CN104452142A - Method for producing retractable lining cloth - Google Patents
Method for producing retractable lining cloth Download PDFInfo
- Publication number
- CN104452142A CN104452142A CN201410624928.7A CN201410624928A CN104452142A CN 104452142 A CN104452142 A CN 104452142A CN 201410624928 A CN201410624928 A CN 201410624928A CN 104452142 A CN104452142 A CN 104452142A
- Authority
- CN
- China
- Prior art keywords
- grams per
- per liter
- agent
- lining cloth
- temperature
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a method for producing retractable lining cloth. The method includes the steps of desizing loosening, dyeing, drying, managing, coating and the like and solves the problem that at prevent, the shrinkage rate and elasticity of traditional lining cloth can not be matched with those of fabric in the garment processing process on the current garment market. The lining cloth has extremely high follow-up performance, compatibility and performance and meets the special requirements of current garment materials for the lining cloth. The novel fabric development and popularization paces are accelerated, and therefore the rapid development of the whole industry chain is promoted.
Description
Technical field
The present invention relates to a kind of production method of lining cloth.
Background technology
Along with the raising of people's living standard, on the one hand people to the comfortableness of clothes, durability, motility, personalized increasing concern is proposed.Coming one after another of fabric with rapid changepl. never-ending changes and improvements, people more and more favor the fabric of natural fabric, water imbibition fabric and elastic fabric as Tencel, cotton, viscose, fiber crops, cuprammonium, real silk, nylon, modified dacron, spandex, cotton and Lycra blending etc., the feature of these fabrics is water absorption and swellings, dry contraction, there is larger change in size, their relative position can be shifted because of wetting-dry, and this is the main cause that lining cloth and fabric bond site are wrinkling, bubble.Therefore have higher requirement to lining cloth washing shrinkage and trackability, common lining cloth can not carry out compatibility with these fabrics; On the other hand along with the rise of " green industry revolution ", low-carbon (LC), low formaldehyde require the important goal becoming current techniques innovation.Lining cloth is as the skeleton of clothes or bridge, and its quality directly determines class and the quality of apparel brand, and the technological innovation that requires of the low-carbon (LC) of ready-made clothes use procedure, low formaldehyde and ready-made clothes washing and wearability improve.Traditional lining cloth is only focused at bonding intensity, holding production cost aspect, and gos deep into the research of fabric, lacks the technical scheme helping clothes to improve quality and brand class.
Summary of the invention
The object of the present invention is to provide a kind of rational in infrastructure, the production method of unfolding the lining cloth that shrinks freely of excellent performance.
Technical solution of the present invention is:
Unfold a production method for the lining cloth that shrinks freely, it is characterized in that: comprise the following steps:
(1) destarch relaxes
In overflow dyeing machine, add destarch auxiliary agent, destarch auxiliary agent comprises desizing agent, powerful degreaser, NaOH, refining agent, wherein desizing agent 1.0-4.0 grams per liter, powerful degreaser 0.5-3 grams per liter, NaOH 1-10 grams per liter, refining agent 0.5-6 grams per liter.Then be warming up to 70 ~ 130 DEG C, keep after 20-60 minute, cooling washing, goes out cloth;
(2) dye
Dyeing continues, with lax state, to adopt high temperature, high pressure liquid stream jet dyeing machine or high temperature, the disperse dyeing of high pressure liquid stream machine; In high-temperature high-pressure liquid stream jet dyeing machine, add the dye liquor prepared, the DISPERSE DYES wherein added requires according to color and determines, levelling agent 0.05-0.3%, wetting softener 0.5-2.5%, dye 15-40 minute at the temperature of 130 DEG C, soaps, and then go out cloth after washing 3-4 time after dyeing;
(3) dry, arrange
Dressing liquid is added in the liquid bath of resin finishing range, dressing liquid is the mixed aqueous solution of softener, antistatic additive, xanthochromia preventing agent, three-proof finishing agent, wherein softener 5-30 grams per liter, antistatic additive 1-25 grams per liter, xanthochromia preventing agent 1-25 grams per liter, three-proof finishing agent 1-50 grams per liter.Drying and shaping temperature is: 130-210 DEG C.The control 25%-80% of work in-process degree of stretching;
(4) coating
Utilize the mode that screen cloth shifts, adopt the method for 3P compound coating to be coated on scrim surfaces with point-like, base slurry can be polyacrylic acid, polyacrylate, polyurethane resin, polyurethane resin, polyamide, polyethylene, polyurethane, the single material of polyurethane or mixture; Oven dry under 120-190 degree temperature range condition, sintering, cooling curing; Coating amount 4-25g/m2, process velocity 20 ~ 80 ms/min.
