CN105625666A - Sand beach shell decorative sheet and manufacturing method thereof - Google Patents
Sand beach shell decorative sheet and manufacturing method thereof Download PDFInfo
- Publication number
- CN105625666A CN105625666A CN201511019326.XA CN201511019326A CN105625666A CN 105625666 A CN105625666 A CN 105625666A CN 201511019326 A CN201511019326 A CN 201511019326A CN 105625666 A CN105625666 A CN 105625666A
- Authority
- CN
- China
- Prior art keywords
- decorative plate
- shell
- sandy beach
- parts
- shell decorative
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a sand beach shell decorative sheet and a manufacturing method thereof. The sand beach shell decorative sheet comprises a base layer, an adhesive layer attached to the base layer, and a coating layer on the outermost layer. The finished product is manufactured through coating preparation, smearing of the coating to the surface of the base layer and drying. The coating on the surface of the sand beach shell decorative sheet is good in adhesive force, high in heat resistance and superior to an existing coating, the service life can be greatly prolonged, secondary pollution of inner wall decoction is avoided, energy conservation and environment friendliness are achieved, and no toxic or harmful matter is released in the using process.
Description
Technical field
The present invention relates to a kind of decorative sheet, in particular to a kind of sandy beach shell decorative plate and its preparation method.
Background technology
Along with raising and the improvement of living standards of the people, the indoor environment building cause of China has had considerable progress, living environment is polluted consciousness and is improving constantly by people, but, overall level still allows of no optimist, room air pollution is still one of primary killers of being detrimental to health, strengthens administering very urgent. It is introduced, the main source of pollution of China's indoor environment are from building, decoration and furniture at present, and formaldehyde, benzene, ammonia pollute to exceed standard and seriously have impact on the healthy of people. House ornamentation is inevitable, paint, and wood furniture is ubiquitous. Existing coating products in existing market, can not adsorb obnoxious flavour, cannot adsorb the obnoxious flavour of the high density that indoor have, and can not meet people to the requirement of quality of life.
Modern science analytical proof, oyster shell whiting is rich in multiple element, and shellfish seafood is the food that people extremely like, but a large amount of shells under leaving over become the rubbish being difficult to disaggregating treatment. Shell is rich in calcium carbonate, the traditional chemical thimerosal of " shell solution " alternative hospital life-time service, and not only sterilisation effect is good, and environment can not produce any chemical pollution. This kind " shell solution " is although alkalescence is very strong, but can not play corrosive nature as other basic solutions, and even the skin of harm people. This is because, owing to shellfish lives in the seawater, and seawater is dissolved with the multiple mineral composition stoping corrosion, therefore " shell solution " is also a kind of safe Household disinfectant, is specially adapted to kitchen, bathroom and toilet disinfection.
Using formaldehyde as tamanori when house fitting and furniture make all in a large number, but formaldehyde is a kind of volatile chemical, after sucking, human body can be had a negative impact by nature, even may bring out cancer. And the paint for wall of oyster shell whiting can make the concentration of formaldehyde in room be reduced to original 1/5th within the short period of time, in addition can also absorb other objectionable constituent that all chemical coatings come out, ensure the harmful chemical component in room air is controlled at lower level. Electron microscope shows, and shell powder contains many duck eyes, and volatile matter formaldehyde is once enter duck eye, and the distinctive calcium carbonate of shell will be decomposed into the harmless element such as hydrogen and carbonic acid gas.
Current shell plate production process is added the secondary pollution that too much chemical reagent raw material can cause indoor wall to be fitted up, the product that the resin-made adopted obtains can discharge a small amount of formaldehyde, harmful, and the mother of pearl paper of surface adhesive due to sticking power limited, easily come off for a long time.
Summary of the invention
The present invention is to overcome defect in above-mentioned prior art, it is proposed to a kind of sandy beach shell decorative plate and its preparation method.
A kind of sandy beach shell decorative plate, described sandy beach shell decorative plate comprises basic unit, is attached to the binder layer on basic unit and outermost dope layer.
Described basic unit is glass magnesium plate or aluminosulfate cement plate.
