CN107033682A - A kind of environment-friendly type styrene-acrylate emulsion coating and preparation method thereof - Google Patents
A kind of environment-friendly type styrene-acrylate emulsion coating and preparation method thereof Download PDFInfo
- Publication number
- CN107033682A CN107033682A CN201611053983.0A CN201611053983A CN107033682A CN 107033682 A CN107033682 A CN 107033682A CN 201611053983 A CN201611053983 A CN 201611053983A CN 107033682 A CN107033682 A CN 107033682A
- Authority
- CN
- China
- Prior art keywords
- parts
- environment
- friendly type
- acrylate emulsion
- type styrene
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of environment-friendly type styrene-acrylate emulsion coating, including following components in parts by weight：20 50 parts of styrene；10 40 parts of methyl acrylate；5 20 parts of epoxy resin；5 10 parts of polyolefin elastomer；10 15 parts of hydroxyethyl cellulose；15 parts of sodium acid carbonate；58 parts of closed perlite；58 parts of talcum powder；18 parts of antiseptic；8 15 parts of emulsifying agent；15 25 parts of water.It is coating composition advantages of simple, nontoxic, tasteless, coating fast drying, any surface finish smooth, water-tolerant, difficult for drop-off, it is adaptable to the brushing of interior wall；Also, the coating antibiosis, anti-mildew, water-fastness wear-resisting, service life is long；Difficult for drop-off, not efflorescence, nondiscolouring, resistance to soiling are excellent, good weatherability, easy to use；Meanwhile, the smooth densification of paint film is applied, heat insulation and preservation effect is good.The invention also discloses a kind of preparation method of environment-friendly type styrene-acrylate emulsion coating, process is simple and safe, workable.
Description
Technical field
The present invention relates to technical field of coatings, more particularly to a kind of environment-friendly type styrene-acrylate emulsion coating and its preparation side.
Background technology
Coating, which refers to, to be coated on body surface and can form film under certain conditions and play protection, decoration or other special work(
A class I liquid I or solid material for energy (waterproof, insulation, antirust, mould proof, heat-resisting etc.).The type of coating is a lot, by film forming matter
Dividing may include organosilicon coating, silicate paint, alkyd paint, epoxy coating, chlorinated rubber coating, acrylic coating, poly- ammonia
Ester paint and ethene coating etc..Various coating are employed for different industries, in different occasions with the advantage of itself.Its
In, the coating for indoor wall is referred to as interior wall coating, and suitable interior wall coating can play protective effect well to interior, together
When cause metope more attractive in appearance, allow people to be comfortable on.But, existing interior wall coating generally existing drying is slow, levelability is poor,
The shortcomings of poor water resistance, poor film adhesiveness.
The content of the invention
In order to overcome the deficiencies in the prior art, first purpose of the invention is that providing a kind of environment-friendly type styrene-acrylic emulsion applies
Material, it is coating composition advantages of simple, nontoxic, tasteless, coating fast drying, any surface finish smooth, water-tolerant, difficult for drop-off, fit
Brushing for interior wall.
Second object of the present invention is to provide a kind of preparation method of environment-friendly type styrene-acrylate emulsion coating, and process is simply pacified
Entirely, it is workable.
First purpose of the present invention is realized using following technical scheme：
A kind of environment-friendly type styrene-acrylate emulsion coating, including following components in parts by weight：
It is preferred that, in addition to following components in parts by weight：
It is preferred that, the antiseptic be triclosan, copper pyrithione, sodium pyrithione and ZPT in one kind or
Any combination；The emulsifying agent is phenethyl phenol polyethenoxy ether, ethoxylated dodecyl alcohol, polyoxyethylene oleic acid ester, tristearin
Sour polyoxyethylene ester, fragrant sour polyoxyethylene ester, sorbitan fatty acid ester, alkylbenzenesulfonate, neopelex,
Alkane sodium olefin sulfonate, secondary alcohol groups sodium sulphate, polyacrylamide and one kind or any combination in two polyglycereol and fatty acid ester.
