CN105563958B - 一种高隔热降噪防辐射真空玻璃及其制造方法 - Google Patents

一种高隔热降噪防辐射真空玻璃及其制造方法 Download PDF

Info

Publication number
CN105563958B
CN105563958B CN201510998449.6A CN201510998449A CN105563958B CN 105563958 B CN105563958 B CN 105563958B CN 201510998449 A CN201510998449 A CN 201510998449A CN 105563958 B CN105563958 B CN 105563958B
Authority
CN
China
Prior art keywords
parts
glass substrate
glass
insulation
heat
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201510998449.6A
Other languages
English (en)
Other versions
CN105563958A (zh
Inventor
顾黎明
徐峰
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
TAICANG YAOHUA GLASS CO Ltd
Original Assignee
TAICANG YAOHUA GLASS CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by TAICANG YAOHUA GLASS CO Ltd filed Critical TAICANG YAOHUA GLASS CO Ltd
Priority to CN201510998449.6A priority Critical patent/CN105563958B/zh
Publication of CN105563958A publication Critical patent/CN105563958A/zh
Application granted granted Critical
Publication of CN105563958B publication Critical patent/CN105563958B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明提供一种高隔热降噪防辐射真空玻璃及其生产方法，所述玻璃包括：真空玻璃基板，包括第一玻璃基片和第二玻璃基片，第一玻璃基片与第二玻璃基片相对面之间分别涂覆有PVB胶膜，且两玻璃基片相对面周向通过密封胶连接并抽真空形成真空内腔；防辐射涂层，涂覆于第一玻璃基片相对第二玻璃基片的另一面；隔热保温涂层，涂覆于第二玻璃基片相对第一玻璃基片的另一面。所述玻璃兼具保温、防辐射及降噪三重功效，防辐射效果好，设计提供专门的隔热保温涂层，涂层成分搭配合理、生产方法易操作，导热系数低，保温效果好，且涂覆后不易脱落，使用寿命长，PVB胶膜设置于真空内腔内，隔音吸音效果良好，经济成本低，使用前景好。

Description

一种高隔热降噪防辐射真空玻璃及其制造方法
技术领域
本发明涉及一种高隔热降噪防辐射真空玻璃及其制造方法。
背景技术
真空玻璃是将两片平板玻璃四周密闭起来，将其间隙抽成真空并密封排气孔，两片玻璃之间的间隙为0.1-0.2mm，真空玻璃的两片一般至少有一片是低辐射玻璃，这样就将通过真空玻璃的传导、对流和辐射方式散失的热降到最低，其工作原理与玻璃保温瓶的保温隔热原理相同。真空玻璃是玻璃工艺与材料科学、真空技术、物理测量技术、工业自动化及建筑科学等，多种学科、多种技术、多种工艺协作配合的硕果。
