CN105461226B - Full raw material crystal thickness throws glaze glaze - Google Patents
Full raw material crystal thickness throws glaze glaze Download PDFInfo
- Publication number
- CN105461226B CN105461226B CN201510822972.3A CN201510822972A CN105461226B CN 105461226 B CN105461226 B CN 105461226B CN 201510822972 A CN201510822972 A CN 201510822972A CN 105461226 B CN105461226 B CN 105461226B
- Authority
- CN
- China
- Prior art keywords
- glaze
- raw material
- crystal thickness
- full raw
- beryl
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention discloses a kind of full raw material crystal thickness to throw glaze glaze, it is grouped as by following group by weight percentage: potassium feldspar 20%~25%, albite 10%~15%, wollastonite 20%~25%, talcum 10%~15%, kaolin 7%~10%, silica flour 6%~9%, zinc oxide 6%~8%, barium carbonate 8%~12%, beryl 1%~5%.Full raw material crystal thickness of the present invention throws glaze glaze, it joined beryl in its formula, since beryl contains natural minerals rare metal beryllium, metallic beryllium can promote its crystal phase to develop during firing crystal thickness and throwing glaze, and the thick high temperature viscosity for throwing the glass phase of glaze in melting process is greatly lowered, has clarified glaze liquid, improve exhaust, to keep glaze paint as clear as crystal, more thoroughly brighter, aesthetics is good.
Description
Technical field
The invention belongs to glaze technical fields, are related to full raw material crystal thickness and throw glaze glaze.
Background technique
Currently, the high temperature viscosity that crystal thickness in the prior art throws the glass phase of glaze glaze in melting process is higher, glaze
Liquid is muddy, and the glaze paint for causing the crystal thickness burnt out to throw glaze is not bright enough, to affect the aesthetics of glaze paint.
Summary of the invention
The object of the present invention is to provide a kind of full raw material crystal thickness to throw glaze glaze, thick using the crystal after the firing of this glaze
The glaze paint for throwing glaze is as clear as crystal, and the aesthetics of glaze paint is good.
In order to solve the above-mentioned technical problem, the technical solution adopted by the present invention is that: a kind of full raw material crystal thickness throws glaze glaze,
It is grouped as by following group by weight percentage: potassium feldspar 20%~25%, albite 10%~15%, wollastonite 20%~
25%, talcum 10%~15%, kaolin 7%~10%, silica flour 6%~9%, zinc oxide 6%~8%, barium carbonate 8%~
12%, beryl 1%~5%.
Preferably, the full raw material crystal thickness throws each component and weight percent of glaze glaze are as follows: potassium feldspar 20%, sodium is long
Stone 10%, wollastonite 20%, talcum 13%, kaolin 10%, silica flour 8%, zinc oxide 7%, barium carbonate 9%, beryl
3%.
Preferably, the full raw material crystal thickness throws glaze glaze once-firing in roller kilns, and firing temperature is 1200 DEG C.
The invention has the advantages that: full raw material crystal thickness of the present invention to throw glaze glaze, joined green column in its formula
Stone, since beryl contains natural minerals rare metal beryllium, metallic beryllium can promote its crystal phase during firing crystal thickness and throwing glaze
Development is greatly lowered the thick high temperature viscosity for throwing the glass phase of glaze in melting process, has clarified glaze liquid, improved exhaust, from
And keep glaze paint as clear as crystal, more thoroughly brighter, aesthetics is good.
Specific embodiment
Below in conjunction with the embodiment of the present invention, technical scheme in the embodiment of the invention is clearly and completely described,
Obviously, described embodiments are only a part of the embodiments of the present invention, instead of all the embodiments.Based in the present invention
Embodiment, every other embodiment obtained by those of ordinary skill in the art without making creative efforts, all
Belong to the scope of protection of the invention.
Full raw material crystal thickness of the invention throws glaze glaze, is grouped as by following group by weight percentage: potassium feldspar 20%,
Albite 10%, wollastonite 20%, talcum 13%, kaolin 10%, silica flour 8%, zinc oxide 7%, barium carbonate 9%, green column
Stone 3%.This full raw material crystal thickness throws glaze glaze once-firing in roller kilns, and firing temperature is 1200 DEG C.
Full raw material crystal thickness of the present invention throws glaze glaze, joined beryl in its formula, since beryl contains
There is natural minerals rare metal beryllium, metallic beryllium can promote crystal phase to develop during firing crystal thickness and throwing glaze, significantly reduce water
The brilliant thick high temperature viscosity for throwing the glass phase of glaze in melting process, has clarified glaze liquid, has improved exhaust, to keep glaze paint limpid
Bright, more thoroughly brighter, aesthetics is more preferable.This glaze, which also has the advantage that, to be all formulated using raw mineral materials, and biography is reduced
Crystal thickness of uniting throws the high melt process of glaze, reduces exhaust gas and discharge of wastewater, to reach energy-saving and environment-friendly purpose;It is this
The crystal thickness throwing glaze glaze volume that glaze burns out is big, and glaze thickness, stereoscopic effect is significant, and wear-resisting acid and alkali-resistance, hardness and gloss
Degree is high, wherein wear-resisting reach three-level, acid and alkali-resistance reaches B grades, and mohs hardness reaches six grades, and glossiness is more than 100.
The foregoing is merely illustrative of the preferred embodiments of the present invention, is not intended to limit the invention, all in essence of the invention
Within mind and principle, any modification, equivalent replacement, improvement and so on be should all be included in the protection scope of the present invention.
Claims (3)
1. a kind of full raw material crystal thickness throws glaze glaze, which is characterized in that be grouped as by following group by weight percentage: potassium feldspar
20%~25%, albite 10%~15%, wollastonite 20%~25%, talcum 10%~15%, kaolin 7%~10%,
Silica flour 6%~9%, zinc oxide 6%~8%, barium carbonate 8%~12%, beryl 1%~5%.
2. a kind of full raw material crystal thickness according to claim 1 throws glaze glaze, which is characterized in that the full raw material crystal is thick
Throw each component and weight percent of glaze glaze are as follows: potassium feldspar 20%, albite 10%, wollastonite 20%, talcum 13%, kaolinite
Soil 10%, silica flour 8%, zinc oxide 7%, barium carbonate 9%, beryl 3%.
3. a kind of full raw material crystal thickness according to claim 1 or 2 throws glaze glaze, which is characterized in that the full raw material water
Brilliant thick throwing glaze glaze once-firing in roller kilns, firing temperature is 1200 DEG C.