It is preferred that, including following components in parts by weight：
It is preferred that, including following components in parts by weight：
It is preferred that, including following components in parts by weight：
It is preferred that, the levelling agent combines for one or both of BYK358 and BYK331；The drier is epoxy
Sour manganese, epoxyeicosatrienoic acid zinc, epoxyeicosatrienoic acid copper, epoxyeicosatrienoic acid iron, epoxyeicosatrienoic acid cobalt, cobalt iso-octoate and one kind in zinc Isoocatanoate or any group
Close；The dispersant is one in vinyl bis-stearamides, glyceryl monostearate, glyceryl tristearate, barium stearate
Plant or be combined；The defoamer is dimethicone, higher alcohols, benzyl carbinol oleate, polyether-modified silicon and phenylacetic acid month
One kind or any combination in cinnamic alcohol ester；The stabilizer is that organotin, antimony organic, rare-earth stabilizer, phosphorous vinegar, epoxy are big
One kind or any combination in soya-bean oil, hindered phenol.
It is preferred that, the levelling agent is BYK358 and BYK331；The drier is epoxyeicosatrienoic acid manganese and zinc Isoocatanoate；It is described
Dispersant is vinyl bis-stearamides and barium stearate；The defoamer is dimethicone；The stabilizer is organotin.
Second object of the present invention is realized using following technical scheme：
A kind of preparation method of environment-friendly type styrene-acrylate emulsion coating, comprises the following steps：
1) styrene of formula ratio, methyl acrylate, epoxy resin and emulsifying agent are added in container, low whipping speed is
Under conditions of 600-1000r/min, 30-50min is stirred, mixed emulsion is obtained；
2) low whipping speed be 350-700r/min under conditions of, by the polyolefin elastomer of formula ratio, hydroxy ethyl fiber
Element, sodium acid carbonate and antiseptic are added in the mixed emulsion, after addition is finished, and are regulated the speed as 100-150r/min, and protect
10-30min is held, semi-finished product are obtained；
3) by the closed perlite of formula ratio, talcum powder, levelling agent, drier, dispersant, defoamer, stabilizer and water
Add in the semi-finished product, stir, that is, obtain the environment-friendly type styrene-acrylate emulsion coating.
It is preferred that, in step 1) in, mixing speed is 600r/min, and mixing time is 30min；In step 2) in, stirring
Speed is mixed under conditions of 350r/min, to add polyolefin elastomer, hydroxyethyl cellulose, sodium acid carbonate and the antibacterial of formula ratio
Agent, after addition is finished, regulates the speed as 100r/min, and keep 10min；In step 3) in, mixing time is 15-25min
Compared with prior art, the beneficial effects of the present invention are：
(1) environment-friendly type styrene-acrylate emulsion coating provided by the present invention, it is adaptable to the brushing of interior wall, nonpoisonous and tasteless, safety collar
Protect, the coating can penetrate into several millimeters within the walls, on wall surface and be internally formed netted moisture film, good water-proof effect, meanwhile, waterproof membrane is simultaneously
It will not stop that moisture sheds out of wall, air permeable effect is good；The smooth densification of paint film is applied, the ash in external environment can be effectively prevented
Dirt adheres to and penetrated into, and water-fastness wear-resisting, service life is long；Difficult for drop-off, not efflorescence, nondiscolouring, mould proof, resistance to soiling are excellent, weather-proof
Property is good, easy to use.
(2) environment-friendly type styrene-acrylate emulsion coating provided by the present invention, adds epoxy resin, and epoxy resin, which can be crosslinked, to be changed
Property styrene-acrylic emulsion, so as to improve the chemical property of paint film, improve the acidproof weatherability of paint film；Add closed perlite, closed pore
Perlite has obvious capillary action so that coating is perfectly adhered on wall, difficult for drop-off, meanwhile, closed pore is precious
Zhu Yan improves the heat insulation and preservation effect of coating.