真空玻璃是一种新型节能玻璃，它基于保温瓶原理，将两片玻璃四周密封，中间间隔为0.1-0.2mm的薄真空层。由于没有气体传热，内表面又有起保温瓶银膜作用的透明低辐射膜，使真空玻璃的保温隔热性能远优于目前已广泛使用的“中空”玻璃。
然而，目前市场上大多真空玻璃保温效果并不好，且如果长时间使用后，密封不严会严重影响其保温效果，且功能单一。
对此，目前国内主要存在如下专利文献：
如授权公告号：CN204782596U，公开了一种真空玻璃，具体为一种真空玻璃。其包括第一玻璃层(1)，第二玻璃层(2)及第一玻璃层(1)与第二玻璃层(2)之间形成的抽真空腔体(3)，且抽真空腔体(3)四周设有密封装置(4)，一端与抽真空阀体(5)连接；所述的抽真空腔体(3)内部均匀的设有支撑物(6)，其一端、第一玻璃层(1)与第二玻璃层(2)之间设有组成密封装置(4)的密封胶条(7)，抽真空腔体(3)与密封装置(4)相对的另一端设置的抽真空阀体(5)包括玻璃安装孔(401)，一侧设置的快速连接头(402)，中心腔体内部安装的抽真空阀(403)。其有益效果在于：生产工艺简单、节省能源、隔音效果好，并且制造、使用成本低，使用广泛。虽然该真空玻璃具有一定的保温、降噪效果，然而，其并没有防辐射效果，且保温效果仅仅通过密封实现，并不明显。
发明内容
为解决上述存在的问题，本发明的目的在于提供一种高隔热降噪防辐射真空玻璃及其制造方法，所述玻璃兼具保温、防辐射及降噪三重功效，防辐射效果好，设计提供专门的隔热保温涂层，涂层成分搭配合理、生产方法易操作，导热系数低，保温效果好，且只需喷涂使用即可在玻璃表面形成涂层，使用简单，且涂覆后不易脱落，使用寿命长，PVB胶膜设置于真空内腔内，隔音吸音效果良好，经济成本低，使用前景好。
为达到上述目的，本发明的技术方案是：
一种高隔热降噪防辐射真空玻璃，所述玻璃包括：真空玻璃基板，包括由下至上层叠设置的第一玻璃基片和第二玻璃基片，所述第一玻璃基片与第二玻璃基片相对面之间分别涂覆有PVB胶膜，且两玻璃基片相对面周向通过密封胶连接并抽真空形成真空内腔；所述第一玻璃基片与第二玻璃基片之间间隙为0.1～0.2mm，所述PVB胶膜厚度为5～10μm；防辐射涂层，涂覆于所述第一玻璃基片相对第二玻璃基片的另一面；隔热保温涂层，涂覆于所述第二玻璃基片相对第一玻璃基片的另一面；所述防辐射涂层包括由内至外层叠设置的锌铝合金层、镍铬合金层、银层及硅铝合金层；所述隔热保温涂层包括如下重量份的成分：纳米ATO浆料：20～30份，纳米碳化硅：10～15份，己二酸二辛酯：1～5份，纳米氧化锌：1～5份，纳米氧化锑：0.1～1份，聚丙烯酰胺：1～5份，甘露醇：5～10份，壳聚糖：1～5份，苯并三唑：1～5份，凹凸棒土：10～20份，云母粉：6～10份，氧化钴粉：0.1～1份，硅藻土：1～5份，低表面能粘结剂：10～20份，流平剂：1～5份，润湿剂：1～10份，分散剂：5～10份，消泡剂：1～5份，抗氧剂：1～5份，去离子水：50～100份。
进一步，所述隔热保温涂层包括如下重量份的成分：纳米ATO浆料：25～30份，纳米碳化硅：10～13份，己二酸二辛酯：2～5份，纳米氧化锌：3～5份，纳米氧化锑：0.1～0.5份，聚丙烯酰胺：1～3份，甘露醇：5～8份，壳聚糖：1～4份，苯并三唑：2～5份，凹凸棒土：15～20份，云母粉：6～8份，氧化钴粉：0.5～1份，硅藻土：3～5份，低表面能粘结剂：10～13份，流平剂：1～3份，润湿剂：1～5份，分散剂：5～10份，消泡剂：1～5份，抗氧剂：1～5份，去离子水：50～80份。
优选地，所述隔热保温涂层包括如下重量份的成分：纳米ATO浆料：25份，纳米碳化硅：13份，己二酸二辛酯：3份，纳米氧化锌：4份，纳米氧化锑：0.5份，聚丙烯酰胺：2份，甘露醇：6份，壳聚糖：1份，苯并三唑：2份，凹凸棒土：15份，云母粉：7份，氧化钴粉：0.5份，硅藻土：4份，低表面能粘结剂：13份，流平剂：2份，润湿剂：3份，分散剂：6份，消泡剂：3份，抗氧剂：2份，去离子水：60份。
