CN102899842A - Process for producing hot-melting bonding double-point lining in production of low-elasticity cloth - Google Patents
Process for producing hot-melting bonding double-point lining in production of low-elasticity cloth Download PDFInfo
- Publication number
- CN102899842A CN102899842A CN2012104348486A CN201210434848A CN102899842A CN 102899842 A CN102899842 A CN 102899842A CN 2012104348486 A CN2012104348486 A CN 2012104348486A CN 201210434848 A CN201210434848 A CN 201210434848A CN 102899842 A CN102899842 A CN 102899842A
- Authority
- CN
- China
- Prior art keywords
- cloth
- low
- drying room
- jibu
- bullet
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a process for producing a hot-melting bonding double-point lining in the production of low-elasticity cloth. The process comprises the following steps of: weaving raw materials by an automatic air injection machine to form base cloth of the low-elasticity cloth; performing curling and end sewing on the base cloth of the low-elasticity cloth; softening, and washing; performing overflow dyeing, after dyeing, padding the base cloth, and drying; padding the dried base cloth, and conveying the base cloth to a drying room for arranging; after arranging, performing double-point coating treatment on the base cloth of the low-elasticity cloth; and performing quality inspection for packaging. According to the process, polyester silks are used as the raw materials and are subjected to softening, washing, overflow dyeing and the like, so that the problems of dyeing defects, color spots, flaws and the like in the process of producing lining cloth are solved, and the softness and planeness of the lining cloth are improved effectively; and by dyeing, drying, arranging and double-point coating, the initial stripping strength of the lining cloth is enhanced, the quality of the lining cloth is improved, the stability of products is improved, the production efficiency is improved, and the production cost is reduced.
Description
[technical field]
The present invention relates to the low production technology that plays the hot melt adhesive two point lining of cloth production.
[background technology]
Along with China's binding lining industrial expansion, binding lining is with its product diversity, best in quality, advantages such as cost is moderate and in lining cloth market, occupy increasing share, most clothes have all adopted binding lining to improve apparel quality, binding lining early adopts single-point slurry point production technology, but single-point slurry point and the bonding weak effect of base cloth pressing, people had adopted two point slurry point production technology afterwards, use the anti-dry-cleaning of PADDING CLOTH of two point slurry point production technology, water-fastness, but the initial separation strength of the PADDING CLOTH that adopts at present the two point explained hereafter is lower, and decay is very fast after the washing, and easily produce seep through, fault, not only affect the lining cloth quality, and shortened the service life of clothes.
[summary of the invention]
Purpose of the present invention solves the problems of the prior art exactly, propose the production technology of the hot melt adhesive two point lining that a kind of low bullet cloth produces, not only can improve lining cloth and the base cloth initial separation strength after bonding, reduce the separation strength attenuation amplitude, and the lining cloth quality is good, avoids cloth cover seep through, fault.
For achieving the above object, the present invention proposes a kind of production technology of hot melt adhesive two point lining of low bullet cloth production, may further comprise the steps successively:
A) base cloth is weaved: adopt 100% terylene thread DTY as raw material, warp thread is 110dtex/48F, and weft yarn is 84dtex/36F, and warp thread and weft count are respectively 205/10 centimetres and 158/10 centimetres, warp thread and weft yarn are weaved through automatic jet plane, form the low Bu Jibu of bullet;
B) hai roll margin to seam: the low Bu Jibu of bullet is carried out the hai roll margin to seam process, and do a large knot at per 900～1100m place;
C) lax softening washing: the low Bu Jibu that plays is carried out mechanical soften handled, then the low bullet Bu Jibu behind the mechanical soften handled is washed, the low cloth speed of advancing that plays Bu Jibu is 25～35m/min;
D) High Temperature High Pressure overflow dyeing: will be through C) the low bullet fabricbase of step is arranged on the fabric guide roll, and fabric guide roll adopts nozzle that the low Bu Jibu of bullet is carried out overflow dyeing with 150 rev/mins rotation speed operation, and the pressure of described nozzle is 0.3～0.5kg/cm
