CN105439611A - 一种抗冻自清洁透水砖及其制作方法 - Google Patents

一种抗冻自清洁透水砖及其制作方法 Download PDF

Info

Publication number
CN105439611A
CN105439611A CN201510762394.9A CN201510762394A CN105439611A CN 105439611 A CN105439611 A CN 105439611A CN 201510762394 A CN201510762394 A CN 201510762394A CN 105439611 A CN105439611 A CN 105439611A
Authority
CN
China
Prior art keywords
dry
water permeable
water
permeable bricks
cleaning water
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Withdrawn
Application number
CN201510762394.9A
Other languages
English (en)
Inventor
李诺
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Hefei Linuo New Materials Trade Co Ltd
Original Assignee
Hefei Linuo New Materials Trade Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Hefei Linuo New Materials Trade Co Ltd filed Critical Hefei Linuo New Materials Trade Co Ltd
Priority to CN201510762394.9A priority Critical patent/CN105439611A/zh
Publication of CN105439611A publication Critical patent/CN105439611A/zh
Withdrawn legal-status Critical Current

Abstract

本发明公开了一种抗冻自清洁透水砖,本发明将蓝藻干粉、芦苇杆炭化处理后经室温研磨,孔隙表面吸附光催化材料纳米二氧化钛,经光照射时生成羟基自由基、超氧离子自由基以及H2O自由基均具有很强的氧化、分解能力,将各种有机物直接氧化为CO2和H2O等无机小分子,应用于透水砖中不仅可以降解大气中的汽车尾气等,还具有较强的吸附性,本发明以改性糖滤泥为成孔剂,锆莫来石、钠基膨润土为骨料,添加聚苯乙烯泡沫微粒、氧化石墨烯等成分,经高温烧结后制得的透水砖孔隙率大自清洁效果优,具有抗冻、透水性好、实现废渣再利用的优点。