The invention solves the problem that current garment market occurs because traditional lining cloth can not match with fabric shrinkage, elasticity to clothes process, there is splendid trackability, compatibility, high-performance.This product has catered to the particular/special requirement of current dress materials to lining cloth.The paces accelerating novel fabric development and promote, thus promoted the fast development of whole industrial chain.
The lining cloth that the present invention produces, there is softness and plentiful feel, frivolous, splendid resilience, more common lining cloth has splendid good with kinetic force (following the feature of fabric), compatibility, wearability, high cohesive force, ultralow free formaldehyde, elasticity advantages of higher, bring comfort and soft feeling more to consumer, dress has more random, nature, fashion.The more important thing is that the lining cloth of unfolding and shrinking freely is compared with general lining cloth, unfold the lining cloth shunk freely and meet in water, steam treatment and clothes last handling process the change that can adapt to or follow fabric and stretch, the foaming that the relative position solving them can be shifted because of wetting-dry and wrinkling problem, unfold the advantage that the lining cloth shunk freely has low temperature pressing and ultra-low formaldehyde simultaneously, not only meet current people pursue the fashionable element of clothes and take performance requirement, and meet the environmental protection low-carbon (LC) requirement of industrial technology revolution.Unfold the lining cloth shunk freely, promote the class of clothes, problem demanding prompt solution in solution garment market demand, courageously develops for garment sector and design provides great scope of land.
The use of lining cloth that the present invention produces: the present invention be directed to natural fabric and water imbibition fabric and elastic fabric, (as Tencel, cotton, viscose, fiber crops, cuprammonium, real silk, nylon, modified dacron, spandex, cotton and Lycra blending etc.) water absorption and swelling, dry to shrink, there is larger change in size, the problem be shifted because of wetting-dry for the relative position solving them and develop the lining cloth of taking the course of its own and unfolding and shrinking freely.The present invention unfold the lining cloth that shrinks freely can show in the taking of fashionable dress, sportswear, Casual Wear, jacket etc. in it various premium properties, substantially increase trackability and the compatibility of product, improve the class of clothes.
Below in conjunction with embodiment, the invention will be further described.
Detailed description of the invention
Adopt PTT, PBT, the Ji Bu of PET or cladded yarn composition
(1) destarch relaxes
Destarch auxiliary agent is added in High Temperature High Pressure overflow dyeing machine, destarch auxiliary agent comprises desizing agent TF-127, powerful degreaser TF-129B, NaOH, refining agent TF-108 etc., wherein desizing agent TF-127 1.0-4.0 grams per liter, powerful degreaser TF-129B 0.5-3 grams per liter, NaOH 1-10 grams per liter, refining agent TF-108 0.5-6 grams per liter.Then be warming up to 70 ~ 130 DEG C, keep after 20-60 minute, cooling washing, goes out cloth.