2The nozzle specification is 60～80mm, the working solution that adopts is: the levelling agent of the dyeing acid of soft water, 0.4g/l, the defoamer of 0.25g/l, 1.25g/l, to account for embryo cloth weight be 0.9% black dyes, account for embryo cloth weight is 0.18% blue dyes, account for embryo cloth weight be 0.009% orchil, then add soft water full to cylinder till, the pH value of described dyeing acid is 4.5～5.5, described dyeing acid, defoamer, levelling agent and dyestuff are in harmonious proportion by soft water, then the low bullet Bu Jibu after the overflow dyeing are carried out the washing of at least twice running water;
E) drying and processing: to through D) the low bullet Bu Jibu of step carries out soaking one and rolls, and used padding machine pressure is 2～3kg/cm
2The speed of a motor vehicle is 50～60m/min, described low bullet Bu Jibu advances cloth with overfeeding 6%～10%, entering successively ten drying rooms dries, the temperature of the first five drying room all is set to 130～150 ℃, the temperature of rear five drying rooms all is set to 140～160 ℃, and the low Bu Jibu that plays is with the door width of cloth cropping of 106～108cm at last;
F) arrangement: to through E) the low bullet Bu Jibu of step carries out soaking one and rolls, and used padding machine pressure is 2～3kg/cm
2Then advance cloth speed successively through ten drying rooms with 45～55m/min, the temperature of first drying room and second drying room all is set to 150～170 ℃, the temperature of the 3rd drying room and the 4th drying room all is set to 160～180 ℃, the temperature of the 5th drying room and the 6th drying room all is set to 170～180 ℃, the 7th drying room, the 8th drying room, the temperature of the 9th drying room and the tenth drying room all is set to 180～190 ℃, the low Bu Jibu that plays is with the door width of cloth cropping of 123～124cm at last, and described one soaks one rolls the dressing liquid that adopts and be: the antistatic additive of 20g/l, the first softener of 5g/l, the second softener of 10g/l and the 3rd softener of 15g/l;
G) two point coating: to finishing F) the low bullet Bu Jibu of step enters the two point coating machine and carries out the two point coating with the cloth speed of advancing of 20～22m/min, and adopts first slurry coating materials point in the two point coating procedure, adopts hot-melt adhesive powder to carry out dusting again and forms two point; The constituent of described slurry is: stabilizing agent, 0.5KG defoamer and the water 58.4KG of the permeability-reducing admixture of the HDPE fine powder of the dispersant of 2.1KG, 13.3KG, the PA fine powder of 20KG, 1.3KG, the thickener of 1.4KG, 3KG, the said components mix and blend obtained slurry in ten minutes, then use scraper that slurry coating is played on the Bu Jibu to hanging down, the coating amount of slurry is 6～8g/m
2Described dusting hot-melt adhesive powder is mixed by powder among the powder PES among powder among the PA and the 2nd PA, and the rotating speed of dusting head is 10.5～11.5 rev/mins in the dusting process; After finishing, dusting carries out air sucking/blowing, the hot-melt adhesive powder that does not stick on the slurry point is absorbed, then entered the drying room oven dry, the temperature of drying room is 130～150 ℃, by 3 groups of tentering electrothermal tubes the low Bu Jibu that plays is added hot baked in the drying room, described tentering electrothermal tube height is 16～20cm;
H) quality inspection packing: with the standard packing of every volume 90～110m, every bag comprises at least two volumes, forms finished product.
As preferably, described B) in the step, every 1000m does at the place a large knot, take a km as boundary, is convenient to the subsequent treatment to base cloth.
As preferably, described C) in the step, the low cloth speed of advancing that plays Bu Jibu is 30m/min, has both improved speed of production and has also guaranteed softening washing effect, makes the cloth of producing more soft, better quality.
As preferably, described D) in the step, the pressure of described nozzle is 0.4kg/cm
2, the nozzle specification is 70mm, and described is 5 with DA accent pH value, and described washing is twice, through the base cloth better quality of twice washing, effectively avoids seep through and fault.
As preferably, described E) in the step, used padding machine pressure is 2.5kg/cm
2, the speed of a motor vehicle is 55m/min, described overfeeding speed is 8%, the temperature of described the first five drying room all is set to 140 ℃, and the temperature of rear five drying rooms all is set to 150 ℃, and the described cropping door width of cloth is 107cm, the initial separation strength of base cloth through drying and processing is higher, and the peel strength decay reduces.
