CN107471776A - A kind of antibacterial sports jackets fabric and preparation method thereof - Google Patents
A kind of antibacterial sports jackets fabric and preparation method thereof Download PDFInfo
- Publication number
- CN107471776A CN107471776A CN201710787132.7A CN201710787132A CN107471776A CN 107471776 A CN107471776 A CN 107471776A CN 201710787132 A CN201710787132 A CN 201710787132A CN 107471776 A CN107471776 A CN 107471776A
- Authority
- CN
- China
- Prior art keywords
- fiber
- fabric
- sports jackets
- antibacterial
- antibacterial sports
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention provides a kind of antibacterial sports jackets fabric, including following component：Banana fiber, pineapple vein fiber, flax fiber and terylene Europe root yarn.Fabric is obtained with banana fiber, pineapple vein fiber and flax fiber blending；Outer shell fabric is used as using terylene Europe root yarn.Fabric need not carry out antimicrobial treatment, reach more than 90% to the bacteriostasis rate can of the common bacterias such as Escherichia coli, Candida albicans and staphylococcus aureus；Further to improve fabric to the adsorption effect of the slops such as sweat, peculiar smell, flax fiber is ultrasonically treated using the honeycomb micron little particle after activation, adsorption capacity significantly increases；Simultaneously because honeycomb micron little particle hardness is not high, coordinates the frequency being suitably ultrasonically treated, the intensity of flax fiber will not be damaged.The terylene Europe root yarn of outer layer not only can be with waterproof, and permeability is good, and outward appearance is beautiful, the esthetic requirement of compound modern society, and market prospects are extensive.
Description
Technical field
The present invention relates to sportswear technical field, more particularly to a kind of antibacterial sports jackets fabric and preparation method thereof.
Background technology
Modern more and more focus on improve quality of the life, outdoor exercises turn into people after work with household, friend
A kind of mode of share, it can not only physical fitness, mutual relation and friendship can also be promoted, be at one stroke it is more
.People are during outdoor exercises are done, and the clothing worn is in addition to it will have good absorption of perspiration, gas permeability and elasticity, also
Must possess certain wearability and soil resistance；, can during motion especially for the fan of some extreme sports
Rainwater or high temperature or severe cold can be run into, now, atrocious weather proposes very high requirement, clothing to their clothing
Object plane material except material is slim and graceful, quality firmly in addition to, it is necessary to can waterproof, windproof, warming, cold-resistant, can be provided more for sporter
More safety guarantee.
Outdoor sports coat fabric currently on the market typically just thinks of thermal property, and ignores the lightness of gym suit；
On the other hand, due to the water resistance of these materials, while water proof wind proof, the gas permeability of fabric is reduced, causes to perspire
It is not smooth.Further, such clothes washing gets up slightly difficulty, is difficult to remove due to perspiring the bacterium not grown freely, these problems are all
It is present in the outdoor sports coat fabric of in the market, up for solving.
The content of the invention
Based on technical problem existing for background technology, the invention provides a kind of antibacterial sports jackets fabric.
Technical scheme is as follows：
A kind of antibacterial sports jackets fabric, including following component：Banana fiber, pineapple vein fiber, flax fiber and wash
Synthetic fibre Europe root yarn.
Preferably, described antibacterial sports jackets fabric, the composition of following percentage by weight is included：Banana fiber 10-
20%th, arghan 8-15%, flax fiber 60-75% and terylene Europe root yarn surplus.
Preferably, described antibacterial sports jackets fabric, is obtained with banana fiber, pineapple vein fiber and flax fiber blending
To fabric；Outer shell fabric is used as using terylene Europe root yarn.
Preferably, the polyester fiber that described terylene Europe root yarn uses is modified Profile Polyester Fibre.
It is further preferred that described modification Profile Polyester Fibre is antiultraviolet Triangle Polyester Fiber.
It is further preferred that described antiultraviolet Triangle Polyester Fiber is water-repellent modified antiultraviolet triangle polyester
Fiber.
