CN105648740A - 一种新型的纤维洗净方法 - Google Patents
一种新型的纤维洗净方法 Download PDFInfo
- Publication number
- CN105648740A CN105648740A CN201510902246.2A CN201510902246A CN105648740A CN 105648740 A CN105648740 A CN 105648740A CN 201510902246 A CN201510902246 A CN 201510902246A CN 105648740 A CN105648740 A CN 105648740A
- Authority
- CN
- China
- Prior art keywords
- fiber
- fibers
- acetone
- cleaning
- water
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及纤维处理技术领域,具体涉及一种新型的纤维洗净方法。它的处理方法:将纤维丝放入软化水池中进行热处理,温度保持在60-80℃,加热半小时,然后通过清水进行清洗干净;将前处理过的纤维称好置于盘中,加入清水搅拌均匀,加入丙酮-水溶液,其中丙酮为4%-6%,同时加入NaHCO3,再搅拌10min,使丙酮与纤维充分混和,最后加入已经溶解好的4-6g/L的过硫酸氢钾溶液,搅拌均匀后将纤维置于塑料袋中,密封后放入恒温水浴中,通过梳理刷将经过步骤二处理过的纤维进行快速梳理,再进行二次清洗烘干即可。
Description
技术领域:
本发明涉及纤维处理技术领域,具体涉及一种新型的纤维洗净方法。
背景技术:
我国竹类资源丰富,是世界上最大的产竹国。目前,竹材的应用已拓展到建筑、造纸、食品、家具、医药、纺织等领域,但其在纺织上的应用十分有限。影响竹纤维可纺性的最主要因素在于竹纤维中含有大量的半纤维素和木质素。碱煮可去除半纤维素,但对于耐碱性强的木质素只有通过漂白工序去除。
传统的工业漂白过程中使用了大量的含氯试剂,对环境和人类健康造成了极大危害,因此工业漂白技术也渐渐向无元素氯和全无氯漂白发展,如采用O2、O3,和H2O2等。然而,这些漂白剂也都有各自的缺点,氧脱木质素不能超过50%,否则会引起碳水化合物的严重降解,纤维素成分降低;O3是有效的脱木素剂,但是会产生攻击性的游离基反应,和碳水化合物发生降解反应;H2O2是一种较好的漂白剂,而无论在酸性还是碱性条件下都不是有效的脱木素试剂。
发明内容:
本发明的目的是提供一种新型的纤维洗净方法,它设计巧妙,通过软化、漂白配合清洗烘干,对纤维组织进行内部洗净处理,保证纤维材料的洁净。
为了解决背景技术所存在的问题,本发明是采用以下技术方案:它的处理方法:
步骤一:将纤维丝放入软化水池中进行热处理,温度保持在60-80℃,加热半小时,然后通过清水进行清洗干净;
步骤二:将前处理过的纤维称好置于盘中,加入清水搅拌均匀,加入丙酮-水溶液,其中丙酮为4%-6%,同时加入NaHCO3,再搅拌10min,使丙酮与纤维充分混和,最后加入已经溶解好的4-6g/L的过硫酸氢钾溶液,搅拌均匀后将纤维置于塑料袋中,密封后放入恒温水浴中,保持40℃-60℃,反应时间60min-100min,取出纤维,用清水洗净。
步骤三:通过梳理刷将经过步骤二处理过的纤维进行快速梳理,再进行二次清洗烘干即可。
本发明的有益效果:它设计巧妙,通过软化、漂白配合清洗烘干,对纤维组织进行内部洗净处理,保证纤维材料的洁净。
具体实施方式:
本具体实施方式采用以下技术方案:它的处理方法:
步骤一:将纤维丝放入软化水池中进行热处理,温度保持在60-80℃,加热半小时,然后通过清水进行清洗干净;
步骤二:将前处理过的纤维称好置于盘中,加入清水搅拌均匀,加入丙酮-水溶液,其中丙酮为4%-6%,同时加入NaHCO3,再搅拌10min,使丙酮与纤维充分混和,最后加入已经溶解好的4-6g/L的过硫酸氢钾溶液,搅拌均匀后将纤维置于塑料袋中,密封后放入恒温水浴中,保持40℃-60℃,反应时间60min-100min,取出纤维,用清水洗净。
步骤三:通过梳理刷将经过步骤二处理过的纤维进行快速梳理,再进行二次清洗烘干即可。
本发明的有益效果:它设计巧妙,通过软化、漂白配合清洗烘干,对纤维组织进行内部洗净处理,保证纤维材料的洁净。
以上所述,仅用以说明本发明的技术方案而非限制,本领域普通技术人员对本发明的技术方案所做的其它修改或者等同替换,只要不脱离本发明技术方案的精神和范围,均应涵盖在本发明的权利要求范围当中。
Claims (1)
1.一种新型的纤维洗净方法,其特征在于它的处理方法:
步骤一:将纤维丝放入软化水池中进行热处理,温度保持在60-80℃,加热半小时,然后通过清水进行清洗干净;
步骤二:将前处理过的纤维称好置于盘中,加入清水搅拌均匀,加入丙酮-水溶液,其中丙酮为4%-6%,同时加入NaHCO3,再搅拌10min,使丙酮与纤维充分混和,最后加入已经溶解好的4-6g/L的过硫酸氢钾溶液,搅拌均匀后将纤维置于塑料袋中,密封后放入恒温水浴中,保持40℃-60℃,反应时间60min-100min,取出纤维,用清水洗净。
步骤三:通过梳理刷将经过步骤二处理过的纤维进行快速梳理,再进行二次清洗烘干即可。