另，所述流平剂为聚二甲基硅氧烷、聚甲基苯基硅氧烷或聚酯改性有机硅氧烷。
另有，所述所述分散剂为卵磷脂、甜菜碱或脂肪酸甘油酯。
再，所述消泡剂为乳化硅油、高碳醇或苯乙醇油酸酯。
再有，所述低表面能物质为氟硅烷、硅氧烷、聚四氟乙烯、硅烷偶联剂、甲基三乙氧基硅烷、乙烯基三甲氧基硅烷或苯基三甲氧基硅烷。
且，所述抗氧剂为抗氧剂1010或抗氧剂1098。
同时，本发明还提供一种高隔热降噪防辐射真空玻璃的制造方法，包括如下步骤：
1)制备隔热保温粉体
将纳米碳化硅于600～800℃下高温处理30～60min，在10～20min内冷却至室温，超声波研磨10～20min成粉，加入分散釜中，并加入去离子水和纳米ATO浆料，以800～1000转/min的速度进行剪切分散30～50min；将转速调至1000～1200转/min，在分散釜中加入聚丙烯酰胺、己二酸二辛酯、纳米氧化锌、纳米氧化锑搅拌5～10min；将转速调至1200～1400转/min，加入甘露醇、壳聚糖、苯并三唑、凹凸棒土、云母粉、氧化钴粉及硅藻土搅拌10～20min；将转速调至1400～1600转/min，依次加入低表面能粘结剂、流平剂、润湿剂、分散剂、消泡剂、抗氧剂均匀搅拌30～50min；将分散后的物料在室温下烘干干燥，烘干温度100～120℃，烘干时间20～30min，固化，研磨分散，得所述隔热保温粉体；
2)烧结靶材
将锌铝合金、镍铬合金、银及硅铝合金分别烧结在镀膜机的磁控溅射靶材上，备用；
3)预处理
将所述第一玻璃基片及第二玻璃基片相对面分别涂覆PVB胶膜，再通过密封胶粘结、抽真空形成真空内腔，得所述真空玻璃基板，并对真空玻璃基板表面进行去污、去油、脱湿处理；
4)喷涂
用喷枪将将步骤1)所得隔热保温粉体均匀地喷涂到由步骤3)处理后的真空玻璃基板第二玻璃基片相对第一玻璃基片的另一面，喷涂温度30～40℃，喷枪压力0.5～1MPa，喷涂完成后在室温下放置1～2小时；
5)固化
将步骤4)处理后的真空玻璃基板送入烘箱加热固化，加热固化的温度为160～180℃，加热固化的时间为10～20min，冷却至室温，在所述真空玻璃基板第二玻璃基片相对第一玻璃基片的另一面形成隔热保温涂层；
6)镀防辐射涂层
将步骤5)固化处理后的真空玻璃基板送入磁控溅射室内，真空玻璃基板第一玻璃基片相对第二玻璃基片的另一面对准磁控溅射靶材，在所述第一玻璃基片表面由内至外依次形成锌铝合金层、镍铬合金层、银层及硅铝合金层，得到所述防辐射涂层的镀膜，完成所述高隔热降噪防辐射真空玻璃的制造。
另有，所述隔热保温涂层厚度为5～10μm，导热系数为0.01～0.05W/m·K。
本发明的有益效果在于：
所述玻璃兼具保温、防辐射及降噪三重功效，防辐射效果好，设计提供专门的隔热保温涂层，涂层成分搭配合理、生产方法易操作，导热系数低，保温效果好，且只需喷涂使用即可在玻璃表面形成涂层，使用简单，且涂覆后不易脱落，使用寿命长，PVB胶膜设置于真空内腔内，隔音吸音效果良好，经济成本低，使用前景好。
附图说明
图1为本发明实施例所提供的一种高隔热降噪防辐射真空玻璃的结构示意图。
具体实施方式
下面结合具体实施例对本发明进行详细说明。以下实施例将有助于本领域的技术人员进一步理解本发明，但不以任何形式限制本发明。应当指出的是，对本领域的普通技术人员来说，在不脱离本发明构思的前提下，还可以做出若干变形和改进。这些都属于本发明的保护范围。
