CN105568275A - 一种汽车铝制踏板防腐蚀处理用防腐基础液 - Google Patents

一种汽车铝制踏板防腐蚀处理用防腐基础液 Download PDF

Info

Publication number
CN105568275A
CN105568275A CN201511013713.2A CN201511013713A CN105568275A CN 105568275 A CN105568275 A CN 105568275A CN 201511013713 A CN201511013713 A CN 201511013713A CN 105568275 A CN105568275 A CN 105568275A
Authority
CN
China
Prior art keywords
parts
corrosion resistant
foundation liquid
pedal
aluminum
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201511013713.2A
Other languages
English (en)
Inventor
金晶
金哲
王信
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Jin Yu Petrochemical Equipment Co Ltd Of Wuhu City
Original Assignee
Jin Yu Petrochemical Equipment Co Ltd Of Wuhu City
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Jin Yu Petrochemical Equipment Co Ltd Of Wuhu City filed Critical Jin Yu Petrochemical Equipment Co Ltd Of Wuhu City
Priority to CN201511013713.2A priority Critical patent/CN105568275A/zh
Publication of CN105568275A publication Critical patent/CN105568275A/zh
Pending legal-status Critical Current

Abstract

本发明涉及模具加工技术领域，具体是涉及一种汽车铝制踏板防腐蚀处理用防腐基础液。由20份聚醋酸乙烯乳液、20份二乙醇胺、10份1,4-二氧六环、5份稀盐酸、0.5份甘草皂甙、10份乙醇和50份水制成。本发明的防腐基础液，其配方设计合理、新颖，特别是添加了少量的甘草皂甙，可以显著提高后续防腐处理的效率，使铝制踏板的防腐性能得到显著提升，并极大地延长踏板的使用寿命。

Description

一种汽车铝制踏板防腐蚀处理用防腐基础液
技术领域
本发明涉及模具加工技术领域，具体是涉及一种汽车铝制踏板防腐蚀处理用防腐基础液。
背景技术
铝制踏板在加工成型时，需要对其进行防腐蚀处理。现有技术在进行防腐处理时，不存在任何的预处理方案，直接进行防腐蚀处理。这种加工模式容易导致铝制踏板的的防腐层的使用寿命大大折扣。
发明内容
针对现有技术中存在的技术问题，本发明的目的在于提供一种汽车铝制踏板防腐蚀处理用防腐基础液，为实现上述目的，本发明采用了以下技术方案：
一种汽车铝制踏板防腐蚀处理用防腐基础液，由20份聚醋酸乙烯乳液、20份二乙醇胺、10份1,4-二氧六环、5份稀盐酸、0.5份甘草皂甙、10份乙醇和50份水制成。
本发明的有益效果表现在：
1）、防腐蚀处理方法中使用的防腐基础液，其配方设计合理、新颖，特别是添加了少量的甘草皂甙，可以显著提高后续防腐处理的效率，使铝制踏板的防腐性能得到显著提升，并极大地延长踏板的使用寿命。
2）、防腐基础液的制备方法，通过逐步添加的方法，通过合理设计加料顺序，不仅能够提高各物质之间的溶解性能，还能避免颗粒团聚的可能，并使防腐基础液的防腐处理效率得到显著提升。
3）、防腐蚀处理方法，操作工艺简单，通过添加合理的防腐基础液进行浸泡，并合理设计防腐基础液的配方以及防腐基础液的制备方法，使铝制踏板的防腐性能得到显著提升，并极大地延长踏板的使用寿命。
具体实施方式
以下将结合实施例，对本发明进行较为详细的说明。但是，实施例内容仅是对本发明所作的举例和说明，所属本技术领域的技术人员对所描述的具体实施例做各种各样的修改或补充或采用类似的方式替代，只要不偏离发明的构思或者超越本权利要求书所定义的范围，均应属于本发明的保护范围。
一、防腐基础液的组成
20份聚醋酸乙烯乳液、20份二乙醇胺、10份1,4-二氧六环、5份稀盐酸、0.5份甘草皂甙、10份乙醇和50份水。
二、防腐基础液的制备方法为：
首先向容器中加入20份聚醋酸乙烯乳液、20份二乙醇胺和15份水，搅拌5分钟；接着缓慢加入5份稀盐酸，边加边搅拌，添加完毕后搅拌10分钟；接着缓慢加入10份1,4-二氧六环和15份水，边加边搅拌，添加完毕后搅拌5分钟；然后缓慢加入0.5份甘草皂甙，边加边搅拌，添加完毕后搅拌5分钟；最后快速加入10份乙醇和20份水，搅拌20分钟。
三、汽车铝制踏板防腐蚀处理用防腐基础液
步骤①、将铝制踏板放入预先加热至55℃的防腐基础液中浸泡30分钟；
步骤②、在铝制踏板表面采用离子注入方式注入磷酸锆、二氧化硅、铬酸铬和氟硅酸钠形成厚度为100nm的不溶共络层；
步骤③、再在铝制踏板表面形成金属氧化层；
步骤④、在铝制踏板的金属氧化层上涂厚度为200nm的底漆。

Claims (1)

1.一种汽车铝制踏板防腐蚀处理用防腐基础液，其特征在于由20份聚醋酸乙烯乳液、20份二乙醇胺、10份1,4-二氧六环、5份稀盐酸、0.5份甘草皂甙、10份乙醇和50份水制成。
CN201511013713.2A 2015-12-31 2015-12-31 一种汽车铝制踏板防腐蚀处理用防腐基础液 Pending CN105568275A (zh)