CN1055766A - 从含锌烟道灰制取氧化锌的工艺 - Google Patents

从含锌烟道灰制取氧化锌的工艺 Download PDF

Info

Publication number
CN1055766A
CN1055766A CN91103361A CN91103361A CN1055766A CN 1055766 A CN1055766 A CN 1055766A CN 91103361 A CN91103361 A CN 91103361A CN 91103361 A CN91103361 A CN 91103361A CN 1055766 A CN1055766 A CN 1055766A
Authority
CN
China
Prior art keywords
zinc
leaching
impurities
removal
zinc oxide
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN91103361A
Other languages
English (en)
Other versions
CN1029691C (zh
Inventor
张建昌
郭中杰
王永
张吉敏
张立秋
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
GAOCHENG CHEMICAL FERTILIZER FACTORY HEBEI PROV
Original Assignee
GAOCHENG CHEMICAL FERTILIZER FACTORY HEBEI PROV
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by GAOCHENG CHEMICAL FERTILIZER FACTORY HEBEI PROV filed Critical GAOCHENG CHEMICAL FERTILIZER FACTORY HEBEI PROV
Priority to CN91103361A priority Critical patent/CN1029691C/zh
Publication of CN1055766A publication Critical patent/CN1055766A/zh
Application granted granted Critical
Publication of CN1029691C publication Critical patent/CN1029691C/zh
Anticipated expiration legal-status Critical
Expired - Fee Related legal-status Critical Current

Abstract

本发明为一种从含锌烟道灰制取氧化锌技术，它 采用氨——铵法制取，经浸取、除杂、热解、煅烧工艺 流程。在除杂流程中，在浸取罐中加入氢氧化钙，能 将溶液中严重影响产品质量的锰离子除去，并再加入 杂质含量3-5倍的过量锌粉，进一步除杂。本发明 采用常规设备实现了工业上生产，得到氧化锌达 99.7％以上，锌的总收率大于85％，除杂率达 100％。

