CN105524416A - 耐低温peek材料及其制备方法 - Google Patents

耐低温peek材料及其制备方法 Download PDF

Info

Publication number
CN105524416A
CN105524416A CN201510741370.5A CN201510741370A CN105524416A CN 105524416 A CN105524416 A CN 105524416A CN 201510741370 A CN201510741370 A CN 201510741370A CN 105524416 A CN105524416 A CN 105524416A
Authority
CN
China
Prior art keywords
peek
low temperature
peek material
preparation
pctfe
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201510741370.5A
Other languages
English (en)
Inventor
杨文光
陈佩民
靳予
孙克原
杨勇
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Nanjing CompTECH New Material Co., Ltd.
Nanjing Kent composites Limited by Share Ltd
NANJING RUNTE NEW MATERIAL CO., LTD.
Original Assignee
NANJING COMPTECH NEW MATERIAL CO Ltd
NANJING JIAFA MACHINERY Co Ltd
Nanjing Runte New Material Co Ltd
NANJING KENTE COMPOSITE MATERIAL CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by NANJING COMPTECH NEW MATERIAL CO Ltd, NANJING JIAFA MACHINERY Co Ltd, Nanjing Runte New Material Co Ltd, NANJING KENTE COMPOSITE MATERIAL CO Ltd filed Critical NANJING COMPTECH NEW MATERIAL CO Ltd
Priority to CN201510741370.5A priority Critical patent/CN105524416A/zh
Publication of CN105524416A publication Critical patent/CN105524416A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种耐低温PEEK材料，其特征在于由以下重量份原料组成：PEEK？70-83份；PCTFE？12-20份；PEI？5-10份。还公开了其制备方法。本发明在PEEK中加入PCTFE和PEI，可以改善其低温性能，在-100--60℃的环境中长期使用而保持韧性，防止脆变，而PEEK的其余优良性能也得以保留，制得的PEEK材料适用于极寒地区的高铁。

Description

耐低温PEEK材料及其制备方法
技术领域
本发明涉及耐低温PEEK材料及其制备方法，属于复合材料领域。
背景技术
聚醚醚酮(PEEK)是80年代开发的一种全芳香族半结晶性的热塑性材料，由于PEEK的大分子链上含有刚性的苯环、柔性醚键以及提高分子间作用的羰基，结构规整，故而具有耐高温、自润滑、易加工、机械强度高等特性。PEEK具有良好的耐化学药品性、阻燃性、耐剥离性、耐水解性、耐疲劳性、绝缘性、稳定性、耐高温等性能，还具有良好的耐磨性。因为PEEK材料的优良性能，已经广泛应用到航天航空、汽车制造、电子电气、医疗和食品等工业领域。
在极寒地区的高铁建设中，各种垫片材料的选择非常关键，垫片材料需要一直保持韧性，整个系统才会运转正常。PEEK材料在一般低温下使用性能比较出色，但长期处于-60℃低温环境会发生脆变。需要发明一种更耐寒的新材料。
发明内容
本发明的目的是提供一种耐低温PEEK材料，具有很好的耐寒性，可以在-100--60℃的环境中长期使用而保持韧性。
为达到上述目的，本发明采用的技术方案为：一种耐低温PEEK材料，其特征在于由以下重量份原料组成：
PEEK70-83份；
聚三氟乙烯(PCTFE)12-20份；
聚醚酰亚胺(PEI)5-10份。
本发明还公开了上述的耐低温PEEK材料的制备方法，其步骤包括：
A、将PEEK、PCTFE和PEI粉末分别烘干；
B、按质量比称取烘干后的粉末，放入高速混合机中混料；
C、混合粉料熔融挤出，挤出温度为380-390℃，得到成品。
本发明在PEEK中加入PCTFE和PEI，可以改善其低温性能，在-100--60℃的环境中长期使用而保持韧性，防止脆变，而PEEK的其余优良性能也得以保留，制得的PEEK材料适用于极寒地区的高铁。
具体实施方式
PEEK，粉末状，粒径500目，购自长春吉大高新材料公司。
PCTFE，粉末状，购自山东青岛宏丰氟硅科技有限。
PEI，粉末状，购自GE公司。
实施例1
本耐低温PEEK材料的制备方法，其步骤包括：
A、将PEEK、PCTFE和PEI粉末分别在110℃烘箱中烘干；
B、称取77份PEEK、15份PCTFE和8份PEI，放入高速混合机中混匀；
C、混合粉料熔融挤出，挤出温度为390℃，得到成品。
对制得的耐低温PEEK材料进行性能测试，测试结果见表1。
实施例2
本耐低温PEEK材料的制备方法，其步骤包括：
A、将PEEK、PCTFE和PEI粉末分别在110℃烘箱中烘干；
B、称取83份PEEK、12份PCTFE和5份PEI，放入高速混合机中混匀；
C、混合粉料熔融挤出，挤出温度为380℃，得到成品。
对制得的耐低温PEEK材料进行性能测试，测试结果见表1。
实施例3
本耐低温PEEK材料的制备方法，其步骤包括：
A、将PEEK、PCTFE和PEI粉末分别在110℃烘箱中烘干；
B、称取70份PEEK、20份PCTFE和10份PEI，放入高速混合机中混匀；
C、混合粉料熔融挤出，挤出温度为380℃，得到成品。
对制得的耐低温PEEK材料进行性能测试，测试结果见表1。
备注：摩擦磨损试验条件：初始负荷196N，转速200r/min,干摩擦2h。对磨轮：45钢，42-45HRC。

Claims (2)

1.一种耐低温PEEK材料，其特征在于由以下重量份原料组成：
PEEK70-83份；
PCTFE12-20份；
PEI5-10份。
2.一种权利要求1所述的耐低温PEEK材料的制备方法，其步骤包括：
A、将PEEK、PCTFE和PEI粉末分别烘干；
B、按质量比称取烘干后的粉末，放入高速混合机中混料；
C、混合粉料熔融挤出，挤出温度为380-390℃，得到成品。
CN201510741370.5A 2015-11-03 2015-11-03 耐低温peek材料及其制备方法 Pending CN105524416A (zh)