CN105618145B - 一种三[三(间‑磺酸钠苯基)膦]氯化铑催化剂的制备方法 - Google Patents
一种三[三(间‑磺酸钠苯基)膦]氯化铑催化剂的制备方法 Download PDFInfo
- Publication number
- CN105618145B CN105618145B CN201410643580.6A CN201410643580A CN105618145B CN 105618145 B CN105618145 B CN 105618145B CN 201410643580 A CN201410643580 A CN 201410643580A CN 105618145 B CN105618145 B CN 105618145B
- Authority
- CN
- China
- Prior art keywords
- phosphine
- sodium sulfonate
- sulfonate phenyl
- rhodium catalyst
- water solubility
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明属于催化剂制备技术领域,为一种三[三(间‑磺酸钠苯基)膦]氯化铑催化剂的制备方法,该方法如下:在氮气保护下,将抗坏血酸盐与铑氯化物混溶于无水醇中,在60℃~100℃下,加入到三(间‑磺酸钠苯基)膦的水溶液中反应0.5小时~2小时。反应完成后,在反应液中加入醇沉淀,分离回收目标催化剂三[三(间‑磺酸钠苯基)膦]氯化铑。本发明的优点:该方法具有原料易得、配体三(间‑磺酸钠苯基)膦用量少、制备过程简单、产品收率高、质量好的优点。催化剂可应用于氢甲酰化反应,同样也应用于加氢、碳‑碳偶联反应中。
Description
技术领域
本发明属于催化剂制备技术领域,涉及一种三[三(间-磺酸钠苯基)膦]氯化铑催化剂的制备方法,本发明除了应用于水-有机两相的烯烃氢甲酰化反应外,还适用于水-有机两相的加氢反应、碳-碳偶联反应。
技术背景
烯烃氢甲酰化反应是烯烃与合成气在催化剂催化作用下生成多一个碳的醛的反应,由此生成的醛经过缩合加氢生成的醇被广泛应用于增塑剂领域。水-有机两相烯烃氢甲酰化反应(B.Cornils,W.A.Herrmann(Eds.),Aqueous-Phase OrganometalllicCatalysis,2nd ed.,Wiley-VCH,Weinheim,2004)通过简单的液-液分离就可解决含催化剂的水相与产物有机相的分离,实现水溶性催化剂的循环利用,能耗大幅度降低。三[三(间-磺酸钠苯基)膦]氯化铑是水-有机两相体系中烯烃氢甲酰化反应制备醛的一种催化剂,具有良好的催化活性和选择性。目前,该催化剂制备的原料大致分为简单的铑氯化物与油溶性含氯的铑配合物。如Marcetta York Darensbourg(Ed.),Inorganic Syntheses,Volume32,pp.40-42,John Wiley&Sons,Inc.,1998中所述三[三(间-磺酸钠苯基)膦]氯化铑催化剂的制备方法,当采用RhCl3·3H2O为原料与三(间-磺酸钠苯基)膦(TPPTS)反应制备时,将10倍于RhCl3·3H2O摩尔的TPPTS的水溶液滴加至RhCl3·3H2O的溶液中,搅拌3小时,然后用硅胶柱色谱(Sephadex G-15)进行分离得目标催化剂。该制备方法虽然简单,但TPPTS用量大,其与Rh的摩尔比高达10,导致成本高的TPPTS浪费严重,特别在工业化制备中,造成合成成本高;此同时,反应时间较长达3小时,后续分离操作复杂,尽管这样,收率仅73%。