CN105461226A - Full raw crystal thick polish glaze material - Google Patents
Full raw crystal thick polish glaze material Download PDFInfo
- Publication number
- CN105461226A CN105461226A CN201510822972.3A CN201510822972A CN105461226A CN 105461226 A CN105461226 A CN 105461226A CN 201510822972 A CN201510822972 A CN 201510822972A CN 105461226 A CN105461226 A CN 105461226A
- Authority
- CN
- China
- Prior art keywords
- glaze
- crystal thick
- full raw
- raw material
- thick throwing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a full raw crystal thick polish glaze material, which is composed of the following ingredients (by weight): 20-25% of potash feldspar, 10-15% of albite, 20-25% of wollastonite, 10-15% of talcum, 7-10% of kaolin, 6-9% of quartz powder, 6-8% of zinc oxide, 8-12% of barium carbonate and 1-5% of aquamarine. As aquamarine is added into the formula of the full raw crystal thick polish glaze material and aquamarine contains natural mineral rare metal beryllium, metal beryllium can promote growth of crystalline phase during the process of sintering crystal thick polish glaze, high temperature viscosity of a glass phase during fusion process of the thick polish glaze is greatly reduced, glaze liquid is clarified, and exhausting is improved. Therefore, glaze is clear and transparent, is more transparent and brighter and has good aesthetics.
Description
Technical field
The invention belongs to glaze technical field, relate to full raw material crystal thick throwing glaze glaze.
Background technology
At present, the high temperature viscosity of the glassy phase of crystal of the prior art thick throwing glaze glaze in melting process is higher, and glaze liquid is muddy, causes the glaze paint of the crystal thick Throwing glaze burnt out bright not, thus have impact on the aesthetics of glaze paint.
Summary of the invention
The object of this invention is to provide a kind of full raw material crystal thick throwing glaze glaze, the glaze paint of the crystal thick throwing glaze after adopting this glaze to burn till is as clear as crystal, and the aesthetics of glaze paint is good.
In order to solve the problems of the technologies described above, the technical solution used in the present invention is: a kind of full raw material crystal thick throwing glaze glaze, be made up of following component by weight percentage: potassium felspar sand 20% ~ 25%, albite 10% ~ 15%, wollastonite 20% ~ 25%, talcum 10% ~ 15%, kaolin 7% ~ 10%, silica powder 6% ~ 9%, zinc oxide 6% ~ 8%, barium carbonate 8% ~ 12%, beryl 1% ~ 5%.
Preferably, each component of described full raw material crystal thick throwing glaze glaze and weight percent are: potassium felspar sand 20%, albite 10%, wollastonite 20%, talcum 13%, kaolin 10%, silica powder 8%, zinc oxide 7%, barium carbonate 9%, beryl 3%.
Preferably, described full raw material crystal thick throwing glaze glaze once-firing in roller kiln, firing temperature is 1200 DEG C.
Beneficial effect of the present invention: full raw material crystal of the present invention thick throwing glaze glaze, beryl is added in its formula, because beryl contains natural mineral rare metal beryllium, can promote that its crystalline phase is grown firing metallic beryllium in crystal thick throwing glaze process, significantly reduce the high temperature viscosity of the glassy phase of thick Throwing glaze in melting process, clarified glaze liquid, improve exhaust, thus make glaze paint as clear as crystal, more thoroughly brighter, aesthetics is good.
Embodiment
Below in conjunction with the embodiment of the present invention, be clearly and completely described the technical scheme in the embodiment of the present invention, obviously, described embodiment is only the present invention's part embodiment, instead of whole embodiments.Based on the embodiment in the present invention, those of ordinary skill in the art, not making the every other embodiment obtained under creative work prerequisite, belong to the scope of protection of the invention.
Full raw material crystal of the present invention thick throwing glaze glaze, is made up of following component by weight percentage: potassium felspar sand 20%, albite 10%, wollastonite 20%, talcum 13%, kaolin 10%, silica powder 8%, zinc oxide 7%, barium carbonate 9%, beryl 3%.This full raw material crystal thick throwing glaze glaze once-firing in roller kiln, firing temperature is 1200 DEG C.
Full raw material crystal of the present invention thick throwing glaze glaze, beryl is added in its formula, because beryl contains natural mineral rare metal beryllium, can promote that crystalline phase is grown firing metallic beryllium in crystal thick throwing glaze process, significantly reduce the high temperature viscosity of the glassy phase of the thick Throwing glaze of crystal in melting process, clarified glaze liquid, improve exhaust, thus make glaze paint as clear as crystal, more thoroughly brighter, aesthetics is better.This glaze also has following advantage: all adopt raw mineral materials formulated, decrease the high melt process of the thick Throwing glaze of traditional crystal, decrease waste gas and discharge of wastewater, thus reach the object of energy-conserving and environment-protective; The crystal that this glaze burns out thick Throwing glaze glaze volume is large, glaze thickness, and stereoeffect is remarkable, and wear-resisting acid and alkali-resistance, hardness and glossiness high, wherein wear-resistingly reach three grades, acid and alkali-resistance reaches B level, and mohs hardness reaches six grades, and glossiness is more than 100.
The foregoing is only preferred embodiment of the present invention, not in order to limit the present invention, within the spirit and principles in the present invention all, any amendment done, equivalent replacement, improvement etc., all should be included within protection scope of the present invention.
Claims (3)
1. a full raw material crystal thick throwing glaze glaze, it is characterized in that, be made up of following component by weight percentage: potassium felspar sand 20% ~ 25%, albite 10% ~ 15%, wollastonite 20% ~ 25%, talcum 10% ~ 15%, kaolin 7% ~ 10%, silica powder 6% ~ 9%, zinc oxide 6% ~ 8%, barium carbonate 8% ~ 12%, beryl 1% ~ 5%.
2. one according to claim 1 full raw material crystal thick throwing glaze glaze, it is characterized in that, each component and the weight percent of described full raw material crystal thick throwing glaze glaze are: potassium felspar sand 20%, albite 10%, wollastonite 20%, talcum 13%, kaolin 10%, silica powder 8%, zinc oxide 7%, barium carbonate 9%, beryl 3%.
3. one according to claim 1 and 2 full raw material crystal thick throwing glaze glaze, is characterized in that, described full raw material crystal thick throwing glaze glaze once-firing in roller kiln, firing temperature is 1200 DEG C.