CN105400197A - 一种聚苯硫醚复合材料 - Google Patents

一种聚苯硫醚复合材料 Download PDF

Info

Publication number
CN105400197A
CN105400197A CN201510968599.2A CN201510968599A CN105400197A CN 105400197 A CN105400197 A CN 105400197A CN 201510968599 A CN201510968599 A CN 201510968599A CN 105400197 A CN105400197 A CN 105400197A
Authority
CN
China
Prior art keywords
polyphenylene sulfide
composite material
parts
compatilizer
polyphenyl thioether
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201510968599.2A
Other languages
English (en)
Inventor
杨磊
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Hefei Zhongnong Biotechnology Co Ltd
Original Assignee
Hefei Zhongnong Biotechnology Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Hefei Zhongnong Biotechnology Co Ltd filed Critical Hefei Zhongnong Biotechnology Co Ltd
Priority to CN201510968599.2A priority Critical patent/CN105400197A/zh
Publication of CN105400197A publication Critical patent/CN105400197A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种聚苯硫醚复合材料，按重量份数计，包括43~57份的聚苯硫醚，33~41份的玻璃纤维，15~25份的相容剂，3~9份的加工助剂。本发明材料显著改善了聚苯硫醚的韧性不足的缺点，复合材料的力学性能得到极大提高，工艺成本大幅度降低，有益于其市场推广与应用。

Description

一种聚苯硫醚复合材料
技术领域
本发明涉及复合材料领域，尤其涉及一种聚苯硫醚复合材料。
背景技术
聚苯硫醚(PPS)又称聚苯撑硫、聚次苯基硫醚，1968年由美国首创并投产的一种新型特种工程塑料。由于其分子结构特殊性使得其具有许多独特的性能，主要表现在：优良的热稳定性、化学稳定性、尺寸稳定性、耐腐蚀性、良好的粘接性能、优良的阻燃性、良好的电性能、可共混改性。目前在汽车制造、电子电气、化工、仪器仪表和航天工业等方面具有广泛的应用。但聚苯硫醚也有较明显的缺点：韧性较差，合成成本高，这就给其市场推广带来了一定得困扰。
发明内容
本发明的目的在于克服现有技术存在的以上问题，提供一种聚苯硫醚复合材料，满足市场的基本需求。
为实现上述技术目的，达到上述技术效果，本发明通过以下技术方案实现：
一种聚苯硫醚复合材料，按重量份数计，包括43~57份的聚苯硫醚，33~41份的玻璃纤维，15~25份的相容剂，3~9份的加工助剂。
进一步地，所述聚苯硫醚、玻璃纤维、相容剂、加工助剂中还添加有抗氧剂。
进一步地，所述聚苯硫醚混合添加有聚四氟乙烯。
进一步地，所述相容剂为环氧型反应型相容剂。
进一步地，所述复合材料制备方法包括以下步骤：将聚苯硫醚预干燥后与玻璃纤维、相容剂、加工助剂经高速混合机混合均匀，再通过挤出机挤出造粒且造粒温度为270~290℃，挤出后经120℃风干12小时最终由注塑机注塑成型。
本发明的有益效果是：
本发明材料显著改善了聚苯硫醚的韧性不足的的缺点，复合材料的力学性能得到极大提高，工艺成本大幅度降低，有益于其市场推广与应用。
具体实施方式
下面将结合实施例，来详细说明本发明。
一种聚苯硫醚复合材料，按重量份数计，包括43~57份的聚苯硫醚，33~41份的玻璃纤维，15~25份的相容剂，3~9份的加工助剂。
其中，聚苯硫醚、玻璃纤维、相容剂、加工助剂中还添加有抗氧剂。
其中，聚苯硫醚混合添加有聚四氟乙烯。
其中，相容剂为环氧型反应型相容剂。
其中，复合材料制备方法包括以下步骤：将聚苯硫醚预干燥后与玻璃纤维、相容剂、加工助剂经高速混合机混合均匀，再通过挤出机挤出造粒且造粒温度为270~290℃，挤出后经120℃风干12小时最终由注塑机注塑成型。
以上显示和描述了本发明的基本原理、主要特征和本发明的优点。本行业的技术人员应该了解，本发明不受上述实施例的限制，上述实施例和说明书中描述的只是说明本发明的原理，在不脱离本发明精神和范围的前提下，本发明还会有各种变化和改进，这些变化和改进都落入要求保护的本发明范围内。

Claims (5)

1.一种聚苯硫醚复合材料，其特征在于：按重量份数计，包括43~57份的聚苯硫醚，33~41份的玻璃纤维，15~25份的相容剂，3~9份的加工助剂。
2.根据权利要求1所述的一种聚苯硫醚复合材料，其特征在于：所述聚苯硫醚、玻璃纤维、相容剂、加工助剂中还添加有抗氧剂。
3.根据权利要求1所述的一种聚苯硫醚复合材料，其特征在于：所述聚苯硫醚混合添加有聚四氟乙烯。
4.根据权利要求1所述的一种聚苯硫醚复合材料，其特征在于：所述相容剂为环氧型反应型相容剂。
5.根据权利要求1所述的一种聚苯硫醚复合材料，其特征在于：所述复合材料制备方法包括以下步骤：将聚苯硫醚预干燥后与玻璃纤维、相容剂、加工助剂经高速混合机混合均匀，再通过挤出机挤出造粒且造粒温度为270~290℃，挤出后经120℃风干12小时最终由注塑机注塑成型。
CN201510968599.2A 2015-12-22 2015-12-22 一种聚苯硫醚复合材料 Pending CN105400197A (zh)