(2) dye
Dyestuff is adhered to or set (entering) fibrous inside, makes lining cloth obtain even, firm, colourful color, and guarantee the same with sample.In order to the elasticity keeping fiber good, dyeing continues, with lax state, to adopt high temperature, high pressure liquid stream jet dyeing machine or high temperature, the disperse dyeing of high pressure liquid stream machine.The dye liquor prepared is added in high-temperature high-pressure liquid stream jet dyeing machine, the DISPERSE DYES wherein added requires according to color and determines, levelling agent WF8805 0.05-0.3%, wetting softener RL-205 0.5-2.5%, dye 15-40 minute at the temperature of 130 DEG C, soap after dyeing, and then go out cloth after washing 3-4 time.
(3) dry, arrange
Dressing liquid is added in the liquid bath of high-speed resin collator, dressing liquid is softener TF405C, antistatic additive TF-480, xanthochromia preventing agent (1,6-hexa-methylene-bis-(N, N-dimethylamino urea), the mixed aqueous solution of three-proof finishing agent RHSF, wherein softener TF405C 5-30 grams per liter, antistatic additive TF-480 1-25 grams per liter, xanthochromia preventing agent (1,6-hexa-methylene-bis-(N, N-dimethylamino urea) 1-25 grams per liter, three-proof finishing agent RHSF 1-50 grams per liter.Drying and shaping temperature is: 130-210 DEG C.The control 25%-80% of work in-process degree of stretching
(4) coating
Utilize the mode that screen cloth shifts, adopt the method for the compound coating of 3P to be coated on scrim surfaces with point-like, wherein base slurry can be single material or the mixture of polyacrylic acid, polyacrylate, polyurethane resin, polyurethane resin, polyamide, polyethylene, polyurethane, polyurethane etc.Oven dry under 120-190 degree temperature range condition, sintering, cooling curing.Coating amount 4-25g/m2, process velocity 20 ~ 80 ms/min.What profit was produced in this way unfolds the compound spot printing lining cloth of the lining cloth 3p shunk freely for a kind of.
Claims (1)
1. unfold a production method for the lining cloth that shrinks freely, it is characterized in that: comprise the following steps:
(1) destarch relaxes
In overflow dyeing machine, add destarch auxiliary agent, destarch auxiliary agent comprises desizing agent, powerful degreaser, NaOH, refining agent, wherein desizing agent 1.0-4.0 grams per liter, powerful degreaser 0.5-3 grams per liter, NaOH 1-10 grams per liter, refining agent 0.5-6 grams per liter.Then be warming up to 70 ~ 130 DEG C, keep after 20-60 minute, cooling washing, goes out cloth;
(2) dye
Dyeing continues, with lax state, to adopt high temperature, high pressure liquid stream jet dyeing machine or high temperature, the disperse dyeing of high pressure liquid stream machine; In high-temperature high-pressure liquid stream jet dyeing machine, add the dye liquor prepared, the DISPERSE DYES wherein added requires according to color and determines, levelling agent 0.05-0.3%, wetting softener 0.5-2.5%, dye 15-40 minute at the temperature of 130 DEG C, soaps, and then go out cloth after washing 3-4 time after dyeing;
(3) dry, arrange
Dressing liquid is added in the liquid bath of resin finishing range, dressing liquid is the mixed aqueous solution of softener, antistatic additive, xanthochromia preventing agent, three-proof finishing agent, wherein softener 5-30 grams per liter, antistatic additive 1-25 grams per liter, xanthochromia preventing agent 1-25 grams per liter, three-proof finishing agent 1-50 grams per liter.Drying and shaping temperature is: 130-210 DEG C.The control 25%-80% of work in-process degree of stretching;
(4) coating
Utilize the mode that screen cloth shifts, adopt the method for 3P compound coating to be coated on scrim surfaces with point-like, base slurry can be polyacrylic acid, polyacrylate, polyurethane resin, polyurethane resin, polyamide, polyethylene, polyurethane, the single material of polyurethane or mixture; Oven dry under 120-190 degree temperature range condition, sintering, cooling curing; Coating amount 4-25g/m2, process velocity 20 ~ 80 ms/min.