而当以ClRh[P(C6H5)3]3配合物为原料制备时,其具体的操作为,将30倍于ClRh[P(C6H5)3]3摩尔的TPPTS水溶液加入到ClRh[P(C6H5)3]3的甲苯和四氢呋喃混合溶剂中,强烈搅拌12小时,目标催化剂在水/有机两相中经配体TPPTS与三苯基膦交换而制得,分离水相,二氯甲烷洗涤两次,再经硅胶柱色谱(Sephadex G-15)进行分离得目标催化剂,收率82%。同样当以[RhCl(η4-C8H12)]2为原料时,操作为将3倍于铑摩尔的TPPTS水溶液加入到[RhCl(η4-C8H12)]2的二氯甲烷溶剂中,强烈搅拌30分钟,分离水相,有机相用水萃取两次,合并的水相以二氯甲烷洗涤两次,在10-2torr真空下除水,再经硅胶柱色谱(Sephadex G-15)分离得目标催化剂,收率93%。此外,2004年,黄俊在文献(Catal.Lett.98(4):225-228,2004)中提及了该催化剂的制备,采用6倍于Rh2(CO)4Cl2摩尔的TPPTS与其交换来制备水溶性三[三(间-磺酸钠苯基)膦]氯化铑催化剂,但未见其收率的报道。以油溶性含氯的铑配合物为原料制备水溶性三[三(间-磺酸钠苯基)膦]氯化铑催化剂存在如下不足,配体交换反应时间长(如第二种制备方法为12小时),采用了对环境有害的有机溶剂,整个过程分两步进行,后续分离操作复杂。以上油溶性含氯的铑配合物都是先用RhCl3·3H2O制备的,且制备过程复杂。
中国专利CN101053843A公开了一种用于双环戊二烯氢甲醛化制醛的水溶性配体铑配合催化剂,该催化剂由活性组分、助剂、水溶性配体以及相转移剂四部分组成,活性组分是铑的水溶性盐,助剂是钴或锰水溶性盐,水溶性配体是三苯基膦三间磺酸钠(TPPTS),相转移剂是十六烷基三甲基溴化铵(CTAB),活性组分Rh3+的浓度为5.0×10-4M~4.0×10- 3M,助剂Co2+或Mn2+与Rh3+的摩尔比为0.2~1。该催化剂的制备方法简单,催化剂易于反应产物分离且可重复使用,助剂的加入大大提高了催化剂的选择性,该催化剂还可用于通过烯烃氢甲醛化制取碳原子数增加一个的各类醛。
中国专利CN102351913A公开了一种三[三(3-磺酸钠基苯基)膦]氯化铑的制备方法,其特征在于:将三(3-磺酸钠基苯基)膦水溶液加入到已置换成氮气氛围的水合六氯铑酸钠醇溶液中,将反应液加热到70-90℃,保持1-2小时,反应液冷却后分离回收物;所述醇选自乙醇、1-丙醇、2-丙醇;所述水合六氯铑酸钠醇溶液的摩尔浓度为0.1-1.0mol/L,三(3-磺酸钠基苯基)膦水溶液的摩尔浓度为1.0-2.0mol/L,三(3-磺酸钠基苯基)膦与水合六氯铑酸钠的摩尔比为:6-12。
该专利提供的方法使得由铑粉制备三[三(3-磺酸钠基苯基)膦]氯化铑的过程不需要经过水合三氯化铑的中间步骤,整个操作过程更为简单,更具经济效益。使用水合六氯铑酸钠作为原料,反应条件温和,生成的氯化钠副产物能够提高反应液的离子强度,使产物从反应液中析出更完全,反应收率更高。三[三(3-磺酸钠基苯基)膦]氯化铑经分析检测各项指标均达到使用要求。