Described dope layer is made up of the raw material of following weight: oyster shell whiting 200 parts, sodium polyacrylate 60-90 part, tripoly phosphate sodium STPP 70-90 part, Sodium hexametaphosphate 99 70-90 part, defoamer 15-45 part, anti-settling agent 15-45 part, ethene-vinyl acetate copolymer emulsion 55-75 part, water-white rosin 10-50 part, polyacrylic ester 20-40 part, urethane 20-40 part, dicyclohexyl phthalate 20-40 part and mill base 40-70 part;
The preparation method of described sandy beach shell decorative plate, carries out in accordance with the following steps:
(1) coating is prepared;
(2) by paint in substrate surface;
(3) dry, equilibrium water content;
The method that described step (1) prepares coating carries out in accordance with the following steps:
1. prepare oyster shell whiting: take powder of natural shell as raw material, after cleaning, sterilising treatment, it is crushed to 120-300 order, after dry, obtain oyster shell whiting;
2. in pill tank, add 800-1000 part water, when opening whipping appts, 60-90 part sodium polyacrylate, 70-90 part tripoly phosphate sodium STPP and 70-90 part Sodium hexametaphosphate 99 are evenly spread in pill tank slowly, slowly add 200 parts of oyster shell whitings under agitation, and then add 15-45 part defoamer, 15-45 part anti-settling agent, stirring makes it fully dissolve, and obtains mixed solution;
3. by 55-75 part ethene-vinyl acetate copolymer emulsion under agitation, evenly slowly add in the mixed solution of step 2. gained, more successively add 10-50 part water-white rosin, 20-40 part polyacrylic ester, 20-40 part urethane, 20-40 part dicyclohexyl phthalate and 40-70 part mill base;
4. finally coating is obtained under agitation;
Described step sterilising method 1. is moist heat sterilization, sterilizing 20-30min under 116 DEG C of conditions;
Described step 1.-4. stir for stir 10-20min when rotating speed 1000-2000r/min;
Step (2) paint described in the preparation method of a kind of sandy beach shell decorative plate is manual print roll coating mode in the mode of substrate surface; Described step (3) drying means is dry 20-50min under 40-100 DEG C of condition.
For in technical scheme mentioned above, except raw material oyster shell whiting, remaining auxiliary agent, comprises anti-settling agent, thickening material, wetting agent, flow agent, defoamer, stablizer, according to the technician of this area, tinting materials etc. can know that general knowledge carries out the replacement of equivalence altogether, the replacement of modification done when why not deviateing technical solution of the present invention in office, increase and decrease or equivalent manners, then all should be included within scope of the present invention.
Compared with prior art, the present invention has following useful effect: the present invention provides a kind of topcoating strong adhesion, topcoating has good sticking power, snappiness and wear-resisting weather-proof, difficult drop-off, long service life, it is applicable to the sandy beach shell decorative plate of multiple decoration places, by adopting coating specialty tackiness agent on the plate face of sheet material, local or overall coating decorative paint, thus prepare sturdy and durable, texture is good, pattern is changeable, price is moderate, the decoration material that cost performance is good, avoid secondary decoration to pollute simultaneously, and produce without any toxic and harmful.
Embodiment
Below the specific embodiment of the present invention is described in detail, it should be understood that protection scope of the present invention is not by the restriction of embodiment.
Embodiment 1
A kind of sandy beach shell decorative plate, comprises basic unit, is attached to the binder layer on basic unit and outermost dope layer; Basic unit is 12mm glass magnesium plate;
The preparation method of above-mentioned sandy beach shell decorative plate, carries out in accordance with the following steps:
(1) coating is prepared;
1. prepare oyster shell whiting: take powder of natural shell as raw material, after cleaning, sterilising treatment, it is crushed to 120-300 order, after dry, obtain oyster shell whiting; Described sterilising method is moist heat sterilization, sterilizing 25min under 116 DEG C of conditions;
2. in pill tank, add 900 parts of water, when opening whipping appts, 70 parts of sodium polyacrylates, 80 parts of tripoly phosphate sodium STPPs and 90 parts of Sodium hexametaphosphate 99s are evenly spread in pill tank slowly, 15min is stirred when 2000r/min, slowly add 200 part of 300 order oyster shell whiting under agitation, and then add 25 parts of dimethyl silicone oils, 25 parts of whiterusss, stir 20min and make it fully dissolve, obtain mixed solution;
3. 75 parts of ethene-vinyl acetate copolymer emulsions are stirred when 2000r/min, evenly slowly add in the mixed solution of step 2. gained, stir 20min, more successively add 20 parts of water-white rosin, 30 parts of polyacrylic ester, 40 parts of urethane, 40 parts of dicyclohexyl phthalates and 60 parts of mill bases;
4. finally coating is obtained under agitation.
