CN105566564A - pH敏感性水凝胶的制备 - Google Patents
pH敏感性水凝胶的制备 Download PDFInfo
- Publication number
- CN105566564A CN105566564A CN201510792937.1A CN201510792937A CN105566564A CN 105566564 A CN105566564 A CN 105566564A CN 201510792937 A CN201510792937 A CN 201510792937A CN 105566564 A CN105566564 A CN 105566564A
- Authority
- CN
- China
- Prior art keywords
- hydrogel
- preparation
- water
- sensitive
- room temperature
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明pH敏感性水凝胶的制备方法涉及一种医用PH敏感性水凝胶的制备方法。本发明所述水凝胶包括以下步骤:(1)分别取等质量5mg的功能单体HEMA,MAA,AM于烧杯中,加入一定体积的水,室温下搅拌5min;(2)再加入一定量的交联剂EGDMA和引发剂APS,室温下继续搅拌10min;(3)将上述溶液转移到试管中,通氮10min,密封,60℃下反应16h,生成水凝胶(4)取出水凝胶切成小块,放于蒸馏水中浸泡,每隔一段时间换一次蒸馏水(5)然后置于50℃下真空干燥至恒重,即得pH敏感性水凝胶。本发明所述水凝胶制备方法简单,敏感度高,可工业化生产。
Description
技术领域
本发明涉及一种医用pH敏感性水凝胶的制备方法。
背景技术
水凝胶吸水溶胀但不溶解,兼有液体和固体的性质。同时,水凝胶结构中存在大量的功能性基团,可作为吸附分离材料广泛应用于农林、园艺、医药、石油化工、建材、日用品和化妆品等领域。
发明内容
本发明提供一种pH敏感性较好的水凝胶制备方法。
本发明pH敏感性水凝胶的制备方法,包括以下步骤:pH敏感性水凝胶的制备方法:其包括以下原料:α-甲基丙烯酸(MAA),(化学纯,国药(集团)上海化学试剂公司);甲基丙烯酸羟乙酯(HEMA),(化学纯,三菱化工有限公司);丙烯酰胺(AM),(分析纯,天津市大茂化学试剂厂);乙二醇二甲基丙烯酸酯(EGDMA),(化学纯,Fluka公司);过硫酸铵(APs),(分析纯,广东省化学试剂工程技术研究开发中心);
具体制备方法如下:(1)分别取等质量5mg的功能单体HEMA,MAA,AM于烧杯中,加入一定体积的水,室温下搅拌5min;(2)再加入一定量的交联剂EGDMA和引发剂APS,室温下继续搅拌10min;(3)将上述溶液转移到试管中,通氮10min,密封,60℃下反应16h,生成水凝胶(4)取出水凝胶切成小块,放于蒸馏水中浸泡,每隔一段时间换一次蒸馏水(5)然后置于50℃下真空干燥至恒重,即得pH敏感性水凝胶。
本发明所述水凝胶制备方法简单,敏感度高,可工业化生产。
具体实施方式:
pH敏感性水凝胶的制备方法,其包括以下原料:α-甲基丙烯酸(MAA),(化学纯,国药(集团)上海化学试剂公司);甲基丙烯酸羟乙酯(HEMA),(化学纯,三菱化工有限公司);丙烯酰胺(AM),(分析纯,天津市大茂化学试剂厂);乙二醇二甲基丙烯酸酯(EGDMA),(化学纯,Fluka公司);过硫酸铵(APs),(分析纯,广东省化学试剂工程技术研究开发中心);
包括以下步骤:(1)分别取等质量5mg的功能单体HEMA,MAA,AM于烧杯中,加入一定体积的水,室温下搅拌5min;(2)再加入一定量的交联剂EGDMA和引发剂APS,室温下继续搅拌10min;(3)将上述溶液转移到试管中,通氮10min,密封,60℃下反应16h,生成水凝胶(4)取出水凝胶切成小块,放于蒸馏水中浸泡,每隔一段时间换一次蒸馏水(5)然后置于50℃下真空干燥至恒重,即得pH敏感性水凝胶。
Claims (1)
1.pH敏感性水凝胶的制备方法,其特征在于包括以下步骤:(1)分别取等质量5mg的功能单体HEMA,MAA,AM于烧杯中,加入一定体积的水,室温下搅拌5min;(2)再加入一定量的交联剂EGDMA和引发剂APS,室温下继续搅拌10min;(3)将上述溶液转移到试管中,通氮10min,密封,60℃下反应16h,生成水凝胶(4)取出水凝胶切成小块,放于蒸馏水中浸泡,每隔一段时间换一次蒸馏水(5)然后置于50℃下真空干燥至恒重,即得pH敏感性水凝胶。