(3) environment-friendly type styrene-acrylate emulsion coating provided by the present invention, adds talcum powder, and talcum powder plays skeleton function,
It can improve the compactness of coating, assign coating very high sintered material hardness, increase the stabilization of shape of product, strengthen the filling of coating
Property, improve application property, increase shear strength, extension rate and the thermal coefficient of expansion of coating so that the processing characteristics of coating and flowing
Property is optimized；Polyolefin elastomer is added, polyolefin elastomer is dispersed in coating, the affine of two-phase can be improved
Power, reduces the stress concentration at interface, and can improve the toughness, lower temperature resistance and environmental stress crack resistance of coating.Meanwhile,
It also add antiseptic so that coating has the function such as the antibacterial of broad spectrum durable, deodorization, anti-mildew, to Escherichia coli, golden yellow
Staphylococcus and Aspergillus flavus etc. have good bactericidal effect, and bacteriostasis rate is up to more than 99.99%, and antiseptic and coating
Matrix can be compatible well, and effect persistently, has no side effect to human body.
(4) environment-friendly type styrene-acrylate emulsion coating provided by the present invention, adds hydroxyethyl cellulose, plays good increasing
The characteristics such as thick, suspension, scattered, emulsification, bonding, film forming, protection moisture；Emulsifying agent is added, emulsion dispersion work well is played
With, be conducive to coating preparation, construction and preserve.Also, levelling agent, drier, dispersant, defoamer and steady can also be increased
Determine a variety of auxiliary agents such as agent, further increase the performance of coating.
(5) preparation method of environment-friendly type styrene-acrylate emulsion coating provided by the present invention, process is simple and safe, operability
By force.
Embodiment
Below, with reference to embodiment, the present invention is described further：
A kind of environment-friendly type styrene-acrylate emulsion coating, including following components in parts by weight：
As preferably scheme, in addition to following components in parts by weight：
A kind of preparation method of environment-friendly type styrene-acrylate emulsion coating, comprises the following steps：
1) styrene of formula ratio, methyl acrylate, epoxy resin and emulsifying agent are added in container, low whipping speed is
Under conditions of 600-1000r/min, 30-50min is stirred, mixed emulsion is obtained；
2) low whipping speed be 350-700r/min under conditions of, by the polyolefin elastomer of formula ratio, hydroxy ethyl fiber
Element, sodium acid carbonate and antiseptic are added in the mixed emulsion, after addition is finished, and are regulated the speed as 100-150r/min, and protect
10-30min is held, semi-finished product are obtained；
3) by the closed perlite of formula ratio, talcum powder, levelling agent, drier, dispersant, defoamer, stabilizer and water
Add in the semi-finished product, stir, that is, obtain the environment-friendly type styrene-acrylate emulsion coating.
Embodiment 1
A kind of environment-friendly type styrene-acrylate emulsion coating, is prepared from by following components in parts by weight and (is referred to table 1).It is made
Standby process is as follows successively：1) styrene of formula ratio, methyl acrylate, epoxy resin and emulsifying agent are added in container, stirred
Speed is mixed under conditions of 600r/min, to stir 50min, obtain mixed emulsion；2) low whipping speed is 700r/min condition
Under, the polyolefin elastomer of formula ratio, hydroxyethyl cellulose, sodium acid carbonate and antiseptic are added in the mixed emulsion, plus
Enter after finishing, regulate the speed as 150r/min, and keep 30min, obtain semi-finished product；3) by the closed perlite of formula ratio, cunning
Stone flour, levelling agent, drier, dispersant, defoamer, stabilizer and water are added in the semi-finished product, are stirred 15min, that is, are obtained
The environment-friendly type styrene-acrylate emulsion coating.