It using banana stalk is raw material that banana fiber, which is, is mainly made up of cellulose, hemicellulose and lignin, chemistry
Fiber after degumming can be used for cotton spinning.Handled using biology enzyme and chemical oxidation combined treatment process, by drying, concise, solution
Fine and manufactured fiber, it has, and light weight, good luster, water imbibition are high, antibiotic property is strong, the degradable and function such as environmentally friendly.Japan
Research to banana fiber walks the country in Southeast Asia for having abundant banana resource in forefront, India etc. and has also carried out largely grinding
Study carefully, extraction and product development of the China to this kind of fiber are also underway, and make some progress.The success of banana fiber
Produce, greatly extend the application of banana stalk, while alleviate the shortage of international natural fiber again.
Pineapple fibre, arghan, practise and claim pineapple fibre, be the fiber extracted from pineapple leaf, belong to vein fiber, can use
Chemistry, biology and mechanical means extraction.The fiber quality extracted using mechanical means is good, natural pollution-free.Pineapple fibre it is main
Function：Superpower natural disinfection bacteria resistance function.Long-term dress can effectively kill bacterium, suppress growing, being numerous for fungi and microorganism
Grow, have positive effect to preventing and mitigating tinea pedis symptom；Excellent deodorization deodorization functions.Socks, footwear, the bacterium on pin and fungi quilt
Kill or suppress, sweat, keratoprotein decomposition active substantially reduce, so as to prevent that foot odour, socks are smelly and footwear are smelly；Good moisture absorption is put
Green permeability energy.The sweat of evaporation secretion can be quickly absorbed, keeps pin dry and comfortable, formation is unfavorable for bacterium and fungi growth, breeding
Environment；Better than addition antibacterial material.Current market sales of antibacterial deodourizing product, its method are addition antibacterial deodourizing things
Matter：Such as phenolic compound, organo-metallic compound, organo-tin compound, organocopper compound.Not only antibacterial effect is durable
Property it is undesirable, also portioned product band is toxic or specific color (such as yellow, blue-green) and bring limitation to application.And spinach
The antibiotic property of trailing plants fiber crops socks from fiber it is naturally peculiar, wash repeatedly and still keep original antibiotic effect, and it is nontoxic do not have yet it is coloured
Limitation.
Flax is one of natural fiber that the mankind use earliest, away from modern existing more than 10,000 years history.Flax fiber is
A kind of rare natural fiber, only accounts for the 1.5% of natural fiber total amount.It is naturally and high due to the natural, simple and unsophisticated, rare of it, color
It is expensive, it is described as " the fiber queen in natural fiber ".Flax fiber has many excellent performances.Its moisture absorption is radiated, health care suppression
Bacterium, antifouling antistatic, antiultraviolet, and flame retardant effect is splendid.Flax fiber fabric is described as " natural air conditioner ".Flax dissipates
Hot property is splendid, because flax is unique bundle fiber in natural fiber.Bundle fiber is unicellular by colloid by flax
It is sticked together what is formed, because it does not leave the condition of air more, the ventilative ratio of sodolin is up to more than 25%, because
And its heat conductivility (gas permeability) is splendid.And 4-8 DEG C of skin surface temperature can be effectively reduced rapidly.The moisture absorption of flax fiber
Moisture releasing speed is fast, can adjust the ecological temperature environment on human body skin top layer in time.This is because it has natural imitative capitate structure
With the pectic substance hypotenuse pore structure of uniqueness.Pore phenomenon is produced when it is with skin contact, skin perspiration can be assisted, and can be clear
Clean skin.Meanwhile its heat is opened, and absorbs the sweat and heat of human body, and the sweat being absorbed to and even heat are transferred out
Go, decline human skin temperature.Then close to the cold, keep heat.Other flax can absorb the moisture of its deadweight 20%.It is same
Highest in the other fabrics of isodensity.
