress ornament, coat-sleeve and the front part of a Chinese robe or jacket, it is possible to be cut into difformity as required. Adhesive lining prepared by the present invention makes base fabric have certain stiffness through the high-temperature shaping of step 3 to be coated with the preparation technology of last layer PUR through step 4 in the one side of base fabric again and add the stiffness of adhesive lining, the adhesive lining of preparation can make clothing more well-pressed and guarantor's type, the collar of dress and personal adornment, coat-sleeve, the front part of a Chinese robe or jacket are more aobvious more wide, abundant, plentiful than the clothing not using this lining cloth after using this lining cloth, and what add clothing wears aesthetics. Making simultaneously because base fabric is polyester low stretch wire material, product price is more less expensive than general product, owing to the production technology of the adhesive lining of the present invention is simple, reducing the cost of product, shortening the time of delivery, thus improving Enterprise Integrated competitiveness.
The foregoing is only presently preferred embodiments of the present invention, not in order to limit the present invention, all within the spirit and principles in the present invention, any amendment of making, equivalent replacement, improvement etc., should be included within protection scope of the present invention.
Claims (7)
1. the preparation method of an adhesive lining, it is characterised in that comprise the following steps:
1) preparing base fabric, described base fabric is made up of polyester low stretch wire material;
2) base fabric is after Song Buji unclamps, and is input to high temperature overflow dye vat through defeated cloth device and carries out high temperature overflow dyeing, and base fabric dyeing condition is that dye liquor temperature is warming up to 120-130 DEG C of maintenance 1-3h according to 1-3 DEG C/min, after dyeing, base fabric is fully washed;
3) base fabric is immersed equipped with, in the stock tank of the resin of 4-25%, the base fabric being soaked with resin being toasted 50-70s at 160-220 DEG C and carries out high-temperature shaping rolling;
4) in step 3) process after the one side of base fabric on coating machine, coat PUR, the coating weight of described PUR is 10-20g/m2, the base fabric of PUR will be scribbled 150-200 DEG C of high-temperature baking 50-65s, after cooling rolling.
2. the preparation method of adhesive lining according to claim 1, it is characterized in that, step 2) described dye liquor proportioning is disperse dyes 2-9%o.w.f, levelling agent 0.2-1.2g/L, degreaser 0.5-2g/L, defoamer 0.05-0.1g/L, dye bath ratio is 1:10-30.
3. the preparation method of adhesive lining according to claim 2, it is characterised in that step 2) described dye liquor proportioning is disperse dyes 9%o.w.f, levelling agent 0.2g/L, degreaser 0.5g/L, defoamer 0.05g/L, dye bath ratio is 1:20.
4. the preparation method of adhesive lining according to claim 1 and 2, it is characterised in that step 1) described base fabric grammes per square metre is 20-200g/m2��
5. the preparation method of adhesive lining according to claim 1 and 2, it is characterised in that step 3) described resin is acrylic resin.
6. the preparation method of adhesive lining according to claim 1 and 2, it is characterised in that step/4) described PUR is one or more of polyamide, polyester, polyethylene and polyesteramide.
7. the adhesive lining that the preparation method according to claim 1 or 2 adhesive lining produces.