CN105602358A - Interior wall latex paint - Google Patents
Interior wall latex paint Download PDFInfo
- Publication number
- CN105602358A CN105602358A CN201410615245.5A CN201410615245A CN105602358A CN 105602358 A CN105602358 A CN 105602358A CN 201410615245 A CN201410615245 A CN 201410615245A CN 105602358 A CN105602358 A CN 105602358A
- Authority
- CN
- China
- Prior art keywords
- parts
- latex paint
- wall latex
- interiro wall
- water
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to an interior wall latex paint, which comprises the following raw materials by weight: 20-30 parts of a styrene-butyl acrylate emulsion, 15-25 parts of an epoxy resin, 5-10 parts of anatase type titanium dioxide, 10-15 parts of barium sulfate, 5-8 parts of bentonite, 0.01-0.05 part of ethanol, 0.5-1 part of hydroxyethyl cellulose, and 10-20 parts of water, wherein all raw materials are subjected to mixing stirring so as to obtain the interior wall latex paint finished product. According to the present invention, the interior wall latex paint has good covering function, is an economic coating material for protecting and beautifying the indoor wall surface, is suitable for coating of indoor wall surfaces, garages, mezzanines, ceilings and other places, and has characteristics of economy, practicality, good whiteness, smooth and delicate paint film, low production cost, and strong promotion and application value.
Description
Technical field
The present invention relates to paint field, relate in particular to a kind of interiro wall latex paint.
Background technology
Emulsion paint is being commonly called as of latex paint, is born in the next period in nineteen seventies, is the large class synthetic resin emulsion coating taking acrylate copolymer emulsion as representative. Emulsion paint is water-dispersible paint, and it is taking synthetic resin emulsion as base-material, and filler adds the refining coating forming of various auxiliary agents after grinding distribution. Emulsion paint has possessed the many merits different from traditional wall covering, as be easy to brushing, dry rapidly, paint film is water-fast, scrub resistance is good etc. In China, people are base-material synthetic resin emulsion traditionally, taking water as decentralized medium, add pigment, filler (also claiming extender pigment) and auxiliary agent, and the coating of making through certain technical process, is called emulsion paint, is also latex paint.
Interiro wall latex paint is one of the most general ornament materials of current house fitting application, and it has many advantages such as easy construction, strong covering power, rich color, scrubbing resistance, and collocation of colour is proper, quality is guaranteed, and can provide a warm environment to family. Water-soluble interiro wall latex paint is pollution-free, nontoxic, without disaster hidden-trouble, be easy to brushing, dry paint film is water-fast, scrub resistance good rapidly, color is soft. Water-soluble interiro wall latex paint, using water as decentralized medium, the problem of environmental pollution that organic solvent-free poisonous gas brings, good permeability, has avoided the film foaming disadvantage that causes because of film internal and external temperature pressure differential, is applicable to undried new metope application. Solvent-borne type interiro wall latex paint, taking high molecular synthetic resin as main film forming substance, must be with an organic solvent diluent, for this coating, certain pigment, filler and auxiliary agent are made through mixed grinding, be a kind of volatile paint, it is high that the water-soluble interiro wall latex paint of cost ratio and water soluble paint are wanted. This type of coating uses flammable solvent in construction, easily to cause fire, in the time of low-temperature construction, performance is better than water-soluble interiro wall latex paint and water soluble paint, there are good weatherability and stain resistance, have good thickness, gloss, resistance to water, alkali resistance, but the easy peeling of constructing bubbles, comes off etc. in moist basic unit.
In existing interiro wall latex paint, high and low shelves are of a great variety, and high-grade price is higher, use cost is high, and low-grade serviceability is poor, are unfavorable for construction. Therefore, need a kind of economical and practical, dependable performance of exploitation badly, be easy to the interiro wall latex paint promoted.
Summary of the invention
For the problems referred to above, the invention provides a kind of interiro wall latex paint, this emulsion paint has good covering function, economical and practical, whiteness good, be easy to promote.
For realizing above-mentioned purpose of the present invention, the invention provides a kind of interiro wall latex paint, formed by the raw material of following parts by weight: Styrene And Butyl-acrylate emulsion 20-30 part, epoxy resin 15-25 part, sharp titanium white 5-10 part, barium sulfate 10-15 part, bentonite 5-8 part, ethanol 0.01-0.05 part, hydroxyethylcellulose 0.5-1 part, water 10-20 part.
After all raw material mix and blends, obtain described interiro wall latex paint finished product.
Described interiro wall latex paint adopts roller coat, brushing or spraying method to construct.
Described interiro wall latex paint can not be at temperature lower than 5 DEG C, relative humidity is greater than under 85% environment constructs.
Described interiro wall latex paint should stir before using, for reaching the best brushing effects that is coated with, when roller coat, brush application, can use according to actual conditions no more than 20% clear water dilution, if use spraying, can use according to actual conditions no more than 10% clear water dilution, excessive being watered can not increase effective brushing area.
In room temperature (23 ± 2) DEG C, under the mensuration environment of relative humidity (50 ± 5) %, the surface drying time of described interiro wall latex paint is 30 minutes, and dry-hard time is 60 minutes.