A kind of preparation method of antibacterial sports jackets fabric, comprises the following steps：
A, after natural honeycomb is cleaned up, the little particle that particle diameter is 20-100 μm is ground into, then adds watery hydrochloric acid
Activated, drying for standby after cleaning；
B, flax fiber and the honeycomb micron little particle after activation are subjected to supersound process 20-30min in water；
C, by the flax fiber after processing and banana fiber and pineapple vein fiber blend into fabric；
D, fabric dyed, post-process to obtain fabric；
E, antibacterial sports jackets fabric will be can obtain after the terylene Europe root yarn suture of fabric and outer layer.
Preferably, the frequency of described supersound process is 15-25kHz.
Compared with prior art, the beneficial effects of the present invention are：A kind of antibacterial sports jackets fabric of the present invention, including
Following component：Banana fiber, pineapple vein fiber, flax fiber and terylene Europe root yarn.With banana fiber, pineapple vein fiber and
Flax fiber blending obtains fabric；Outer shell fabric is used as using terylene Europe root yarn.The antibacterial sports jackets fabric of the present invention, it is interior
Shell fabric is using the pineapple vein fiber and flax fiber of natural antibacterial significant effect as primary raw material, without carrying out antimicrobial treatment,
More than 90% is reached to the bacteriostasis rate can of the common bacterias such as Escherichia coli, Candida albicans and staphylococcus aureus；For
Adsorption effect of the fabric to slops such as sweat, peculiar smell is further improved, using the honeycomb micron little particle pair after activation
Flax fiber is ultrasonically treated, and uniform depression occurs in the flax fiber surface after processing, and adsorption capacity significantly increases；Simultaneously
Because honeycomb micron little particle hardness is not high, coordinates the frequency being suitably ultrasonically treated, the intensity of flax fiber will not be caused
Harm.The terylene Europe root yarn of outer layer not only can be with waterproof, and permeability is good, and outward appearance is beautiful, and compound modern society examines
U.S. requires that market prospects are extensive.
Embodiment
The preferred embodiments of the present invention are described in detail below so that advantages and features of the invention can be easier to by
It will be appreciated by those skilled in the art that apparent clearly defined so as to be made to protection scope of the present invention.
Embodiment 1
A kind of antibacterial sports jackets fabric, include the composition of following percentage by weight：Banana fiber 12%, arghan
12%th, flax fiber 68% and terylene Europe root yarn surplus.
Described antibacterial sports jackets fabric, internal layer is obtained with banana fiber, pineapple vein fiber and flax fiber blending
Fabric；Outer shell fabric is used as using terylene Europe root yarn.
The polyester fiber that described terylene Europe root yarn uses is water-repellent modified antiultraviolet Triangle Polyester Fiber.
A kind of preparation method of antibacterial sports jackets fabric, comprises the following steps：
A, after natural honeycomb is cleaned up, the little particle that particle diameter is 20-100 μm is ground into, then adds watery hydrochloric acid
Activated, drying for standby after cleaning；
B, flax fiber is subjected to 22kHz with the honeycomb micron little particle after activation in water and is ultrasonically treated 25min；
C, by the flax fiber after processing and banana fiber and pineapple vein fiber blend into fabric；
D, fabric dyed, post-process to obtain fabric；
E, antibacterial sports jackets fabric will be can obtain after the terylene Europe root yarn suture of fabric and outer layer.
Embodiment 2
A kind of antibacterial sports jackets fabric, include the composition of following percentage by weight：Banana fiber 10%, arghan
8%th, flax fiber 75% and terylene Europe root yarn surplus.
Described antibacterial sports jackets fabric, internal layer is obtained with banana fiber, pineapple vein fiber and flax fiber blending
Fabric；Outer shell fabric is used as using terylene Europe root yarn.
The polyester fiber that described terylene Europe root yarn uses is water-repellent modified antiultraviolet Triangle Polyester Fiber.
A kind of preparation method of antibacterial sports jackets fabric, comprises the following steps：
A, after natural honeycomb is cleaned up, the little particle that particle diameter is 20-100 μm is ground into, then adds watery hydrochloric acid
Activated, drying for standby after cleaning；
B, flax fiber is subjected to 15kHz with the honeycomb micron little particle after activation in water and is ultrasonically treated 30min；
C, by the flax fiber after processing and banana fiber and pineapple vein fiber blend into fabric；
D, fabric dyed, post-process to obtain fabric；
E, antibacterial sports jackets fabric will be can obtain after the terylene Europe root yarn suture of fabric and outer layer.
