CN105567395A - Enameled wire surface treatment agent and preparation method thereof - Google Patents
Enameled wire surface treatment agent and preparation method thereof Download PDFInfo
- Publication number
- CN105567395A CN105567395A CN201511007147.4A CN201511007147A CN105567395A CN 105567395 A CN105567395 A CN 105567395A CN 201511007147 A CN201511007147 A CN 201511007147A CN 105567395 A CN105567395 A CN 105567395A
- Authority
- CN
- China
- Prior art keywords
- surface treatment
- parts
- treatment agent
- wire surface
- enameled wire
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses an enameled wire surface treatment agent and a preparation method thereof; the enameled wire surface treatment agent comprises the components in parts by mass: 90-99 parts of 3GS refrigerant oil, 1-6 parts of paraffin, 0.5-4 parts of silicone oil, and 0.03-0.5 part of tetrabutyl titanate. After an enameled wire is treated by the enameled wire surface treatment agent, the enameled wire can have smaller static friction coefficient so as to be in favor of high-speed wire wrapping and avoid air pollution and safety hazards.
Description
Technical field
the present invention relates to a kind of enamelled wire surface treatment agent and preparation method thereof, belong to Production of Enamel Wires technical field.
Background technology
in the use procedure of enameled wire, when enameled wire will carry out high-speed winding, need to use surface treatment agent to carry out surface treatment to enameled wire.Existing enamelled wire surface treatment agent mainly mixes with the paraffin of 1:20 and No. 120 gasoline, and it is solvent with gasoline, after being coated to enamelled wire surface, and solvent evaporates, thus make paraffin be uniformly distributed in enamelled wire surface.This existing enamelled wire surface treatment agent is mainly used in the very little material surface of copper-in-aluminum enameled wire and aluminium enamel-covered wire isodensity and coefficient of extension.But there is the too high problem of static friction coefficient when the precipitation of enamelled wire surface still can make enameled wire at high-speed winding in paraffin.And the volatilization of petrolic solvent not only can pollute workshop air, and hold fire hazardous or blast, and larger potential safety hazard will certainly be there is in the storage of the large petrol in workshop.
Summary of the invention
the object of the invention is to, a kind of enamelled wire surface treatment agent and preparation method thereof is provided.After using it to process enameled wire, enameled wire can be made to have less static friction coefficient and be beneficial to high-speed winding, and 3GS oil is non-volatile matter, can avoid atmospheric pollution and potential safety hazard.
technical scheme of the present invention: a kind of enamelled wire surface treatment agent, is characterized in: by mass parts, it comprises every 3GS refrigeration oil 90 ~ 99 parts, 1 ~ 6 part, paraffin, silicone oil 0.5 ~ 4 part and positive butyl (tetra) titanate 0.03 ~ 0.5 part.
in above-mentioned enamelled wire surface treatment agent, as preferably, by mass parts, it comprises every 3GS refrigeration oil 94 ~ 96 parts, 2 ~ 4 parts, paraffin, silicone oil 1 ~ 2 part and positive butyl (tetra) titanate 0.05 ~ 0.2 part.
in aforesaid enamelled wire surface treatment agent, as further preferred: by mass parts, it comprises every 3GS refrigeration oil 95.4 parts, 3 parts, paraffin, silicone oil 1.5 parts and positive butyl (tetra) titanate 0.1 part.
the preparation method of aforesaid enamelled wire surface treatment agent, is characterized in, comprises the following steps:
a, in 3GS refrigeration oil, add paraffin, silicone oil and positive butyl (tetra) titanate, obtain mixed liquor A;
b, mixed liquor A is stirred after, the shearing carried out in high-shear emulsion machine 6 ~ 10 minutes can obtain the mixed solution of high evenness.
in the preparation method of aforesaid enamelled wire surface treatment agent, in order to promote uniformity coefficient, the shearing rotating speed of the high-shear emulsion machine in described step b is 1500rpm.
compared with prior art, the present invention uses 3GS refrigeration oil to coordinate the formula of paraffin, silicone oil 1 and positive butyl (tetra) titanate to form novel enamelled wire surface treatment agent, when using it to carry out surface treatment to enameled wire, volatilization phenomenon can not be there is, higher at the residual rate of enamelled wire surface, can form insulation layer further at enamelled wire surface, and then improve the voltage endurance capability of enameled wire, prevention enamelled wire surface needle outlet is bad.And it can also improve the static friction coefficient of enamelled wire surface, thus be conducive to high-speed winding.Because material of the present invention has higher flame retardant resistance, even if Production of Enamel Wires workshop exists high temperature, naked light (spirit lamp of welding) situation, do not have the risk of fire explosion yet.Through the actual analysis of experiments used, enamelled wire surface treatment agent of the present invention is when the process for copper enameled wire, and performance boost is particularly remarkable.
Embodiment
below in conjunction with embodiment, the present invention is further illustrated, but not as the foundation limited the present invention.
embodiment.A kind of enamelled wire surface treatment agent, by mass parts, it comprises every 3GS refrigeration oil 90 ~ 99 parts, 1 ~ 6 part, paraffin, silicone oil 0.5 ~ 4 part and positive butyl (tetra) titanate 0.03 ~ 0.5 part.
as preferably, by mass parts, it comprises every 3GS refrigeration oil 94 ~ 96 parts, 2 ~ 4 parts, paraffin, silicone oil 1 ~ 2 part and positive butyl (tetra) titanate 0.05 ~ 0.2 part.
further preferably, by mass parts, it comprises every 3GS refrigeration oil 95.4 parts, 3 parts, paraffin, silicone oil 1.5 parts and positive butyl (tetra) titanate 0.1 part.
the preparation method of enamelled wire surface treatment agent, comprises the following steps:
a, in 3GS refrigeration oil, add paraffin, silicone oil and positive butyl (tetra) titanate, obtain mixed liquor A;
b, mixed liquor A is stirred after, in high-shear emulsion machine, carry out the shearing of 6 ~ 10 minutes with the rotating speed of 1500rpm.
Claims (5)
1. an enamelled wire surface treatment agent, is characterized in that: by mass parts, and it comprises every 3GS refrigeration oil 90 ~ 99 parts, 1 ~ 6 part, paraffin, silicone oil 0.5 ~ 4 part and positive butyl (tetra) titanate 0.03 ~ 0.5 part.
2. enamelled wire surface treatment agent according to claim 1, is characterized in that: by mass parts, and it comprises every 3GS refrigeration oil 94 ~ 96 parts, 2 ~ 4 parts, paraffin, silicone oil 1 ~ 2 part and positive butyl (tetra) titanate 0.05 ~ 0.2 part.
3. enamelled wire surface treatment agent according to claim 2, is characterized in that: by mass parts, and it comprises every 3GS refrigeration oil 95.4 parts, 3 parts, paraffin, silicone oil 1.5 parts and positive butyl (tetra) titanate 0.1 part.
4. the preparation method of the enamelled wire surface treatment agent described in claim 1,2 or 3, is characterized in that, comprise the following steps:
A, in 3GS refrigeration oil, add paraffin, silicone oil and positive butyl (tetra) titanate, obtain mixed liquor A;
B, mixed liquor A is stirred after, in high-shear emulsion machine, carry out the shearing of 6 ~ 10 minutes.
5. the preparation method of enamelled wire surface treatment agent according to claim 4, is characterized in that: the shearing rotating speed of the high-shear emulsion machine in described step b is 1500rpm.