中国专利CN1272485A公开了一种醛的制备方法,该方法包括在烯烃氢甲酰化制备醛的工艺条件下,在水和水溶性铑络合物催化剂存在的液相中,将烯烃与一氧化碳和氢气接触,反应体系中还含有外加的水溶性膦配体,一种浓度为5×10-4~6×10-2摩尔/升的水溶性磷酸盐和/或亚磷酸盐和浓度为1×10-4~9×10-3摩尔/升的增溶剂。该方法同时公开了一种铑络合物催化剂,其可以采用如下方法制备:以铑的卤化物或铑的卤化物的水合物、三(间磺酸盐苯基)膦、二(间磺酸盐苯基)苯基膦或三(间磺酸盐苯基)膦及二(间磺酸盐苯基)苯基膦为原料,先将铑的卤化物溶于醇中,将铑的卤化物的醇溶液加入反应釜中,用惰性气体置换瓶中的空气,然后,充入一氧化碳气氛。将三(间磺酸盐苯基)膦、二(间磺酸盐苯基)苯基膦或三(间磺酸盐苯基)膦及二(间磺酸盐苯基)苯基膦溶于脱氧蒸馏水中,将该溶液滴加到反应釜中,在60~90℃,搅拌反应1~3小时,冷却至室温,加入无水乙醇即生成沉淀物。用醇洗涤生成的沉淀物至pH=5~7在70~90℃,103~104帕的压力下干燥,得到铑络合物催化剂。其中,加入的三(间磺酸盐苯基)膦、二(间磺酸盐苯基)苯基膦或三(间磺酸盐苯基)膦及二(间磺酸盐苯基)苯基膦与铑的摩尔比为1~5,优选为1~3,一氧化碳的压力为常压~0.2兆帕,优选为常压~0.1兆帕。铑的化合物可以是氯化铑或其水合物。所述三(间磺酸盐苯基)膦优选TPPTS。所述二(间磺酸盐苯基)苯基膦优选TPPDS。所述醇可以是各种液体醇中的一种或几种,优选乙醇。所述惰性气体可以是氮气、氦气、氖气、氩气中的一种或几种,优选为氮气。
以上专利均存在的不足之处是没有能够解决通过还原剂的替代降低生产成本,并且提高所制得催化剂的收率。所以,存在成本较高、反应效率较低、收率较低的缺点。
发明内容
本发明的技术方案是为了克服现有技术中存在的不足,如以铑氯化物为铑源制备水溶性三[三(间-磺酸钠苯基)膦]氯化铑催化剂,方法虽然简单,但制备过程中PPTS与Rh的摩尔比高达10,TPPTS用量大,导致TPPTS浪费严重,特别在工业化制备中会造成催化剂制备成本较高;同时,后续分离操作复杂,尽管这样,收率仅73%。以油溶性含氯的铑配合物为铑源经配体交换制备时,存在如下不足,配体交换反应时间有时较长,如采用ClRh[P(C6H5)3]3为铑源时,其交换时间长达12小时。此外,该类制备方法都采用对环境有害的有机溶剂,整个过程分两步进行,后续分离操作复杂。以上油溶性含氯的铑配合物都是先用RhCl3·3H2O制备的,且制备过程更为复杂。本发明涉及一种三[三(间-磺酸钠苯基)膦]氯化铑催化剂的制备方法,主要解决现有制备技术中存在的原料三(间-磺酸钠苯基)膦用量大、反应时间长、步骤多、收率低和分离操作复杂等技术问题。提出了一种三[三(间-磺酸钠苯基)膦]氯化铑催化剂的制备方法,该方法以简单的铑氯化物为铑源,采用价廉易得的有机还原剂抗坏血酸(锂、钠、钾、铵盐)替代价格昂贵的三(间-磺酸钠苯基)膦还原三价铑为一价铑,从而减少水溶性三[三(间-磺酸钠苯基)膦]氯化铑催化剂制备过程中配体TPPTS的使用量,不使用对环境有害的有机溶剂。
本发明的技术方案:
一种水溶性三[三(间-磺酸钠苯基)膦]氯化铑催化剂的制备方法,该方法包括如下步骤:
向容器中通入惰性气体进行保护;
将三(间-磺酸钠苯基)膦溶于纯水中配成水溶液,加入所述容器中,反应温度为60℃~100℃;
将抗坏血酸盐与铑氯化物混溶于无水醇中,加入三(间-磺酸钠苯基)膦的水溶液中反应,保持温度60℃~100℃;
反应完成后,加入醇沉淀、分离、回收得到三[三(间-磺酸钠苯基)膦]氯化铑催化剂。
该制备方法还包括向容器内滴加无水乙醇,析出棕红色沉淀的步骤。
该方法所述反应时间为0.5小时~2小时,溶液成棕红色,停止加热。
将回收得到的固体置于真空烘箱中于70℃减压下干燥至恒重,得棕红色的产物为三[三(间-磺酸钠苯基)膦]氯化铑催化剂。
所述的抗坏血酸盐的用量,占总反应物重量的1%~20%。
所述的抗坏血酸盐可以是抗坏血酸锂、抗坏血酸钠、抗坏血酸钾或抗坏血酸铵。
所述的三(间-磺酸钠苯基)膦与铑的摩尔比为3~8。
所述的铑氯化物混溶于无水醇中的醇溶液的浓度为0.08摩尔/升~0.8摩尔/升。