Description

一种抗冻自清洁透水砖及其制作方法
技术领域
本发明涉及建筑材料技术领域,尤其涉及一种抗冻自清洁透水砖及其制作方法。
背景技术
随着城市水资源的不断匾乏,以及城市环境人性化的追求,透水砖的研发引起了材料、环境和市政工程专家的广泛关注。透水砖具有良好的渗水性及保湿性,能很好的缓解城市由于被非透水地面铺装覆盖造成的“城市荒漠化”及“热岛效应”,还可以在一定程度上缓解城市内涝,补充城市地下水,调节城市环境,有利于保持城市水平衡。现有的透水砖向高密实、高强度方向发展,其抗压强度比较高,但依然存在诸多缺陷,一方面是透水性非常差,即使有透水性能好的砖块,但其抗压强度达不到路面铺装要求,同时透水砖经过长期使用,表面以及孔隙很容易落入各种污物形成堵塞而不能自动清除,削弱了透水效果,生态效果较差,并且使用中对排水设施的要求较高,如遇到雨后排水不畅的情况发生,则易产生积水问题。另一方面现有的技术生产的透水砖功能较为单一,它们只是简单的使降水透过砖体渗入地下,不能有效去除水中所含污染物,对透过砖体的污水起不到净化作用。为解决这些问题,需要开发一种新型的同时具有透水和净化功能的自清洁透水砖。
发明内容
本发明目的就是为了弥补已有技术的缺陷,提供一种抗冻自清洁透水砖及其制作方法。
本发明是通过以下技术方案实现的:
一种抗冻自清洁透水砖,由下列重量份的原料制成:锆莫来石25-27、钠基膨润土32-34、水泥10-11、糖滤泥23-25、聚苯乙烯泡沫微粒5-7、明矾1-3、柴油4-6、纳米二氧化钛0.5-0.7、铜纤维3-4、锆乳胶6-8、氧化石墨烯1-2、蓝藻干粉16-19、芦苇杆3-5、适量水。
所述的一种抗冻自清洁透水砖的制作方法,包括以下步骤:
(1)将蓝藻干粉、芦苇杆烘干放入炭化炉中于450-500℃的温度下,隔绝空气炭化20-30分钟,冷却至室温加入纳米二氧化钛、铜纤维、柴油研磨40-50分钟,烘干;
(2)将糖滤泥水洗后于50-60℃温度下烘干,送入高速混合机中加入聚苯乙烯泡沫微粒、明矾、锆乳胶和适量的水,以1400-1500转/min的速度高速搅拌15-20分钟,干燥,超声研磨成粉烘干;
(3)将锆莫来石、钠基膨润土于728-830℃高温煅烧处理后粉碎至120-140目,加入步骤(1)、(2)物料及其他剩余成分混匀,投入球磨机中球磨2-3小时,喷水造粒、陈化2天后压制成生砖坯;
(4)将生砖坯自然晾晒风干,在箱式电阻炉中于1060-1100℃烧结1-2小时,自然冷却至室温出料。
本发明的优点是:本发明将蓝藻干粉、芦苇杆炭化处理后经室温研磨,孔隙表面吸附光催化材料纳米二氧化钛,经光照射时生成羟基自由基、超氧离子自由基以及H2O自由基均具有很强的氧化、分解能力,将各种有机物直接氧化为CO2和H2O等无机小分子,应用于透水砖中不仅可以降解大气中的汽车尾气等,还具有较强的吸附性,本发明以改性糖滤泥为成孔剂,锆莫来石、钠基膨润土为骨料,添加聚苯乙烯泡沫微粒、氧化石墨烯等成分,经高温烧结后制得的透水砖孔隙率大自清洁效果优,具有抗冻、透水性好、实现废渣再利用的优点。
具体实施方式
一种抗冻自清洁透水砖,由下列重量份的原料制成:锆莫来石25、钠基膨润土32、水泥10、糖滤泥23、聚苯乙烯泡沫微粒5、明矾1、柴油4、纳米二氧化钛0.5、铜纤维3、锆乳胶6、氧化石墨烯1、蓝藻干粉16、芦苇杆3、适量水。
所述的一种抗冻自清洁透水砖的制作方法,包括以下步骤:
(1)将蓝藻干粉、芦苇杆烘干放入炭化炉中于450℃的温度下,隔绝空气炭化20分钟,冷却至室温加入纳米二氧化钛、铜纤维、柴油研磨40分钟,烘干;
(2)将糖滤泥水洗后于50℃温度下烘干,送入高速混合机中加入聚苯乙烯泡沫微粒、明矾、锆乳胶和适量的水,以1400转/min的速度高速搅拌15分钟,干燥,超声研磨成粉烘干;
(3)将锆莫来石、钠基膨润土于728℃高温煅烧处理后粉碎至120目,加入步骤(1)、(2)物料及其他剩余成分混匀,投入球磨机中球磨2小时,喷水造粒、陈化2天后压制成生砖坯;
(4)将生砖坯自然晾晒风干,在箱式电阻炉中于1060℃烧结1小时,自然冷却至室温出料。
使用本发明生产的自清洁透水砖的技术参数指标如下:透水砖的抗压强度可达34.7MPa,抗折强度达3.47MPa,透水系数为0.46cm/s。

Claims (2)

1.一种抗冻自清洁透水砖,其特征在于,由下列重量份的原料制成:锆莫来石25-27、钠基膨润土32-34、水泥10-11、糖滤泥23-25、聚苯乙烯泡沫微粒5-7、明矾1-3、柴油4-6、纳米二氧化钛0.5-0.7、铜纤维3-4、锆乳胶6-8、氧化石墨烯1-2、蓝藻干粉16-19、芦苇杆3-5、适量水。
2.根据权利要求1所述的一种抗冻自清洁透水砖的制作方法,其特征在于包括以下步骤:
(1)将蓝藻干粉、芦苇杆烘干放入炭化炉中于450-500℃的温度下,隔绝空气炭化20-30分钟,冷却至室温加入纳米二氧化钛、铜纤维、柴油研磨40-50分钟,烘干;
(2)将糖滤泥水洗后于50-60℃温度下烘干,送入高速混合机中加入聚苯乙烯泡沫微粒、明矾、锆乳胶和适量的水,以1400-1500转/min的速度高速搅拌15-20分钟,干燥,超声研磨成粉烘干;
(3)将锆莫来石、钠基膨润土于728-830℃高温煅烧处理后粉碎至120-140目,加入步骤(1)、(2)物料及其他剩余成分混匀,投入球磨机中球磨2-3小时,喷水造粒、陈化2天后压制成生砖坯;
(4)将生砖坯自然晾晒风干,在箱式电阻炉中于1060-1100℃烧结1-2小时,自然冷却至室温出料。
CN201510762394.9A 2015-11-11 2015-11-11 一种抗冻自清洁透水砖及其制作方法 Withdrawn CN105439611A (zh)