CN105566933A - Wood-plastic floor for basketball court - Google Patents
Wood-plastic floor for basketball court Download PDFInfo
- Publication number
- CN105566933A CN105566933A CN201610073510.0A CN201610073510A CN105566933A CN 105566933 A CN105566933 A CN 105566933A CN 201610073510 A CN201610073510 A CN 201610073510A CN 105566933 A CN105566933 A CN 105566933A
- Authority
- CN
- China
- Prior art keywords
- parts
- wood
- powder
- oil
- plastic floor
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A wood-plastic floor for a basketball court is prepared from, by weight, 52-66 parts of wood powder, 26-31 parts of PVC resin, 9-15 parts of barium carbonate, 31-41 parts of methyl salicylate, 17-25 parts of phenolic resin, 17-25 parts of polypropylene, 15-20 parts of Mongolian snakegourd roots, 2-5 parts of loofah sponges, 8-13 parts of talcum powder, 8-13 parts of montmorillonite, 5-9 parts of kaolin, 5-9 parts of quartz powder, 1-5 parts of polyacrylamide, 6-13 parts of polyethylene glycol distearate, 12-15 parts of poly(methyl sorbate), 7-11 parts of vines of trichosanthes kirilowii Maxim., 2.5-3.5 parts of dandelions, 0.5-1 part of banana peel, 0.2-0.5 part of mint oil and 0.1-0.2 part of sunflower seed oil. The wood-plastic floor is good in water resistance, mould resistance, salt mist resistance and acid and alkali resistance and high in pressure-bearing capacity, the surface of the wood-plastic floor can prevent skid and is not prone to scratch, and the wood-plastic floor can bear long-time water soaking and is particularly suitable for being used for the basketball court and wide in application prospect.
Description
Technical field
The present invention relates to wood-plastic floor board field, be specifically related to a kind of court wood-plastic floor board.
Background technology
Wood plastic boards is a kind of matrix material of main material and other materials based on timber, and topmost purposes is that alternative solid wood is applied in each field, has namely saved timber, and has improved result of use.Court is stood athletic race for a long time and is jumped pressure, and the dipping of the liquid such as sweat, beverage drippage, sometimes may be subject to the scuffing of sharp sharp instrument, all can affect normally carrying out of floor result of use and Basketball Match.Can say that court is very strict to the requirement on floor, so need a kind of floor to meet the demand of court.
Summary of the invention
Technical problem to be solved by this invention is to provide a kind of waterproof, mould proof, Defend salt fog, resistance to acids and bases are good, bearing capacity is strong, surface anti-skidding and not easily anti-scratch, can stand long water soaking, be particularly suitable for the court wood-plastic floor board that court uses.
Technical problem to be solved by this invention realizes by the following technical solutions:
A kind of court wood-plastic floor board, the raw material of following weight part is adopted to make: wood powder 52-66 part, polyvinyl chloride resin 26-31 part, barium carbonate 9-15 part, wintergreen oil 31-41 part, resol 17-25 part, polypropylene 17-25 part, Snakegourd Root 15-20 part, Vegetable Sponge of Luffa 2-5 part, talcum powder 8-13 part, montmorillonite 8-13 part, kaolin 5-9 part, silica powder 5-9 part, polyacrylamide 1-5 part, polyoxyethylene glycol distearyl acid fat 6-13 part, poly-Sorbic Acid formicester 12-15 part, Snakegourd Fruit rattan 7-11 part, taraxacum 2.5-3.5 part, Pericarpium Musae 0.5-1 part, spearmint oil 0.2-0.5 part, sunflower seed oil 0.1-0.2 part.
Preferably, a kind of court wood-plastic floor board, adopts the raw material of following weight part to make: wood powder 52 parts, polyvinyl chloride resin 26 parts, barium carbonate 9 parts, wintergreen oil 31 parts, 17 parts, resol, polypropylene 17 parts, Snakegourd Root 15 parts, Vegetable Sponge of Luffa 2 parts, talcum powder 8 parts, montmorillonite 8 parts, kaolin 5 parts, silica powder 5 parts, polyacrylamide 1 part, polyoxyethylene glycol distearyl acid 6 parts, fat, poly-Sorbic Acid formicester 12 parts, 7 parts, Snakegourd Fruit rattan, taraxacum 2.5 parts, Pericarpium Musae 0.5 part, spearmint oil 0.2 part, sunflower seed oil 0.1 part.