(2) manual print roll coating mode is adopted by paint in substrate surface.
(3) dry 40min under 70 DEG C of conditions, equilibrium water content.
Sandy beach shell decorative plate prepared by the present embodiment, has good thermotolerance, texture is good, pattern is changeable, its topcoating strong adhesion, and difficult drop-off, it may also be useful to the life-span is long, shortcoming is that snappiness is poor.
Embodiment 2
A kind of sandy beach shell decorative plate, comprises basic unit, is attached to the binder layer on basic unit and outermost dope layer; Basic unit is 12mm glass magnesium plate;
The preparation method of above-mentioned sandy beach shell decorative plate, carries out in accordance with the following steps:
(1) coating is prepared;
1. prepare oyster shell whiting: take powder of natural shell as raw material, after cleaning, sterilising treatment, it is crushed to 120-300 order, after dry, obtain oyster shell whiting; Described sterilising method is moist heat sterilization, sterilizing 25min under 116 DEG C of conditions;
2. in pill tank, add 800 parts of water, when opening whipping appts, 80 parts of sodium polyacrylates, 90 parts of tripoly phosphate sodium STPPs and 70 parts of Sodium hexametaphosphate 99s are evenly spread in pill tank slowly, 15min is stirred when 2000r/min, slowly add 200 part of 300 order oyster shell whiting under agitation, and then add 35 parts of tributyl phosphates, 15 parts of Zinic stearass, stir 20min and make it fully dissolve, obtain mixed solution;
3. 55 parts of ethene-vinyl acetate copolymer emulsions are stirred when 2000r/min, evenly slowly add in the mixed solution of step 2. gained, stir 20min, more successively add 10 parts of water-white rosin, 20 parts of polyacrylic ester, 20 parts of urethane, 30 parts of dicyclohexyl phthalates and 50 parts of mill bases;
4. finally coating is obtained under agitation.
(2) manual print roll coating mode is adopted by paint in substrate surface.
(3) dry 30min under 90 DEG C of conditions, equilibrium water content.
Sandy beach shell decorative plate prepared by the present embodiment, has good thermotolerance, texture is good, pattern is changeable, its topcoating strong adhesion, and difficult drop-off, it may also be useful to the life-span is long, shortcoming is that snappiness is poor.
Embodiment 3
A kind of sandy beach shell decorative plate, comprises basic unit, is attached to the binder layer on basic unit and outermost dope layer; Basic unit is 12mm glass magnesium plate;
The preparation method of above-mentioned sandy beach shell decorative plate, carries out in accordance with the following steps:
(1) coating is prepared;
1. prepare oyster shell whiting: take powder of natural shell as raw material, after cleaning, sterilising treatment, it is crushed to 120-300 order, after dry, obtain oyster shell whiting; Described sterilising method is moist heat sterilization, sterilizing 25min under 116 DEG C of conditions;
2. in pill tank, add 1000 parts of water, when opening whipping appts, 60 parts of sodium polyacrylates, 70 parts of tripoly phosphate sodium STPPs and 70 parts of Sodium hexametaphosphate 99s are evenly spread in pill tank slowly, 15min is stirred when 2000r/min, slowly add 200 part of 300 order oyster shell whiting under agitation, and then add 25 parts of polyoxyethylene nonylphenol ethers, 25 parts of vinyl acetic monomers, stir 20min and make it fully dissolve, obtain mixed solution;
3. 75 parts of ethene-vinyl acetate copolymer emulsions are stirred when 2000r/min, evenly slowly add in the mixed solution of step 2. gained, stir 20min, more successively add 20 parts of water-white rosin, 30 parts of polyacrylic ester, 40 parts of urethane, 40 parts of dicyclohexyl phthalates and 60 parts of mill bases;
4. finally coating is obtained under agitation.
(2) manual print roll coating mode is adopted by paint in substrate surface.
(3) dry 40min under 70 DEG C of conditions, equilibrium water content.