As preferably, described F) in the step, described padding machine pressure is 2.5kg/cm
2It is described that to advance cloth speed be 50m/min, the temperature of first drying room and second drying room all is set to 160 ℃, the temperature of the 3rd drying room and the 4th drying room all is set to 170 ℃, the temperature of the 5th drying room and the 6th drying room all is set to 175 ℃, the temperature of the 7th drying room, the 8th drying room, the 9th drying room and the tenth drying room all is set to 185 ℃, the described cropping door width of cloth is 123.5cm, before two point, base cloth is put in order processing, be conducive to finishing of two point process, improve the quality of finished fabric.
As preferably, described G) in the step, the cloth speed of advancing of described low bullet Bu Jibu is 21m/min, and the temperature of described drying room is 140 ℃, and described dusting hot melt adhesive amount is 7g/m
2, the dusting of an adopting rotating speed is 11 rev/mins, the coating amount of described slurry is 7g/m
2, described tentering electric heating height is 18cm; The particle diameter of HDPE and PA fine powder is 1～80 μ in the slurry, by the setting of Reasonable Parameters, makes the two point process more effective, and the lining cloth better quality of producing seep through and flaw can not occur.
As preferably, described G) in the step, the PA that forms hot-melt adhesive powder comprises that the trade mark is that the one PA of Huels AG of D1541 and the trade mark are 730 the 2nd PA of Huels AG, the mass ratio of each component is in the hot-melt adhesive powder: the trade mark is PA:50 part of D1541, the trade mark is PA:33 part of 730, the PES:17 of EMS company part.
As preferably, described H) in the step, described finished product is the standard packing with every volume 100m, every bag two volumes.
Beneficial effect of the present invention: it is raw material that the present invention adopts terylene thread, through steps such as softening washings, the problems such as the look flower of not only having avoided occurring in the lining cloth production process, look stain, fault, and effectively increased pliability and the flatness of lining cloth, through dyeing, dry, put in order again two point coating, improved the lining cloth initial bonding strength, improved the quality of lining cloth, improved the stability of product, and can enhance productivity, reduced production costs.
[specific embodiment]
The low production technology that plays the hot melt adhesive two point lining of cloth production of the present invention may further comprise the steps successively:
A) base cloth is weaved: adopt 100% terylene thread DTY as raw material, warp thread is 110dtex/48F, and weft yarn is 84dtex/36F, and warp thread and weft count are respectively 205/10 centimetres and 158/10 centimetres, warp thread and weft yarn are weaved through automatic jet plane, form the low Bu Jibu of bullet;
B) hai roll margin to seam: the low Bu Jibu of bullet is carried out the hai roll margin to seam process, and do a large knot at every 1000m place;
C) lax softening washing: the low Bu Jibu that plays is carried out mechanical soften handled, then the low bullet Bu Jibu after the softening is washed, the low cloth speed of advancing that plays Bu Jibu is 30m/min;
D) High Temperature High Pressure overflow dyeing: will be through C) the low bullet fabricbase of step is arranged on the fabric guide roll, and fabric guide roll adopts nozzle that the low Bu Jibu of bullet is carried out overflow dyeing with 150 rev/mins rotation speed operation, and the pressure of described nozzle is 0.4kg/cm
2The nozzle specification is 70mm, the working solution that adopts is: soft water, 0.4g/l dyeing acid, 0.25g/l defoamer, 1.25g/l levelling agent, account for embryo cloth weight and be 0.9% black dyes Ex-SF, account for embryo cloth weight and be 0.18% blue dyes E-TB, account for embryo cloth weight and be 0.009% orchil E-GL, described dyeing acid, defoamer, levelling agent and dyestuff are in harmonious proportion by soft water, the pH value of described DA is 5, then the low bullet Bu Jibu after the overflow dyeing is carried out twice from the beginning washing, described dyeing acid is dyeing acid pH-07, described defoamer is tributyl phosphate, and described levelling agent is levelling agent BOF;
E) drying and processing: to finishing D) the low bullet Bu Jibu of step carries out soaking one and rolls, and used padding machine pressure is 2.5kg/cm