Preferably, a kind of court wood-plastic floor board, adopts the raw material of following weight part to make: wood powder 59 parts, polyvinyl chloride resin 28 parts, barium carbonate 12 parts, wintergreen oil 36 parts, 21 parts, resol, polypropylene 21 parts, Snakegourd Root 18 parts, Vegetable Sponge of Luffa 3 parts, talcum powder 11 parts, montmorillonite 11 parts, kaolin 7 parts, silica powder 7 parts, polyacrylamide 3 parts, polyoxyethylene glycol distearyl acid 10 parts, fat, poly-Sorbic Acid formicester 13 parts, 9 parts, Snakegourd Fruit rattan, taraxacum 3 parts, Pericarpium Musae 0.8 part, spearmint oil 0.3 part, sunflower seed oil 0.15 part.
Preferably, a kind of court wood-plastic floor board, adopts the raw material of following weight part to make: wood powder 66 parts, polyvinyl chloride resin 31 parts, barium carbonate 15 parts, wintergreen oil 41 parts, 25 parts, resol, polipropene 25 part, Snakegourd Root 20 parts, Vegetable Sponge of Luffa 5 parts, talcum powder 13 parts, montmorillonite 13 parts, kaolin 9 parts, silica powder 9 parts, polyacrylamide 5 parts, polyoxyethylene glycol distearyl acid 13 parts, fat, poly-Sorbic Acid formicester 15 parts, 11 parts, Snakegourd Fruit rattan, taraxacum 3.5 parts, Pericarpium Musae 1 part, spearmint oil 0.5 part, sunflower seed oil 0.2 part.
A preparation method for court wood-plastic floor board, comprises the following steps,
(1). get the Vegetable Sponge of Luffa of described weight part of filling a prescription, to add 2-5 concentration be doubly that the soda ash solution of 10-20% soaks 24 hours for Snakegourd Fruit rattan, taraxacum, Pericarpium Musae, temperature controls at 70-90 DEG C, pressure-controlling is at 3-5MPa, then use washed with de-ionized water 2-5 minute, drain, then put into dryer inner drying, bake out temperature is 120-160 DEG C, make water ratio be not more than 2.2%, take out, then grind to form 50-80 order powder;
(2). get the wood powder of described weight part of filling a prescription, polyvinyl chloride resin, barium carbonate, wintergreen oil, resol, polypropylene, Snakegourd Root, talcum powder, montmorillonite, kaolin, silica powder, polyacrylamide, polyoxyethylene glycol distearyl acid fat, poly-Sorbic Acid formicester add vulcanizing boiler and carry out sulfidizing, in tank temperature control 125-155 DEG C, pressure-controlling 1-2MPa, sofening treatment time controling is at 5-10 hour, take out, then grind to form 50-80 order powder;
(3). by step (1) and step (2) gained powder through charcoal absorption process, drop into blender spice again, spice temperature is 55-72 DEG C, then the spearmint oil, the sunflower seed oil that add described weight part of filling a prescription together are sent into twin screw extruder high temperature and are extruded, and extrusion temperature is 165-195 DEG C;
(4). the material extruded through mould shape, then uses water quench shaping, and water coolant comprises the citric acid of 2-5%, the wintergreen oil of 1-2%, and temperature of cooling water is 15-27 DEG C;
(5). the floor of cooling forming is cut, polishing.
The invention has the beneficial effects as follows: wood-plastic floor board waterproof of the present invention, mould proof, Defend salt fog, resistance to acids and bases are good, bearing capacity is strong, surface anti-skidding and not easily anti-scratch, can stand long water soaking, be particularly suitable for court and use, have a extensive future.
Embodiment
The technique means realized to make the present invention, creation characteristic, reaching object and effect is easy to understand, below in conjunction with specific embodiment, setting forth the present invention further.