The preparation method of described interiro wall latex paint: add water at stirred tank, then add 1000 turn/min after ethanol, hydroxyethylcellulose to disperse; After adding sharp titanium white, barium sulfate, bentonite, 1500 turn/min disperse again; Finally turn 600 turn/min and add Styrene And Butyl-acrylate emulsion, epoxy resin to stir, to obtain final product.
In the time that reality is used, the interior wall primer of first brushing one time, then brush described interiro wall latex paint twice; Every at least 2 hours time intervals all over brushing.
Compared with prior art beneficial effect of the present invention.
Interiro wall latex paint provided by the invention; there is the interiro wall latex paint of better covering function; protection and the economical coating that beautifies indoor wall; be applicable to the application that indoor wall, garage, interlayer, ceiling etc. are located; and economical and practical, whiteness good, paint film is moist, production cost is low, has stronger popularization and using value.
Detailed description of the invention
Embodiment 1.
The present embodiment provides a kind of interiro wall latex paint, is made up of the raw material of following parts by weight: 25 parts of Styrene And Butyl-acrylate emulsions, 21 parts of epoxy resin, 8 parts of sharp titanium whites (BA01-01), 12 parts, barium sulfate, 6.5 parts of bentonites, 0.03 part of ethanol, 0.85 part of hydroxyethylcellulose, 16 parts, water.
After all raw material mix and blends, obtain described interiro wall latex paint finished product.
Described interiro wall latex paint adopts roller coat, brushing or spraying method to construct.
Described interiro wall latex paint should stir before using, for reaching the best brushing effects that is coated with, when roller coat, brush application, can use according to actual conditions no more than 20% clear water dilution, if use spraying, can use according to actual conditions no more than 10% clear water dilution, excessive being watered can not increase effective brushing area.
Described interiro wall latex paint can not be at temperature lower than 5 DEG C, relative humidity is greater than under 85% environment constructs.
In the time of actual use procedure, twice of first wall primer one time in brushing, then brushing interiro wall latex paint of the present invention; In every at least 2 hours time intervals all over brushing, the in the situation that too high or temperature being too low in humidity, answer the time interval of proper extension brushing.
Described barium sulfate is white unformed powder, and stable in properties is added in the middle of coating can be used as extender pigment aspect coating, can improve the performance such as covering, compactness of paint film, in the performance that to a certain degree improves coating.
Described hydroxyethylcellulose (HEC), a kind of white or faint yellow, tasteless, nontoxic fibrous or pulverulent solids, is prepared through etherification reaction by alkali cellulose and oxirane (or chlorethanol), belongs to nonionic soluble fibre element ethers. There is good thickening, suspension, dispersion, emulsification, bonding, film forming, protection moisture and the characteristics such as protecting colloid are provided. Hydroxyethylcellulose, as a kind of surfactant of nonionic, also has following character: HEC and dissolves in hot water or cold water, and high temperature or boil does not precipitate, and makes it have large-scale dissolubility and viscosity characteristics, and non-thermal gelation; Nonionic own can with on a large scale in other water-soluble polymers, surfactant, salt coexist, and are a kind of good colloid thickeners containing high concentration electrolysis matter solution; Water holding capacity exceeds one times than methylcellulose, has good flow adjustment.
Described bentonite (Bentonite) is taking montmorillonite as main moisture clay pit, has swelling, caking property, adsorptivity, catalytic, thixotropy, suspension and cation exchange.
The key property measurement result of interiro wall latex paint of the present invention.
(1) drying time determination experiment: in room temperature (23 ± 2) DEG C, under the mensuration environment of relative humidity (50 ± 5) %, the surface drying time of this interiro wall latex paint is 30 minutes, and dry-hard time is 60 minutes.
(2) theory of interiro wall latex paint of the present invention consumption paint amount is 6-10 square metre/kilogram/single pass (dry film 30 μ m meters); Because of degree of roughness, packing, aridity and the coating dilution ratio difference on practice of construction surface, consumption paint amount can be different.
(3) condition of storage of interiro wall latex paint of the present invention is: leave the dry and comfortable place, cool place of 5-35 DEG C in, packing specification is 20 kilograms/barrel.
The preparation method of interiro wall latex paint of the present invention is: add 16 parts, water at stirred tank, then add 0.85 part of 0.03 part of ethanol, hydroxyethylcellulose after 1000 turn/min disperse; After adding 6.5 parts of 8 parts of sharp titanium whites (BA01-01), 12 parts, barium sulfate, bentonite, 1500 turn/min disperse again; Last 600 turn/min add 21 parts of 25 parts of Styrene And Butyl-acrylate emulsions, epoxy resin to stir, and to obtain final product.
Embodiment 2.
The present embodiment provides a kind of interiro wall latex paint, is made up of the raw material of following parts by weight: 21 parts of Styrene And Butyl-acrylate emulsions, 15 parts of epoxy resin, 5.5 parts of sharp titanium whites (BA01-01), 11.5 parts, barium sulfate, 5 parts of bentonites, 0.02 part of ethanol, 0.56 part of hydroxyethylcellulose, 12 parts, water.