Description

本发明涉及一种化工技术，适用于制取无机化工锌盐-氧化锌产品。
在炼锌厂和炼钢厂废弃的含锌烟道灰中，含有30-50%的氧化锌，同时含有大量的锰、铅、铜、铁、钴、镍等金属，这种氧化锌在工业上显然不能直接使用，弃之又十分可惜，目前，从含锌烟道灰中制取高纯度的氧化锌产品，是一个迫切需要解决的难题。氨-铵工艺法较好地解决了这个难题，中国专利公开了一种用氨-铵法直接“从菱锌矿中制氧化锌技术”（中国专利申请公开号CN88102610A），但是，应用该技术从含锌烟道灰中制取氧化锌产品，存在有以下缺点：1、溶液中的锰离子不易分离，严重影响了产品质量，2、氨-铵溶液NH3∶CO2大于19.6，该比值过高，造成原料损耗过大，设备要求过高，无法应用于工业上生产，3、使用硫化物除杂剂，由于硫化锌也是一种难溶物质，而影响了锌的回收率。
本发明的目的在于针对上述现有技术中的不足而提供一种用氨-铵法直接从含锌烟道灰中制取高纯度氧化锌的工艺技术，并且该工艺方法除杂彻底，容易净化，适于工业上生产。
本发明的工艺方法是将含锌烟道灰经浸取、除杂、热解、锻烧四个流程，其原理是：
1、浸取
烟道灰中锌主要以氧化锌形式存在，烟道灰用氨水-碳酸氢铵混合溶液进行浸取，其反应为：
同时，一些伴生金属离子也进入溶液，其反应式为：
金属氨络离子的通式为：Me（NH3）n m
在氨-铵混合溶液中，NH∶Me和CO2∶Me的比值应适当，以使锌成为稳定的Zn（NH3）2+ 4络合物进入溶液和获得较高的浸出率，否则，将造成原料损耗过大，设备要求过高，以致于在工业上无法生产。
2、除杂
由于溶液中NH+4的存在抑制了NH3·H2O的电离，使得Mn2+溶于溶液中，不易除去，而Mn2+的存在严重影响了产品的质量。本发明的净化方法是：首先根据氨-铵混合液中的NH3∶Me和CO2∶Me的比值，加入适量的氢氧化钙，增加溶液中OH-的浓度，促使Mn2+沉淀下来，而Ca2+与CO2-3形成CaCO3沉淀，同时，其它不能与氨形成络合物的金属离子也能沉淀下来，其反应式为：
氢氧化钙的加入量过多，将造成氧化锌的损失过大;氢氧化钙的加入量过少，除杂不彻底，因此，氢氧化钙的加入量要适当。
再加入过量的锌粉，锌粉的加入量应是杂质含量的3-5倍，使溶液中的金属离子以单质的形式沉淀下来，从而进一步彻底净化。反应中，Zn先与Cu2+进行置换，再与Pb2+等其它离子进行置换，其反应通式为：
而Zn以Zn（NH3）2+ 4的形式进入溶液，也不会造成浪费。
3、热解
经除杂处理后的溶液，加热裂解为碱式碳酸锌，其反应为：
4、锻烧
经过滤、洗涤后的碱式碳酸锌，在高温下锻烧制得高纯度氧化锌成品，其反应为：
图1是本发明的工艺流程示意图。
以下结合附图对本发明作进一步详述。
按NH3∶ZnO＝4-6，CO2∶ZnO＝1.3-1.6，在浸取罐1中加入氨水、碳酸氢铵，再加入烟道灰，其中，液∶固＝3.5-4.5，溶液PH值在10-11，搅拌速度85转/分钟，浸取罐1中温度控制在40-50℃，搅拌浸取30-60分钟后，加入20-30克/升的氢氧化钙，继续搅拌浸取20-40分钟后，将溶液放入沉降槽2，用三足式离心机过滤，滤渣弃去，清液置于浸取液贮槽4中，用泵5送至置换罐6，溶液PH值在8-10，加入杂质含量3-5倍的锌粉，温度控制在30-50℃，搅拌40-60分钟，除去杂质，液体用泥浆泵7进入过滤器8过滤，并将除杂渣回收，用于提取有用元素。滤液用泵9送至蒸发罐10中进行真空加热分解，真空吸氨回收温度为30-35℃，加热温度为75-85℃，加热后沉淀和母液放入三足式离心机11过滤，母液流入氨回收槽14和蒸发罐10的氨蒸气通过喷射吸氨泵13进入氨回收槽14中，再经泵15送回浸取罐1中循环使用。滤饼送至回转炉12，温度600-700℃，锻烧成高纯度氧化锌成品。
本发明工艺流程短，使用设备少，投资省，操作方便，采用常规设备实现了工业化生产，得到氧化锌达99.7%以上，锌的总收率大于85%，尤其是除去了严重影响产品质量的锰离子，除杂率100%。
本发明的实施例采用辽宁葫芦岛炼锌厂的烟道灰，含氧化锌47%，以工业铵水17.1%、农用碳酸氢铵、氢氧化钙、锌粉为原料。
1、浸出。
2、除Mn2+（取浸取液1升）
浸取液 浸取液 Ca（OH）2渣中 净化液 收率
ZnO克/升 Mn2+克/升 克/升 ZnO克 Mn2+%
92.8  0.0128  20  5.4  无  94.18
92.8  0.0128  25  6.8  无  92.73
92.8  0.0128  30  7.2  无  92.24
3、置换
浸取液  Zn粉  置换液  置换液
ZnO克/升  倍数  ZnO克/升  Pb
92.8  4  94.7  0.04
92.8  4.5  95.2  0.025
92.8  5  96.3  ＜0.025

Claims (4)

1、一种从含锌烟道灰制取氧化锌的工艺，它采用氨水-碳酸氢铵法制取，经浸取、除杂、热解、锻烧等流程获得成品，其特征是，在除杂流程中，在浸取罐中加入氢氧化钙。
2、根据权利要求1所述的工艺，其特征是，在浸取流程中，浸取罐中的氨-铵溶液组份比为NH3∶ZnO＝4-6，CO2∶ZnO＝1.3-1.6。
3、根据权利要求2所述的工艺，其特征是，氢氧化钙的加入量为20-30克/升。
4、根据权利要求1所述的工艺，其特征是，除杂流程还包括在置换罐中加入过量锌粉，其中，锌粉的加入量为杂质含量的3-5倍。
CN91103361A 1991-05-27 1991-05-27 从含锌烟道灰制取氧化锌的工艺 Expired - Fee Related CN1029691C (zh)