CN105586771A - Anti-wrinkle finishing method for hemp fabric - Google Patents

Anti-wrinkle finishing method for hemp fabric Download PDF

Info

Publication number
CN105586771A
CN105586771A CN201610144443.7A CN201610144443A CN105586771A CN 105586771 A CN105586771 A CN 105586771A CN 201610144443 A CN201610144443 A CN 201610144443A CN 105586771 A CN105586771 A CN 105586771A
Authority
CN
China
Prior art keywords
parts
fabric
wrinkle
hemp fabric
hemp
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201610144443.7A
Other languages
Chinese (zh)
Inventor
任新根
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
HUZHOU XINCHUANG SILK CO Ltd
Original Assignee
HUZHOU XINCHUANG SILK CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by HUZHOU XINCHUANG SILK CO Ltd filed Critical HUZHOU XINCHUANG SILK CO Ltd
Priority to CN201610144443.7A priority Critical patent/CN105586771A/en
Publication of CN105586771A publication Critical patent/CN105586771A/en
Pending legal-status Critical Current

Abstract

The invention discloses an anti-wrinkle finishing method for hemp fabric. The method includes the following steps that firstly, a finishing agent is added with water to be prepared into steeping liquor; then, the fabric is put into the steeping liquor for padding, wherein the liquor detention rate is 70-80%; finally, the fabric is washed 2-3 times and then is dewatered and dried. The finishing agent is prepared from, by weight, 6-8 parts of propylene glycol, 2-7 parts of sodium polystyrene sulfonate, 5-8 parts of phenol, 22-24 parts of butyl acetate, 2-6 parts of potassium oxalate, 4-7 parts of ethylenediaminetetraacetic acid disodium salt, 1-8 parts of tetrabutyl titanate, 4-5 parts of phenyltriethoxysilane, 4-9 parts of common fibraurea stem powder, 2-6 parts of sodium xylene sulfonate, 3-6 parts of methyl cyclotetrasiloxane, 6-10 parts of glycerin, 2-6 parts of starch ether, 2-7 parts of borax and 11 parts of zinc acetate. The finishing method is used for anti-wrinkle finishing processing of the hemp fabric, the problem that in the past, hemp fabric is likely to wrinkle is relieved while the anti-wrinkle effect is guaranteed, and the hemp fabric is strong in washability and soft in handfeel.