Embodiment 1
A kind of court wood-plastic floor board, adopts the raw material of following weight part to make: wood powder 52 parts, polyvinyl chloride resin 26 parts, barium carbonate 9 parts, wintergreen oil 31 parts, 17 parts, resol, polypropylene 17 parts, Snakegourd Root 15 parts, Vegetable Sponge of Luffa 2 parts, talcum powder 8 parts, montmorillonite 8 parts, kaolin 5 parts, silica powder 5 parts, polyacrylamide 1 part, polyoxyethylene glycol distearyl acid 6 parts, fat, poly-Sorbic Acid formicester 12 parts, 7 parts, Snakegourd Fruit rattan, taraxacum 2.5 parts, Pericarpium Musae 0.5 part, spearmint oil 0.2 part, sunflower seed oil 0.1 part.
A preparation method for court wood-plastic floor board, comprises the following steps,
(1). get the Vegetable Sponge of Luffa of described weight part of filling a prescription, concentration that Snakegourd Fruit rattan, taraxacum, Pericarpium Musae add 2 times be 10% soda ash solution soak 24 hours, temperature controls at 70 DEG C, pressure-controlling is at 3MPa, then use washed with de-ionized water 2 minutes, drain, then put into dryer inner drying, bake out temperature is 120 DEG C, make water ratio be not more than 2.2%, take out, then grind to form 50 order powder;
(2). get the wood powder of described weight part of filling a prescription, polyvinyl chloride resin, barium carbonate, wintergreen oil, resol, polypropylene, Snakegourd Root, talcum powder, montmorillonite, kaolin, silica powder, polyacrylamide, polyoxyethylene glycol distearyl acid fat, poly-Sorbic Acid formicester add vulcanizing boiler and carry out sulfidizing, in tank temperature control 125 DEG C, pressure-controlling 1MPa, sofening treatment time controling is at 5 hours, take out, then grind to form 50 order powder;
(3). by step (1) and step (2) gained powder through charcoal absorption process, drop into blender spice again, spice temperature is 55 DEG C, then the spearmint oil, the sunflower seed oil that add described weight part of filling a prescription together are sent into twin screw extruder high temperature and are extruded, and extrusion temperature is 165 DEG C;
(4). the material extruded through mould shape, then uses water quench shaping, and water coolant comprises the citric acid of 2%, the wintergreen oil of 1%, and temperature of cooling water is 15 DEG C;
(5). the floor of cooling forming is cut, polishing.
Embodiment 2
A kind of court wood-plastic floor board, adopts the raw material of following weight part to make: wood powder 59 parts, polyvinyl chloride resin 28 parts, barium carbonate 12 parts, wintergreen oil 36 parts, 21 parts, resol, polypropylene 21 parts, Snakegourd Root 18 parts, Vegetable Sponge of Luffa 3 parts, talcum powder 11 parts, montmorillonite 11 parts, kaolin 7 parts, silica powder 7 parts, polyacrylamide 3 parts, polyoxyethylene glycol distearyl acid 10 parts, fat, poly-Sorbic Acid formicester 13 parts, 9 parts, Snakegourd Fruit rattan, taraxacum 3 parts, Pericarpium Musae 0.8 part, spearmint oil 0.3 part, sunflower seed oil 0.15 part.
A preparation method for court wood-plastic floor board, comprises the following steps,
(1). get the Vegetable Sponge of Luffa of described weight part of filling a prescription, concentration that Snakegourd Fruit rattan, taraxacum, Pericarpium Musae add 3 times be 15% soda ash solution soak 24 hours, temperature controls at 80 DEG C, pressure-controlling is at 4MPa, then use washed with de-ionized water 3 minutes, drain, then put into dryer inner drying, bake out temperature is 140 DEG C, make water ratio be not more than 2.2%, take out, then grind to form 60 order powder;
(2). get the wood powder of described weight part of filling a prescription, polyvinyl chloride resin, barium carbonate, wintergreen oil, resol, polypropylene, Snakegourd Root, talcum powder, montmorillonite, kaolin, silica powder, polyacrylamide, polyoxyethylene glycol distearyl acid fat, poly-Sorbic Acid formicester add vulcanizing boiler and carry out sulfidizing, in tank temperature control 140 DEG C, pressure-controlling 1.5MPa, sofening treatment time controling is at 8 hours, take out, then grind to form 60 order powder;
(3). by step (1) and step (2) gained powder through charcoal absorption process, drop into blender spice again, spice temperature is 65 DEG C, then the spearmint oil, the sunflower seed oil that add described weight part of filling a prescription together are sent into twin screw extruder high temperature and are extruded, and extrusion temperature is 180 DEG C;
(4). the material extruded through mould shape, then uses water quench shaping, and water coolant comprises the citric acid of 3%, the wintergreen oil of 1.5%, and temperature of cooling water is 22 DEG C;
(5). the floor of cooling forming is cut, polishing.