参照图1，本发明所述的一种高隔热降噪防辐射真空玻璃，所述玻璃包括：真空玻璃基板1，包括由下至上层叠设置的第一玻璃基片11和第二玻璃基片12，所述第一玻璃基片11与第二玻璃基片12相对面之间分别涂覆有PVB胶膜13，且两玻璃基片相对面周向通过密封胶14连接并抽真空形成真空内腔15；所述第一玻璃基片11与第二玻璃基片12之间间隙为0.1～0.2mm，所述PVB胶膜13厚度为5～10μm；防辐射涂层2，涂覆于所述第一玻璃基片11相对第二玻璃基片12的另一面；隔热保温涂层3，涂覆于所述第二玻璃基片12相对第一玻璃基片11的另一面；所述防辐射涂层2包括由内至外层叠设置的锌铝合金层21、镍铬合金层22、银层23及硅铝合金层24；所述隔热保温涂层3包括如下重量份的成分：纳米ATO浆料：20～30份，纳米碳化硅：10～15份，己二酸二辛酯：1～5份，纳米氧化锌：1～5份，纳米氧化锑：0.1～1份，聚丙烯酰胺：1～5份，甘露醇：5～10份，壳聚糖：1～5份，苯并三唑：1～5份，凹凸棒土：10～20份，云母粉：6～10份，氧化钴粉：0.1～1份，硅藻土：1～5份，低表面能粘结剂：10～20份，流平剂：1～5份，润湿剂：1～10份，分散剂：5～10份，消泡剂：1～5份，抗氧剂：1～5份，去离子水：50～100份。
进一步，所述隔热保温涂层包括如下重量份的成分：纳米ATO浆料：25～30份，纳米碳化硅：10～13份，己二酸二辛酯：2～5份，纳米氧化锌：3～5份，纳米氧化锑：0.1～0.5份，聚丙烯酰胺：1～3份，甘露醇：5～8份，壳聚糖：1～4份，苯并三唑：2～5份，凹凸棒土：15～20份，云母粉：6～8份，氧化钴粉：0.5～1份，硅藻土：3～5份，低表面能粘结剂：10～13份，流平剂：1～3份，润湿剂：1～5份，分散剂：5～10份，消泡剂：1～5份，抗氧剂：1～5份，去离子水：50～80份。
优选地，所述隔热保温涂层包括如下重量份的成分：纳米ATO浆料：25份，纳米碳化硅：13份，己二酸二辛酯：3份，纳米氧化锌：4份，纳米氧化锑：0.5份，聚丙烯酰胺：2份，甘露醇：6份，壳聚糖：1份，苯并三唑：2份，凹凸棒土：15份，云母粉：7份，氧化钴粉：0.5份，硅藻土：4份，低表面能粘结剂：13份，流平剂：2份，润湿剂：3份，分散剂：6份，消泡剂：3份，抗氧剂：2份，去离子水：60份。
另，所述流平剂为聚二甲基硅氧烷、聚甲基苯基硅氧烷或聚酯改性有机硅氧烷。
另有，所述所述分散剂为卵磷脂、甜菜碱或脂肪酸甘油酯。
再，所述消泡剂为乳化硅油、高碳醇或苯乙醇油酸酯。
再有，所述低表面能物质为氟硅烷、硅氧烷、聚四氟乙烯、硅烷偶联剂、甲基三乙氧基硅烷、乙烯基三甲氧基硅烷或苯基三甲氧基硅烷。
且，所述抗氧剂为抗氧剂1010或抗氧剂1098。
同时，本发明还提供一种高隔热降噪防辐射真空玻璃的制造方法，包括如下步骤：
1)制备隔热保温粉体
将纳米碳化硅于600～800℃下高温处理30～60min，在10～20min内冷却至室温，超声波研磨10～20min成粉，加入分散釜中，并加入去离子水和纳米ATO浆料，以800～1000转/min的速度进行剪切分散30～50min；将转速调至1000～1200转/min，在分散釜中加入聚丙烯酰胺、己二酸二辛酯、纳米氧化锌、纳米氧化锑搅拌5～10min；将转速调至1200～1400转/min，加入甘露醇、壳聚糖、苯并三唑、凹凸棒土、云母粉、氧化钴粉及硅藻土搅拌10～20min；将转速调至1400～1600转/min，依次加入低表面能粘结剂、流平剂、润湿剂、分散剂、消泡剂、抗氧剂均匀搅拌30～50min；将分散后的物料在室温下烘干干燥，烘干温度100～120℃，烘干时间20～30min，固化，研磨分散，得所述隔热保温粉体；
2)烧结靶材
将锌铝合金、镍铬合金、银及硅铝合金分别烧结在镀膜机的磁控溅射靶材上，备用；
3)预处理
将所述第一玻璃基片11及第二玻璃基片12相对面分别涂覆PVB胶膜13，再通过密封胶14粘结、抽真空形成真空内腔15，得所述真空玻璃基板1，并对真空玻璃基板1表面进行去污、去油、脱湿处理；
4)喷涂