Description

The anti-wrinkle method for sorting of a kind of hemp fabric
Technical field
The invention belongs to textile technology field, be specifically related to the anti-wrinkle of a kind of hemp fabric arrangement sideMethod.
Technical background
Hemp fabric is the woven fabric of china-hemp fibers, and Chinese fiber crops have another name called hemp, cold fiber crops, fire fiber cropsDeng, another name appellation nearly more than ten is planted. History records carry, and fiber crops originate from China, have " natural fiberKing " good reputation, the clothes finery of being made up of it have moisture absorption, ventilative, pleasant, heat radiation, anti-The several functions such as mould, antibacterial, radioresistance, antiultraviolet, sound-absorbing, not only can be military but also can be civilian.And to make the effect of antimicrobial socks, be just subject to extensive favorable comment. Chinese fiber crops are that the mankind use the earliestIn the natural fiber of fabric, there is " source is spun by state, 10000 years clothing ancestrals " good reputation, its plantation history is extremelyRare more than 8000 years. The plantation of Chinese fiber crops spread, can effectively alleviate Chinese fiber in short supplyPresent situation, breaks a high added value Xin road for solving agriculture, rural areas and farmers problem, and its good characteristic willFor following soldier's food and clothing is lived with bringing revolutionary variation.
Chinese fiber crops are raw materials of various military clothes, high-grade dress ornament, are expected to change world today's weavingProduct structure; Also may become in the future the mineral such as oil, coal substitute, reduce energy resource consumption and causeEnvironmental pollution. Chinese fiber crops are a kind of ecological, environmental protective, reproducible multi-purpose plant, through coming unstuck,The operation such as reel off raw silk from cocoons, becomes as shining white cotton-wool, both can wool spinning, again can cotton spinning, and also canBlending, and with low cost. The hydrofuge of Chinese fiber crops is textile 3 times, and Chinese pitted skin material can be little 1Time in by the killing bacteria adhering to; More than 95% ultraviolet ray of hemp fabric maskable, at 370 DEG CColour-fast when high temperature, in the time of 1000 DEG C, do not burn, there is splendid heat-resisting, ultraviolet resistance;Chinese fiber crops bast with can be used for weaving.
But hemp fabric in use exist poor flexibility, yielding, crease easily, washAfter need the defects such as flatiron, cause hemp fabric after washing and take and in process, can not keep smoothOutward appearance. Therefore,, in order to improve the outward appearance of fabric in wearing process, keep the stable of its formProperty, improve its wearability, need to carry out anti-crease finishing. But use the anti-of traditional finishing agentWrinkle effect is poor, has toxicity, and unreliable to human safety, durability and washability are not high.Therefore how overcoming the deficiencies in the prior art is problems that current field of textiles is needed solution badly.
Summary of the invention
To achieve these goals, the invention provides the anti-wrinkle of a kind of hemp fabric arrangement sideMethod.
The object of the invention is to be achieved through the following technical solutions:
The anti-wrinkle method for sorting of a kind of hemp fabric, the method has following steps: first will arrangeAgent adds water and is mixed with maceration extract, and then fabric is put into maceration extract and pad, pick-up 70-80%,Finally wash 2-3 time dewatered drying; Described finishing agent is by the component of following parts by weightComposition: propane diols 6-8 part, kayexalate 2-7 part, phenol 5-8 part, acetic acid fourthEster 22-24 part, potassium oxalate 2-6 part, disodium ethylene diamine tetraacetate 4-7 part, butyl titanate1-8 part, phenyl triethoxysilane 4-5 part, herba fibraureae recisae powder 4-9 part, sodium xylene sulfonate 2-6Part, methyl cyclosiloxane 3-6 part, glycerine 6-10 part, starch ether 2-6 part, borax 2-711 parts of part, zinc acetates.
The preparation technology of finishing agent is common process, for those of ordinary skill in the art skillfully slapHold.
Described fabric normal temperature dipping 35-40 minute.
Described bake out temperature is 80-90 DEG C, and the time is 30s.
The concentration of the described aqueous solution is 600-1200ppm.
The present invention has following beneficial effect: method for sorting of the present invention is crease-resistant for hemp fabricArrange processing, ensureing in anti-wrinkle effect, improve in the past the hemp fabric problem of easily wrinkling, andWashability is strong, soft.
Detailed description of the invention
The following stated is only the preferred embodiments of the present invention, is not limited to the present invention,Although the present invention is had been described in detail with reference to previous embodiment, for the technology of this areaPersonnel, its technical scheme that still can record aforementioned each embodiment is modified,Or part technical characterictic is wherein equal to replacement. All the spirit and principles in the present invention itIn, any amendment of doing, be equal to replacement, improvement etc., all should be included in protection of the present inventionWithin scope.
Embodiment 1
The anti-wrinkle method for sorting of a kind of hemp fabric, it has following steps: first finishing agent is addedWater is mixed with maceration extract, and then fabric is put into maceration extract and pad, pick-up 70-80%,Finally wash 2-3 time dewatered drying; Described finishing agent is by the component of following parts by weightComposition: 6 parts of propane diols, 2 parts of kayexalates, 5 parts of phenol, butyl acetate 22Part, 2 parts of potassium oxalates, 4 parts of disodium ethylene diamine tetraacetates, 1 part of butyl titanate, phenyl three4 parts of Ethoxysilanes, 4 parts, herba fibraureae recisae powder, 2 parts of sodium xylene sulfonates, methyl cyclosiloxane 3Part, 6 parts of glycerine, 2 parts of starch ethers, 2 parts of boraxs, 11 parts of zinc acetates.
Described fabric normal temperature dipping 35-40 minute.
Described bake out temperature is 80-90 DEG C, and the time is 30s.
The concentration of the described aqueous solution is 600-1200ppm.
Embodiment 2
The anti-wrinkle method for sorting of a kind of hemp fabric, it has following steps: first finishing agent is addedWater is mixed with maceration extract, and then fabric is put into maceration extract and pad, pick-up 70-80%,Finally wash 2-3 time dewatered drying; Described finishing agent is by the component of following parts by weightComposition: 8 parts of propane diols, 7 parts of kayexalates, 8 parts of phenol, butyl acetate 24Part, 6 parts of potassium oxalates, 7 parts of disodium ethylene diamine tetraacetates, 8 parts of butyl titanates, phenyl three5 parts of Ethoxysilanes, 9 parts, herba fibraureae recisae powder, 6 parts of sodium xylene sulfonates, methyl cyclosiloxane 6Part, 10 parts of glycerine, 6 parts of starch ethers, 7 parts of boraxs, 11 parts of zinc acetates.
Described fabric normal temperature dipping 35-40 minute.
Described bake out temperature is 80-90 DEG C, and the time is 30s.
The concentration of the described aqueous solution is 600-1200ppm.
Embodiment 3
The anti-wrinkle method for sorting of a kind of hemp fabric, it has following steps: first finishing agent is addedWater is mixed with maceration extract, and then fabric is put into maceration extract and pad, pick-up 70-80%,Finally wash 2-3 time dewatered drying; Described finishing agent is by the component of following parts by weightComposition: 7 parts of propane diols, 5 parts of kayexalates, 7 parts of phenol, butyl acetate 23Part, 4 parts of potassium oxalates, 5 parts of disodium ethylene diamine tetraacetates, 5 parts of butyl titanates, phenyl three5 parts of Ethoxysilanes, 7 parts, herba fibraureae recisae powder, 4 parts of sodium xylene sulfonates, methyl cyclosiloxane 3Part, 7 parts of glycerine, 4 parts of starch ethers, 5 parts of boraxs, 11 parts of zinc acetates.
Described fabric normal temperature dipping 35-40 minute.
Described bake out temperature is 80-90 DEG C, and the time is 30s.
The concentration of the described aqueous solution is 600-1200ppm.