Embodiment 3
A kind of court wood-plastic floor board, adopts the raw material of following weight part to make: wood powder 66 parts, polyvinyl chloride resin 31 parts, barium carbonate 15 parts, wintergreen oil 41 parts, 25 parts, resol, polipropene 25 part, Snakegourd Root 20 parts, Vegetable Sponge of Luffa 5 parts, talcum powder 13 parts, montmorillonite 13 parts, kaolin 9 parts, silica powder 9 parts, polyacrylamide 5 parts, polyoxyethylene glycol distearyl acid 13 parts, fat, poly-Sorbic Acid formicester 15 parts, 11 parts, Snakegourd Fruit rattan, taraxacum 3.5 parts, Pericarpium Musae 1 part, spearmint oil 0.5 part, sunflower seed oil 0.2 part.
A preparation method for court wood-plastic floor board, comprises the following steps,
(1). get the Vegetable Sponge of Luffa of described weight part of filling a prescription, concentration that Snakegourd Fruit rattan, taraxacum, Pericarpium Musae add 5 times be 20% soda ash solution soak 24 hours, temperature controls at 90 DEG C, pressure-controlling is at 5MPa, then use washed with de-ionized water 5 minutes, drain, then put into dryer inner drying, bake out temperature is 160 DEG C, make water ratio be not more than 2.2%, take out, then grind to form 80 order powder;
(2). get the wood powder of described weight part of filling a prescription, polyvinyl chloride resin, barium carbonate, wintergreen oil, resol, polypropylene, Snakegourd Root, talcum powder, montmorillonite, kaolin, silica powder, polyacrylamide, polyoxyethylene glycol distearyl acid fat, poly-Sorbic Acid formicester add vulcanizing boiler and carry out sulfidizing, in tank temperature control 155 DEG C, pressure-controlling 2MPa, sofening treatment time controling is at 10 hours, take out, then grind to form 80 order powder;
(3). by step (1) and step (2) gained powder through charcoal absorption process, drop into blender spice again, spice temperature is 72 DEG C, then the spearmint oil, the sunflower seed oil that add described weight part of filling a prescription together are sent into twin screw extruder high temperature and are extruded, and extrusion temperature is 195 DEG C;
(4). the material extruded through mould shape, then uses water quench shaping, and water coolant comprises the citric acid of 5%, the wintergreen oil of 2%, and temperature of cooling water is 27 DEG C;
(5). the floor of cooling forming is cut, polishing.
More than show and describe ultimate principle of the present invention and principal character and advantage of the present invention.The technician of the industry should understand; the present invention is not restricted to the described embodiments; what describe in above-described embodiment and specification sheets just illustrates principle of the present invention; without departing from the spirit and scope of the present invention; the present invention also has various changes and modifications, and these changes and improvements all fall in the claimed scope of the invention.Application claims protection domain is defined by appending claims and equivalent thereof.
Claims (5)
1. a court wood-plastic floor board, it is characterized in that, the raw material of following weight part is adopted to make: wood powder 52-66 part, polyvinyl chloride resin 26-31 part, barium carbonate 9-15 part, wintergreen oil 31-41 part, resol 17-25 part, polypropylene 17-25 part, Snakegourd Root 15-20 part, Vegetable Sponge of Luffa 2-5 part, talcum powder 8-13 part, montmorillonite 8-13 part, kaolin 5-9 part, silica powder 5-9 part, polyacrylamide 1-5 part, polyoxyethylene glycol distearyl acid fat 6-13 part, poly-Sorbic Acid formicester 12-15 part, Snakegourd Fruit rattan 7-11 part, taraxacum 2.5-3.5 part, Pericarpium Musae 0.5-1 part, spearmint oil 0.2-0.5 part, sunflower seed oil 0.1-0.2 part.