Embodiment 2
A kind of environment-friendly type styrene-acrylate emulsion coating, is prepared from by following components in parts by weight and (is referred to table 1).It is made
Standby process is as follows successively：1) styrene of formula ratio, methyl acrylate, epoxy resin and emulsifying agent are added in container, stirred
Speed is mixed under conditions of 600r/min, to stir 50min, obtain mixed emulsion；2) low whipping speed is 700r/min condition
Under, the polyolefin elastomer of formula ratio, hydroxyethyl cellulose, sodium acid carbonate and antiseptic are added in the mixed emulsion, plus
Enter after finishing, regulate the speed as 150r/min, and keep 30min, obtain semi-finished product；3) by the closed perlite of formula ratio, cunning
Stone flour, levelling agent, drier, dispersant, defoamer, stabilizer and water are added in the semi-finished product, are stirred 15min, that is, are obtained
The environment-friendly type styrene-acrylate emulsion coating.
Embodiment 3
A kind of environment-friendly type styrene-acrylate emulsion coating, is prepared from by following components in parts by weight and (is referred to table 1).It is made
Standby process is as follows successively：1) styrene of formula ratio, methyl acrylate, epoxy resin and emulsifying agent are added in container, stirred
Speed is mixed under conditions of 700r/min, to stir 40min, obtain mixed emulsion；2) low whipping speed is 500r/min condition
Under, the polyolefin elastomer of formula ratio, hydroxyethyl cellulose, sodium acid carbonate and antiseptic are added in the mixed emulsion, plus
Enter after finishing, regulate the speed as 120r/min, and keep 15min, obtain semi-finished product；3) by the closed perlite of formula ratio, cunning
Stone flour, levelling agent, drier, dispersant, defoamer, stabilizer and water are added in the semi-finished product, are stirred 20min, that is, are obtained
The environment-friendly type styrene-acrylate emulsion coating.
Embodiment 4
A kind of environment-friendly type styrene-acrylate emulsion coating, is prepared from by following components in parts by weight and (is referred to table 1).It is made
Standby process is as follows successively：1) styrene of formula ratio, methyl acrylate, epoxy resin and emulsifying agent are added in container, stirred
Speed is mixed under conditions of 800r/min, to stir 35min, obtain mixed emulsion；2) low whipping speed is 600r/min condition
Under, the polyolefin elastomer of formula ratio, hydroxyethyl cellulose, sodium acid carbonate and antiseptic are added in the mixed emulsion, plus
Enter after finishing, regulate the speed as 130r/min, and keep 25min, obtain semi-finished product；3) by the closed perlite of formula ratio, cunning
Stone flour, levelling agent, drier, dispersant, defoamer, stabilizer and water are added in the semi-finished product, are stirred 22min, that is, are obtained
The environment-friendly type styrene-acrylate emulsion coating.
The formula table of the embodiment 1-4 of table 1 environment-friendly type styrene-acrylate emulsion coating
Test case
The environment-friendly type styrene-acrylate emulsion coating acquired in Example 1-4, is brushed, correlated performance to predetermined interior wall respectively
Assay method and evaluation index respectively with GB/T 9756-2009《Resin latex dope》And GB18528-2001
《Limits of harmful substances in indoor decorating and refurnishing materials interior wall coating》For foundation.Test result refers to table 2 below.
The performance test record sheet of the embodiment 1-4 of table 2 environment-friendly type styrene-acrylate emulsion coating
It can be obtained from the data of table 2, the environment-friendly type styrene-acrylate emulsion coating properties that embodiment 1-4 is provided reach or excellent
In GB/T 9756-2009《Resin latex dope》Regulation, coating application performance is good, and Yi Gan is difficult for drop-off, prevents
Water, alkaline-resisting, weather-proof, low temperature resistant, paint film is smooth.Meanwhile, the harmful substance index tested meets environmental requirement, nontoxic nothing
Taste, safety and environmental protection.It can be seen that, environment-friendly type styrene-acrylate emulsion coating performance provided by the present invention is more excellent, with application prospect well.
It will be apparent to those skilled in the art that technical scheme that can be as described above and design, make other various
It is corresponding to change and deformation, and all these change and deformation should all belong to the protection domain of the claims in the present invention
Within.