用喷枪将将步骤1)所得隔热保温粉体均匀地喷涂到由步骤3)处理后的真空玻璃基板1第二玻璃基片12相对第一玻璃基片11的另一面，喷涂温度30～40℃，喷枪压力0.5～1MPa，喷涂完成后在室温下放置1～2小时；
5)固化
将步骤4)处理后的真空玻璃基板1送入烘箱加热固化，加热固化的温度为160～180℃，加热固化的时间为10～20min，冷却至室温，在所述真空玻璃基板1第二玻璃基片12相对第一玻璃基片11的另一面形成隔热保温涂层3；
6)镀防辐射涂层
将步骤5)固化处理后的真空玻璃基板1送入磁控溅射室内，真空玻璃基板1第一玻璃基片11相对第二玻璃基片12的另一面对准磁控溅射靶材，在所述第一玻璃基片11表面由内至外依次形成锌铝合金层21、镍铬合金层22、银层23及硅铝合金层24，得到所述防辐射涂层2的镀膜，完成所述高隔热降噪防辐射真空玻璃的制造。
另有，所述隔热保温涂层厚度为5～10μm，导热系数为0.01～0.05W/m·K。
其中，表1为本发明各实施例所提供的一种高隔热降噪防辐射真空玻璃中隔热保温涂层的成分列表。表2为本发明各实施例所提供的一种高隔热降噪防辐射真空玻璃的隔热性能及防结露结霜性能列表。
表1(单位：重量份)
表2
由表2可见，本发明所提供的高隔热降噪防辐射真空玻璃保温隔热性能好且结露温度低，具有良好的抗结霜、抗结露能力。
本发明所提供的一种高隔热降噪防辐射真空玻璃及其制造方法，所述玻璃兼具保温、防辐射及降噪三重功效，防辐射效果好，设计提供专门的隔热保温涂层，涂层成分搭配合理、生产方法易操作，导热系数低，保温效果好，且只需喷涂使用即可在玻璃表面形成涂层，使用简单，且涂覆后不易脱落，使用寿命长，PVB胶膜设置于真空内腔内，隔音吸音效果良好，经济成本低，使用前景好。
需要说明的是，以上实施例仅用以说明本发明的技术方案而非限制。尽管参照较佳实施例对本发明进行了详细说明，本领域的普通技术人员应当理解，可以对发明的技术方案进行修改或者等同替换，而不脱离本发明技术方案的范围，其均应涵盖在本发明的权利要求范围中。

Claims (10)

1.一种高隔热降噪防辐射真空玻璃，其特征在于，所述玻璃包括：
真空玻璃基板，包括由下至上层叠设置的第一玻璃基片和第二玻璃基片，所述第一玻璃基片与第二玻璃基片相对面之间分别涂覆有PVB胶膜，且两玻璃基片相对面周向通过密封胶连接并抽真空形成真空内腔；
所述第一玻璃基片与第二玻璃基片之间间隙为0.1~0.2mm，所述PVB胶膜厚度为5~10μm；
防辐射涂层，涂覆于所述第一玻璃基片相对第二玻璃基片的另一面；
隔热保温涂层，涂覆于所述第二玻璃基片相对第一玻璃基片的另一面；
所述防辐射涂层包括由内至外层叠设置的锌铝合金层、镍铬合金层、银层及硅铝合金层；
所述隔热保温涂层包括如下重量份的成分：纳米ATO浆料：20~30份，纳米碳化硅：10~15份，己二酸二辛酯：1~5份，纳米氧化锌：1~5份，纳米氧化锑：0.1~1份，聚丙烯酰胺：1~5份，甘露醇：5~10份，壳聚糖：1~5份，苯并三唑：1~5份，凹凸棒土：10~20份，云母粉：6~10份，氧化钴粉：0.1~1份，硅藻土：1~5份，低表面能粘结剂：10~20份，流平剂：1~5份，润湿剂：1~10份，分散剂：5~10份，消泡剂：1~5份，抗氧剂：1~5份，去离子水：50~100份。
2.根据权利要求1所述的一种高隔热降噪防辐射真空玻璃，其特征在于，所述隔热保温涂层包括如下重量份的成分：纳米ATO浆料：25~30份，纳米碳化硅：10~13份，己二酸二辛酯：2~5份，纳米氧化锌：3~5份，纳米氧化锑：0.1~0.5份，聚丙烯酰胺：1~3份，甘露醇：5~8份，壳聚糖：1~4份，苯并三唑：2~5份，凹凸棒土：15~20份，云母粉：6~8份，氧化钴粉：0.5~1份，硅藻土：3~5份，低表面能粘结剂：10~13份，流平剂：1~3份，润湿剂：1~5份，分散剂：5~10份，消泡剂：1~5份，抗氧剂：1~5份，去离子水：50~80份。