Embodiment 3
A kind of antibacterial sports jackets fabric, include the composition of following percentage by weight：Banana fiber 20%, arghan
15%th, flax fiber 60% and terylene Europe root yarn surplus.
Described antibacterial sports jackets fabric, internal layer is obtained with banana fiber, pineapple vein fiber and flax fiber blending
Fabric；Outer shell fabric is used as using terylene Europe root yarn.
The polyester fiber that described terylene Europe root yarn uses is water-repellent modified antiultraviolet Triangle Polyester Fiber.
A kind of preparation method of antibacterial sports jackets fabric, comprises the following steps：
A, after natural honeycomb is cleaned up, the little particle that particle diameter is 20-100 μm is ground into, then adds watery hydrochloric acid
Activated, drying for standby after cleaning；
B, flax fiber is subjected to 25kHz with the honeycomb micron little particle after activation in water and is ultrasonically treated 20min；
C, by the flax fiber after processing and banana fiber and pineapple vein fiber blend into fabric；
D, fabric dyed, post-process to obtain fabric；
E, antibacterial sports jackets fabric will be can obtain after the terylene Europe root yarn suture of fabric and outer layer.
Biocidal property detection is carried out to embodiment 1-3 sample below：
Examination criteria is GB/T20944.3-2008《The evaluation third portion of antibacterial textile performance：Succusion》, use is resistance to
Color fastness testing machine washing methods is washed, the bacteriostasis rate of fabric after test is washed 50 times.
Table 1：Embodiment 1-3 sample biocidal property testing result
The foregoing is only a preferred embodiment of the present invention, but protection scope of the present invention be not limited thereto,
Any one skilled in the art the invention discloses technical scope in, technique according to the invention scheme and its
Inventive concept is subject to equivalent substitution or change, should all be included within the scope of the present invention.
Claims (8)
1. a kind of antibacterial sports jackets fabric, it is characterised in that including following component：Banana fiber, pineapple vein fiber, flax
Fiber and terylene Europe root yarn.
2. antibacterial sports jackets fabric as claimed in claim 1, it is characterised in that include the composition of following percentage by weight：
Banana fiber 10-20%, arghan 8-15%, flax fiber 60-75% and terylene Europe root yarn surplus.
3. antibacterial sports jackets fabric as claimed in claim 1 or 2, it is characterised in that described antibacterial sports jackets fabric,
Fabric is obtained with banana fiber, pineapple vein fiber and flax fiber blending；Outer shell fabric is used as using terylene Europe root yarn.
4. the antibacterial sports jackets fabric as described in claim 1-3 is any, it is characterised in that described terylene Europe root yarn uses
Polyester fiber be modified Profile Polyester Fibre.
5. the antibacterial sports jackets fabric as described in claim 4 is any, it is characterised in that described modification Profile Polyester Fibre
For antiultraviolet Triangle Polyester Fiber.
6. the antibacterial sports jackets fabric as described in claim 4 is any, it is characterised in that described antiultraviolet triangle is washed
Synthetic fibre fiber is water-repellent modified antiultraviolet Triangle Polyester Fiber.
7. a kind of preparation method of antibacterial sports jackets fabric, it is characterised in that comprise the following steps：
A, after natural honeycomb is cleaned up, the little particle that particle diameter is 20-100 μm is ground into, watery hydrochloric acid is then added and carries out
Activation, drying for standby after cleaning；
B, flax fiber and the honeycomb micron little particle after activation are subjected to supersound process 20-30min in water；
C, by the flax fiber after processing and banana fiber and pineapple vein fiber blend into fabric；
D, fabric dyed, post-process to obtain fabric；
E, antibacterial sports jackets fabric will be can obtain after the terylene Europe root yarn suture of fabric and outer layer.
8. the preparation method of antibacterial sports jackets fabric as claimed in claim 7, it is characterised in that described supersound process
Frequency is 15-25kHz.