2. a kind of court as claimed in claim 1 wood-plastic floor board, it is characterized in that, adopt the raw material of following weight part to make: wood powder 52 parts, polyvinyl chloride resin 26 parts, barium carbonate 9 parts, wintergreen oil 31 parts, 17 parts, resol, polypropylene 17 parts, Snakegourd Root 15 parts, Vegetable Sponge of Luffa 2 parts, talcum powder 8 parts, montmorillonite 8 parts, kaolin 5 parts, silica powder 5 parts, polyacrylamide 1 part, polyoxyethylene glycol distearyl acid 6 parts, fat, poly-Sorbic Acid formicester 12 parts, 7 parts, Snakegourd Fruit rattan, taraxacum 2.5 parts, Pericarpium Musae 0.5 part, spearmint oil 0.2 part, sunflower seed oil 0.1 part.
3. a kind of court as claimed in claim 1 wood-plastic floor board, it is characterized in that, adopt the raw material of following weight part to make: wood powder 59 parts, polyvinyl chloride resin 28 parts, barium carbonate 12 parts, wintergreen oil 36 parts, 21 parts, resol, polypropylene 21 parts, Snakegourd Root 18 parts, Vegetable Sponge of Luffa 3 parts, talcum powder 11 parts, montmorillonite 11 parts, kaolin 7 parts, silica powder 7 parts, polyacrylamide 3 parts, polyoxyethylene glycol distearyl acid 10 parts, fat, poly-Sorbic Acid formicester 13 parts, 9 parts, Snakegourd Fruit rattan, taraxacum 3 parts, Pericarpium Musae 0.8 part, spearmint oil 0.3 part, sunflower seed oil 0.15 part.
4. a kind of court as claimed in claim 1 wood-plastic floor board, it is characterized in that, adopt the raw material of following weight part to make: wood powder 66 parts, polyvinyl chloride resin 31 parts, barium carbonate 15 parts, wintergreen oil 41 parts, 25 parts, resol, polipropene 25 part, Snakegourd Root 20 parts, Vegetable Sponge of Luffa 5 parts, talcum powder 13 parts, montmorillonite 13 parts, kaolin 9 parts, silica powder 9 parts, polyacrylamide 5 parts, polyoxyethylene glycol distearyl acid 13 parts, fat, poly-Sorbic Acid formicester 15 parts, 11 parts, Snakegourd Fruit rattan, taraxacum 3.5 parts, Pericarpium Musae 1 part, spearmint oil 0.5 part, sunflower seed oil 0.2 part.
5. the preparation method of a kind of court as claimed in claim 1 wood-plastic floor board, is characterized in that: comprise the following steps,
(1). get the Vegetable Sponge of Luffa of described weight part of filling a prescription, to add 2-5 concentration be doubly that the soda ash solution of 10-20% soaks 24 hours for Snakegourd Fruit rattan, taraxacum, Pericarpium Musae, temperature controls at 70-90 DEG C, pressure-controlling is at 3-5MPa, then use washed with de-ionized water 2-5 minute, drain, then put into dryer inner drying, bake out temperature is 120-160 DEG C, make water ratio be not more than 2.2%, take out, then grind to form 50-80 order powder;
(2). get the wood powder of described weight part of filling a prescription, polyvinyl chloride resin, barium carbonate, wintergreen oil, resol, polypropylene, Snakegourd Root, talcum powder, montmorillonite, kaolin, silica powder, polyacrylamide, polyoxyethylene glycol distearyl acid fat, poly-Sorbic Acid formicester add vulcanizing boiler and carry out sulfidizing, in tank temperature control 125-155 DEG C, pressure-controlling 1-2MPa, sofening treatment time controling is at 5-10 hour, take out, then grind to form 50-80 order powder;
(3). by step (1) and step (2) gained powder through charcoal absorption process, drop into blender spice again, spice temperature is 55-72 DEG C, then the spearmint oil, the sunflower seed oil that add described weight part of filling a prescription together are sent into twin screw extruder high temperature and are extruded, and extrusion temperature is 165-195 DEG C;
(4). the material extruded through mould shape, then uses water quench shaping, and water coolant comprises the citric acid of 2-5%, the wintergreen oil of 1-2%, and temperature of cooling water is 15-27 DEG C;
(5). the floor of cooling forming is cut, polishing.