Claims (4)

1. the anti-wrinkle method for sorting of hemp fabric, is characterized in that the step of described methodAs follows: first finishing agent is added water and is mixed with maceration extract, then fabric is put into maceration extract and pad,Pick-up 70-80%, finally washes 2-3 time, dewatered drying; Described finishing agent by asThe component composition of lower parts by weight: propane diols 6-8 part, kayexalate 2-7 part, benzenePhenol 5-8 part, butyl acetate 22-24 part, potassium oxalate 2-6 part, disodium ethylene diamine tetraacetate4-7 part, butyl titanate 1-8 part, phenyl triethoxysilane 4-5 part, herba fibraureae recisae powder 4-9Part, sodium xylene sulfonate 2-6 part, methyl cyclosiloxane 3-6 part, glycerine 6-10 part, shallow lake11 parts of powder ether 2-6 parts, borax 2-7 part, zinc acetate.
2. the anti-wrinkle method for sorting of a kind of hemp fabric according to claim 1, its featureBe: described fabric normal temperature dipping 35-40 minute.
3. the anti-wrinkle method for sorting of a kind of hemp fabric according to claim 1, its featureBe: described bake out temperature is 80-90 DEG C, the time is 30s.
4. the anti-wrinkle method for sorting of a kind of hemp fabric according to claim 1, its featureBe: the concentration of the described aqueous solution is 600-1200ppm.
CN201610144443.7A 2016-03-14 2016-03-14 Anti-wrinkle finishing method for hemp fabric Pending CN105586771A (en)