After all raw material mix and blends, obtain described interiro wall latex paint finished product.
Described interiro wall latex paint adopts roller coat, brushing or spraying method to construct.
Described interiro wall latex paint can not be at temperature lower than 5 DEG C, relative humidity is greater than under 85% environment constructs.
Described interiro wall latex paint should stir before using, for reaching the best brushing effects that is coated with, when roller coat, brush application, can use according to actual conditions no more than 20% clear water dilution, if use spraying, can use according to actual conditions no more than 10% clear water dilution, excessive being watered can not increase effective brushing area.
Embodiment 3.
The present embodiment provides a kind of interiro wall latex paint, is made up of the raw material of following parts by weight: 30 parts of Styrene And Butyl-acrylate emulsions, 24 parts of epoxy resin, 9.5 parts of sharp titanium whites (BA01-01), 14.5 parts, barium sulfate, 8 parts of bentonites, 0.04 part of ethanol, 0.95 part of hydroxyethylcellulose, 19 parts, water.
After all raw material mix and blends, obtain described interiro wall latex paint finished product.
Described interiro wall latex paint adopts roller coat, brushing or spraying method to construct.
Described interiro wall latex paint can not be at temperature lower than 5 DEG C, relative humidity is greater than under 85% environment constructs.
Described interiro wall latex paint should stir before using, for reaching the best brushing effects that is coated with, when roller coat, brush application, can use according to actual conditions no more than 20% clear water dilution, if use spraying, can use according to actual conditions no more than 10% clear water dilution, excessive being watered can not increase effective brushing area.
The above, be only to preferred embodiment of the present invention, not the present invention done to other forms of restriction, and any those skilled in the art may utilize the technology contents of above-mentioned announcement to be changed or be modified as the equivalent embodiment of equal variation. Every the present invention program's content that do not depart from,, all drops in protection scope of the present invention any simple modification made for any of the above embodiments, equivalent variations and remodeling according to technical spirit of the present invention.
Claims (10)
1. an interiro wall latex paint, it is characterized in that, formed by the raw material of following parts by weight: Styrene And Butyl-acrylate emulsion 20-30 part, epoxy resin 15-25 part, sharp titanium white 5-10 part, barium sulfate 10-15 part, bentonite 5-8 part, ethanol 0.01-0.05 part, hydroxyethylcellulose 0.5-1 part, water 10-20 part.
2. interiro wall latex paint as claimed in claim 1, it is characterized in that, formed by the raw material of following parts by weight: 25 parts of Styrene And Butyl-acrylate emulsions, 21 parts of epoxy resin, 8 parts of sharp titanium whites, 12 parts, barium sulfate, 6.5 parts of bentonites, 0.03 part of ethanol, 0.85 part of hydroxyethylcellulose, 16 parts, water.
3. interiro wall latex paint as claimed in claim 1, it is characterized in that, formed by the raw material of following parts by weight: 21 parts of Styrene And Butyl-acrylate emulsions, 15 parts of epoxy resin, 5.5 parts of sharp titanium whites, 11.5 parts, barium sulfate, 5 parts of bentonites, 0.02 part of ethanol, 0.56 part of hydroxyethylcellulose, 12 parts, water.
4. interiro wall latex paint as claimed in claim 1, it is characterized in that, formed by the raw material of following parts by weight: 30 parts of Styrene And Butyl-acrylate emulsions, 24 parts of epoxy resin, 9.5 parts of sharp titanium whites, 14.5 parts, barium sulfate, 8 parts of bentonites, 0.04 part of ethanol, 0.95 part of hydroxyethylcellulose, 19 parts, water.
5. the interiro wall latex paint as described in arbitrary claim in claim 1-4, is characterized in that, obtains described interiro wall latex paint finished product after all raw material mix and blends.
6. interiro wall latex paint as claimed in claim 1, is characterized in that, described interiro wall latex paint adopts roller coat, brushing or spraying method to construct.
7. interiro wall latex paint as claimed in claim 6, is characterized in that, uses no more than 20% clear water dilution when described roller coat, brush application; When spraying application, use no more than 10% clear water dilution.
8. interiro wall latex paint as claimed in claim 1, is characterized in that, in room temperature (23 ± 2) DEG C, under the mensuration environment of relative humidity (50 ± 5) %, the surface drying time of described interiro wall latex paint is 30 minutes, and dry-hard time is 60 minutes.
9. the preparation method of interiro wall latex paint as claimed in claim 1, is characterized in that, adds water at stirred tank, then add ethanol, hydroxyethylcellulose after 1000 turn/min disperse; After adding sharp titanium white, barium sulfate, bentonite, 1500 turn/min disperse again; Last 600 turn/min add Styrene And Butyl-acrylate emulsion, epoxy resin to stir, and to obtain final product.
10. the using method of interiro wall latex paint as claimed in claim 1, is characterized in that, first wall primer one time in brushing, then brush described interiro wall latex paint twice; Every at least 2 hours time intervals all over brushing.