2, the speed of a motor vehicle is 55m/min, and described low bullet Bu Jibu enters ten drying rooms with 8% overfeeding speed and finishes oven dry, and the temperature of the first five drying room all is set to 140 ℃, and the temperature of rear five drying rooms all is set to 150 ℃, and the low Bu Jibu that plays is with the width of cloth cropping of 107cm at last;
F) arrangement: to finishing E) the low bullet Bu Jibu of step carries out soaking one and rolls, and used padding machine pressure is 2.5kg/cm
2Then advance cloth speed successively through ten drying rooms with 50m/min, the temperature of first drying room and second drying room all is set to 160 ℃, the temperature of the 3rd drying room and the 4th drying room all is set to 170 ℃, the temperature of the 5th drying room and the 6th drying room all is set to 175 ℃, the 7th drying room, the 8th drying room, the temperature of the 9th drying room and the tenth drying room all is set to 185 ℃, the low Bu Jibu that plays is with the door width of cloth cropping of 123.5cm at last, the dressing liquid that adopts is: the antistatic additive of 20g/l, the first softener of 5g/l, the second softener of 10g/l and the 3rd softener of 15g/l, described antistatic additive is the SAS93 antistatic additive that Shanghai Industrial Co., Ltd. of warship nation produces, the SAS93 antistatic additive is a kind of light yellow particle of not chloride ion-containing, has strong antistatic behaviour, described the first softener is the Hangzhou softener ZL-010 that chemical industry Co., Ltd produces that stands upright, softener ZL-010 has certain antistatic effect, can make fabric more soft, described the second softener is the Hangzhou soft and smooth finishing agent ZL-DCG of spun polyester thread that chemical industry Co., Ltd produces that stands upright, the soft and smooth finishing agent ZL-DCG of spun polyester thread good penetrability, can make fabric more suitable more sliding, described the 3rd softener is the Hangzhou soft lubrication prescription ZL-A1000 that chemical industry Co., Ltd produces that stands upright;
G) two point coating: to finishing F) the low bullet Bu Jibu of step enters the two point coating machine and carries out the two point coating with the cloth speed of advancing of 20～22m/min, and adopts first slurry coating materials point in the two point coating procedure, adopts hot-melt adhesive powder to carry out dusting again and forms two point; The constituent of described slurry is: stabilizing agent and 0.5KG defoamer and the water 58.4KG of the permeability-reducing admixture of the HDPE fine powder of the dispersant of 2.1KG, 13.3KG, the PA fine powder of 20KG, 1.3KG, the thickener of 1.4KG, 3KG, the said components mix and blend obtained slurry in ten minutes, then use scraper that slurry coating is played on the Bu Jibu to hanging down, the coating amount of slurry is 6～8g/m
2Described hot melt adhesive dusting is mixed by powder among PA and the PES, and the rotating speed of dusting head is 10.5～11.5 rev/mins in the dusting process; After finishing, dusting carries out air sucking/blowing, the hot-melt adhesive powder that does not stick on the slurry point is absorbed, then enter drying room and cure oven dry, the temperature of drying room is 130～150 ℃, by 3 groups of tentering electrothermal tubes the low Bu Jibu that plays is heated in the drying room, described tentering electrothermal tube height is 16～20cm, described dispersant adopt Hangzhou to stand upright chelated dispersants that chemical industry Co., Ltd produces, described HDPE adopts the high density polyethylene (HDPE) fine powder, described PA adopts fine powder, described permeability-reducing admixture adopts Ningbo to foretell the DD1 that Saite chemical industry Co., Ltd produces, can guarantee the flatness of slurry, described thickener adopts Ningbo to foretell the ethylene oxide polymer MiroxHP that Saite chemical industry Co., Ltd produces, and MiroxHP is the high dense thickener of thixotropy, and described stabilizing agent adopts Ningbo to foretell the MiroxOX that Saite chemical industry Co., Ltd produces, can keep the unobstructed of mesh, described defoamer adopts tributyl phosphate, and the size of powder particles of described fine powder is the 1-80 micron, and the size of powder particles of described middle powder is the 81-160 micron;
H) quality inspection packing: with the standard packing of every volume 100m, every bag comprises two volumes, forms finished product.