Sandy beach shell decorative plate prepared by the present embodiment, has good thermotolerance, texture is good, pattern is changeable, its topcoating strong adhesion, and difficult drop-off, it may also be useful to the life-span is long, shortcoming is that snappiness is poor.
Embodiment 4
A kind of sandy beach shell decorative plate, comprises basic unit, is attached to the binder layer on basic unit and outermost dope layer; Basic unit is 12mm glass magnesium plate;
The preparation method of above-mentioned sandy beach shell decorative plate, carries out in accordance with the following steps:
(1) coating is prepared;
1. prepare oyster shell whiting: taking powder of natural shell and cicada slough shell powder as raw material, mass ratio 10:1, through cleaning, after sterilising treatment, it is crushed to 120-300 order, after dry, obtains shell cicada slough powder; Described sterilising method is moist heat sterilization, sterilizing 25min under 116 DEG C of conditions;
2. in pill tank, add 900 parts of water, when opening whipping appts, 70 parts of sodium polyacrylates, 80 parts of tripoly phosphate sodium STPPs and 90 parts of Sodium hexametaphosphate 99s are evenly spread in pill tank slowly, 15min is stirred when 2000r/min, slowly add 200 part of 300 order shell cicada slough powder under agitation, and then add 25 parts of dimethyl silicone oils, 25 parts of whiterusss, stir 20min and make it fully dissolve, obtain mixed solution;
3. 75 parts of ethene-vinyl acetate copolymer emulsions are stirred when 2000r/min, evenly slowly add in the mixed solution of step 2. gained, stir 20min, more successively add 20 parts of water-white rosin, 30 parts of polyacrylic ester, 40 parts of urethane, 40 parts of dicyclohexyl phthalates and 60 parts of mill bases;
4. finally coating is obtained under agitation.
(2) manual print roll coating mode is adopted by paint in substrate surface.
(3) dry 40min under 70 DEG C of conditions, equilibrium water content.
Sandy beach shell decorative plate prepared by the present embodiment, has good thermotolerance, texture is good, pattern is changeable, and its topcoating strong adhesion, has good snappiness, difficult drop-off, it may also be useful to the life-span is long.
Comparative example 1
A kind of sandy beach shell decorative plate, comprises basic unit, is attached to the binder layer on basic unit and outermost dope layer; Basic unit is 12mm glass magnesium plate;
The preparation method of above-mentioned sandy beach shell decorative plate, carries out in accordance with the following steps:
(1) coating is prepared;
1. in pill tank, add 900 parts of water, when opening whipping appts, 70 parts of sodium polyacrylates, 80 parts of tripoly phosphate sodium STPPs and 90 parts of Sodium hexametaphosphate 99s are evenly spread in pill tank slowly, 15min is stirred when 2000r/min, then 25 parts of dimethyl silicone oils, 25 parts of whiterusss are added, stirring 20min makes it fully dissolve, and obtains mixed solution;
2. 75 parts of ethene-vinyl acetate copolymer emulsions are stirred when 2000r/min, evenly slowly add in the mixed solution of step 1. gained, stir 20min, more successively add 20 parts of water-white rosin, 30 parts of polyacrylic ester, 40 parts of urethane, 40 parts of dicyclohexyl phthalates and 60 parts of mill bases;
3. finally coating is obtained under agitation.
(2) manual print roll coating mode is adopted by paint in substrate surface.
(3) dry 40min under 70 DEG C of conditions, equilibrium water content.
Sandy beach shell decorative plate prepared by the present embodiment, snappiness is poor, texture is poor, its topcoating poor adhesion, and poor heat resistance, easily comes off, it may also be useful to the life-span is short.