所述的抗坏血酸盐混溶于无水醇中的醇溶液的浓度为0.1摩尔/升~1.0摩尔/升。
所述的三(间-磺酸钠苯基)膦的水溶液的浓度为0.2~1.6摩尔/升。
所述的反应温度为78℃~90℃;
所述的回流反应时间为1小时。
所述的醇为甲醇、乙醇、丙醇、丁醇及其混合溶剂中的任意一种。
所述惰性气体为氮体。
本发明的有益效果:
本发明主要解决现有制备技术中存在的原料三(间-磺酸钠苯基)膦用量大、反应时间长、步骤多、收率低和分离操作复杂等技术问题。本发明是以简单的铑氯化物为铑源,采用价廉易得的有机还原剂抗坏血酸(锂、钠、钾、铵盐)替代价格昂贵的三(间-磺酸钠苯基)膦还原三价铑为一价铑,从而减少水溶性三[三(间-磺酸钠苯基)膦]氯化铑催化剂制备过程中配体TPPTS的使用量,不使用对环境有害的有机溶剂。本发明包括在氮气保护下,将抗坏血酸(盐)与铑氯化物混溶于无水醇中,在60~100℃下,加入到三(间-磺酸钠苯基)膦的水溶液中反应30~120分钟。反应完成后,在反应液中加入醇沉淀,分离回收目标催化剂三[三(间-磺酸钠苯基)膦]氯化铑。该方法具有原料易得、配体三(间-磺酸钠苯基)膦用量少、制备过程简单、产品收率高、质量好的优点。催化剂可应用于氢甲酰化反应,同样也应用于加氢、碳-碳偶联反应中。
本发明结果表明,配体TPPTS用量少、反应时间短、收率高,制备过程简单。是对水溶性三[三(间-磺酸钠苯基)膦]氯化铑催化剂制备方法的进一步发展,为该催化剂的工业化应用奠定了基础。
附图说明
本说明书共有1幅附图。
图1.为本发明的流程图。
具体实施方式
下面结合附图对本发明的实施例作进一步描述。
本发明的方法如图1所示,向容器中通入惰性气体进行保护,本方法具体采用通入氮气进行保护,将抗坏血酸(钠盐)与铑氯化物混溶于无水醇中,在一定温度下加入到三(间-磺酸钠苯基)膦的水溶液中反应一定时间,反应完成后,在反应液中加入醇沉淀,分离回收产物三[三(间-磺酸钠苯基)膦]氯化铑。
本发明的特征在于,在反应体系中加入占总反应物重量1%~20%的抗坏血酸(盐),优选6%~12%;反应体系中三(间-磺酸钠苯基)膦与铑的摩尔比3~8,优选为3~4;反应温度60℃~100℃,优选为80℃~90℃;反应时间30分钟~120分钟,优选为45分钟~60分钟。
所述铑氯化物的醇溶液或三(间-磺酸钠苯基)膦的水溶液的浓度可以在较稀的溶液至其饱和溶液的范围内变动,但若溶液太稀时,所使用沉淀溶剂醇的量太大,因此,铑氯化物的醇溶液的浓度优选为0.08摩尔/升~0.8摩尔/升;三(间-磺酸钠苯基)膦的水溶液的浓度优选为0.2摩尔/升~1.6摩尔/升;抗坏血酸(盐)的醇溶液的浓度优选为0.1摩尔/升~1.0摩尔/升。
所述醇为甲醇、乙醇、丙醇和丁醇或其混合物,优选为乙醇。加入乙醇,沉淀出所需催化剂产品,抽滤,洗涤、滤饼在70℃下真空干燥3小时~4小时即得催化剂产品。体系中加入的抗坏血酸(钠盐)在抽滤过程中进入母液而与催化剂产品分离。
采用本发明制备出的水溶性催化剂三[三(间-磺酸钠苯基)膦]氯化铑中铑含量在4.8%~5.4%,催化剂产品收率84%~95%。
本发明所涉及的三[三(间-磺酸钠苯基)膦]氯化铑催化剂的制备方法的具体步骤如下:
第一步:向容器中通入惰性气体进行保护;
第二步:配置TPPS溶液;
第三步:加热;
第四步:向容器中加入抗坏血酸盐与铑氯化物混合溶液;
第五步:保温;
第六步:沉淀、分离、干燥,得到产品。
实施例1
向150毫升装有电磁搅拌,温度计,回流冷疑管和恒压滴液漏斗的三颈圆底烧瓶中通人氮气进行保护;
将7.0gTPPTS溶于10毫升纯水配成的溶液加入三颈圆底烧瓶中,加热至90℃;