The course of work of the present invention:
At first adopt 100% terylene thread DTY as raw material, warp thread is 110dtex/48F, and weft yarn is 84dtex/36F, and warp thread and weft count are respectively 205/10 centimetres and 158/10 centimetres, and warp thread and weft yarn are weaved through automatic jet plane, forms the low Bu Jibu of bullet; Then the low Bu Jibu of bullet is carried out the hai roll margin to seam and process, and do a large knot at every 1000m place; Then it is carried out the softening washing, make base cloth more soft, lax, be convenient to following step; Then the low bullet Bu Jibu after the softening washing is carried out overflow dyeing with nozzle to it; Finish after the dyeing, first the low Bu Jibu that plays is padded processing, again with its input drying room oven dry; Then the low bullet Bu Jibu after the oven dry is padded processing again, pad after the processing, with its input drying room arrangement, and use dressing liquid; After the arrangement step, the low Bu Jibu of bullet is carried out two point process, at first at the low a certain amount of slurry of Bu Jibu coating that plays, then spread a certain amount of hot-melt adhesive powder at the low Bu Jibu that plays, by 3 groups of tentering electric heating the low Bu Jibu that plays is heated at last; With the standard packing of every volume 100m, every bag comprises two volumes, forms finished product at last.
Through the lining cloth good stability of the dimension that above step is produced, all in 1%, lining cloth door width of cloth basic controlling is between 122 to 123 to washing change in size, oven dry change in size in length and breadth, product size is suitable, does not have flaw, and the product initial bonding strength is high, the product quality is soft, and is best in quality.
Above-described embodiment is to explanation of the present invention, is not limitation of the invention, any scheme after the simple transformation of the present invention is all belonged to protection scope of the present invention.
Claims (9)
1. hang down the production technology of the hot melt adhesive two point lining that plays cloth production, it is characterized in that: may further comprise the steps successively:
A) base cloth is weaved: adopt 100% terylene thread DTY as raw material, warp thread is 110dtex/48F, and weft yarn is 84dtex/36F, and warp thread and weft count are respectively 205/10 centimetres and 158/10 centimetres, warp thread and weft yarn are weaved through automatic jet plane, form the low Bu Jibu of bullet;
B) hai roll margin to seam: the low Bu Jibu of bullet is carried out the hai roll margin to seam process, and do a large knot at per 900～1100m place;
C) lax softening washing: the low Bu Jibu that plays is carried out mechanical soften handled, then the low bullet Bu Jibu behind the mechanical soften handled is washed, the low cloth speed of advancing that plays Bu Jibu is 25～35m/min;
D) High Temperature High Pressure overflow dyeing: will be through C) the low bullet fabricbase of step is arranged on the fabric guide roll, and fabric guide roll adopts nozzle that the low Bu Jibu of bullet is carried out overflow dyeing with 150 rev/mins rotation speed operation, and the pressure of described nozzle is 0.3～0.5kg/cm
2The nozzle specification is 60～80mm, the working solution that adopts is: the levelling agent of the dyeing acid of soft water, 0.4g/l, the defoamer of 0.25g/l, 1.25g/l, to account for embryo cloth weight be 0.9% black dyes, account for embryo cloth weight is 0.18% blue dyes, account for embryo cloth weight is 0.009% orchil, the pH value of described dyeing acid is 4.5～5.5, described dyeing acid, defoamer, levelling agent and dyestuff are in harmonious proportion by soft water, then the low bullet Bu Jibu after the overflow dyeing are carried out the washing of at least twice running water;
E) drying and processing: to through D) the low bullet Bu Jibu of step carries out soaking one and rolls, and used padding machine pressure is 2～3kg/cm
2The speed of a motor vehicle is 50～60m/min, described low bullet Bu Jibu advances cloth with overfeeding 6%～10%, entering successively ten drying rooms dries, the temperature of the first five drying room all is set to 130～150 ℃, the temperature of rear five drying rooms all is set to 140～160 ℃, and the low Bu Jibu that plays is with the door width of cloth cropping of 106～108cm at last;
F) arrangement: to through E) the low bullet Bu Jibu of step carries out soaking one and rolls, and used padding machine pressure is 2～3kg/cm
2Then advance cloth speed successively through ten drying rooms with 45～55m/min, the temperature of first drying room and second drying room all is set to 150～170 ℃, the temperature of the 3rd drying room and the 4th drying room all is set to 160～180 ℃, the temperature of the 5th drying room and the 6th drying room all is set to 170～180 ℃, the 7th drying room, the 8th drying room, the temperature of the 9th drying room and the tenth drying room all is set to 180～190 ℃, the low Bu Jibu that plays is with the door width of cloth cropping of 123～124cm at last, and described one soaks one rolls the dressing liquid that adopts and be: the antistatic additive of 20g/l, the first softener of 5g/l, the second softener of 10g/l and the 3rd softener of 15g/l;