Claims (10)
1. a kind of environment-friendly type styrene-acrylate emulsion coating, it is characterised in that including following components in parts by weight：
2. environment-friendly type styrene-acrylate emulsion coating according to claim 1, it is characterised in that also including in parts by weight with
Lower component：
3. environment-friendly type styrene-acrylate emulsion coating according to claim 1, it is characterised in that the antiseptic is triclosan, pyrrole
Pyridine thioketones copper, sodium pyrithione and one kind or any combination in ZPT；The emulsifying agent is phenethyl phenol polyoxy second
Alkene ether, ethoxylated dodecyl alcohol, polyoxyethylene oleic acid ester, polyoxyethylene stearic acid ester, fragrant sour polyoxyethylene ester, Sorbitan
Alcohol fatty acid ester, alkylbenzenesulfonate, neopelex, alkane sodium olefin sulfonate, secondary alcohol groups sodium sulphate, polyacrylamide
With one kind or any combination in two polyglycereol and fatty acid ester.
4. environment-friendly type styrene-acrylate emulsion coating according to claim 1, it is characterised in that below in parts by weight
Component：
5. environment-friendly type styrene-acrylate emulsion coating according to claim 3, it is characterised in that below in parts by weight
Component：
6. environment-friendly type styrene-acrylate emulsion coating according to claim 3, it is characterised in that below in parts by weight
Component：
7. environment-friendly type styrene-acrylate emulsion coating according to claim 2, it is characterised in that the levelling agent be BYK358 and
One or both of BYK331 is combined；The drier is epoxyeicosatrienoic acid manganese, epoxyeicosatrienoic acid zinc, epoxyeicosatrienoic acid copper, epoxyeicosatrienoic acid iron, epoxy
One kind or any combination in sour cobalt, cobalt iso-octoate and zinc Isoocatanoate；The dispersant is vinyl bis-stearamides, stearic acid
One kind or any combination in monoglyceride, glyceryl tristearate, barium stearate；The defoamer is dimethicone, height
Carbon alcohol, benzyl carbinol oleate, polyether-modified silicon and one kind or any combination in Laurate alcohol ester phenylacetate；The stabilizer is to have
Machine tin, antimony organic, rare-earth stabilizer, phosphorous vinegar, epoxidized soybean oil, one kind or any combination in hindered phenol.
8. environment-friendly type styrene-acrylate emulsion coating according to claim 7, it is characterised in that the levelling agent be BYK358 and
BYK331；The drier is epoxyeicosatrienoic acid manganese and zinc Isoocatanoate；The dispersant is vinyl bis-stearamides and barium stearate；
The defoamer is dimethicone；The stabilizer is organotin.
9. the preparation method of environment-friendly type styrene-acrylate emulsion coating as claimed in claim 2, it is characterised in that comprise the following steps：
1) styrene of formula ratio, methyl acrylate, epoxy resin and emulsifying agent are added in container, low whipping speed is 600-
Under conditions of 1000r/min, 30-50min is stirred, mixed emulsion is obtained；
2) low whipping speed be 350-700r/min under conditions of, by the polyolefin elastomer, hydroxyethyl cellulose, carbon of formula ratio
Sour hydrogen sodium and antiseptic are added in the mixed emulsion, after addition is finished, and are regulated the speed as 100-150r/min, and keep 10-
30min, obtains semi-finished product；
3) closed perlite of formula ratio, talcum powder, levelling agent, drier, dispersant, defoamer, stabilizer and water are added
In the semi-finished product, stir, that is, obtain the environment-friendly type styrene-acrylate emulsion coating.
10. the preparation method of environment-friendly type styrene-acrylate emulsion coating according to claim 9, it is characterised in that in step 1) in,
Mixing speed is 600r/min, and mixing time is 30min；In step 2) in, low whipping speed be 350r/min under conditions of, plus
Enter polyolefin elastomer, hydroxyethyl cellulose, sodium acid carbonate and the antiseptic of formula ratio, after addition is finished, regulate the speed for
100r/min, and keep 10min；In step 3) in, mixing time is 15-25min.