CN104909834A - Glaze for whitening ceramics - Google Patents
Glaze for whitening ceramics Download PDFInfo
- Publication number
- CN104909834A CN104909834A CN201510265494.0A CN201510265494A CN104909834A CN 104909834 A CN104909834 A CN 104909834A CN 201510265494 A CN201510265494 A CN 201510265494A CN 104909834 A CN104909834 A CN 104909834A
- Authority
- CN
- China
- Prior art keywords
- parts
- glaze
- ceramics
- pottery
- whitening
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to glaze for whitening ceramics. The glaze is prepared from the following raw materials in parts by weight: 6-12 parts of A12O3, 7-9 parts of chromium oxide, 6-8 parts of minerals in feldspar groups, 3-5 parts of a fluxing agent, 1-4 parts of potassium feldspar, 8-13 parts of tetrabutyl titanate, 2-5 parts of sodium hydroxide, 6-11 parts of dodecyl sodium sulphate, 3-9 parts of carborundum, 2.5-6 parts of sodium pyrophosphate, 2.3-6 parts of algeldrate, 2-6 parts of barium carbonate, 1-4 parts of raw kaolin, 1-3 parts of boric acid and 2-4 parts of mineralizer sodium carbonate. The glaze for whitening the ceramics, disclosed by the invention, has the benefits that the glaze can well enhance the brightness and the lustrousness of the ceramics, besides, the glaze is uniform, and the quality of the ceramics is improved.
Description
Technical field
The present invention relates to a kind of pottery and brighten glaze.
Background technology
At present, there are architectural pottery, family up to ten thousand of snitaryware producer in China, tens thousand of production lines, thousands of family of domestic ceramics factory.Produce nearly 3,000,000,000 square metres of architectural pottery per year, snitaryware tens million of, domestic ceramics sets hundred million.In existing ceramic sintering process, the formula of ceramic glaze usually adopts the powder of the natural mineral matters such as feldspar, quartz, Wingdale, calcium carbonate, lead to be used as solvent or increases the suspension of glaze.But existing glaze is limited for the whitening effect of pottery, brightness and the glossiness of pottery well can not be improved; And glaze easily cracking phenomena occurs, cause the work-ing life of pottery low, add use cost.
Summary of the invention
For the deficiencies in the prior art, the problem to be solved in the present invention is, provides a kind of pottery to brighten glaze, and can be good at the brightness and the glossiness that strengthen pottery, glaze is even simultaneously, improves the quality of pottery.
For solving prior art problem, technical scheme provided by the invention is, a kind of pottery brightens glaze, and it is made up of the raw material of following parts by weight:
A12O36-12 part, chromic oxide 7-9 part, feldspar race mineral 6-8 part, fusing assistant 3-5 part, potassium felspar sand 1-4 part, tetrabutyl titanate 8-13 part, sodium hydroxide 2-5 part, sodium lauryl sulphate 6-11 part, silicon carbide 3-9 part, trisodium phosphate 2.5-6 part, W 4600 2.3-6 part, barium carbonate 2-6 part, Sheng Gao ridge 1-4 part, boric acid 1-3 part, mineralizer sodium carbonate 2-4 part.
The invention has the beneficial effects as follows: pottery of the present invention brightens glaze, can be good at the brightness and the glossiness that strengthen pottery, glaze is even simultaneously, improves the quality of pottery.
Embodiment
embodiment 1
A kind of pottery brightens glaze, and it is made up of the raw material of following parts by weight:
A12O36 part, 7 parts, chromic oxide, feldspar race mineral 6 parts, fusing assistant 3 parts, potassium felspar sand 1 part, tetrabutyl titanate 8 parts, 2 parts, sodium hydroxide, sodium lauryl sulphate 6 parts, 3 parts, silicon carbide, trisodium phosphate 2.5 parts, W 4600 2.3 parts, barium carbonate 2 parts, 1 part, Sheng Gao ridge, boric acid 1 part, 2 parts, mineralizer sodium carbonate.
embodiment 2
A kind of pottery brightens glaze, and it is made up of the raw material of following parts by weight:
A12O312 part, 9 parts, chromic oxide, feldspar race mineral 8 parts, fusing assistant 5 parts, potassium felspar sand 4 parts, tetrabutyl titanate 13 parts, 5 parts, sodium hydroxide, sodium lauryl sulphate 11 parts, 9 parts, silicon carbide, trisodium phosphate 6 parts, W 4600 6 parts, barium carbonate 6 parts, 4 parts, Sheng Gao ridge, boric acid 3 parts, 4 parts, mineralizer sodium carbonate.
Claims (1)
1. pottery brightens a glaze, it is characterized in that: it is made up of the raw material of following parts by weight:
A12O36-12 part, chromic oxide 7-9 part, feldspar race mineral 6-8 part, fusing assistant 3-5 part, potassium felspar sand 1-4 part, tetrabutyl titanate 8-13 part, sodium hydroxide 2-5 part, sodium lauryl sulphate 6-11 part, silicon carbide 3-9 part, trisodium phosphate 2.5-6 part, W 4600 2.3-6 part, barium carbonate 2-6 part, Sheng Gao ridge 1-4 part, boric acid 1-3 part, mineralizer sodium carbonate 2-4 part.