CN103396861A - Lubricating oil for varnished wires and application thereof - Google Patents
Lubricating oil for varnished wires and application thereof Download PDFInfo
- Publication number
- CN103396861A CN103396861A CN2013103446452A CN201310344645A CN103396861A CN 103396861 A CN103396861 A CN 103396861A CN 2013103446452 A CN2013103446452 A CN 2013103446452A CN 201310344645 A CN201310344645 A CN 201310344645A CN 103396861 A CN103396861 A CN 103396861A
- Authority
- CN
- China
- Prior art keywords
- lubricating oil
- oil
- lacquered wire
- methyl
- varnished wires
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses lubricating oil for varnished wires and an application thereof. The lubricating oil for the varnished wires comprises the following components: 1-3% of methyl silicone oil, 2-5% of 848 lubricating oil, and the balance being 3GS machine oil, wherein the percentage is the mass percentage. The obtained lubricating oil for the varnished wires is not easy to burn while meeting electronic sparks or open fire, and has quite high safety; the obtained lubricating oil has low coefficient of friction, thereby allowing the wire breaking rate to be low, quickening the pay-off speed during production, and allowing the yield to be greatly improved; the obtained varnished wires have more smooth and more bright surfaces, and the insulation performance of the varnished wires can be also better ensured; and the cost is low.
Description
Technical field
What the present invention relates to is a kind of Lacquered wire lubricating oil and application thereof.
Background technology
Enameled wire is a principal item of winding wire, by conductor and two ones of insulation layers, formed, bare wire after annealing softening, then through repeatedly the japanning, cure and form.Due to when coiling, between enameled wire and mechanical means, have friction, so enameled wire itself needs that not only enough physical strengths are arranged, it is enough smooth that also want on its surface, the coil that enameled wire successfully could be turned to closely like this, be suitable for.
Enameled wire makes with lubricator when producing, can make winding displacement neat, and take-up is tight.At present, in China's Production of Enamel Wires, be to adopt kerosene, the countless transformer oil lubricant as surface of insulating layer mostly.Along with updating of winding machine, its threading speed improves constantly, and from original 4000, turns and brings up to 12000-15000 and turn, and the wear-resisting quality of enameled wire is also had to requirements at the higher level, and original lubricating oil can not meet the demands gradually.Also useful paraffin is dissolved in gasoline as enameled wire surface lubricating oil, although the slip of enameled wire has had larger improvement, the solvability of paraffin is bad, separating out of precipitation easily occur, during such enameled wire coiling, is dissolved in and long-pending wax occurs, produces broken string.
Summary of the invention
The present invention seeks to be to provide a kind of Lacquered wire lubricating oil and application thereof.
To achieve these goals, the present invention realizes by the following technical solutions:
A kind of Lacquered wire lubricating oil comprises following component: methyl-silicone oil 1-3%, 848 lubricating oil 2-5%, and 3GS machine oil surplus, described per-cent is mass percent.
Above-mentioned each component has produced good synergistic effect, and the gained Lacquered wire lubricating oil is nonflammable, high pressure resistant, makes the gained enamelled wire surface more smooth, brighter, has also better guaranteed the insulating property of enameled wire; And with low cost.
Lubricity, high voltage performance in order to improve product, strengthen the synergistic effect between each component simultaneously, above-mentioned Lacquered wire lubricating oil, comprise following component: methyl-silicone oil 1-3%, 848 lubricating oil 2-5%, turps 3-5%, 3GS machine oil surplus, described per-cent is mass percent.
In order to improve the use properties of product, especially weather resistance, strengthen simultaneously the synergistic effect between each component, above-mentioned Lacquered wire lubricating oil, comprise following component: methyl-silicone oil 1-3%, 848 lubricating oil 2-5%, turps 3-5%, polyethylene wax 0.5-1%, 3GS machine oil surplus, described per-cent are mass percent.
In order further to guarantee the use properties of products obtained therefrom, polyethylene wax is the CH-2 polyethylene wax.
In order further to guarantee the use properties of product, above-mentioned Lacquered wire lubricating oil comprises following component: methyl-silicone oil 1.4-1.6%, 848 lubricating oil 2.8-3.2%, turps 3.5-4.5%, polyethylene wax 0.6-0.8%, 3GS machine oil surplus.Preferably, above-mentioned Lacquered wire lubricating oil comprises following component: methyl-silicone oil 1.5%, 848 lubricating oil 3%, turps 4%, polyethylene wax 0.7%, 3GS machine oil surplus.
In order further to guarantee the use properties of gained lubricating oil, methyl-silicone oil is dimethyl silicone oil.
The use temperature of above-mentioned Lacquered wire lubricating oil is 80-100 ℃.Preferably, the use temperature of Lacquered wire lubricating oil is 80 ℃.
The NM technology of the present invention is prior art.
Gained Lacquered wire lubricating oil of the present invention is met the electronics spark, naked light can not burn easily yet, and security is very high; Frictional coefficient is low, so outage is few, in production, can accelerate payingoff speed, and output has had significantly lifting; The gained enamelled wire surface is more smooth, brighter, has also better guaranteed the insulating property of enameled wire; And with low cost.
Embodiment
In order to understand better the present invention, below in conjunction with embodiment, further illustrate content of the present invention, but content of the present invention not only is confined to the following examples.