3.根据权利要求1所述的一种高隔热降噪防辐射真空玻璃，其特征在于，所述隔热保温涂层包括如下重量份的成分：纳米ATO浆料：25份，纳米碳化硅：13份，己二酸二辛酯：3份，纳米氧化锌：4份，纳米氧化锑：0.5份，聚丙烯酰胺：2份，甘露醇：6份，壳聚糖：1份，苯并三唑：2份，凹凸棒土：15份，云母粉：7份，氧化钴粉：0.5份，硅藻土：4份，低表面能粘结剂：13份，流平剂：2份，润湿剂：3份，分散剂：6份，消泡剂：3份，抗氧剂：2份，去离子水：60份。
4.根据权利要求1所述的一种高隔热降噪防辐射真空玻璃，其特征在于，所述流平剂为聚二甲基硅氧烷、聚甲基苯基硅氧烷或聚酯改性有机硅氧烷。
5.根据权利要求1所述的一种高隔热降噪防辐射真空玻璃，其特征在于，所述分散剂为卵磷脂、甜菜碱或脂肪酸甘油酯。
6.根据权利要求1所述的一种高隔热降噪防辐射真空玻璃，其特征在于，所述消泡剂为乳化硅油、高碳醇或苯乙醇油酸酯。
7.根据权利要求1所述的一种高隔热降噪防辐射真空玻璃，其特征在于，所述低表面能粘结剂为氟硅烷、聚四氟乙烯、甲基三乙氧基硅烷、乙烯基三甲氧基硅烷或苯基三甲氧基硅烷。
8.根据权利要求1所述的一种高隔热降噪防辐射真空玻璃，其特征在于，所述抗氧剂为抗氧剂1010或抗氧剂1098。
9.一种如权利要求1~8中任一项所述的高隔热降噪防辐射真空玻璃的制造方法，其特征在于，包括如下步骤：
1)制备隔热保温粉体
将纳米碳化硅于600~800℃下高温处理30~60min，在10~20min内冷却至室温，超声波研磨10~20min成粉，加入分散釜中，并加入去离子水和纳米ATO浆料，以800~1000转/min的速度进行剪切分散30~50min；将转速调至1000~1200转/min，在分散釜中加入聚丙烯酰胺、己二酸二辛酯、纳米氧化锌、纳米氧化锑搅拌5~10min；将转速调至1200~1400转/min，加入甘露醇、壳聚糖、苯并三唑、凹凸棒土、云母粉、氧化钴粉及硅藻土搅拌10~20min；将转速调至1400~1600转/min，依次加入低表面能粘结剂、流平剂、润湿剂、分散剂、消泡剂、抗氧剂均匀搅拌30~50min；将分散后的物料在室温下烘干干燥，烘干温度100~120℃，烘干时间20~30min，固化，研磨分散，得所述隔热保温粉体；
2)烧结靶材
将锌铝合金、镍铬合金、银及硅铝合金分别烧结在镀膜机的磁控溅射靶材上，备用；
3)预处理
将所述第一玻璃基片及第二玻璃基片相对面分别涂覆PVB胶膜，再通过密封胶粘结、抽真空形成真空内腔，得所述真空玻璃基板，并对真空玻璃基板表面进行去污、去油、脱湿处理；
4)喷涂
用喷枪将步骤1)所得隔热保温粉体均匀地喷涂到由步骤3)处理后的真空玻璃基板第二玻璃基片相对第一玻璃基片的另一面，喷涂温度30~40℃，喷枪压力0.5~1MPa，喷涂完成后在室温下放置1~2小时；
5)固化
将步骤4)处理后的真空玻璃基板送入烘箱加热固化，加热固化的温度为160~180℃，加热固化的时间为10~20min，冷却至室温，在所述真空玻璃基板第二玻璃基片相对第一玻璃基片的另一面形成隔热保温涂层；
6)镀防辐射涂层
将步骤5)固化处理后的真空玻璃基板送入磁控溅射室内，真空玻璃基板第一玻璃基片相对第二玻璃基片的另一面对准磁控溅射靶材，在所述第一玻璃基片表面由内至外依次形成锌铝合金层、镍铬合金层、银层及硅铝合金层，得到所述防辐射涂层的镀膜，完成所述高隔热降噪防辐射真空玻璃的制造。
10.根据权利要求9所述的一种高隔热降噪防辐射真空玻璃的制造方法，其特征在于，所述隔热保温涂层厚度为5~10μm，导热系数为0.01~0.05W/m·K。
CN201510998449.6A 2015-12-28 2015-12-28 一种高隔热降噪防辐射真空玻璃及其制造方法 Active CN105563958B (zh)