G) two point coating: to finishing F) the low bullet Bu Jibu of step enters the two point coating machine and carries out the two point coating with the cloth speed of advancing of 20～22m/min, and adopts first slurry coating materials point in the two point coating procedure, adopts hot-melt adhesive powder to carry out dusting again and forms two point; The constituent of described slurry is: stabilizing agent, 0.5KG defoamer and the water 58.4KG of the permeability-reducing admixture of the HDPE fine powder of the dispersant of 2.1KG, 13.3KG, the PA fine powder of 20KG, 1.3KG, the thickener of 1.4KG, 3KG, the said components mix and blend obtained slurry in ten minutes, then use scraper that slurry coating is played on the Bu Jibu to hanging down, the coating amount of slurry is 6～8g/m
2Described dusting hot-melt adhesive powder is mixed by powder among powder and the PES among powder among the PA and the 2nd PA, and the rotating speed of dusting head is 10.5～11.5 rev/mins in the dusting process; After finishing, dusting carries out air sucking/blowing, the hot-melt adhesive powder that does not stick on the slurry point is absorbed, then entered the drying room oven dry, the temperature of drying room is 130～150 ℃, by 3 groups of tentering electrothermal tubes the low Bu Jibu that plays is added hot baked in the drying room, described tentering electrothermal tube height is 16～20cm;
H) quality inspection packing: with the standard packing of every volume 90～110m, every bag comprises at least two volumes, forms finished product.
2. the production technology of the hot melt adhesive two point lining produced of low bullet cloth as claimed in claim 1 is characterized in that: described B) every 1000m does at place one and ties greatly in the step.
3. the production technology of the hot melt adhesive two point lining produced of low bullet cloth as claimed in claim 1, it is characterized in that: described C) the cloth speed of advancing of the low Bu Jibu of bullet is 30m/min in the step.
4. the production technology of the hot melt adhesive two point lining produced of low bullet cloth as claimed in claim 1, it is characterized in that: described D) pressure of nozzle described in the step is 0.4kg/cm
2, the nozzle specification is 70mm, and the pH value of described dyeing acid is 5, and described washing is twice.
5. the production technology of the hot melt adhesive two point lining produced of low bullet cloth as claimed in claim 1, it is characterized in that: described E) used padding machine pressure is 2.5kg/cm in the step
2, the speed of a motor vehicle is 55m/min, and overfeeding 8% improves, and the temperature of described the first five drying room all is set to 140 ℃, and the temperature of rear five drying rooms all is set to 150 ℃, and the described cropping door width of cloth is 107cm.
6. the production technology of the hot melt adhesive two point lining produced of low bullet cloth as claimed in claim 1, it is characterized in that: described F) padding machine pressure described in the step is 2.5kg/cm
2It is described that to advance cloth speed be 50m/min, the temperature of first drying room and second drying room all is set to 160 ℃, the temperature of the 3rd drying room and the 4th drying room all is set to 170 ℃, the temperature of the 5th drying room and the 6th drying room all is set to 175 ℃, the temperature of the 7th drying room, the 8th drying room, the 9th drying room and the tenth drying room all is set to 185 ℃, and the described cropping door width of cloth is 123.5cm.
7. the production technology of the hot melt adhesive two point lining produced of low bullet cloth as claimed in claim 1, it is characterized in that: described G) the cloth speed of advancing of the low Bu Jibu of bullet is 21m/min described in the step, the temperature of described drying room is 140 ℃, and described dusting hot melt adhesive amount is 7g/m
2, the dusting of an adopting rotating speed is 11 rev/mins, the coating amount of described slurry is 7g/m
2, described tentering electric heating height is 18cm; The particle diameter of HDPE fine powder is 1～80 μ in the slurry.
8. the production technology of the hot melt adhesive two point lining produced of low bullet cloth as claimed in claim 1, it is characterized in that: the PA that described G) forms hot-melt adhesive powder in the step comprises that the trade mark is that the PA of D1541 and the trade mark are 730 the 2nd PA, the mass ratio of each component is in the hot-melt adhesive powder: the trade mark is PA:50 part of D1541, the trade mark is PA:33 part of 730, PES:17 part.
9. the production technology that the hot melt adhesive two point of producing such as each described low bullet cloth in the claim 1 to 8 serves as a contrast is characterized in that: described H) finished product described in the step is the standard packing with every volume 100m, every bag two volumes.