CN105542661A - 一种标志漆的制作及使用方法 - Google Patents
一种标志漆的制作及使用方法 Download PDFInfo
- Publication number
- CN105542661A CN105542661A CN201610108722.8A CN201610108722A CN105542661A CN 105542661 A CN105542661 A CN 105542661A CN 201610108722 A CN201610108722 A CN 201610108722A CN 105542661 A CN105542661 A CN 105542661A
- Authority
- CN
- China
- Prior art keywords
- paint
- signal paint
- signal
- ethanol
- resistance
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种标志漆的制作方法和使用方法,上述的方法解决零件标识在使用中长期存在的掉漆、不耐高温、不耐油、不耐酸碱等难题,保证机体零件在恶劣的工作环境中,零件标记能有效的存在,提供可识别性、可追溯性,有效提高飞机后勤保障能力、维护性。提升了我公司产品的质量品质和公司形象,而且在航空、兵器等国防工业中,具有广阔的推广应用价值。该涂层体系的成功应用,填补了国内的技术空白,将进一步推动相关技术领域发展,为航空科技进步作出新贡献。
Description
技术领域
本发明涉及一种标志漆的制作及使用方法,属于零件标示与零件表面防护技术,涉及到标志漆的制作、施工工艺的制定、零件表面的腐蚀与防护等方面的技术学科。
背景技术
由于我国地域辽阔,有6种地貌、4种海洋气候,有着非常复杂的物理环境,而飞机就长期工作在这种恶劣的自然条件下,机体零件经常受到高温、高湿、高盐雾、高频率振动等恶劣条件的侵害,为保证飞机装备的安全性、可靠性,因此对飞机的三防性能提出很高的要求。而我国使用的防护体系大部分沿用原苏联上世纪60-70年代的防护体系,性与现在欧美使用的防护体系在性能上已经有很大的差距,尤其在功能性防护、特种防护方面存在很多空白,都急需进行提升和解决。其中一个特种防护方面就是零件的标识技术,保证机体零件在恶劣的工作环境中,零件标记能有效的存在,提供可识别性、可追溯性,有效提高飞机后勤保障能力、维护性。
发明内容
解决的技术问题
本发明解决了在高温、高湿、高盐雾、高频率振动等恶劣环境下,零件标识不脱落,在一个大修周期内零件标识能明显识别。标志漆的涂层体系强度、耐冲击性、耐温性、抗腐蚀、等项目满足了使用要求和设计要求,工艺施工性能适应大规模的生产要求,装机试验中解决长期存在的掉漆、不耐高温、不耐油、不耐酸碱等难题。
技术方案
提供一种标志漆的制作方法,
步骤一、室温环境下将100克的虫胶清漆加入到100毫升的乙醇内,搅拌均匀后加热至80度,使虫胶清漆充分溶解,形成混合溶液A;将10~14克的苯胺黑加入到另一份100毫升的乙醇内,搅拌均匀使其溶解,形成混合溶液B;
步骤二、将混合溶液A和混合溶液B混合后,搅拌均匀,之后用金属丝网或四层纱布过滤得到所述标志漆。
进一步,将配制好的标志漆装入棕色玻璃瓶或金属容器进行贮存。
提供一种上述标志漆的使用方法,
⑴清理干净零件表面的污渍及灰尘;
⑵对标志漆进行稀释,稀释液为乙醇;
⑶以橡胶印章打印或手工书写的方式将标志漆涂在所述的零件上;
⑷使得标志漆在室温下进行干燥。
进一步,所述的零件为金属零件。
有益效果
解决零件标识在使用中长期存在的掉漆、不耐高温、不耐油、不耐酸碱等难题,保证机体零件在恶劣的工作环境中,零件标记能有效的存在,提供可识别性、可追溯性,有效提高飞机后勤保障能力、维护性。提升了我公司产品的质量品质和公司形象,而且在航空、兵器等国防工业中,具有广阔的推广应用价值。该涂层体系的成功应用,填补了国内的技术空白,将进一步推动相关技术领域发展,为航空科技进步作出新贡献。
附图说明
无
具体实施方式
具体提供一种标志漆的制作方法,
步骤一、室温环境下将100克的虫胶清漆加入到100毫升的乙醇内,搅拌均匀后加热至80度,使虫胶清漆充分溶解,形成混合溶液A;将10~14克的苯胺黑加入到另一份100毫升的乙醇内,搅拌均匀使其溶解,形成混合溶液B;
步骤二、将混合溶液A和混合溶液B混合后,搅拌均匀,之后用金属丝网或四层纱布过滤得到所述标志漆。
进一步,将配制好的标志漆装入棕色玻璃瓶或金属容器进行贮存。
提供一种上述标志漆的使用方法,
⑴清理干净零件表面的污渍及灰尘;
⑵对标志漆进行稀释,稀释液为乙醇;
⑶以橡胶印章打印或手工书写的方式将标志漆涂在所述的零件上;
⑷使得标志漆在室温下进行干燥。
进一步,所述的零件为金属零件。
Claims (4)
1.一种标志漆的制作方法,其特征在于,
步骤一、室温环境下将100克的虫胶清漆加入到100毫升的乙醇内,搅拌均匀后加热至80度,使虫胶清漆充分溶解,形成混合溶液A;将10~14克的苯胺黑加入到另一份100毫升的乙醇内,搅拌均匀使其溶解,形成混合溶液B;
步骤二、将混合溶液A和混合溶液B混合后,搅拌均匀,之后用金属丝网或四层纱布过滤得到所述标志漆。
2.根据权利要求1所述的标志漆的制作方法,将配制好的标志漆装入棕色玻璃瓶或金属容器进行贮存。
3.一种权利要求1-2之一的方法制作的标志漆的使用方法,其特征在于,
⑴清理干净零件表面的污渍及灰尘;
⑵对标志漆进行稀释,稀释液为乙醇;
⑶以橡胶印章打印或手工书写的方式将标志漆涂在所述的零件上;
⑷使得标志漆在室温下进行干燥。
4.根据权利要求3所述的使用方法,其特征在于,所述的零件为金属零件。