然后,将0.5克RhCl3·3H2O(化学纯,铑含量41.72%)和0.15克抗坏血酸(钠盐)溶于10毫升无水乙醇的溶液通过恒压滴液漏斗加入圆底烧瓶中,保持温度90℃;
回流反应1小时,溶液成棕红色,停止加热;
滴加约50毫升无水乙醇,析出棕红色沉淀,过滤,滤饼用乙醇洗涤得到棕红色固体;
将固体催化剂置于真空烘箱中于70℃减压下干燥至恒重,得棕红色催化剂4.3克,收率95%。
实施例2
向150毫升装有电磁搅拌,温度计,回流冷疑管和恒压滴液漏斗的三颈圆底烧瓶中通人氮气进行保护;
将7.0gTPPTS溶于10毫升纯水配成的溶液加入三颈圆底烧瓶中,加热至82℃;
然后,将0.5克RhCl3·3H2O(化学纯,铑含量41.72%)和0.15克抗坏血酸(钠盐)溶于10毫升无水乙醇的溶液通过恒压滴液漏斗加入圆底烧瓶中,保持温度82℃;
回流反应1小时,溶液成棕红色,停止加热;
滴加约50毫升无水乙醇,析出棕红色沉淀,过滤,滤饼用乙醇洗涤得到棕红色固体;
将固体催化剂置于真空烘箱中于70℃减压下干燥至恒重,得棕红色催化剂4.3克,收率95%。
实施例3
向150毫升装有电磁搅拌,温度计,回流冷疑管和恒压滴液漏斗的三颈圆底烧瓶中通人氮气进行保护;
将4.0gTPPTS溶于5毫升纯水配成的溶液加入三颈圆底烧瓶中,加热至78℃;
然后,将0.5克RhCl3·3H2O(化学纯,铑含量41.72%)和0.45克抗坏血酸(钠盐)溶于10毫升无水乙醇的溶液通过恒压滴液漏斗加入圆底烧瓶中,保持温度78℃;
反应1小时,溶液成棕红色,停止加热;
滴加约40毫升无水乙醇,析出棕红色沉淀,过滤,滤饼用乙醇洗涤得到棕红色固体;
将固体催化剂置于真空烘箱中于70℃减压下干燥至恒重,得棕红色催化剂3.8克,收率95%。
实施例4
向150毫升装有电磁搅拌,温度计,回流冷疑管和恒压滴液漏斗的三颈圆底烧瓶中通人氮气进行保护;
将5.5gTPPTS溶于8毫升纯水配成的溶液加入三颈圆底烧瓶中,加热至65℃;
然后,将0.5克RhCl3·3H2O(化学纯,铑含量41.72%)和0.3克抗坏血酸(钠盐)溶于10毫升无水乙醇的溶液通过恒压滴液漏斗加入圆底烧瓶中,保持温度65℃;
反应2小时,溶液成棕红色,停止加热;
滴加约50毫升无水乙醇,析出棕红色沉淀,过滤,滤饼用乙醇洗涤得到棕红色固体;
将固体催化剂置于真空烘箱中于70℃减压下干燥至恒重,得棕红色催化剂4.1克,收率86%。
实施例5
向250毫升装有电磁搅拌,温度计,回流冷疑管和恒压滴液漏斗的三颈圆底烧瓶中通人氮气进行保护;
将12g TPPTS溶于15毫升纯水配成的溶液加入三颈圆底烧瓶中,加热至70℃;
然后,将1.0克RhCl3·3H2O(化学纯,铑含量41.72%)和2克抗坏血酸(钠盐)溶于10毫升无水甲醇的溶液通过恒压滴液漏斗加入圆底烧瓶中,保持温度70℃;
继续反应45分钟,溶液成棕红色,停止加热;
滴加约150毫升无水甲醇,析出棕红色沉淀,过滤,滤饼用甲醇洗涤得到棕红色固体;
将固体催化剂置于真空烘箱中于70℃减压下干燥至恒重,得棕红色催化剂8.1克,收率89%。
实施例6
向150毫升装有电磁搅拌,温度计,回流冷疑管和恒压滴液漏斗的三颈圆底烧瓶中通人氮气进行保护;
将5.5gTPPTS溶于8毫升纯水配成的溶液加入三颈圆底烧瓶中,加热至60℃;
然后,将0.5克RhCl3·3H2O(化学纯,铑含量41.72%)和0.3克抗坏血酸(钠盐)溶于10毫升无水乙醇的溶液通过恒压滴液漏斗加入圆底烧瓶中,保持温度60℃;
反应2小时,溶液成棕红色,停止加热;
滴加约50毫升无水乙醇,析出棕红色沉淀,过滤,滤饼用乙醇洗涤得到棕红色固体;
将固体催化剂置于真空烘箱中于70℃减压下干燥至恒重,得棕红色催化剂4.0克,收率83%。