Comparative example 2
A kind of sandy beach shell decorative plate, comprises basic unit, is attached to the binder layer on basic unit and outermost dope layer; Basic unit is 12mm glass magnesium plate;
The preparation method of above-mentioned sandy beach shell decorative plate, carries out in accordance with the following steps:
(1) coating is prepared;
1. prepare oyster shell whiting: take powder of natural shell as raw material, after cleaning, sterilising treatment, it is crushed to 120-300 order, after dry, obtain oyster shell whiting; Described sterilising method is moist heat sterilization, sterilizing 25min under 116 DEG C of conditions;
2. in pill tank, add 900 parts of water, when opening whipping appts, 70 parts of sodium polyacrylates, 80 parts of tripoly phosphate sodium STPPs and 90 parts of Sodium hexametaphosphate 99s are evenly spread in pill tank slowly, 15min is stirred when 2000r/min, slowly add 200 part of 300 order oyster shell whiting under agitation, and then add 25 parts of dimethyl silicone oils, 25 parts of whiterusss, stir 20min and make it fully dissolve, obtain mixed solution;
3. 20 parts of water-white rosin, 30 parts of polyacrylic ester, 40 parts of urethane, 40 parts of dicyclohexyl phthalates and 60 parts of mill bases are added;
4. finally coating is obtained under agitation.
(2) manual print roll coating mode is adopted by paint in substrate surface.
(3) dry 40min under 70 DEG C of conditions, equilibrium water content.
Sandy beach shell decorative plate prepared by the present embodiment, snappiness is poor, texture is poor, its topcoating poor adhesion, and poor heat resistance, easily comes off, it may also be useful to the life-span is short.
Specific embodiments of the invention it are only disclosed in above, but, the present invention is not limited thereto, and the changes that any person skilled in the art can think of all should fall into protection scope of the present invention.
Claims (9)
1. a sandy beach shell decorative plate, it is characterised in that, described sandy beach shell decorative plate comprises basic unit, is attached to the binder layer on basic unit and outermost dope layer.
2. a kind of sandy beach according to claim 1 shell decorative plate, it is characterised in that, described basic unit is glass magnesium plate or aluminosulfate cement plate.
3. a kind of sandy beach according to claim 1 shell decorative plate, it is characterized in that, described dope layer is made up of the raw material of following weight: oyster shell whiting 200 parts, sodium polyacrylate 60-90 part, tripoly phosphate sodium STPP 70-90 part, Sodium hexametaphosphate 99 70-90 part, defoamer 15-45 part, anti-settling agent 15-45 part, ethene-vinyl acetate copolymer emulsion 55-75 part, water-white rosin 10-50 part, polyacrylic ester 20-40 part, urethane 20-40 part, dicyclohexyl phthalate 20-40 part and mill base 40-70 part.
4. the preparation method of sandy beach according to claim 1 shell decorative plate, it is characterised in that, carry out in accordance with the following steps:
(1) coating is prepared;
(2) by paint in substrate surface;
(3) dry, equilibrium water content.
5. the preparation method of a kind of sandy beach according to claim 4 shell decorative plate, it is characterised in that, the method that described step (1) prepares coating carries out in accordance with the following steps:
1. prepare oyster shell whiting: take powder of natural shell as raw material, after cleaning, sterilising treatment, it is crushed to 120-300 order, after dry, obtain oyster shell whiting;
2. according to weight part number, 800-1000 part water is added in pill tank, when opening whipping appts, 60-90 part sodium polyacrylate, 70-90 part tripoly phosphate sodium STPP and 70-90 part Sodium hexametaphosphate 99 are evenly spread in pill tank slowly, slowly add 200 parts of oyster shell whitings under agitation, and then add 15-45 part defoamer, 15-45 part anti-settling agent, stir and make it fully dissolve, obtain mixed solution;
3. by 55-75 part ethene-vinyl acetate copolymer emulsion under agitation, evenly slowly add in the mixed solution of step 2. gained, more successively add 10-50 part water-white rosin, 20-40 part polyacrylic ester, 20-40 part urethane, 20-40 part dicyclohexyl phthalate and 40-70 part mill base;
4. finally coating is obtained under agitation.
6. the preparation method of a kind of sandy beach according to claim 5 shell decorative plate, it is characterised in that, described step sterilising method 1. is moist heat sterilization, sterilizing 20-30min under 116 DEG C of conditions.
7. the preparation method of a kind of sandy beach according to claim 5 shell decorative plate, it is characterised in that, described step 1.-4. stir for stir 10-20min when rotating speed 1000-2000r/min.
8. the preparation method of a kind of sandy beach according to claim 4 shell decorative plate, it is characterised in that, described step (2) paint is manual print roll coating mode in the mode of substrate surface.
9. the preparation method of a kind of sandy beach according to claim 4 shell decorative plate, it is characterised in that, described step (3) drying means is dry 20-50min under 40-100 DEG C of condition.