In embodiment, 3GS machine oil used is SUN 3GS refrigerator oil, and 848 lubricating oil are purchased from Shanghai logical vast and boundless industry and trade Development Co., Ltd.
Each performance test instrument is: voltage breakdown: Hunan, Changsha letter instrument QDS-15KV8358; Frictional coefficient: stiction tester: JMC-1-0461; Pin hole: salt solution pin hole tester: YZK-1-8183; Pliability: be the pliability tester in 2013202668530 embodiment with reference to application number.
Embodiment 1
201 methyl-silicone oils 1%, 848 lubricating oil 2%, 3GS machine oil surplus, mix, and obtains Lacquered wire lubricating oil a, and chance electronics spark, naked light do not burn yet, and described per-cent is mass percent.
Embodiment 2
201 methyl-silicone oils 3%, 848 lubricating oil 5%, 3GS machine oil surplus, mix, and obtains Lacquered wire lubricating oil b, and chance electronics spark, naked light do not burn yet, and described per-cent is mass percent.
Embodiment 3
201 methyl-silicone oils 1.4%, 848 lubricating oil 2.8%, turps (taking chemical industry company limited purchased from the Ward, Tianjin) 3.5%, polyethylene wax (model: STKJ-101 type, brand: contain and rise) 0.6%, 3GS machine oil surplus, mix, and obtains Lacquered wire lubricating oil c, chance electronics spark, naked light do not burn yet, and described per-cent is mass percent.
Embodiment 4
201 methyl-silicone oils 1.6%, 848 lubricating oil 3.2%, turps (taking chemical industry company limited purchased from the Ward, Tianjin) 4.5%, polyethylene wax (model: CH-2A polyethylene wax pattern, brand: Hua Yi) 0.8%, 3GS machine oil surplus, mix, and obtains Lacquered wire lubricating oil d, chance electronics spark, naked light do not burn yet, and described per-cent is mass percent.
Embodiment 5
Dimethyl silicone oil 1.5%, 848 lubricating oil 3%, turps (taking chemical industry company limited purchased from the Ward, Tianjin) 4%, polyethylene wax (model: CH-2A polyethylene wax pattern, brand: Hua Yi) 0.7%, 3GS machine oil surplus, mix, and obtains Lacquered wire lubricating oil e, chance electronics spark, naked light do not burn yet, and described per-cent is mass percent.
The using method of the various embodiments described above: in the various embodiments described above, the use temperature of the Lacquered wire lubricating oil of gained is 80 ℃, and concrete using method is with reference to prior art, and the specification of each embodiment enameled wire used is 0.17mm, and performance is as shown in table 1.
Performance when enameled wire is arranged with the various embodiments described above gained lubricating oil outward is as shown in table 1:
| Embodiment | Voltage breakdown | Frictional coefficient | Pin hole | Pliability |
| Enameled wire | 5.0kv | 0.170 | 1 | 220mm |
| Lacquered wire lubricating oil a | 5.6kv | 0.096 | 0 | 255mm |
| Lacquered wire lubricating oil b | 5.3kv | 0.160 | 0 | 240mm |
| Lacquered wire lubricating oil c | 6.0kv | 0.086 | 0 | 255mm |
| Lacquered wire lubricating oil d | 6.2kv | 0.082 | 0 | 260mm |
| Lacquered wire lubricating oil e | 6.3kv | 0.076 | 0 | 260mm |
Claims (9)
1. Lacquered wire lubricating oil is characterized in that: comprise following component: methyl-silicone oil 1-3%, 848 lubricating oil 2-5%, and 3GS machine oil surplus, described per-cent is mass percent.
2. Lacquered wire lubricating oil as claimed in claim 1 is characterized in that: comprise following component: methyl-silicone oil 1-3%, 848 lubricating oil 2-5%, and turps 3-5%, 3GS machine oil surplus, described per-cent is mass percent.
3. Lacquered wire lubricating oil as claimed in claim 1 is characterized in that: comprise following component: methyl-silicone oil 1-3%, 848 lubricating oil 2-5%, and turps 3-5%, polyethylene wax 0.5-1%, 3GS machine oil surplus, described per-cent is mass percent.
4. Lacquered wire lubricating oil as claimed in claim 3, it is characterized in that: described polyethylene wax is the CH-2 polyethylene wax.
5. Lacquered wire lubricating oil as described as claim 3 or 4, is characterized in that: comprise following component: methyl-silicone oil 1.4-1.6%, 848 lubricating oil 2.8-3.2%, turps 3.5-4.5%, polyethylene wax 0.6-0.8%, 3GS machine oil surplus.
6. Lacquered wire lubricating oil as claimed in claim 2, is characterized in that: comprise following component: methyl-silicone oil 1.5%, 848 lubricating oil 3%, turps 4%, polyethylene wax 0.7%, 3GS machine oil surplus.
7. as the described Lacquered wire lubricating oil of claim 1-4 any one, it is characterized in that: methyl-silicone oil is dimethyl silicone oil.
8. the application of the described Lacquered wire lubricating oil of claim 1-7 any one is characterized in that: the use temperature of Lacquered wire lubricating oil is 80-100 ℃.
9. application as claimed in claim 8 is characterized in that: the use temperature of Lacquered wire lubricating oil is 80 ℃.