实施例7
向150毫升装有电磁搅拌,温度计,回流冷疑管和恒压滴液漏斗的三颈圆底烧瓶中通人氮气进行保护;
将4.0gTPPTS溶于5毫升纯水配成的溶液加入三颈圆底烧瓶中,加热至85℃;
然后,将0.5克RhCl3·3H2O(化学纯,铑含量41.72%)和0.45克抗坏血酸(钠盐)溶于10毫升无水乙醇的溶液通过恒压滴液漏斗加入圆底烧瓶中,保持温度85℃;
反应1小时,溶液成棕红色,停止加热;
滴加约40毫升无水乙醇,析出棕红色沉淀,过滤,滤饼用乙醇洗涤得到棕红色固体;
将固体催化剂置于真空烘箱中于70℃减压下干燥至恒重,得棕红色催化剂3.5克,收率95%。
以上所述实施例仅是为说明本发明而所举的较佳的实施例,本发明的保护范围不限于此。本技术领域的技术人员在本发明基础上所做出的等同替代或变换,均在本发明的保护范围之内。本发明的保护范围以权利要求书为准。
Claims (12)
1.一种水溶性三[三(间-磺酸钠苯基)膦]氯化铑催化剂的制备方法,其特点在于:该方法包括如下步骤:
向容器中通入惰性气氛进行保护;
将三(间-磺酸钠苯基)膦溶于纯水中配成水溶液,加入所述容器中,反应温度为60℃~100℃;
将抗坏血酸盐与铑氯化物混溶于无水醇中,加入三(间-磺酸钠苯基)膦的水溶液中反应,保持温度60℃~100℃;
反应完成后,加入醇沉淀、分离、回收得到三[三(间-磺酸钠苯基)膦]氯化铑催化剂;
其中,所述反应时间为0.5小时~2小时,溶液成棕红色,停止加热;所述的抗坏血酸盐的用量,占总反应物重量的1%~20%。
2.根据权利要求1所述的一种水溶性三[三(间-磺酸钠苯基)膦]氯化铑催化剂的制备方法,其特征在于;还包括向容器内滴加无水乙醇,析出棕红色沉淀的步骤。
3.根据权利要求1所述的一种水溶性三[三(间-磺酸钠苯基)膦]氯化铑催化剂的制备方法,其特征在于;将回收得到的固体置于真空烘箱中于70℃减压下干燥至恒重,得棕红色的产物为三[三(间-磺酸钠苯基)膦]氯化铑催化剂。
4.根据权利要求1所述的一种水溶性三[三(间-磺酸钠苯基)膦]氯化铑催化剂的制备方法,其特征在于:所述的抗坏血酸盐可以是抗坏血酸锂、抗坏血酸钠、抗坏血酸钾或抗坏血酸铵。
5.根据权利要求1所述的一种水溶性三[三(间-磺酸钠苯基)膦]氯化铑催化剂的制备方法,其特征在于:所述的三(间-磺酸钠苯基)膦与铑的摩尔比为3~8。
6.根据权利要求1所述的一种水溶性三[三(间-磺酸钠苯基)膦]氯化铑催化剂的制备方法,其特征在于:所述的铑氯化物混溶于无水醇中的醇溶液的浓度为0.08摩尔/升~0.8摩尔/升。
7.根据权利要求1所述的一种水溶性三[三(间-磺酸钠苯基)膦]氯化铑催化剂的制备方法,其特征在于:所述的抗坏血酸盐混溶于无水醇中的醇溶液的浓度为0.1摩尔/升~1.0摩尔/升。
8.根据权利要求1所述的一种水溶性三[三(间-磺酸钠苯基)膦]氯化铑催化剂的制备方法,其特征在于:所述的三(间-磺酸钠苯基)膦的水溶液的浓度为0.2 ~1.6摩尔/升。
9.根据权利要求1所述的一种水溶性三[三(间-磺酸钠苯基)膦]氯化铑催化剂的制备方法,其特征在于:所述的反应温度为78℃~90℃。
10.根据权利要求1所述的一种水溶性三[三(间-磺酸钠苯基)膦]氯化铑催化剂的制备方法,其特征在于:所述的反应时间为1小时。
11.根据权利要求1所述的一种水溶性三[三(间-磺酸钠苯基)膦]氯化铑催化剂的制备方法,其特征在于:所述无水醇和加入醇沉淀中的醇皆为甲醇、乙醇、丙醇、丁醇及其混合溶剂中的任意一种。
12.根据权利要求1所述的一种水溶性三[三(间-磺酸钠苯基)膦]氯化铑催化剂的制备方法,其特征在于,所述惰性气氛为氮气。